WO2018021117A1 - Procédé de production d'éléments semi-conducteurs et procédé de production de cellules solaires - Google Patents

Procédé de production d'éléments semi-conducteurs et procédé de production de cellules solaires Download PDF

Info

Publication number
WO2018021117A1
WO2018021117A1 PCT/JP2017/026143 JP2017026143W WO2018021117A1 WO 2018021117 A1 WO2018021117 A1 WO 2018021117A1 JP 2017026143 W JP2017026143 W JP 2017026143W WO 2018021117 A1 WO2018021117 A1 WO 2018021117A1
Authority
WO
WIPO (PCT)
Prior art keywords
composition
film
layer
impurity diffusion
semiconductor substrate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2017/026143
Other languages
English (en)
Japanese (ja)
Inventor
剛 北田
白沢　信彦
村瀬　清一郎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toray Industries Inc
Original Assignee
Toray Industries Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toray Industries Inc filed Critical Toray Industries Inc
Priority to JP2017538749A priority Critical patent/JPWO2018021117A1/ja
Publication of WO2018021117A1 publication Critical patent/WO2018021117A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Selon un mode de réalisation, l'invention concerne un procédé de production d'éléments semi-conducteurs qui consiste en une étape de formation de couche de pellicules et en une étape de diffusion. Selon l'étape de formation de couche de pellicules, une pellicule A et une pellicule B sont formées sur un substrat semi-conducteur. La pellicule A est une pellicule de composition de diffusion d'impuretés qui est formée au moyen d'une composition A qui contient un composant de diffusion d'impuretés. La pellicule B est une couche de suppression de diffusion dans l'air qui supprime la diffusion dans l'air du composant de diffusion d'impuretés depuis au moins la pellicule A et qui est formée au moyen d'une composition B qui contient du polysiloxane. Selon l'étape de diffusion, le substrat semi-conducteur sur lequel la pellicule A et la pellicule B sont formées est traité thermiquement, et le composant de diffusion d'impuretés est ainsi diffusé dans le substrat semi-conducteur. Ce procédé de production d'éléments semi-conducteurs est utilisable dans un procédé de production de cellules solaires.
PCT/JP2017/026143 2016-07-26 2017-07-19 Procédé de production d'éléments semi-conducteurs et procédé de production de cellules solaires Ceased WO2018021117A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2017538749A JPWO2018021117A1 (ja) 2016-07-26 2017-07-19 半導体素子の製造方法および太陽電池の製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016-146036 2016-07-26
JP2016146036 2016-07-26

Publications (1)

Publication Number Publication Date
WO2018021117A1 true WO2018021117A1 (fr) 2018-02-01

Family

ID=61016245

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/026143 Ceased WO2018021117A1 (fr) 2016-07-26 2017-07-19 Procédé de production d'éléments semi-conducteurs et procédé de production de cellules solaires

Country Status (3)

Country Link
JP (1) JPWO2018021117A1 (fr)
TW (1) TW201813120A (fr)
WO (1) WO2018021117A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020116270A1 (fr) * 2018-12-07 2020-06-11 東レ株式会社 Composition pour diffusion d'impuretés du type p et son procédé de production, procédé de fabrication d'élément à semi-conducteur utilisant ladite composition pour diffusion, et batterie solaire
JP2023531891A (ja) * 2020-06-15 2023-07-26 コンセホ・スペリオール・デ・インベスティガシオネス・シエンティフィカス 分子半導体対象膜の構造的および／または組成的改質を提供するための方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2006117975A1 (fr) * 2005-04-26 2006-11-09 Shin-Etsu Handotai Co., Ltd. Procédé de fabrication d’une cellule solaire et cellule solaire
JP2008078665A (ja) * 2006-09-22 2008-04-03 Commiss Energ Atom 基板にドープ領域を形成する方法及び光電池
JP2014175407A (ja) * 2013-03-07 2014-09-22 Tokyo Ohka Kogyo Co Ltd 拡散剤組成物、不純物拡散層の形成方法、及び太陽電池
WO2015002132A1 (fr) * 2013-07-04 2015-01-08 東レ株式会社 Composition de diffusion d'impuretés et procédé de production d'un élément à semiconducteur

