WO2017039004A1 - Film intercouches pour verre feuilleté, et verre feuilleté - Google Patents

Film intercouches pour verre feuilleté, et verre feuilleté Download PDF

Info

Publication number
WO2017039004A1
WO2017039004A1 PCT/JP2016/075901 JP2016075901W WO2017039004A1 WO 2017039004 A1 WO2017039004 A1 WO 2017039004A1 JP 2016075901 W JP2016075901 W JP 2016075901W WO 2017039004 A1 WO2017039004 A1 WO 2017039004A1
Authority
WO
WIPO (PCT)
Prior art keywords
laminated glass
display
display corresponding
interlayer film
intermediate film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2016/075901
Other languages
English (en)
Japanese (ja)
Inventor
悦朗 廣田
博満 西野
孝次 熊倉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sekisui Chemical Co Ltd
Original Assignee
Sekisui Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sekisui Chemical Co Ltd filed Critical Sekisui Chemical Co Ltd
Priority to JP2016558414A priority Critical patent/JPWO2017039004A1/ja
Publication of WO2017039004A1 publication Critical patent/WO2017039004A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un film intercouches pour verre feuilleté permettant de reconnaître facilement la région de correspondance d'affichage du film intercouches correspondant à la région d'affichage d'un affichage tête haute lors de l'obtention d'un verre feuilleté, de positionner plus précisément la région de correspondance d'affichage du film intercouches sur la région d'affichage d'un affichage tête haute dans un verre feuilleté, et de bien afficher les informations dans un affichage tête haute. Ledit film intercouches pour verre feuilleté selon la présente invention comprend une résine thermoplastique, présente une extrémité et une autre extrémité plus épaisse que ladite extrémité sur le côté en regard de ladite extrémité, présente une région de correspondance d'affichage correspondant à la région d'affichage d'un affichage tête haute, et permet de distinguer visuellement la région de correspondance d'affichage de la région environnante adjacente à la région de correspondance d'affichage, ou la couleur ou la brillance de la région de correspondance d'affichage diffère de la couleur ou de la brillance de la région environnante adjacente à la région de correspondance d'affichage.
PCT/JP2016/075901 2015-09-03 2016-09-02 Film intercouches pour verre feuilleté, et verre feuilleté Ceased WO2017039004A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2016558414A JPWO2017039004A1 (ja) 2015-09-03 2016-09-02 合わせガラス用中間膜及び合わせガラス

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2015-173947 2015-09-03
JP2015173947 2015-09-03

Publications (1)

Publication Number Publication Date
WO2017039004A1 true WO2017039004A1 (fr) 2017-03-09

Family

ID=58188896

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/075901 Ceased WO2017039004A1 (fr) 2015-09-03 2016-09-02 Film intercouches pour verre feuilleté, et verre feuilleté

Country Status (3)

Country Link
JP (1) JPWO2017039004A1 (fr)
TW (1) TW201718429A (fr)
WO (1) WO2017039004A1 (fr)

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019012919A1 (fr) * 2017-07-12 2019-01-17 セントラル硝子株式会社 Verre feuilleté pour pare-brise automobile
CN110045502A (zh) * 2019-03-23 2019-07-23 深圳京龙睿信科技有限公司 抬头显示器
CN111225887A (zh) * 2017-12-28 2020-06-02 积水化学工业株式会社 夹层玻璃用中间膜和夹层玻璃
CN111247110A (zh) * 2017-12-19 2020-06-05 积水化学工业株式会社 夹层玻璃
WO2020137851A1 (fr) 2018-12-28 2020-07-02 積水化学工業株式会社 Couche intercalaire de verre feuilleté, corps de rouleau, et procédé de fabrication d'un verre feuilleté
CN111566066A (zh) * 2017-12-19 2020-08-21 积水化学工业株式会社 夹层玻璃用中间膜及夹层玻璃
KR20210071208A (ko) * 2019-12-06 2021-06-16 에스케이씨 주식회사 접합용 필름 및 이를 포함하는 광투과 적층체
KR20210085840A (ko) * 2019-12-31 2021-07-08 에스케이씨 주식회사 접합용 필름 및 이를 포함하는 광투과 적층체
CN114206610A (zh) * 2019-08-09 2022-03-18 Skc株式会社 接合用膜及包括其的透光层叠体
WO2023200013A1 (fr) * 2022-04-15 2023-10-19 積水化学工業株式会社 Couche intercalaire pour verre feuilleté et son procédé de production et verre feuilleté et son procédé de production

