WO2018174206A1 - Fibre maintenant la polarisation, dispositif optique, préforme de fibre maintenant la polarisation, et procédé de fabrication - Google Patents

Fibre maintenant la polarisation, dispositif optique, préforme de fibre maintenant la polarisation, et procédé de fabrication Download PDF

Info

Publication number
WO2018174206A1
WO2018174206A1 PCT/JP2018/011543 JP2018011543W WO2018174206A1 WO 2018174206 A1 WO2018174206 A1 WO 2018174206A1 JP 2018011543 W JP2018011543 W JP 2018011543W WO 2018174206 A1 WO2018174206 A1 WO 2018174206A1
Authority
WO
WIPO (PCT)
Prior art keywords
maintaining fiber
core
polarization maintaining
stress applying
cross
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2018/011543
Other languages
English (en)
Japanese (ja)
Inventor
健太郎 市井
圭祐 平川
和幸 林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujikura Ltd
Original Assignee
Fujikura Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujikura Ltd filed Critical Fujikura Ltd
Priority to DKPA201970653A priority Critical patent/DK201970653A1/da
Priority to US16/495,870 priority patent/US20200012041A1/en
Priority to CN201880019812.7A priority patent/CN110446957A/zh
Priority claimed from JP2018055353A external-priority patent/JP7133328B2/ja
Publication of WO2018174206A1 publication Critical patent/WO2018174206A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention met en œuvre une fibre maintenant la polarisation, qui possède un cœur présentant une section droite aplatie et qui est facile à fabriquer. Une fibre (1) maintenant la polarisation est dotée d'un cœur (11), d'une gaine intérieure (12), de deux parties (13a-13b) d'application de contraintes, et d'une gaine extérieure (14). La gaine intérieure (12) est ajustée dans chacune des deux parties (13a-13b) d'application de contraintes. La section droite du cœur (11) est aplatie de telle façon que la direction d'agencement des deux parties (13a-13b) d'application de contraintes soit utilisée comme son grand axe.
PCT/JP2018/011543 2017-03-22 2018-03-22 Fibre maintenant la polarisation, dispositif optique, préforme de fibre maintenant la polarisation, et procédé de fabrication Ceased WO2018174206A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
DKPA201970653A DK201970653A1 (da) 2017-03-22 2018-03-22 Polarization maintaining fiber, optical device, preform of polarization maintaining fiber, and manufacturing method
US16/495,870 US20200012041A1 (en) 2017-03-22 2018-03-22 Polarization maintaining fiber, optical device, preform of polarization maintaining fiber, and manufacturing method
CN201880019812.7A CN110446957A (zh) 2017-03-22 2018-03-22 保偏光纤、光器件、保偏光纤的母材以及制造方法

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2017-056175 2017-03-22
JP2017056175 2017-03-22
JP2018055353A JP7133328B2 (ja) 2017-03-22 2018-03-22 偏波保持ファイバ、光デバイス、偏波保持ファイバの母材、及び製造方法
JP2018-055353 2018-03-22

Publications (1)

Publication Number Publication Date
WO2018174206A1 true WO2018174206A1 (fr) 2018-09-27

Family

ID=63585474

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/011543 Ceased WO2018174206A1 (fr) 2017-03-22 2018-03-22 Fibre maintenant la polarisation, dispositif optique, préforme de fibre maintenant la polarisation, et procédé de fabrication

Country Status (1)

Country Link
WO (1) WO2018174206A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2020160260A (ja) * 2019-03-26 2020-10-01 株式会社フジクラ 光学入出力デバイスの製造方法及び光学入出力デバイス
WO2025004909A1 (fr) * 2023-06-28 2025-01-02 住友電気工業株式会社 Fibre optique à âmes multiples à maintien de polarisation et procédé de fabrication de fibre optique à âmes multiples à maintien de polarisation

