WO2018237216A1 - Compositions de nanolignocellulose et leurs procédés de production - Google Patents

Compositions de nanolignocellulose et leurs procédés de production Download PDF

Info

Publication number
WO2018237216A1
WO2018237216A1 PCT/US2018/038899 US2018038899W WO2018237216A1 WO 2018237216 A1 WO2018237216 A1 WO 2018237216A1 US 2018038899 W US2018038899 W US 2018038899W WO 2018237216 A1 WO2018237216 A1 WO 2018237216A1
Authority
WO
WIPO (PCT)
Prior art keywords
nanolignocellulose
cellulose
biomass
lignin
composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2018/038899
Other languages
English (en)
Inventor
Kimberly Nelson
Theodora Retsina
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Granbio Intellectual Property Holdings LLC
Original Assignee
API Intellectual Property Holdings LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US16/014,589 external-priority patent/US20180298113A1/en
Priority to RU2019140283A priority Critical patent/RU2019140283A/ru
Application filed by API Intellectual Property Holdings LLC filed Critical API Intellectual Property Holdings LLC
Priority to AU2018290293A priority patent/AU2018290293B2/en
Priority to CN201880040716.0A priority patent/CN110832139A/zh
Priority to CA3067586A priority patent/CA3067586A1/fr
Priority to BR112019027082-5A priority patent/BR112019027082B1/pt
Priority to EP18820744.3A priority patent/EP3642415A4/fr
Priority to JP2019570562A priority patent/JP2020525659A/ja
Priority to MYPI2019007449A priority patent/MY204818A/en
Publication of WO2018237216A1 publication Critical patent/WO2018237216A1/fr
Priority to ZA2019/08402A priority patent/ZA201908402B/en
Anticipated expiration legal-status Critical
Priority to JP2023036412A priority patent/JP2023060307A/ja
Priority to JP2025031699A priority patent/JP2025096271A/ja
Ceased legal-status Critical Current

Abstract

Cette invention concerne certaines variantes qui fournissent une nouvelle composition de nanolignocellulose comprenant, sur une base sèche d'os, exempte de cendres et exempte d'acétyle, de 35 à 80 % en poids de nanofibrilles de cellulose, de microfibrilles de cellulose, ou d'une combinaison de celles-ci, de 15 à 45 % en poids de lignine, et de 5 à 20 % en poids d'hémicelluloses. Les hémicelluloses peuvent contenir du xylane ou du mannane à titre de composant principal. Les nouvelles propriétés proviennent de la teneur en hémicellulose qui est intermédiaire entre une teneur élevée en hémicellulose de la biomasse brute et une faible teneur en hémicellulose de la nanocellulose classique. La composition de nanolignocellulose est hydrophobe en raison de la présence de lignine. Des procédés de préparation et d'utilisation des compositions de nanolignocellulose selon l'invention sont en outre décrits.
PCT/US2018/038899 2017-06-22 2018-06-22 Compositions de nanolignocellulose et leurs procédés de production Ceased WO2018237216A1 (fr)

Priority Applications (11)

Application Number Priority Date Filing Date Title
JP2019570562A JP2020525659A (ja) 2017-06-22 2018-06-22 ナノリグノセルロース組成物およびこれらの組成物を生成するプロセス
EP18820744.3A EP3642415A4 (fr) 2017-06-22 2018-06-22 Compositions de nanolignocellulose et leurs procédés de production
AU2018290293A AU2018290293B2 (en) 2017-06-22 2018-06-22 Nanolignocellulose compositions and processes to produce these compositions
CN201880040716.0A CN110832139A (zh) 2017-06-22 2018-06-22 纳米木质纤维素组合物以及用于生产这些组合物的方法
CA3067586A CA3067586A1 (fr) 2017-06-22 2018-06-22 Compositions de nanolignocellulose et leurs procedes de production
BR112019027082-5A BR112019027082B1 (pt) 2017-06-22 2018-06-22 Composições de nanolignocelulose e processos para produzir estas composições
MYPI2019007449A MY204818A (en) 2017-06-22 2018-06-22 Nanolignocellulose compositions and processes to produce these compositions
RU2019140283A RU2019140283A (ru) 2017-06-22 2018-06-22 Композиции нанолигноцеллюлозы и способы получения указанных композиций
ZA2019/08402A ZA201908402B (en) 2017-06-22 2019-12-17 Nanolignocellulose compositions and processes to produce these compositions
JP2023036412A JP2023060307A (ja) 2017-06-22 2023-03-09 ナノリグノセルロース組成物およびこれらの組成物を生成するプロセス
JP2025031699A JP2025096271A (ja) 2017-06-22 2025-02-28 ナノリグノセルロース組成物およびこれらの組成物を生成するプロセス

