WO2019052670A1 - Fabrication de nanostructures composites - Google Patents

Fabrication de nanostructures composites Download PDF

Info

Publication number
WO2019052670A1
WO2019052670A1 PCT/EP2017/073515 EP2017073515W WO2019052670A1 WO 2019052670 A1 WO2019052670 A1 WO 2019052670A1 EP 2017073515 W EP2017073515 W EP 2017073515W WO 2019052670 A1 WO2019052670 A1 WO 2019052670A1
Authority
WO
WIPO (PCT)
Prior art keywords
plasma
particles
core
carbon nanotubes
core particles
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2017/073515
Other languages
English (en)
Inventor
Adam Meyer BOIES
Michael Franciscus DE VOLDER
Jean Leclerc DE LA VERPILLIERE
Brian Graves
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Cambridge Enterprise Ltd
Original Assignee
Cambridge Enterprise Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Cambridge Enterprise Ltd filed Critical Cambridge Enterprise Ltd
Priority to PCT/EP2017/073515 priority Critical patent/WO2019052670A1/fr
Publication of WO2019052670A1 publication Critical patent/WO2019052670A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Des particules nanostructurées composites comprennent chacune au moins une particule de noyau et des nanotubes de carbone, les nanotubes de carbone étant ancrés à une extrémité sur ladite particule de noyau. Les particules nanostructurées composites sont fabriquées par l'intermédiaire d'un procédé comprenant les étapes consistant à : générer un plasma dans une chambre à plasma ; ajouter un matériau précurseur de particules de noyau dans le plasma pour vaporiser le matériau précurseur de particules de noyau à l'aide du plasma ; faire s'écouler le matériau précurseur de particules de noyau vaporisé à l'opposé du plasma pour permettre la nucléation et la croissance de particules de noyau à partir du matériau précurseur de particules de noyau vaporisé ; et ajouter un matériau précurseur de nanotubes de carbone aux particules de noyau dans des conditions permettant de provoquer la croissance de nanomatériaux de carbone à partir des particules de noyau.
PCT/EP2017/073515 2017-09-18 2017-09-18 Fabrication de nanostructures composites Ceased WO2019052670A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/EP2017/073515 WO2019052670A1 (fr) 2017-09-18 2017-09-18 Fabrication de nanostructures composites

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/EP2017/073515 WO2019052670A1 (fr) 2017-09-18 2017-09-18 Fabrication de nanostructures composites

Publications (1)

Publication Number Publication Date
WO2019052670A1 true WO2019052670A1 (fr) 2019-03-21

Family

ID=59923431

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2017/073515 Ceased WO2019052670A1 (fr) 2017-09-18 2017-09-18 Fabrication de nanostructures composites

Country Status (1)

Country Link
WO (1) WO2019052670A1 (fr)

