WO2017114298A1 - 一种环保型耐油密封胶 - Google Patents

一种环保型耐油密封胶 Download PDF

Info

Publication number
WO2017114298A1
WO2017114298A1 PCT/CN2016/111675 CN2016111675W WO2017114298A1 WO 2017114298 A1 WO2017114298 A1 WO 2017114298A1 CN 2016111675 W CN2016111675 W CN 2016111675W WO 2017114298 A1 WO2017114298 A1 WO 2017114298A1
Authority
WO
WIPO (PCT)
Prior art keywords
parts
oil
resistant sealant
plasticizer
paraffin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/CN2016/111675
Other languages
English (en)
French (fr)
Inventor
李栋军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of WO2017114298A1 publication Critical patent/WO2017114298A1/zh
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

一种环保型耐油密封胶，其由以下重量份数的原料制成：乙二醇8-15份，滑石粉6-14份，苯基硅油8-15份，二乙基甲氧基硅氧基12-24份，炭黑15-30份，增塑剂12-20份，纳米碳酸钙15-24份，增粘树脂0.8-1.7份，阻燃填料20-32份，水分清除剂1.5-4份，热稳定剂2-7份，玻璃纤维0.8-1.8份，二甲基丙烯酸镁0.8-1.5份，石蜡1.5-2.5份，过氧化二乙酰0.5-3.2份，环氧树脂4-6份。本发明的有益效果是，本发明的环保型耐油密封胶，具有很好的耐酸碱、耐油性能，粘接稳定，有弹性，制备工艺简单，无毒、无腐蚀，对环境没有污染。