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2006117975A1 (fr) * 2005-04-26 2006-11-09 Shin-Etsu Handotai Co., Ltd. Procédé de fabrication d’une cellule solaire et cellule solaire
JP2008078665A (ja) * 2006-09-22 2008-04-03 Commiss Energ Atom 基板にドープ領域を形成する方法及び光電池
JP2014175407A (ja) * 2013-03-07 2014-09-22 Tokyo Ohka Kogyo Co Ltd 拡散剤組成物、不純物拡散層の形成方法、及び太陽電池
WO2015002132A1 (fr) * 2013-07-04 2015-01-08 東レ株式会社 Composition de diffusion d'impuretés et procédé de production d'un élément à semiconducteur

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020116270A1 (fr) * 2018-12-07 2020-06-11 東レ株式会社 Composition pour diffusion d'impuretés du type p et son procédé de production, procédé de fabrication d'élément à semi-conducteur utilisant ladite composition pour diffusion, et batterie solaire
CN113169247A (zh) * 2018-12-07 2021-07-23 东丽株式会社 p型杂质扩散组合物及其制造方法、使用其的半导体元件的制造方法和太阳能电池
JPWO2020116270A1 (ja) * 2018-12-07 2021-10-14 東レ株式会社 ｐ型不純物拡散組成物とその製造方法、それを用いた半導体素子の製造方法および太陽電池
JP7463725B2 (ja) 2018-12-07 2024-04-09 東レ株式会社 ｐ型不純物拡散組成物とその製造方法、それを用いた半導体素子の製造方法および太陽電池
JP2023531891A (ja) * 2020-06-15 2023-07-26 コンセホ・スペリオール・デ・インベスティガシオネス・シエンティフィカス 分子半導体対象膜の構造的および／または組成的改質を提供するための方法
JP7562710B2 (ja) 2020-06-15 2024-10-07 コンセホ・スペリオール・デ・インベスティガシオネス・シエンティフィカス 分子半導体対象膜の構造的および／または組成的改質を提供するための方法

Also Published As

Publication number Publication date
JPWO2018021117A1 (ja) 2019-05-09
TW201813120A (zh) 2018-04-01

Similar Documents

Publication Publication Date Title
US9691935B2 (en) Impurity-diffusing composition and method for producing semiconductor element
CN102986004B (zh) 扩散剂组合物及杂质扩散层的形成方法
KR20170122198A (ko) p형 불순물 확산 조성물, 그것을 사용한 반도체 소자의 제조 방법, 및 태양 전지 및 그의 제조 방법
WO2015146524A1 (fr) Procédé de formation de motif
JP7459511B2 (ja) 半導体素子の製造方法、および、太陽電池の製造方法
JP2016195203A (ja) ｐ型不純物拡散組成物、それを用いた半導体素子の製造方法および太陽電池。
WO2018021117A1 (fr) Procédé de production d'éléments semi-conducteurs et procédé de production de cellules solaires
JP2017103379A (ja) 不純物拡散組成物、およびそれを用いた半導体素子の製造方法
JP6772836B2 (ja) ｐ型不純物拡散組成物、それを用いた半導体素子の製造方法および太陽電池の製造方法
JP7463725B2 (ja) ｐ型不純物拡散組成物とその製造方法、それを用いた半導体素子の製造方法および太陽電池
JP2014168026A (ja) マスクペースト組成物、これを用いて得られる半導体素子および半導体素子の製造方法
KR102124920B1 (ko) 마스크 페이스트 조성물, 이것을 사용해서 얻어지는 반도체 소자 및 반도체 소자의 제조 방법
TW201639007A (zh) 不純物擴散組成物、使用其的半導體元件的製造方法及太陽電池
CN111771258B (zh) 杂质扩散组合物、使用了该杂质扩散组合物的半导体元件的制造方法及太阳能电池的制造方法
CN108391449B (zh) 半导体元件的制造方法和太阳能电池的制造方法
TWI591127B (zh) 罩幕漿組成物、罩幕層、使用其所得到的半導體元件及半導體元件的製造方法
TW201829625A (zh) 不純物擴散組成物及使用其的半導體元件的製造方法

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2017538749

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17834125

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase