[go: up one dir, main page]

WO2018143017A1 - Élément à cristaux liquides et son procédé de production, et dispositif d'affichage - Google Patents

Élément à cristaux liquides et son procédé de production, et dispositif d'affichage Download PDF

Info

Publication number
WO2018143017A1
WO2018143017A1 PCT/JP2018/002007 JP2018002007W WO2018143017A1 WO 2018143017 A1 WO2018143017 A1 WO 2018143017A1 JP 2018002007 W JP2018002007 W JP 2018002007W WO 2018143017 A1 WO2018143017 A1 WO 2018143017A1
Authority
WO
WIPO (PCT)
Prior art keywords
liquid crystal
group
compound
polymer
aligning agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2018/002007
Other languages
English (en)
Japanese (ja)
Inventor
幸志 樫下
内山　克博
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JSR Corp
Original Assignee
JSR Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JSR Corp filed Critical JSR Corp
Priority to CN201880006576.5A priority Critical patent/CN110168439B/zh
Priority to JP2018566077A priority patent/JP6766894B2/ja
Publication of WO2018143017A1 publication Critical patent/WO2018143017A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Cet élément à cristaux liquides comporte : une paire de substrats qui sont disposés l'un en face de l'autre; des électrodes qui sont disposées sur les surfaces opposées de la paire de substrats; une couche de cristaux liquides qui est interposée entre la paire de substrats et qui est formée par durcissement d'une composition de cristaux liquides comprenant un cristal liquide et un composé polymérisable; et un film d'alignement de cristaux liquides qui est formé sur les surfaces sur lesquelles les électrodes sont disposées. Le composé polymérisable contient un composé (méth) acrylate monofonctionnel, un composé (méth) acrylate polyfonctionnel et similaire. Le film d'alignement de cristaux liquides est formé à l'aide d'un agent d'alignement de cristaux liquides contenant un composant polymère. L'agent d'alignement de cristaux liquides contient au moins un type de composé qui est choisi dans le groupe constitué de composés de silane et de polysiloxanes et dans lequel le rapport de teneur d'une unité structurelle dérivée d'un monomère ayant une structure de chaîne latérale spécifique est de 10 % en moles ou moins par rapport à la quantité totale de toutes les unités structurales du composant polymère.
PCT/JP2018/002007 2017-02-06 2018-01-23 Élément à cristaux liquides et son procédé de production, et dispositif d'affichage Ceased WO2018143017A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN201880006576.5A CN110168439B (zh) 2017-02-06 2018-01-23 液晶元件及其制造方法、液晶取向剂、以及显示装置
JP2018566077A JP6766894B2 (ja) 2017-02-06 2018-01-23 液晶素子及びその製造方法、並びに表示装置

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017-019833 2017-02-06
JP2017019833 2017-02-06

Publications (1)

Publication Number Publication Date
WO2018143017A1 true WO2018143017A1 (fr) 2018-08-09

Family

ID=63039612

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/002007 Ceased WO2018143017A1 (fr) 2017-02-06 2018-01-23 Élément à cristaux liquides et son procédé de production, et dispositif d'affichage

Country Status (4)

Country Link
JP (1) JP6766894B2 (fr)
CN (1) CN110168439B (fr)
TW (1) TWI745537B (fr)
WO (1) WO2018143017A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111142290A (zh) * 2018-11-06 2020-05-12 Dic株式会社 液晶显示元件
KR20200104481A (ko) * 2019-02-26 2020-09-04 주식회사 디케이티 고분자 분산형 박막액정 표시장치
WO2022196361A1 (fr) * 2021-03-15 2022-09-22 株式会社ジャパンディスプレイ Procédé de fabrication de dispositif d'affichage

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE112021002330T5 (de) * 2020-06-25 2023-02-23 Nippon Kayaku Kabushiki Kaisha Anthrachinonverbindung, flüssigkristallzusammensetzung zum dimmen, die diese verbindung beinhaltet, und dimmelement

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0829759A (ja) * 1994-07-18 1996-02-02 Kawamura Inst Of Chem Res 液晶デバイス及びその製造方法
JP2003253265A (ja) * 2002-02-27 2003-09-10 Dainippon Ink & Chem Inc 調光層形成材料及び液晶デバイス
JP2004317908A (ja) * 2003-04-18 2004-11-11 Sony Corp 携帯式情報表示装置
JP2007334344A (ja) * 2006-05-19 2007-12-27 Nec Lcd Technologies Ltd 光源装置、表示装置、端末装置及び透明・散乱切替素子
JP2011059589A (ja) * 2009-09-14 2011-03-24 Sony Ericsson Mobilecommunications Japan Inc 表示装置、携帯情報端末、携帯情報端末の表示制御方法及び表示制御プログラム、
US20140078455A1 (en) * 2011-11-29 2014-03-20 Beijing Boe Optoelectronics Technology Co., Ltd. Liquid display panel and process for preparing same
WO2014167885A1 (fr) * 2013-04-12 2014-10-16 Jsr株式会社 Dispositif optique