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US201762523293P 2017-06-22 2017-06-22
US62/523,293 2017-06-22
US16/014,589 US20180298113A1 (en) 2015-09-30 2018-06-21 Nanolignocellulose compositions and processes to produce these compositions
US16/014,589 2018-06-21

Publications (1)

Publication Number Publication Date
WO2018237216A1 true WO2018237216A1 (fr) 2018-12-27

Family

ID=64737846

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2018/038899 Ceased WO2018237216A1 (fr) 2017-06-22 2018-06-22 Compositions de nanolignocellulose et leurs procédés de production

Country Status (10)

Country Link
EP (1) EP3642415A4 (fr)
JP (3) JP2020525659A (fr)
CN (1) CN110832139A (fr)
AU (1) AU2018290293B2 (fr)
BR (1) BR112019027082B1 (fr)
CA (1) CA3067586A1 (fr)
MY (1) MY204818A (fr)
RU (1) RU2019140283A (fr)
WO (1) WO2018237216A1 (fr)
ZA (1) ZA201908402B (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111470495A (zh) * 2020-04-24 2020-07-31 山东龙力生物科技股份有限公司 一种制备石墨烯的原料及使用该原料制备石墨烯的方法
WO2022023502A3 (fr) * 2020-07-29 2022-03-10 Envopap Limited Perfectionnements apportés ou se rapportant à des matériaux d'emballage
CN115304690A (zh) * 2022-04-15 2022-11-08 北京林业大学 一种具有生物相容性的木聚糖纳米晶的制备方法
KR102582306B1 (ko) * 2022-03-16 2023-09-25 한국화학연구원 목질계 바이오매스의 열수처리 잔사 고형물을 이용한 리그닌 연속 추출방법
US12123143B2 (en) 2018-07-17 2024-10-22 Suzano S.A. Process for producing a nanocelullosic material comprising at least two stages of defibrillation of cellulosic feedstock and at least one intermediate fractioning stage

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114350335B (zh) * 2022-03-21 2022-06-07 胜利油田新海兴达实业集团有限责任公司 一种油田用起泡剂及其制备方法

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016177395A1 (fr) * 2015-05-04 2016-11-10 Upm-Kymmene Corporation Produit à base de cellulose nanofibrillaire
WO2016195506A1 (fr) * 2015-05-29 2016-12-08 Elkem As Cellulose nanofibrillée destinée à être utilisée dans des fluides pour la récupération de pétrole primaire

Family Cites Families (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5398180B2 (ja) * 2007-06-11 2014-01-29 国立大学法人京都大学 リグニン含有ミクロフィブリル化植物繊維及びその製造方法
KR20100093080A (ko) * 2007-12-21 2010-08-24 미쓰비시 가가꾸 가부시키가이샤 섬유 복합체
CN101851801A (zh) * 2010-06-30 2010-10-06 东北林业大学 一种超声结合高压匀质处理制备纳米纤维素纤维的方法
CN103502529B (zh) * 2011-01-21 2016-08-24 Fp创新研究中心 高长径比纤维素纳米长丝及其生产方法
CN104704005A (zh) * 2012-10-16 2015-06-10 日本制纸株式会社 纤维素纳米纤维
US9187865B2 (en) * 2012-11-30 2015-11-17 Api Intellectual Property Holdings, Llc Processes and apparatus for producing nanocellulose, and compositions and products produced therefrom
JP5995239B2 (ja) * 2013-03-26 2016-09-21 国立研究開発法人産業技術総合研究所 水晶振動子微量天秤用バイオセンサー及びその製造方法
EP3071517B1 (fr) * 2013-11-22 2018-10-10 The University of Queensland Nanocellulose
JP6656960B2 (ja) * 2015-03-13 2020-03-04 国立大学法人京都大学 リグニンを構成するフェニルプロパン単位のα位が化学修飾されたリグノセルロース誘導体、それを含む繊維、繊維集合体、それらを含有する組成物及び成形体
JP2016204277A (ja) * 2015-04-17 2016-12-08 真庭バイオケミカル株式会社 リグニンの抽出方法
US20170210826A1 (en) * 2015-09-30 2017-07-27 Api Intellectual Property Holdings, Llc Processes for producing nanocellulose, and nanocellulose compositions produced therefrom

