WO2018216739A1 - Composition électroconductrice - Google Patents

Composition électroconductrice Download PDF

Info

Publication number
WO2018216739A1
WO2018216739A1 PCT/JP2018/019876 JP2018019876W WO2018216739A1 WO 2018216739 A1 WO2018216739 A1 WO 2018216739A1 JP 2018019876 W JP2018019876 W JP 2018019876W WO 2018216739 A1 WO2018216739 A1 WO 2018216739A1
Authority
WO
WIPO (PCT)
Prior art keywords
epoxy resin
composition
present
resin
conductive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2018/019876
Other languages
English (en)
Japanese (ja)
Inventor
一雄 荒川
丈章 齋木
石川　和憲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yokohama Rubber Co Ltd
Original Assignee
Yokohama Rubber Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yokohama Rubber Co Ltd filed Critical Yokohama Rubber Co Ltd
Priority to JP2019520291A priority Critical patent/JP7231537B2/ja
Priority to CN201880030071.2A priority patent/CN110603293A/zh
Publication of WO2018216739A1 publication Critical patent/WO2018216739A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'objet de la présente invention est de fournir une composition de film électroconducteur qui est excellente en termes d'aptitude à la soudure, d'aptitude à la sérigraphie, de faible résistance, d'adhésion aux substrats, et de stabilité au stockage. La composition électroconductrice de la présente invention comprend des particules électroconductrices, une résine époxy A qui présente un équivalent en groupe époxy inférieur à 500 g/éq. et qui est liquide à 25 °C, une résine époxy B qui présente un équivalent en groupe époxy de 400 à 5 000 g/éq. et qui est solide à 25 °C, une résine thermoplastique C présentant un poids moléculaire moyen en poids de 25 000 à 65 000, un agent de durcissement D, et un solvant, la quantité totale des constituants A, B, C, et D étant de 3 à 10 parties en masse pour 100 parties en masse des particules électroconductrices, le rapport en masse de la somme des constituants A et B à la teneur du constituant C, (A + B)/C, étant de 50/50 à 95/5, le rapport en masse de la teneur du constituant A à la somme des constituants B et C, A/(B + C), étant de 15/85 à 85/15, et le rapport en masse du constituant D à la somme des constituants A et B, D/(A + B), étant de 2/98 à 10/90. La composition électroconductrice ne contient sensiblement pas de carboxylate métallique.
PCT/JP2018/019876 2017-05-25 2018-05-23 Composition électroconductrice Ceased WO2018216739A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2019520291A JP7231537B2 (ja) 2017-05-25 2018-05-23 導電性組成物
CN201880030071.2A CN110603293A (zh) 2017-05-25 2018-05-23 导电性组合物

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017-103781 2017-05-25
JP2017103781 2017-05-25

Publications (1)

Publication Number Publication Date
WO2018216739A1 true WO2018216739A1 (fr) 2018-11-29

Family

ID=64396083

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/019876 Ceased WO2018216739A1 (fr) 2017-05-25 2018-05-23 Composition électroconductrice

Country Status (4)

Country Link
JP (1) JP7231537B2 (fr)
CN (1) CN110603293A (fr)
TW (1) TW201901699A (fr)
WO (1) WO2018216739A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109903885A (zh) * 2018-12-29 2019-06-18 无锡帝科电子材料股份有限公司 导电浆料及其应用、太阳能电池电极和太阳能电池

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TWI743683B (zh) * 2020-02-14 2021-10-21 碩禾電子材料股份有限公司 用於hjt太陽能電池的導電漿料、hjt太陽能電池與電極結構