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7113241B2 (en) * 2001-08-31 2006-09-26 Sharp Kabushiki Kaisha Liquid crystal display and method of manufacturing the same
JP4627484B2 (ja) * 2005-10-28 2011-02-09 大日本印刷株式会社 光学素子の製造方法、および、液晶表示装置
US8446548B2 (en) * 2006-05-19 2013-05-21 Nlt Technologies, Ltd. Light source device, display device, terminal device, and transparent/scattering state switching element
JP4708287B2 (ja) * 2006-08-25 2011-06-22 富士フイルム株式会社 光学フィルムの製造方法、光学フィルム、偏光板、転写材料、液晶表示装置、及び偏光紫外線露光装置
JP6241058B2 (ja) * 2013-04-15 2017-12-06 ソニー株式会社 液晶表示装置

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0829759A (ja) * 1994-07-18 1996-02-02 Kawamura Inst Of Chem Res 液晶デバイス及びその製造方法
JP2003253265A (ja) * 2002-02-27 2003-09-10 Dainippon Ink & Chem Inc 調光層形成材料及び液晶デバイス
JP2004317908A (ja) * 2003-04-18 2004-11-11 Sony Corp 携帯式情報表示装置
JP2007334344A (ja) * 2006-05-19 2007-12-27 Nec Lcd Technologies Ltd 光源装置、表示装置、端末装置及び透明・散乱切替素子
JP2011059589A (ja) * 2009-09-14 2011-03-24 Sony Ericsson Mobilecommunications Japan Inc 表示装置、携帯情報端末、携帯情報端末の表示制御方法及び表示制御プログラム、
US20140078455A1 (en) * 2011-11-29 2014-03-20 Beijing Boe Optoelectronics Technology Co., Ltd. Liquid display panel and process for preparing same
WO2014167885A1 (fr) * 2013-04-12 2014-10-16 Jsr株式会社 Dispositif optique

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111142290A (zh) * 2018-11-06 2020-05-12 Dic株式会社 液晶显示元件
KR20200104481A (ko) * 2019-02-26 2020-09-04 주식회사 디케이티 고분자 분산형 박막액정 표시장치
KR102178886B1 (ko) 2019-02-26 2020-11-17 재단법인 구미전자정보기술원 고분자 분산형 박막액정 표시장치
WO2022196361A1 (fr) * 2021-03-15 2022-09-22 株式会社ジャパンディスプレイ Procédé de fabrication de dispositif d'affichage
CN116981990A (zh) * 2021-03-15 2023-10-31 株式会社日本显示器 显示装置的制造方法

Also Published As

Publication number Publication date
JPWO2018143017A1 (ja) 2019-11-07
TWI745537B (zh) 2021-11-11
TW201835317A (zh) 2018-10-01
CN110168439A (zh) 2019-08-23
JP6766894B2 (ja) 2020-10-14
CN110168439B (zh) 2022-05-17

Similar Documents

Publication Publication Date Title
JP6870689B2 (ja) 液晶素子及びその製造方法、並びに表示装置
CN104140826B (zh) 液晶取向剂、液晶取向膜、相位差膜与它们的制造方法、以及液晶显示元件
KR101726250B1 (ko) 액정 표시 소자 및 그의 제조 방법
CN103509562B (zh) 液晶配向剂、液晶配向膜、相位差膜、相位差膜的制造方法、液晶显示元件及聚合物
JP6766894B2 (ja) 液晶素子及びその製造方法、並びに表示装置
CN103320146B (zh) 液晶配向剂、液晶配向膜、液晶显示元件以及液晶显示元件的制造方法
TWI510464B (zh) 顯示器用材料、液晶配向劑、液晶顯示元件及液晶顯示元件的製造方法
JP6658213B2 (ja) 視野角補償フィルム、視野角補償フィルムの製造方法、偏光板、液晶表示素子及び有機ｅｌ素子
JP2014112192A (ja) Ｐｓａモード液晶表示素子用液晶配向剤、ｐｓａモード液晶表示素子用液晶配向膜、並びにｐｓａモード液晶表示素子及びその製造方法
CN103820129B (zh) 液晶取向剂、液晶取向膜及其形成方法、液晶显示元件的相位差膜及液晶单元
CN115443429B (zh) 液晶元件及其制造方法
TW201928478A (zh) 液晶元件的製造方法
JP6264053B2 (ja) Ｐｓａモード液晶表示素子用液晶配向剤、ｐｓａモード液晶表示素子用液晶配向膜、並びにｐｓａモード液晶表示素子及びその製造方法
JP2020016710A (ja) 液晶素子及びその製造方法、表示装置、並びに液晶組成物
CN109073934B (zh) 取向膜及液晶显示装置
TW201835163A (zh) 液晶元件及其製造方法
KR102237289B1 (ko) 액정 배향제, 액정 배향막 및 그의 제조 방법, 액정 표시 소자, 그리고 위상차 필름 및 그의 제조 방법
JP6451941B2 (ja) 液晶配向剤および液晶表示素子
JP2015180916A (ja) 液晶表示素子の製造方法
WO2017086040A1 (fr) Procédé de fabrication d'élément de commande de lumière, et élément de commande de lumière

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18748669

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2018566077

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase