WO2018181405A1 - Stratifié et sac composé dudit stratifié - Google Patents

Stratifié et sac composé dudit stratifié Download PDF

Info

Publication number
WO2018181405A1
WO2018181405A1 PCT/JP2018/012605 JP2018012605W WO2018181405A1 WO 2018181405 A1 WO2018181405 A1 WO 2018181405A1 JP 2018012605 W JP2018012605 W JP 2018012605W WO 2018181405 A1 WO2018181405 A1 WO 2018181405A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
bag
base material
layer
laminate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2018/012605
Other languages
English (en)
Japanese (ja)
Inventor
靖也 飯尾
和佳子 仙頭
満 武士田
和弘 多久島
潮美 中川
岸本　好弘
鈴木　梓
可成 青野
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dai Nippon Printing Co Ltd
Original Assignee
Dai Nippon Printing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2018011912A external-priority patent/JP7056175B2/ja
Priority claimed from JP2018011906A external-priority patent/JP7056174B2/ja
Application filed by Dai Nippon Printing Co Ltd filed Critical Dai Nippon Printing Co Ltd
Publication of WO2018181405A1 publication Critical patent/WO2018181405A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un stratifié ayant une résistance à la pénétration et des propriétés de glissement. Un stratifié comprenant une surface externe et une surface interne comprend : un substrat constituant la couche externe du stratifié et ayant un film plastique qui comprend 51 % en masse ou plus de polybutylène téréphtalate ; et une couche de matériau d'étanchéité constituant la surface interne du stratifié. La couche du substrat qui constitue la surface externe du stratifié comprend du polyéthylène téréphtalate ou du polybutylène téréphtalate.
PCT/JP2018/012605 2017-03-29 2018-03-27 Stratifié et sac composé dudit stratifié Ceased WO2018181405A1 (fr)

Applications Claiming Priority (8)

Application Number Priority Date Filing Date Title
JP2017065934 2017-03-29
JP2017-065934 2017-03-29
JP2017-065924 2017-03-29
JP2017065924 2017-03-29
JP2018011912A JP7056175B2 (ja) 2017-03-29 2018-01-26 積層体及び該積層体で構成される袋
JP2018011906A JP7056174B2 (ja) 2017-03-29 2018-01-26 積層体及び該積層体で構成される袋
JP2018-011906 2018-01-26
JP2018-011912 2018-01-26

Publications (1)

Publication Number Publication Date
WO2018181405A1 true WO2018181405A1 (fr) 2018-10-04

Family

ID=63676334

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/012605 Ceased WO2018181405A1 (fr) 2017-03-29 2018-03-27 Stratifié et sac composé dudit stratifié

Country Status (1)

Country Link
WO (1) WO2018181405A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20200407136A1 (en) * 2018-03-22 2020-12-31 Dai Nippon Printing Co., Ltd. Barrier laminate film, and packaging material which uses barrier laminate film
CN112864501A (zh) * 2019-11-27 2021-05-28 无锡恩捷新材料科技有限公司 一种电池用包装材料及其制造方法
JP2021102349A (ja) * 2019-09-19 2021-07-15 大日本印刷株式会社 バリアフィルム、該バリアフィルムを用いた積層体、該積層体を用いた包装製品
JP2021133679A (ja) * 2020-02-27 2021-09-13 住友ベークライト株式会社 透明多層フィルム及び包装体
CN117203050A (zh) * 2021-04-19 2023-12-08 东丽薄膜先端加工股份有限公司 层叠体、及层叠体的制造方法
EP4328016A4 (fr) * 2021-04-19 2025-08-13 Toray Advanced Film Co Ltd Stratifié et procédé de fabrication de stratifié

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0970917A (ja) * 1995-09-07 1997-03-18 Oike Ind Co Ltd 透明ガスバリア性積層体
JPH11151774A (ja) * 1997-11-19 1999-06-08 Dainippon Printing Co Ltd 透明ガスバリア−性フィルム
JP2004042488A (ja) * 2002-07-12 2004-02-12 Toray Ind Inc 蒸着フィルム
JP2005281473A (ja) * 2004-03-29 2005-10-13 J-Film Corp ポリブチレンテレフタレートフィルム、積層フィルム及び樹脂製カップ用の蓋材
JP2007045130A (ja) * 2005-08-12 2007-02-22 Shikoku Kako Kk 未延伸積層フィルム
WO2015178390A1 (fr) * 2014-05-21 2015-11-26 東洋紡株式会社 Film de poly(téréphtalate de butylène) étiré de façon biaxiale, son procédé de fabrication, et film stratifié faisant barrière aux gaz
WO2016171173A1 (fr) * 2015-04-24 2016-10-27 東洋紡株式会社 Film polyester étiré bi-axialement, et procédé de fabrication de celui-ci
JP2016199722A (ja) * 2015-04-14 2016-12-01 凸版印刷株式会社 ガスバリア用塗液、ガスバリア性包装材料および熱水処理用包装袋
WO2016190431A1 (fr) * 2015-05-28 2016-12-01 凸版印刷株式会社 Film disposé en couches, et sac d'emballage
JP2016203630A (ja) * 2015-04-24 2016-12-08 東洋紡株式会社 二軸延伸ポリエステルフィルムおよびその製造方法