Cited By (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019243614A1 (fr) 2018-06-21 2019-12-26 Cambridge Enterprise Limited Matériaux actifs d'électrode et leur procédé de fabrication
CN112209362A (zh) * 2020-09-27 2021-01-12 电子科技大学 一种等离子体诱导活化氟化碳的方法及锂一次电池制备
US11590568B2 (en) 2019-12-19 2023-02-28 6K Inc. Process for producing spheroidized powder from feedstock materials
US11633785B2 (en) 2019-04-30 2023-04-25 6K Inc. Mechanically alloyed powder feedstock
US11717886B2 (en) 2019-11-18 2023-08-08 6K Inc. Unique feedstocks for spherical powders and methods of manufacturing
US11839919B2 (en) 2015-12-16 2023-12-12 6K Inc. Spheroidal dehydrogenated metals and metal alloy particles
US11919071B2 (en) 2020-10-30 2024-03-05 6K Inc. Systems and methods for synthesis of spheroidized metal powders
US11963287B2 (en) 2020-09-24 2024-04-16 6K Inc. Systems, devices, and methods for starting plasma
US12040162B2 (en) 2022-06-09 2024-07-16 6K Inc. Plasma apparatus and methods for processing feed material utilizing an upstream swirl module and composite gas flows
US12042861B2 (en) 2021-03-31 2024-07-23 6K Inc. Systems and methods for additive manufacturing of metal nitride ceramics
US12094688B2 (en) 2022-08-25 2024-09-17 6K Inc. Plasma apparatus and methods for processing feed material utilizing a powder ingress preventor (PIP)
US12176529B2 (en) 2020-06-25 2024-12-24 6K Inc. Microcomposite alloy structure
US12195338B2 (en) 2022-12-15 2025-01-14 6K Inc. Systems, methods, and device for pyrolysis of methane in a microwave plasma for hydrogen and structured carbon powder production
US12214420B2 (en) 2015-12-16 2025-02-04 6K Inc. Spheroidal titanium metallic powders with custom microstructures
US12261023B2 (en) 2022-05-23 2025-03-25 6K Inc. Microwave plasma apparatus and methods for processing materials using an interior liner
US12311447B2 (en) 2018-06-19 2025-05-27 6K Inc. Process for producing spheroidized powder from feedstock materials
US12406829B2 (en) 2021-01-11 2025-09-02 6K Inc. Methods and systems for reclamation of Li-ion cathode materials using microwave plasma processing

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008166013A (ja) * 2006-12-27 2008-07-17 Matsushita Electric Ind Co Ltd 複合活物質およびそれを用いた電気化学素子
US8628747B2 (en) 2005-07-07 2014-01-14 University Of Maryland College Park Carbon nanotube structures formed on large free floating substrates
US20170069916A1 (en) * 2015-09-03 2017-03-09 Korea Institute Of Energy Research Metal oxide-carbon nanomaterial composite, method of preparing the same, catalyst, method of preparing the same, and catalyst layer for fuel cell electrodes

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8628747B2 (en) 2005-07-07 2014-01-14 University Of Maryland College Park Carbon nanotube structures formed on large free floating substrates
JP2008166013A (ja) * 2006-12-27 2008-07-17 Matsushita Electric Ind Co Ltd 複合活物質およびそれを用いた電気化学素子
US20170069916A1 (en) * 2015-09-03 2017-03-09 Korea Institute Of Energy Research Metal oxide-carbon nanomaterial composite, method of preparing the same, catalyst, method of preparing the same, and catalyst layer for fuel cell electrodes

Non-Patent Citations (39)

