WO2018142721A1 - Particules de diffusion de lumière, feuille de diffusion et de transmission de lumière et procédé de production de particules de diffusion de lumière - Google Patents

Particules de diffusion de lumière, feuille de diffusion et de transmission de lumière et procédé de production de particules de diffusion de lumière Download PDF

Info

Publication number
WO2018142721A1
WO2018142721A1 PCT/JP2017/041170 JP2017041170W WO2018142721A1 WO 2018142721 A1 WO2018142721 A1 WO 2018142721A1 JP 2017041170 W JP2017041170 W JP 2017041170W WO 2018142721 A1 WO2018142721 A1 WO 2018142721A1
Authority
WO
WIPO (PCT)
Prior art keywords
particles
light diffusing
refractive index
light
binder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2017/041170
Other languages
English (en)
Japanese (ja)
Inventor
多佳子 岩井
耕一郎 壹岐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Sheet Glass Co Ltd
Original Assignee
Nippon Sheet Glass Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Sheet Glass Co Ltd filed Critical Nippon Sheet Glass Co Ltd
Priority to JP2018565951A priority Critical patent/JP6793210B2/ja
Publication of WO2018142721A1 publication Critical patent/WO2018142721A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne des particules de diffusion de lumière (10) qui comprennent un cœur (10c) et une enveloppe (10s). Le cœur (10c) est formé à partir d'un premier liant (11) et de premières particules fines (12). Les premières particules fines (12) comprennent une particule fine à faible indice de réfraction (12a) qui a un indice de réfraction inférieur à celui du premier liant (11). Les premières particules fines (12) entrent en contact et sont recouvertes par le premier liant. L'enveloppe (10s) entre en contact avec une surface extérieure du cœur (10c) et recouvre le cœur (10c). Le cœur (10s) comprend des particules sphériques (13) qui ont un diamètre de particule de 50 à 450 nm et donnent la rugosité (A) de surface de l'enveloppe (10s).
PCT/JP2017/041170 2017-01-31 2017-11-16 Particules de diffusion de lumière, feuille de diffusion et de transmission de lumière et procédé de production de particules de diffusion de lumière Ceased WO2018142721A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2018565951A JP6793210B2 (ja) 2017-01-31 2017-11-16 光拡散粒子、光拡散透過シート、及び光拡散粒子を製造する方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017016018 2017-01-31
JP2017-016018 2017-01-31

Publications (1)

Publication Number Publication Date
WO2018142721A1 true WO2018142721A1 (fr) 2018-08-09

Family

ID=63040386

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/041170 Ceased WO2018142721A1 (fr) 2017-01-31 2017-11-16 Particules de diffusion de lumière, feuille de diffusion et de transmission de lumière et procédé de production de particules de diffusion de lumière

Country Status (2)

Country Link
JP (1) JP6793210B2 (fr)
WO (1) WO2018142721A1 (fr)

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH1129318A (ja) * 1997-05-06 1999-02-02 Nippon Millipore Kk ミクロンサイズの球状シリカ粒子とその製造法
JPH1160230A (ja) * 1997-08-08 1999-03-02 Mizusawa Ind Chem Ltd 非晶質シリカ系複合粒子及びその用途
JPH11237506A (ja) * 1998-02-20 1999-08-31 Nippon Shokubai Co Ltd 光選択透過膜
JP2001233611A (ja) * 2000-02-24 2001-08-28 Catalysts & Chem Ind Co Ltd シリカ系微粒子、該微粒子分散液の製造方法、および被膜付基材
JP2003107217A (ja) * 2001-09-28 2003-04-09 Fuji Photo Film Co Ltd 光拡散板及びその製造方法
JP2006084927A (ja) * 2004-09-17 2006-03-30 Gantsu Kasei Kk 光拡散剤およびその製造法
JP2008291253A (ja) * 2007-04-27 2008-12-04 Daicel Chem Ind Ltd 無機粒子を含む複合樹脂粒子
JP2009080256A (ja) * 2007-09-26 2009-04-16 Dainippon Printing Co Ltd 防眩フィルム
JP2016532162A (ja) * 2013-09-16 2016-10-13 コエルクス・エッセ・エッレ・エッレＣｏｅＬｕｘ Ｓ．ｒ．ｌ． ポリマーマトリクスとナノ粒子を含む複合材料、その製造方法及び使用
WO2017047055A1 (fr) * 2015-09-15 2017-03-23 日本板硝子株式会社 Feuille diffusant et transmettant la lumière

