WO2019066203A1 - Composé permettant d'améliorer les propriétés d'adhérence d'une résine de polyimide et copolymère de polyimide produit à l'aide de celui-ci - Google Patents

Composé permettant d'améliorer les propriétés d'adhérence d'une résine de polyimide et copolymère de polyimide produit à l'aide de celui-ci Download PDF

Info

Publication number
WO2019066203A1
WO2019066203A1 PCT/KR2018/007267 KR2018007267W WO2019066203A1 WO 2019066203 A1 WO2019066203 A1 WO 2019066203A1 KR 2018007267 W KR2018007267 W KR 2018007267W WO 2019066203 A1 WO2019066203 A1 WO 2019066203A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyimide
formula
compound
independently
carbon atoms
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2018/007267
Other languages
English (en)
Korean (ko)
Inventor
윤철민
김경준
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LG Chem Ltd
Original Assignee
LG Chem Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from KR1020180072773A external-priority patent/KR102178216B1/ko
Application filed by LG Chem Ltd filed Critical LG Chem Ltd
Priority to US16/492,012 priority Critical patent/US11773117B2/en
Priority to EP18862503.2A priority patent/EP3567046B1/fr
Priority to CN201880020672.5A priority patent/CN110461857B/zh
Priority to JP2019541765A priority patent/JP6852852B2/ja
Publication of WO2019066203A1 publication Critical patent/WO2019066203A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un nouvel amplificateur d'adhérence de résine de polyimide ayant une structure de fluorène, un film de polyimide produit à l'aide de celui-ci présentant des propriétés classiques telles qu'une résistance thermique et des propriétés mécaniques, et maintient l'adhérence avec un substrat de support tout en n'étant pas affecté par rapport au retard même pendant un processus à haute température.
PCT/KR2018/007267 2017-09-28 2018-06-27 Composé permettant d'améliorer les propriétés d'adhérence d'une résine de polyimide et copolymère de polyimide produit à l'aide de celui-ci Ceased WO2019066203A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
US16/492,012 US11773117B2 (en) 2017-09-28 2018-06-27 Compound for enhancing adhesion properties of polyimide resin and polyimide copolymer produced using same
EP18862503.2A EP3567046B1 (fr) 2017-09-28 2018-06-27 Copolymère de polyimide produit à l'aide d'un composé permettant d'améliorer les propriétés d'adhérence d'une résine de polyimide
CN201880020672.5A CN110461857B (zh) 2017-09-28 2018-06-27 用于提高聚酰亚胺树脂的粘合特性的化合物和使用其制备的聚酰亚胺共聚物
JP2019541765A JP6852852B2 (ja) 2017-09-28 2018-06-27 ポリイミド樹脂の接着性を増進させる化合物及びそれを用いて製造されたポリイミド共重合体

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
KR10-2017-0125671 2017-09-28
KR20170125671 2017-09-28
KR1020180072773A KR102178216B1 (ko) 2017-09-28 2018-06-25 폴리이미드 수지의 접착성을 증진시키는 화합물 및 이를 이용하여 제조된 폴리이미드 공중합체
KR10-2018-0072773 2018-06-25

Publications (1)

Publication Number Publication Date
WO2019066203A1 true WO2019066203A1 (fr) 2019-04-04

Family

ID=65903603

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2018/007267 Ceased WO2019066203A1 (fr) 2017-09-28 2018-06-27 Composé permettant d'améliorer les propriétés d'adhérence d'une résine de polyimide et copolymère de polyimide produit à l'aide de celui-ci

Country Status (1)

Country Link
WO (1) WO2019066203A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2025143694A1 (fr) * 2023-12-29 2025-07-03 피아이첨단소재 주식회사 Composition de polyimide comprenant un solvant écologique et vernis polyimide pour affichage produit à partir de celle-ci

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4923948A (en) * 1987-09-24 1990-05-08 Japan Synthetic Rubber Co., Ltd. Curable composition
US5061809A (en) * 1990-05-25 1991-10-29 Air Products And Chemicals, Inc. 9,9-bis-(3,4-dicarboxyphenyl)fluorene dianhydrides
US20150368402A1 (en) * 2013-02-07 2015-12-24 Kaneka Corporation Alkoxysilane-modified polyamic acid solution, laminate and flexible device each produced using same, and method for producing laminate
KR20160097685A (ko) * 2015-02-09 2016-08-18 주식회사 엘지화학 폴리이미드계 필름 형성용 조성물 및 이를 이용하여 제조된 폴리이미드계 필름
KR20170057458A (ko) * 2014-12-24 2017-05-24 유니티카 가부시끼가이샤 다공질 폴리이미드 필름 및 그의 제조 방법
KR20170125671A (ko) 2016-05-06 2017-11-15 안규환 로또, 신용카드, 치매 진단, 암 진단 과이용(과몰입) 위험 상시 자가 예방 방법과 그 시스템
KR20180072773A (ko) 2015-10-19 2018-06-29 지.디 쏘씨에타'퍼 아지오니 실질적으로 원통형 물품을 제조하기 위한 기계