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016177395A1 (fr) * 2015-05-04 2016-11-10 Upm-Kymmene Corporation Produit à base de cellulose nanofibrillaire
WO2016195506A1 (fr) * 2015-05-29 2016-12-08 Elkem As Cellulose nanofibrillée destinée à être utilisée dans des fluides pour la récupération de pétrole primaire

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
SINKE HENSHAW OSONG: "Mechanical Pulp Based Nano-ligno-cellulose: Production, Characterization and their Effect on Paper Properties", THESIS FOR DEGREE OF LICENTIATE OF TECHNOLOGY, January 2014 (2014-01-01), Sandsvall, pages 1, XP055560274 *

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US12123143B2 (en) 2018-07-17 2024-10-22 Suzano S.A. Process for producing a nanocelullosic material comprising at least two stages of defibrillation of cellulosic feedstock and at least one intermediate fractioning stage
CN111470495A (zh) * 2020-04-24 2020-07-31 山东龙力生物科技股份有限公司 一种制备石墨烯的原料及使用该原料制备石墨烯的方法
CN111470495B (zh) * 2020-04-24 2023-05-12 山东龙力生物科技股份有限公司 一种制备石墨烯的原料及使用该原料制备石墨烯的方法
WO2022023502A3 (fr) * 2020-07-29 2022-03-10 Envopap Limited Perfectionnements apportés ou se rapportant à des matériaux d'emballage
KR102582306B1 (ko) * 2022-03-16 2023-09-25 한국화학연구원 목질계 바이오매스의 열수처리 잔사 고형물을 이용한 리그닌 연속 추출방법
CN115304690A (zh) * 2022-04-15 2022-11-08 北京林业大学 一种具有生物相容性的木聚糖纳米晶的制备方法

Also Published As

Publication number Publication date
JP2025096271A (ja) 2025-06-26
RU2019140283A3 (fr) 2022-02-17
JP2020525659A (ja) 2020-08-27
EP3642415A1 (fr) 2020-04-29
BR112019027082A2 (pt) 2020-07-07
EP3642415A4 (fr) 2021-04-28
ZA201908402B (en) 2021-08-25
AU2018290293B2 (en) 2024-01-18
RU2019140283A (ru) 2021-07-22
AU2018290293A1 (en) 2020-01-02
CN110832139A (zh) 2020-02-21
JP2023060307A (ja) 2023-04-27
CA3067586A1 (fr) 2018-12-27
MY204818A (en) 2024-09-17
BR112019027082B1 (pt) 2023-12-05

Similar Documents

Publication Publication Date Title
US11834523B2 (en) Nanolignocellulose compositions and processes to produce these compositions
US12077915B2 (en) Nanocellulose-reinforced corrugated medium
US12188181B2 (en) Sulfite-based processes for producing nanocellulose, and compositions and products produced therefrom
US9322134B2 (en) Nanocellulose production using lignosulfonic acid
US20250059707A1 (en) Nanocellulose production co-located at a pulp and paper mill
AU2018290293B2 (en) Nanolignocellulose compositions and processes to produce these compositions
US20250043508A1 (en) Processes and systems for producing nanocellulose from old corrugated containers
WO2015153536A1 (fr) Production de nanocellulose à l'aide d'acide lignosulfonique

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18820744

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 3067586

Country of ref document: CA

Ref document number: 2019570562

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

REG Reference to national code

Ref country code: BR

Ref legal event code: B01A

Ref document number: 112019027082

Country of ref document: BR

ENP Entry into the national phase

Ref document number: 2018290293

Country of ref document: AU

Date of ref document: 20180622

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 2019140283

Country of ref document: RU

ENP Entry into the national phase

Ref document number: 2018820744

Country of ref document: EP

Effective date: 20200122

ENP Entry into the national phase

Ref document number: 112019027082

Country of ref document: BR

Kind code of ref document: A2

Effective date: 20191218