* Cited by examiner, † Cited by third party
Title
A. VELON; I. OLEFJORD: "Oxidation Behavior of Ni3AI and Fe3AI: I. XPS Calibrations of Pure Compounds and Quantification of the Results", OXID. MET., vol. 56, 2001, pages 415 - 424
A.B.D. NANDIYANTO; Y. KAIHATSU; F. ISKANDAR; K. OKUYAMA: "Rapid synthesis of a BN/CNT composite particle via spray routes using ferrocene/ethanol as a catalyst/carbon source", MATER. LETT., vol. 63, 2009, pages 1847 - 1850, XP026250816, DOI: doi:10.1016/j.matlet.2009.05.052
A.C. TURNOCK; H.P. EUGSTER: "Fe-AI oxides: Phase relationships below 1000° C", J. PETROL., vol. 3, 1962, pages 533 - 565
B. GRAVES; J. OLFERT; B. PATYCHUK; R. DASTANPOUR; S. ROGAK: "Characterization of Particulate Matter Morphology and Volatility from a Compression-Ignition Natural-Gas Direct-Injection Engine", AEROSOL SCI. TECHNOL., vol. 49, 2015, pages 589 - 598
CABANA, J.; MONCONDUIT, L.; LARCHER, D.; PALACIN, M. R., ADV. MATER., vol. 22, no. 35, 2010
D. GONZALEZ; A.G. NASIBULIN; A.M. BAKLANOV; S.D. SHANDAKOV; D.P. BROWN; P. QUEIPO: "E.I. Kauppinen, A New Thermophoretic Precipitator for Collection of Nanometer-Sized Aerosol Particles", AEROSOL SCI. TECHNOL., vol. 39, 2005, pages 1064 - 1071
D. HE; H. LI; W. LI; P. HAGHI-ASHTIANI; P. LEJAY; J. BAI: "Growth of carbon nanotubes in six orthogonal directions on spherical alumina microparticles", CARBON N. Y., vol. 49, 2011, pages 2273 - 2286, XP028368356, DOI: doi:10.1016/j.carbon.2011.01.060
D. HE; M. BOZLAR; M. GENESTOUX; J. BAI: "Diameter- and length-dependent self-organizations of multi-walled carbon nanotubes on spherical alumina microparticles", CARBON N. Y., vol. 48, 2010, pages 1159 - 1170, XP026859559
F.S. BOI; G. MOUNTJOY; M. BAXENDALE: "Boundary layer chemical vapor synthesis of self-organized radial filled-carbon-nanotube structures", CARBON N. Y., vol. 64, 2013, pages 516 - 526, XP028708255, DOI: doi:10.1016/j.carbon.2013.08.001
G. ALAN; C. RODRIGUEZ; G. GARC; M. ISABEL; M. PALMA; K. DAS ROY; A. MARIA; G. HERNANDEZ, SYNTHESIS AND CHARACTERIZATION OF HERCYNITE NANOPARTICLES BY PULSED LASER ABLATION IN LIQUID TECHNIQUE, vol. 43, 2015, pages 34 - 43
GLAIZE, C.; GENIES, S.: "Lithium Batteries and Other Electrochemical Storage Systems", 2013, WILEY
HAN, Z. H.; YANG, B.; KIM, S. H.; ZACHARIAH, M. R.: "Application of hybrid sphere/carbon nanotube particles in nanofluids", NANOTECHNOLOGY, vol. 18, no. 10, 2007, pages 105701, XP020118878, DOI: doi:10.1088/0957-4484/18/10/105701
J. CABANA; L. MONCONDUIT; D. LARCHER; M.R. PALACIN: "Beyond intercalation-based Li-ion batteries: The state of the art and challenges of electrode materials reacting through conversion reactions", ADV. MATER., vol. 22, 2010, XP055150871, DOI: doi:10.1002/adma.201000717
J.H. KIM; J.Y. AHN; S.H. KIM, AEROSOL SYNTHESIS AND OPTICAL IGNITION OF SEA URCHIN-LIKE CARBON NANOTUBE-NANOENERGETIC COMPOSITE MATERIALS, 2014, pages 2014
J.S. OLFERT; N. COLLINGS: "New method for particle mass classification - The Couette centrifugal particle mass analyzer", J. AEROSOL SCI., vol. 36, 2005, pages 1338 - 1352, XP005124375, DOI: doi:10.1016/j.jaerosci.2005.03.006
KIM, J. H.; AHN, J. Y.; KIM, S. H., AEROSOL SYNTHESIS AND OPTICAL IGNITION OF SEA URCHIN-LIKE CARBON NANOTUBE-NANOENERGETIC COMPOSITE MATERIALS, no. 2014, 2014
KIM, S. H.; WANG, C.; ZACHARIAH, M. R.: "Aerosol formation of Sea-Urchin-like nanostructures of carbon nanotubes on bimetallic nanocomposite particles", JOURNAL OF NANOPARTICLE RESEARCH, vol. 13, no. 1, 2011, pages 139 - 146, XP019878150, DOI: doi:10.1007/s11051-010-0011-6
LIANG, X.; HART, C.; PANG, Q.; GARSUCH, A.; WEISS, T.; NAZAR, L. F., NAT. COMMUN., vol. 6, 2015, pages 5682
LIN, J.; RAJI, A. R. O.; NAN, K. W.; PENG, Z. W.; YAN, Z.; SAMUEL, E. L. G.; NATELSON, D.; TOUR, J. M., ADV. FUNCT. MATER., vol. 24, no. 14, 2014, pages 2044 - 2048
LIU, N.; LU, Z.; ZHAO, J.; MCDOWELL, M. T.; LEE, H.-W.; ZHAO, W.; CUI, Y., NAT. NANOTECHNOL., vol. 9, no. 3, 2014, pages 187 - 192