Description

说明书 发明名称：一种环保型耐油密封胶
技术领域
[0001] 本发明涉及一种环保型耐油密封胶。
背景技术
[0002] 七十年代以后， 密封胶已幵始用于建筑结构接缝密封， 逐渐成为主体材料。 随 着密封胶的发展， 密封胶不但被用于建筑、 土木、 桥梁， 而且也广泛的应用于 集装箱、 船舶、 电气、 航天等众多工程领域。 密封胶可以用来填充构形间隙、 以起到很好密封作用， 具有防泄漏、 防水、 防振动及隔音、 隔热等作用。 随着 市场需求量的增加， 对密封胶的性能的要求也越来越高， 传统的密封胶存在耐 油性差、 易撕裂的缺陷， 而且会对环境造成一定的污染， 不符合现在的使用要 求。
技术问题
[0003] 针对现有技术的不足， 本发明要解决的问题是， 提供一种环保型耐油密封胶， 具有很好的耐酸碱、 耐油性能， 粘接稳定， 有弹性， 制备工艺简单， 无毒、 无 腐蚀， 对环境没有污染。
问题的解决方案
技术解决方案
[0004] 为解决上述技术问题， 本发明的技术方案是， 一种环保型耐油密封胶， 其由以 下重量份数的原料制成： 乙二醇 8-15份， 滑石粉 6-14份， 苯基硅油 8-15份， 二乙 基甲氧基硅氧基 12-24份， 炭黑 15-30份， 增塑剂 12-20份， 纳米碳酸钙 15-24份， 增粘树脂 0.8-1.7份， 阻燃填料 20-32份， 水分清除剂 1.5-4份， 热稳定剂 2-7份， 玻 璃纤维 0.8-1.8份， 二甲基丙烯酸镁 0.8-1.5份， 石蜡 1.5-2.5份， 过氧化二乙酰 0.5-3. 2份， 环氧树脂 4-6份。
[0005] 优化的， 一种环保型耐油密封胶， 其由以下重量份数的原料制成： 乙二醇 12份 ， 滑石粉 10份， 苯基硅油 11份， 二乙基甲氧基硅氧基 18份， 炭黑 23份， 增塑剂 1 6份， 纳米碳酸钙 19份， 增粘树脂 1.3份， 阻燃填料 26份， 水分清除剂 2.9份， 热 稳定剂 4.5份， 玻璃纤维 1.3份， 二甲基丙烯酸镁 1份， 石蜡 2份， 过氧化二乙酰 2.3 份， 环氧树脂 5份。
发明的有益效果
有益效果
[0006] 本发明的有益效果是， 本发明的环保型耐油密封胶， 具有很好的耐酸碱、 耐油 性能， 粘接稳定， 有弹性， 制备工艺简单， 无毒、 无腐蚀， 对环境没有污染。 实施该发明的最佳实施例
本发明的最佳实施方式
[0007] 一种环保型耐油密封胶， 其由以下重量份数的原料制成： 乙二醇 12份， 滑石粉 10份， 苯基硅油 11份， 二乙基甲氧基硅氧基 18份， 炭黑 23份， 增塑剂 16份， 纳 米碳酸钙 19份， 增粘树脂 1.3份， 阻燃填料 26份， 水分清除剂 2.9份， 热稳定剂 4.5 份， 玻璃纤维 1.3份， 二甲基丙烯酸镁 1份， 石蜡 2份， 过氧化二乙酰 2.3份， 环氧 树脂 5份。
本发明的实施方式
[0008] 实施例 1
[0009] 一种环保型耐油密封胶， 其由以下重量份数的原料制成： 乙二醇 8份， 滑石粉 6 份， 苯基硅油 8份， 二乙基甲氧基硅氧基 12份， 炭黑 15份， 增塑剂 12份， 纳米碳 酸钙 15份， 增粘树脂 0.8份， 阻燃填料 20份， 水分清除剂 1.5份， 热稳定剂 2份， 玻璃纤维 0.8份， 二甲基丙烯酸镁 0.8份， 石蜡 1.5份， 过氧化二乙酰 0.5份， 环氧 树脂 4份。
[0010] 实施例 2
[0011] 一种环保型耐油密封胶， 其由以下重量份数的原料制成： 乙二醇 15份， 滑石粉 14份， 苯基硅油 15份， 二乙基甲氧基硅氧基 24份， 炭黑 30份， 增塑剂 20份， 纳 米碳酸钙 24份， 增粘树脂 1.7份， 阻燃填料 32份， 水分清除剂 4份， 热稳定剂 7份 ， 玻璃纤维 1.8份， 二甲基丙烯酸镁 1.5份， 石蜡 2.5份， 过氧化二乙酰 3.2份， 环 氧树脂 6份。 [0012] 实施例 3
[0013] 一种环保型耐油密封胶， 其由以下重量份数的原料制成： 乙二醇 12份， 滑石粉 10份， 苯基硅油 11份， 二乙基甲氧基硅氧基 18份， 炭黑 23份， 增塑剂 16份， 纳 米碳酸钙 19份， 增粘树脂 1.3份， 阻燃填料 26份， 水分清除剂 2.9份， 热稳定剂 4.5 份， 玻璃纤维 1.3份， 二甲基丙烯酸镁 1份， 石蜡 2份， 过氧化二乙酰 2.3份， 环氧 树脂 5份。

Claims

权利要求书
[权利要求 1] 一种环保型耐油密封胶， 其特征在于： 其由以下重量份数的原料制成
： 乙二醇 8-15份， 滑石粉 6-14份， 苯基硅油 8-15份， 二乙基甲氧基硅 氧基 12-24份， 炭黑 15-30份， 增塑剂 12-20份， 纳米碳酸钙 15-24份， 增粘树脂 0.8-1.7份， 阻燃填料 20-32份， 水分清除剂 1.5-4份， 热稳定 剂 2-7份， 玻璃纤维 0.8-1.8份， 二甲基丙烯酸镁 0.8-1.5份， 石蜡 1.5-2.5 份， 过氧化二乙酰 0.5-3.2份， 环氧树脂 4-6份。
[权利要求 2] 根据权利要求 1所述的环保型耐油密封胶， 其特征在于： 其由以下重 量份数的原料制成： 乙二醇 12份， 滑石粉 10份， 苯基硅油 11份， 二乙 基甲氧基硅氧基 18份， 炭黑 23份， 增塑剂 16份， 纳米碳酸钙 19份， 增 粘树脂 1.3份， 阻燃填料 26份， 水分清除剂 2.9份， 热稳定剂 4.5份， 玻 璃纤维 1.3份， 二甲基丙烯酸镁 1份， 石蜡 2份， 过氧化二乙酰 2.3份， 环氧树脂 5份。
PCT/CN2016/111675 2015-12-30 2016-12-23 一种环保型耐油密封胶 Ceased WO2017114298A1 (zh)