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4923948A (en) * 1987-09-24 1990-05-08 Japan Synthetic Rubber Co., Ltd. Curable composition
US5061809A (en) * 1990-05-25 1991-10-29 Air Products And Chemicals, Inc. 9,9-bis-(3,4-dicarboxyphenyl)fluorene dianhydrides
US20150368402A1 (en) * 2013-02-07 2015-12-24 Kaneka Corporation Alkoxysilane-modified polyamic acid solution, laminate and flexible device each produced using same, and method for producing laminate
KR20170057458A (ko) * 2014-12-24 2017-05-24 유니티카 가부시끼가이샤 다공질 폴리이미드 필름 및 그의 제조 방법
KR20160097685A (ko) * 2015-02-09 2016-08-18 주식회사 엘지화학 폴리이미드계 필름 형성용 조성물 및 이를 이용하여 제조된 폴리이미드계 필름
KR20180072773A (ko) 2015-10-19 2018-06-29 지.디 쏘씨에타'퍼 아지오니 실질적으로 원통형 물품을 제조하기 위한 기계
KR20170125671A (ko) 2016-05-06 2017-11-15 안규환 로또, 신용카드, 치매 진단, 암 진단 과이용(과몰입) 위험 상시 자가 예방 방법과 그 시스템

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2025143694A1 (fr) * 2023-12-29 2025-07-03 피아이첨단소재 주식회사 Composition de polyimide comprenant un solvant écologique et vernis polyimide pour affichage produit à partir de celle-ci

Similar Documents

Publication Publication Date Title
WO2019054616A1 (fr) Copolymère de polyimide et film de polyimide utilisant celui-ci
WO2015183056A1 (fr) Liquide à base de polyimide et film à base de polyimide produit en l'utilisant
WO2019054612A1 (fr) Composition de précurseur de polyimide et film de polyimide utilisant ladite composition
WO2017111299A1 (fr) Composition d'acide polyamique ayant une force adhésive supérieure et film de polyimide comprenant la composition
WO2018056573A1 (fr) Solution de précurseur de polyamide et procédé pour sa production
WO2017209414A1 (fr) Polyamidimide transparent à haute résistance et son procédé de préparation
WO2018080222A2 (fr) Composition de formation de film polyimide et film polyimide ainsi produit
WO2019235712A1 (fr) Composé siloxane et composition précurseur de polyimide le comprenant
WO2017188630A1 (fr) Polyamide-imide transparent de haute résistance et son procédé de fabrication
WO2017047917A1 (fr) Polyimide modifié et composition de résine durcissable le contenant
WO2018038436A1 (fr) Composé diamine et son procédé de production
WO2019103274A1 (fr) Film de polyimide pour substrat d'écran
WO2020159085A1 (fr) Film de résine polyamide, et stratifié de résine faisant appel à celui-ci
WO2020138645A1 (fr) Composition d'acide polyamique et film de polyimide transparent l'utilisant
WO2022145890A1 (fr) Film optique présentant des propriétés optiques améliorées, appareil d'affichage le comprenant et procédé de fabrication associé
WO2016140559A1 (fr) Composition de film polyimide pour substrat souple de dispositif optoélectronique
WO2020141713A1 (fr) Procédé de préparation d'une composition d'acide polyamique contenant un nouveau composé dicarbonylé, composition d'acide polyamique, procédé de fabrication d'un film de polyamide-imide l'utilisant et film de polyamide-imide produit par le même procédé de fabrication
WO2020159193A1 (fr) Composition de précurseur de polyimide et film de polyimide, substrat pour dispositif d'affichage, et dispositif optique, chacun fabriqué à partir de celle-ci
WO2020209625A1 (fr) Copolymère séquencé de polyamide-imide, son procédé de préparation et film polyamide-imide le comprenant
WO2020159035A1 (fr) Film de polyimide, substrat souple l'utilisant, et dispositif d'affichage souple comprenant un substrat souple
WO2010008213A2 (fr) Composé à base de silane, procédé de préparation de ce dernier et composition d'agent de traitement de surface pour feuille de cuivre comprenant le composé à base de silane
WO2019066203A1 (fr) Composé permettant d'améliorer les propriétés d'adhérence d'une résine de polyimide et copolymère de polyimide produit à l'aide de celui-ci
WO2018021747A1 (fr) Solution de précurseur de polyimide et procédé de production associé
WO2016021746A1 (fr) Film mince de polyimide incolore et transparent ayant un facteur de transmission élevé et une faible différence de phase, et son procédé de fabrication
WO2018147617A1 (fr) Film de polyamide-imide et son procédé de production

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18862503

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2019541765

Country of ref document: JP

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 2018862503

Country of ref document: EP

Effective date: 20190808

NENP Non-entry into the national phase

Ref country code: DE