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7960021B2 (en) * 2007-05-16 2011-06-14 Lg Chem, Ltd. Composition for anti-glare film and anti-glare film prepared using the same
JP5824678B2 (ja) * 2011-04-05 2015-11-25 パナソニックＩｐマネジメント株式会社 有機エレクトロルミネッセンス素子
JP6009241B2 (ja) * 2012-06-25 2016-10-19 早川ゴム株式会社 コアシェル微粒子の製造方法
CN107709430B (zh) * 2015-03-18 2019-11-01 科勒克斯有限责任公司 包含基体和散射成分的复合材料系统及其制备方法和用途

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH1129318A (ja) * 1997-05-06 1999-02-02 Nippon Millipore Kk ミクロンサイズの球状シリカ粒子とその製造法
JPH1160230A (ja) * 1997-08-08 1999-03-02 Mizusawa Ind Chem Ltd 非晶質シリカ系複合粒子及びその用途
JPH11237506A (ja) * 1998-02-20 1999-08-31 Nippon Shokubai Co Ltd 光選択透過膜
JP2001233611A (ja) * 2000-02-24 2001-08-28 Catalysts & Chem Ind Co Ltd シリカ系微粒子、該微粒子分散液の製造方法、および被膜付基材
JP2003107217A (ja) * 2001-09-28 2003-04-09 Fuji Photo Film Co Ltd 光拡散板及びその製造方法
JP2006084927A (ja) * 2004-09-17 2006-03-30 Gantsu Kasei Kk 光拡散剤およびその製造法
JP2008291253A (ja) * 2007-04-27 2008-12-04 Daicel Chem Ind Ltd 無機粒子を含む複合樹脂粒子
JP2009080256A (ja) * 2007-09-26 2009-04-16 Dainippon Printing Co Ltd 防眩フィルム
JP2016532162A (ja) * 2013-09-16 2016-10-13 コエルクス・エッセ・エッレ・エッレＣｏｅＬｕｘ Ｓ．ｒ．ｌ． ポリマーマトリクスとナノ粒子を含む複合材料、その製造方法及び使用
WO2017047055A1 (fr) * 2015-09-15 2017-03-23 日本板硝子株式会社 Feuille diffusant et transmettant la lumière

Also Published As

Publication number Publication date
JPWO2018142721A1 (ja) 2019-11-07
JP6793210B2 (ja) 2020-12-02

Similar Documents

Publication Publication Date Title
JP4199038B2 (ja) 防眩フィルム
TWI460475B (zh) 光學片材
CN103109212B (zh) 光扩散元件、带光扩散元件的偏振板、及使用其的液晶显示装置
KR20130041344A (ko) 광확산 소자 및 광확산 소자를 가진 편광판
WO2018062442A1 (fr) Film de revêtement dur antiéblouissement antiréflexion, dispositif d'affichage d'image, et procédé de production d'un film de revêtement dur antiéblouissement antireflet
JP7446663B2 (ja) 光学フィルムおよびこれを含むマイクロｌｅｄディスプレイ
CN103109214A (zh) 光扩散膜、带光扩散膜的偏振板、液晶显示装置及照明器具
JP5883598B2 (ja) 光拡散素子および光拡散素子付偏光板の製造方法、ならびに、これらの方法で得られた光拡散素子および光拡散素子付偏光板
TWI468739B (zh) 光學片材
JP5129379B2 (ja) 光拡散素子
JP6475849B2 (ja) 光拡散透過シート及び複合粒子の製造方法
JP5488430B2 (ja) 動画像と静止画像との混用に適した液晶表示装置の黒彩感及び画像の切れの改善方法
JP6793211B2 (ja) 光拡散粒子、光拡散透過シート、及び光拡散粒子を製造する方法
JP6793210B2 (ja) 光拡散粒子、光拡散透過シート、及び光拡散粒子を製造する方法
CN105164557A (zh) 光扩散元件及光扩散元件的制造方法
CN101713837A (zh) 多层次微粒体及其抗眩膜
CN105190368A (zh) 光扩散元件的制造方法及光扩散元件
TW201814005A (zh) 光擴散透射片
WO2017047056A1 (fr) Feuille émettant et diffusant la lumière
TWI484227B (zh) Light diffusion element
TW201814007A (zh) 光擴散透射片

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17895165

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2018565951

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17895165

Country of ref document: EP

Kind code of ref document: A1