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6028703U (ja) * 1983-08-01 1985-02-26 古河電気工業株式会社 単一偏波光フアイバ
JP2002533743A (ja) * 1998-12-04 2002-10-08 シドラ コーポレイション 管に収容されたブラッグ回折格子を形成する方法および装置
US20070177846A1 (en) * 2006-01-30 2007-08-02 Xin Chen Rare earth doped double clad optical fiber with plurality of air holes and stress rods
JP2008078629A (ja) * 2006-09-20 2008-04-03 Imra America Inc ファイバ・レーザおよびファイバ増幅器用の希土類がドープされ有効区域が大きい光ファイバ
JP2009145423A (ja) * 2007-12-11 2009-07-02 Furukawa Electric Co Ltd:The 波長変換モジュール

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6028703U (ja) * 1983-08-01 1985-02-26 古河電気工業株式会社 単一偏波光フアイバ
JP2002533743A (ja) * 1998-12-04 2002-10-08 シドラ コーポレイション 管に収容されたブラッグ回折格子を形成する方法および装置
US20070177846A1 (en) * 2006-01-30 2007-08-02 Xin Chen Rare earth doped double clad optical fiber with plurality of air holes and stress rods
JP2008078629A (ja) * 2006-09-20 2008-04-03 Imra America Inc ファイバ・レーザおよびファイバ増幅器用の希土類がドープされ有効区域が大きい光ファイバ
JP2009145423A (ja) * 2007-12-11 2009-07-02 Furukawa Electric Co Ltd:The 波長変換モジュール

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2020160260A (ja) * 2019-03-26 2020-10-01 株式会社フジクラ 光学入出力デバイスの製造方法及び光学入出力デバイス
WO2025004909A1 (fr) * 2023-06-28 2025-01-02 住友電気工業株式会社 Fibre optique à âmes multiples à maintien de polarisation et procédé de fabrication de fibre optique à âmes multiples à maintien de polarisation

Similar Documents

Publication Publication Date Title
JP7133328B2 (ja) 偏波保持ファイバ、光デバイス、偏波保持ファイバの母材、及び製造方法
JP5409928B2 (ja) 偏波保持光ファイバ
US9213140B2 (en) Fiber component and laser device
CN109799572B (zh) 一种纤维集成的高斯-环形模场适配器
US7455464B2 (en) Optical fiber processing method
US7813608B2 (en) Optical fiber fabrication
WO2025082137A1 (fr) Fibre microstructurée à âme creuse avec marques additives, et préforme et procédé de détection de dessin
CN109642983B (zh) 光纤
EP3850408A1 (fr) Épissure de fibres optiques encapsulée par un suppresseur de lumière de mode de gaine
WO2018174206A1 (fr) Fibre maintenant la polarisation, dispositif optique, préforme de fibre maintenant la polarisation, et procédé de fabrication
CN118169811A (zh) 光纤熔接组件及其制备方法、熔接方法
JP4252238B2 (ja) 光ファイバの接続方法
JP2019095783A (ja) 光ファイバのコア径変換体及び異種光ファイバ接続体
JP4805181B2 (ja) 光結合デバイスの製造方法及び光増幅装置の製造方法
JP2017525127A (ja) 楕円形クラッド層の偏波保持ラージモードエリア利得ファイバー
CN114072712B (zh) 光合并器、激光装置、以及光合并器的制造方法
JP2004295010A (ja) 光ファイバ
JP2023003952A (ja) 光ファイバ接続構造
JP2005289766A (ja) 光学素子用母材およびそれを用いて製造される光学素子、並びに光学素子用母材の製造方法
JP7400152B2 (ja) 光ファイバー接続体、及びその光ファイバー接続体と光デバイスとの接続構造
KR101055312B1 (ko) 포토닉 밴드갭 광섬유 및 그 제조 방법
CN105929482A (zh) 光纤端帽及其制造方法
Xie et al. Thermally induced mode amplification characteristics of large mode area segmented cladding fiber
CN106199826A (zh) 保偏光纤
JP6746625B2 (ja) 光ファイバ

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18770705

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18770705

Country of ref document: EP

Kind code of ref document: A1