M. HAN; W. ZHANG; C. GAO; Y. LIANG; Z. XU; J. ZHU; J. HE: "Hollow nickel microspheres covered with oriented carbon nanotubes and its magnetic property", CARBON N. Y., vol. 44, 2006, pages 211 - 215, XP025011082, DOI: doi:10.1016/j.carbon.2005.07.039
N. LOEFFLER; D. BRESSER; S. PASSERINI: "Secondary Lithium-Ion Battery Anodes: From First Commercial Batteries to Recent Research Activities", JOHNSON MATTHEY TECHNOL. REV., vol. 59, 2015, pages 34 - 44
N.J. MORALES; S. GOYANES; C. CHILIOTTE; V. BEKERIS; R.J. CANDAL; G.H. RUBIOLO: "One-step chemical vapor deposition synthesis of magnetic CNT-hercynite (FeAI204) hybrids with good aqueous colloidal stability", CARBON N. Y., vol. 61, 2013, pages 515 - 524
PAOLELLA, A.; BRESCIA, R.; PRATO, M.; POVIA, M.; MARRAS, S.; DE TRIZIO, L.; FALQUI, A.; MANNA, L.; GEORGE, C., ACS APPL. MATER. INTERFACES, vol. 5, no. 7, 2013, pages 2745 - 2751
PARK, S.-Y.; KIM, W.-D.; KIM, D.-G.; KIM, J.-K.; JEONG, Y.-S.; KIM, J. H.; KANG, J.-W.: "Effect of hybrid carbon nanotubes-bimetallic composite particles on the performance of polymer solar cells", SOLAR ENERGY MATERIALS AND SOLAR CELLS, vol. 94, no. 5, 2010, pages 750 - 754
R.C. FLAGAN, DIFFERENTIAL MOBILITY ANALYSIS OF AEROSOLS: A TUTORIAL, KONA POWDER PART. J., vol. 26, 2008, pages 254 - 268
R.J. HARRISON: "The temperature dependence of the cation distribution in synthetic hercynite (FeAI204) from in-situ neutron structure refinements", AM. MINERAL., vol. 83, 1998, pages 1092 - 1099
REN, S.; ZHAO, X.; CHEN, R.; FICHTNER, M.: "Carbon-Nanofibers Encapsulated Metal Oxide Nanocomposite and Its Application as Conversion Anode Material for Lithium Ion Batteries", ECS TRANSACTIONS, vol. 64, no. 22, 2015, pages 155 - 164
S. AHMAD; D. COPIC; C. GEORGE; M. DE VOIDER: "Hierarchical Assemblies of Carbon Nanotubes for Ultraflexible Li-Ion Batteries", ADV. MATER., 2016, pages 1 - 6
S.H. KIM; C. WANG; M.R. ZACHARIAH: "Aerosol formation of Sea-Urchin-like nanostructures of carbon nanotubes on bimetallic nanocomposite particles", J. NANOPARTICLE RES., vol. 13, 2011, pages 139 - 146, XP019878150, DOI: doi:10.1007/s11051-010-0011-6
S.S. LEE; C. ZHANG; Z.A. LEWICKA; M. CHO; J.T. MAYO; W.W. YU; R.H. HAUGE; V.L. COLVIN: "Control over the diameter, length, and structure of carbon nanotube carpets using aluminum ferrite and iron oxide nanocrystals as catalyst precursors", J. PHYS. CHEM. C., vol. 116, 2012, pages 10287 - 10295
T.C. LIN; G. SESHADRI; J.A. KELBER: "A consistent method for quantitative XPS peak analysis of thin oxide films on clean polycrystalline iron surfaces", APPL. SURF. SCI., vol. 119, 1997, pages 83 - 92, XP029093127, DOI: doi:10.1016/S0169-4332(97)00167-0
TING J-M ET AL: "Carbon nanowires with new microstructures", CAR, ELSEVIER, OXFORD, GB, vol. 41, no. 3, January 2003 (2003-01-01), pages 601 - 603, XP004408943, ISSN: 0008-6223, DOI: 10.1016/S0008-6223(02)00394-9 *
U. GOLLA-SCHINDLER: "Direct observation of spinodal decomposition in the magnetite-hercynite system by susceptibility measurements and transmission electron microscopy", AM. MINERAL., vol. 90, 2005, pages 1278 - 1283
W.D. KIM; J.Y. AHN; D.G. LEE; H.W. LEE; S.W. HONG; H.S. PARK; S.H. KIM: "Tailoring the carbon nanostructures grown on the surface of Ni-AI bimetallic nanoparticles in the gas phase.", J. COLLOID INTERFACE SCI., vol. 362, 2011, pages 261 - 6, XP028261796, DOI: doi:10.1016/j.jcis.2011.06.043
WU, Y. P.; RAHM, E.; HOLZE, R. J., POWER SOURCES, vol. 114, no. 2, 2003, pages 228 - 236
Y. PIAO; K. AN; J. KIM; T. YU; T. HYEON: "Sea urchin shaped carbon nanostructured materials: carbon nanotubes immobilized on hollow carbon spheres", J. MATER. CHEM., vol. 16, 2006, pages 2984
Y.-L. LI; I. KINLOCH; A.H. WINDLE: "Direct spinning of carbon nanotube fibers from chemical vapor deposition synthesis", SCIENCE, vol. 304, 2004, pages 276 - 278, XP008128720, DOI: doi:10.1126/science.1094982
Z.H. HAN; B. YANG; S.H. KIM; M.R. ZACHARIAH: "Application of hybrid sphere/carbon nanotube particles in nanofluids", NANOTECHNOLOGY, vol. 18, 2007, pages 105701, XP020118878, DOI: doi:10.1088/0957-4484/18/10/105701