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016006467A1 (fr) * 2014-07-11 2016-01-14 横浜ゴム株式会社 Composition conductrice pour former une électrode de collecte de batterie solaire, cellule de batterie solaire et module de batterie solaire
WO2016017618A1 (fr) * 2014-07-29 2016-02-04 横浜ゴム株式会社 Composition conductrice, cellule solaire et module de cellule solaire
WO2016021535A1 (fr) * 2014-08-08 2016-02-11 横浜ゴム株式会社 Composition conductrice, cellule solaire et module de cellules solaires
JP2016160413A (ja) * 2015-03-05 2016-09-05 横浜ゴム株式会社 導電性組成物、太陽電池セルおよび太陽電池モジュール
JP2016160415A (ja) * 2015-03-05 2016-09-05 横浜ゴム株式会社 導電性組成物、太陽電池セルおよび太陽電池モジュール

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3557938B2 (ja) * 1999-02-17 2004-08-25 三菱電機株式会社 熱硬化性樹脂組成物およびそれを用いた絶縁コイル
CN105452414B (zh) * 2013-08-06 2017-05-17 千住金属工业株式会社 导电性粘接剂、接合体和接头

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016006467A1 (fr) * 2014-07-11 2016-01-14 横浜ゴム株式会社 Composition conductrice pour former une électrode de collecte de batterie solaire, cellule de batterie solaire et module de batterie solaire
WO2016017618A1 (fr) * 2014-07-29 2016-02-04 横浜ゴム株式会社 Composition conductrice, cellule solaire et module de cellule solaire
WO2016021535A1 (fr) * 2014-08-08 2016-02-11 横浜ゴム株式会社 Composition conductrice, cellule solaire et module de cellules solaires
JP2016160413A (ja) * 2015-03-05 2016-09-05 横浜ゴム株式会社 導電性組成物、太陽電池セルおよび太陽電池モジュール
JP2016160415A (ja) * 2015-03-05 2016-09-05 横浜ゴム株式会社 導電性組成物、太陽電池セルおよび太陽電池モジュール

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN109903885A (zh) * 2018-12-29 2019-06-18 无锡帝科电子材料股份有限公司 导电浆料及其应用、太阳能电池电极和太阳能电池

Also Published As

Publication number Publication date
CN110603293A (zh) 2019-12-20
JP7231537B2 (ja) 2023-03-01
JPWO2018216739A1 (ja) 2020-04-02
TW201901699A (zh) 2019-01-01

Similar Documents

Publication Publication Date Title
JP6447504B2 (ja) 導電性ペースト
JP6156393B2 (ja) 導電性接着剤組成物及びそれを用いた電子素子
JP5045803B2 (ja) 導電性組成物および太陽電池セル
TWI783078B (zh) 導電性膏
WO2018139463A1 (fr) Composition conductrice
US20160329122A1 (en) Conductive paste and conductive film
JP5976382B2 (ja) ダイアタッチペーストおよびその製造方法、ならびに半導体装置
JP7231537B2 (ja) 導電性組成物
JP2019056104A (ja) 導電性組成物及びそれを用いた配線板
KR20120004122A (ko) 전도성 페이스트 및 이를 이용한 전극
CN106537607B (zh) 太阳能电池集电电极形成用导电性组合物、太阳能电池单元和太阳能电池模块
JP2016160415A (ja) 導電性組成物、太陽電池セルおよび太陽電池モジュール
JPH10279903A (ja) 導電性接着剤
CN103571370A (zh) 电路连接材料
JP6361843B1 (ja) 導電性組成物
JP6092754B2 (ja) 導電性エポキシ樹脂組成物、該組成物を用いた太陽電池セル、及び該太陽電池セルの製造方法
JP2006140206A (ja) 銀とカーボンナノチューブを含む導電性樹脂ペースト組成物およびこれを用いた半導体装置
JP6705568B1 (ja) 導電性組成物
JP7264662B2 (ja) 導電性組成物
WO2020166137A1 (fr) Composition électroconductrice
WO2025059200A1 (fr) Adhésifs conducteurs flexibles
TW202523727A (zh) 導電性組成物
JP2023071376A (ja) 導電性ペースト及びその硬化物からなる電極を備えた太陽電池セル

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18806863

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2019520291

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18806863

Country of ref document: EP

Kind code of ref document: A1