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0970917A (ja) * 1995-09-07 1997-03-18 Oike Ind Co Ltd 透明ガスバリア性積層体
JPH11151774A (ja) * 1997-11-19 1999-06-08 Dainippon Printing Co Ltd 透明ガスバリア−性フィルム
JP2004042488A (ja) * 2002-07-12 2004-02-12 Toray Ind Inc 蒸着フィルム
JP2005281473A (ja) * 2004-03-29 2005-10-13 J-Film Corp ポリブチレンテレフタレートフィルム、積層フィルム及び樹脂製カップ用の蓋材
JP2007045130A (ja) * 2005-08-12 2007-02-22 Shikoku Kako Kk 未延伸積層フィルム
WO2015178390A1 (fr) * 2014-05-21 2015-11-26 東洋紡株式会社 Film de poly(téréphtalate de butylène) étiré de façon biaxiale, son procédé de fabrication, et film stratifié faisant barrière aux gaz
JP2016199722A (ja) * 2015-04-14 2016-12-01 凸版印刷株式会社 ガスバリア用塗液、ガスバリア性包装材料および熱水処理用包装袋
WO2016171173A1 (fr) * 2015-04-24 2016-10-27 東洋紡株式会社 Film polyester étiré bi-axialement, et procédé de fabrication de celui-ci
JP2016203630A (ja) * 2015-04-24 2016-12-08 東洋紡株式会社 二軸延伸ポリエステルフィルムおよびその製造方法
WO2016190431A1 (fr) * 2015-05-28 2016-12-01 凸版印刷株式会社 Film disposé en couches, et sac d'emballage

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20200407136A1 (en) * 2018-03-22 2020-12-31 Dai Nippon Printing Co., Ltd. Barrier laminate film, and packaging material which uses barrier laminate film
US12060207B2 (en) * 2018-03-22 2024-08-13 Dai Nippon Printing Co., Ltd. Barrier laminate film, and packaging material which uses barrier laminate film
JP2021102349A (ja) * 2019-09-19 2021-07-15 大日本印刷株式会社 バリアフィルム、該バリアフィルムを用いた積層体、該積層体を用いた包装製品
JP7031772B2 (ja) 2019-09-19 2022-03-08 大日本印刷株式会社 バリアフィルム、該バリアフィルムを用いた積層体、該積層体を用いた包装製品
CN112864501A (zh) * 2019-11-27 2021-05-28 无锡恩捷新材料科技有限公司 一种电池用包装材料及其制造方法
JP2021133679A (ja) * 2020-02-27 2021-09-13 住友ベークライト株式会社 透明多層フィルム及び包装体
CN117203050A (zh) * 2021-04-19 2023-12-08 东丽薄膜先端加工股份有限公司 层叠体、及层叠体的制造方法
EP4328016A4 (fr) * 2021-04-19 2025-08-13 Toray Advanced Film Co Ltd Stratifié et procédé de fabrication de stratifié

Similar Documents

Publication Publication Date Title
WO2018181405A1 (fr) Stratifié et sac composé dudit stratifié
JP2023001195A (ja) 袋
WO2018052042A1 (fr) Sachet
JP2024009168A (ja) 袋
KR102411863B1 (ko) 푸란디카르복실산 유닛을 갖는 폴리에스테르 필름과 히트 시일성 수지층을 구비하는 적층체 및 포장 주머니
WO2018062331A1 (fr) Corps stratifié
WO2019189490A1 (fr) Matériau d'emballage et poche stérilisable en autoclave ou poche pour micro-ondes pourvue d'un matériau d'emballage
WO2020129291A1 (fr) Film de barrière vis-à-vis des gaz et procédé de production pour celui-ci, film d'emballage et sac d'emballage
JP2023042595A (ja) 積層体、包装体及び包装物品
JP7124285B2 (ja) 積層体及び該積層体で構成される袋
JP7591193B2 (ja) バリアフィルム、積層体、及び包装容器
JP2016222277A (ja) 包装袋
JP7554387B2 (ja) 包装用二軸配向ポリエステルフィルム
JP7056175B2 (ja) 積層体及び該積層体で構成される袋
JP7056174B2 (ja) 積層体及び該積層体で構成される袋
JP7735042B2 (ja) 積層体及び該積層体で構成される袋
JP6424997B1 (ja) シーラントフィルム及び包装材
JP7033266B2 (ja) 積層体及び該積層体で構成される袋並びに積層体の製造方法
JP2018058358A (ja) 積層体及び該積層体で構成される袋
JP7153251B2 (ja) 積層体及び該積層体で構成される蓋材を用いた輸液容器
US20250010593A1 (en) Recyclable packaging film with dimensional stability
JP2025097046A (ja) 多層フィルム、積層体、包装袋、包装製品及び多層フィルムの選定方法
JP2001171035A (ja) 積層材
CN115151422A (zh) 层叠体

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18777185

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18777185

Country of ref document: EP

Kind code of ref document: A1