Cited By (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US12214420B2 (en) 2015-12-16 2025-02-04 6K Inc. Spheroidal titanium metallic powders with custom microstructures
US11839919B2 (en) 2015-12-16 2023-12-12 6K Inc. Spheroidal dehydrogenated metals and metal alloy particles
US12311447B2 (en) 2018-06-19 2025-05-27 6K Inc. Process for producing spheroidized powder from feedstock materials
WO2019243614A1 (fr) 2018-06-21 2019-12-26 Cambridge Enterprise Limited Matériaux actifs d'électrode et leur procédé de fabrication
US11633785B2 (en) 2019-04-30 2023-04-25 6K Inc. Mechanically alloyed powder feedstock
US11717886B2 (en) 2019-11-18 2023-08-08 6K Inc. Unique feedstocks for spherical powders and methods of manufacturing
US11590568B2 (en) 2019-12-19 2023-02-28 6K Inc. Process for producing spheroidized powder from feedstock materials
US12176529B2 (en) 2020-06-25 2024-12-24 6K Inc. Microcomposite alloy structure
US11963287B2 (en) 2020-09-24 2024-04-16 6K Inc. Systems, devices, and methods for starting plasma
CN112209362B (zh) * 2020-09-27 2021-12-03 电子科技大学 一种等离子体诱导活化氟化碳的方法及锂一次电池制备
CN112209362A (zh) * 2020-09-27 2021-01-12 电子科技大学 一种等离子体诱导活化氟化碳的方法及锂一次电池制备
US11919071B2 (en) 2020-10-30 2024-03-05 6K Inc. Systems and methods for synthesis of spheroidized metal powders
US12406829B2 (en) 2021-01-11 2025-09-02 6K Inc. Methods and systems for reclamation of Li-ion cathode materials using microwave plasma processing
US12042861B2 (en) 2021-03-31 2024-07-23 6K Inc. Systems and methods for additive manufacturing of metal nitride ceramics
US12261023B2 (en) 2022-05-23 2025-03-25 6K Inc. Microwave plasma apparatus and methods for processing materials using an interior liner
US12040162B2 (en) 2022-06-09 2024-07-16 6K Inc. Plasma apparatus and methods for processing feed material utilizing an upstream swirl module and composite gas flows
US12094688B2 (en) 2022-08-25 2024-09-17 6K Inc. Plasma apparatus and methods for processing feed material utilizing a powder ingress preventor (PIP)
US12195338B2 (en) 2022-12-15 2025-01-14 6K Inc. Systems, methods, and device for pyrolysis of methane in a microwave plasma for hydrogen and structured carbon powder production

