WO2018143299A1 - Ensemble d'encres pour stéréolithographie, article stéréolithographique et procédé de production d'article stéréolithographique - Google Patents

Ensemble d'encres pour stéréolithographie, article stéréolithographique et procédé de production d'article stéréolithographique Download PDF

Info

Publication number
WO2018143299A1
WO2018143299A1 PCT/JP2018/003290 JP2018003290W WO2018143299A1 WO 2018143299 A1 WO2018143299 A1 WO 2018143299A1 JP 2018003290 W JP2018003290 W JP 2018003290W WO 2018143299 A1 WO2018143299 A1 WO 2018143299A1
Authority
WO
WIPO (PCT)
Prior art keywords
weight
parts
material composition
support material
ink set
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2018/003290
Other languages
English (en)
Japanese (ja)
Inventor
克幸 鬼頭
妥江子 出雲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Maxell Ltd
Original Assignee
Maxell Holdings Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Maxell Holdings Ltd filed Critical Maxell Holdings Ltd
Priority to JP2018565622A priority Critical patent/JPWO2018143299A1/ja
Publication of WO2018143299A1 publication Critical patent/WO2018143299A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention aborde le problème consistant à fournir : un ensemble d'encres pour stéréolithographie qui permet d'obtenir un article stéréolithographique présentant une excellente précision dimensionnelle ; un article stéréolithographique formé à l'aide de l'ensemble d'encres pour stéréolithographie ; et un procédé de production de l'article stéréolithographique à l'aide de l'ensemble d'encres pour stéréolithographie. Un ensemble d'encres pour stéréolithographie selon la présente invention est pourvu d'une composition de matériau de modèle et d'une composition de matériau de support. La composition de matériau de modèle comprend : un composé polymérisable par voie radicalaire (A) ; un composé polymérisable par voie cationique (B) ; un initiateur de polymérisation radicalaire (C) ; et un initiateur de polymérisation cationique (D). La composition de matériau de support comprend : 20 à 50 parties en poids de monomères à insaturation éthylénique monofonctionnels hydrosolubles (a) ; 20 à 49 parties en poids de polyalkylène glycol (b) comprenant des groupes oxyéthylène et/ou des groupes oxypropylène ; 35 parties en poids ou moins d'un solvant organique soluble dans l'eau (c) ; et 1 à 20 parties en poids d'un initiateur de photopolymérisation (d).
PCT/JP2018/003290 2017-01-31 2018-01-31 Ensemble d'encres pour stéréolithographie, article stéréolithographique et procédé de production d'article stéréolithographique Ceased WO2018143299A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2018565622A JPWO2018143299A1 (ja) 2017-01-31 2018-01-31 光造形用インクセット、光造形品、及び、光造形品の製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017-016123 2017-01-31
JP2017016123 2017-01-31

Publications (1)

Publication Number Publication Date
WO2018143299A1 true WO2018143299A1 (fr) 2018-08-09

Family

ID=63039860

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/003290 Ceased WO2018143299A1 (fr) 2017-01-31 2018-01-31 Ensemble d'encres pour stéréolithographie, article stéréolithographique et procédé de production d'article stéréolithographique

Country Status (2)

Country Link
JP (1) JPWO2018143299A1 (fr)
WO (1) WO2018143299A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11325315B2 (en) * 2017-12-29 2022-05-10 Basf Se Composition to produce support sub-structures for 3D photopolymer jetting

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016020474A (ja) * 2014-06-20 2016-02-04 株式会社キーエンス インクジェット光造形法における光造形品形成用モデル材及び光造形品の製造方法
JP2016098324A (ja) * 2014-11-21 2016-05-30 東洋インキＳｃホールディングス株式会社 光学的立体造形活性エネルギー線重合性樹脂組成物、及び立体造形物

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016020474A (ja) * 2014-06-20 2016-02-04 株式会社キーエンス インクジェット光造形法における光造形品形成用モデル材及び光造形品の製造方法
JP2016098324A (ja) * 2014-11-21 2016-05-30 東洋インキＳｃホールディングス株式会社 光学的立体造形活性エネルギー線重合性樹脂組成物、及び立体造形物

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11325315B2 (en) * 2017-12-29 2022-05-10 Basf Se Composition to produce support sub-structures for 3D photopolymer jetting

Also Published As

Publication number Publication date
JPWO2018143299A1 (ja) 2019-11-21

Similar Documents

Publication Publication Date Title
US11485067B2 (en) Resin composition for modeling material, resin composition for supporting material, photofabrication product, and process for producing photofabrication product
JP6751096B2 (ja) モデル材用樹脂組成物、光造形用インクセット、および、光造形品の製造方法
JP6796069B2 (ja) 光造形用インクセット、および、光造形品の製造方法
US10557032B2 (en) Composition for support material and ink set for stereolithography
WO2018142485A1 (fr) Jeu d'encres pour stéréolithographie, article stéréolithographique et procédé de production d'article stéréolithographique
EP3476874B1 (fr) Composition de résine destinée à un élément de modèle et procédé de fabrication d'un article optiquement mis en forme
JP6615849B2 (ja) モデル材用組成物
JPWO2019176139A1 (ja) モデル材用組成物、及び光造形用組成物セット
JP6517456B2 (ja) 光造形用インクセット、光造形品、及び、光造形品の製造方法
CN108713033B (zh) 模型材用组合物、光造型品以及光造型品的制造方法
WO2018143299A1 (fr) Ensemble d'encres pour stéréolithographie, article stéréolithographique et procédé de production d'article stéréolithographique
JP7133619B2 (ja) サポート材組成物
JP7217160B2 (ja) モデル材クリア組成物
JP2020040407A (ja) モデル材用組成物
JP2020040408A (ja) モデル材用組成物
WO2019230134A1 (fr) Ensemble de composition de photo-fabrication, article photo-fabriqué, et méthode de production d'un article photo-fabriqué
JP2019155801A (ja) モデル材用組成物、及びマテリアルジェット光造形用組成物セット
JP2021130724A (ja) 光造形用組成物セット
JP2019206112A (ja) 光造形用組成物セット、光造形品、及び光造形品の製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18748521

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2018565622

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18748521

Country of ref document: EP

Kind code of ref document: A1