Similar Documents

Publication Publication Date Title
WO2019052670A1 (fr) Fabrication de nanostructures composites
Jo et al. Continuous-flow synthesis of carbon-coated silicon/iron silicide secondary particles for Li-ion batteries
JP6448057B2 (ja) 多孔性シリコン系負極活物質、この製造方法、及びこれを含むリチウム二次電池
Mahmood et al. Electrode nanostructures in lithium‐based batteries
TWI387150B (zh) Lithium ion accumulation. Release material manufacturing method, lithium ion accumulation. A release material, and an electrode structure and a power storage device using the same
US20190341617A1 (en) Anode materials for lithium ion batteries
CN119943920A (zh) 碳涂覆的硅氧化物/石墨复合颗粒及其制备方法和应用
KR100835883B1 (ko) 탄소나노섬유를 혼성화시킨 리튬이차전지용 음극 활물질
WO2006123601A1 (fr) Batterie rechargeable avec électrolyte non aqueux, son électrode négative et son matériau
JP6311948B2 (ja) 炭素被覆シリコン材料の製造方法
CN114788049A (zh) 包含乱层碳涂层的热歧化阳极活性材料
JP2023548928A (ja) シリコン酸素材料、負極材料及びその製造方法、並びに、リチウムイオン電池
JP6093570B2 (ja) 剥離マイクロチューブならびに空間制御された付着ナノスケール粒子および層を含有する高性能エネルギー貯蔵および収集装置
US20200295356A1 (en) Process for producing semiconductor nanowires and carbon/semiconductor nanowire hybrid materials
CN102623696A (zh) 一种壳核型碳包覆氮化铁纳米复合粒子制备方法与应用
JP6743159B2 (ja) Ｓｉ粒子結合体及びその製造方法
Maddipatla et al. Electrochemical performance of an ultrathin surface oxide-modulated nano-Si anode confined in a graphite matrix for highly reversible lithium-ion batteries
Febrian et al. Recent advances of carbon-based nanocomposites as the anode materials for lithium-ion batteries: Synthesis and performance
CN117795723A (zh) 锂二次电池
CN115836404A (zh) 负极及其制造方法
Yang et al. Enhanced Electrochemical Performances of Cu/Cu x O-Composite-Decorated LiFePO4 through a Facile Magnetron Sputtering
CN113728459A (zh) 负极和包含所述负极的二次电池
JP6686652B2 (ja) 炭素被覆Ｓｉ含有負極活物質の製造方法
Hasegawa et al. Thermogravimetric evolved gas analysis and microscopic elemental mapping of the solid electrolyte interphase on silicon incorporated in free-standing porous carbon electrodes
JP2020042987A (ja) 電解液及びリチウムイオン二次電池

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17771413

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17771413

Country of ref document: EP

Kind code of ref document: A1