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN116419869A (zh) * 2020-10-21 2023-07-11 积水化学工业株式会社 夹层玻璃和车辆

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06279071A (ja) * 1993-03-26 1994-10-04 Asahi Glass Co Ltd 積層ガラス
JPH0899561A (ja) * 1994-09-30 1996-04-16 Asahi Glass Co Ltd ヘッドアップディスプレイ
JPH08319141A (ja) * 1995-05-25 1996-12-03 Asahi Glass Co Ltd ホログラム封入合せガラス
JP2000187181A (ja) * 1998-12-22 2000-07-04 Central Glass Co Ltd 車両用表示装置
JP2007223883A (ja) * 2005-12-26 2007-09-06 Asahi Glass Co Ltd 車両用合せガラス
JP2014024312A (ja) * 2011-12-12 2014-02-06 Sekisui Chem Co Ltd 発光シート、合わせガラス用中間膜及び合わせガラス
WO2016133187A1 (fr) * 2015-02-20 2016-08-25 富士フイルム株式会社 Verre de pare-brise, et dispositif d'affichage tête haute

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06279071A (ja) * 1993-03-26 1994-10-04 Asahi Glass Co Ltd 積層ガラス
JPH0899561A (ja) * 1994-09-30 1996-04-16 Asahi Glass Co Ltd ヘッドアップディスプレイ
JPH08319141A (ja) * 1995-05-25 1996-12-03 Asahi Glass Co Ltd ホログラム封入合せガラス
JP2000187181A (ja) * 1998-12-22 2000-07-04 Central Glass Co Ltd 車両用表示装置
JP2007223883A (ja) * 2005-12-26 2007-09-06 Asahi Glass Co Ltd 車両用合せガラス
JP2014024312A (ja) * 2011-12-12 2014-02-06 Sekisui Chem Co Ltd 発光シート、合わせガラス用中間膜及び合わせガラス
WO2016133187A1 (fr) * 2015-02-20 2016-08-25 富士フイルム株式会社 Verre de pare-brise, et dispositif d'affichage tête haute

Cited By (34)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7206495B2 (ja) 2017-07-12 2023-01-18 セントラル硝子株式会社 車両フロント窓用の合せガラス
CN110891913A (zh) * 2017-07-12 2020-03-17 中央硝子株式会社 车辆前车窗用的夹层玻璃
JPWO2019012919A1 (ja) * 2017-07-12 2020-07-16 セントラル硝子株式会社 車両フロント窓用の合せガラス
WO2019012919A1 (fr) * 2017-07-12 2019-01-17 セントラル硝子株式会社 Verre feuilleté pour pare-brise automobile
CN110891913B (zh) * 2017-07-12 2022-06-10 中央硝子株式会社 车辆前车窗用的夹层玻璃
CN111247110B (zh) * 2017-12-19 2022-10-04 积水化学工业株式会社 夹层玻璃
US11458706B2 (en) 2017-12-19 2022-10-04 Sekisui Chemical Co., Ltd. Interlayer film for laminated glass, and laminated glass
CN111247110A (zh) * 2017-12-19 2020-06-05 积水化学工业株式会社 夹层玻璃
CN111566066B (zh) * 2017-12-19 2022-09-30 积水化学工业株式会社 夹层玻璃用中间膜及夹层玻璃
CN111566066A (zh) * 2017-12-19 2020-08-21 积水化学工业株式会社 夹层玻璃用中间膜及夹层玻璃
US11446904B2 (en) 2017-12-19 2022-09-20 Sekisui Chemical Co., Ltd. Laminated glass
CN111225887B (zh) * 2017-12-28 2023-03-28 积水化学工业株式会社 夹层玻璃用中间膜和夹层玻璃
US11945192B2 (en) 2017-12-28 2024-04-02 Sekisui Chemical Co., Ltd. Interlayer film for laminated glass, and laminated glass
CN111225887A (zh) * 2017-12-28 2020-06-02 积水化学工业株式会社 夹层玻璃用中间膜和夹层玻璃
KR102809625B1 (ko) * 2018-12-28 2025-05-20 세키스이가가쿠 고교가부시키가이샤 접합 유리용 중간막, 롤체 및 접합 유리의 제조 방법
JP7557366B2 (ja) 2018-12-28 2024-09-27 積水化学工業株式会社 合わせガラス用中間膜、ロール体及び合わせガラスの製造方法
KR20210109518A (ko) 2018-12-28 2021-09-06 세키스이가가쿠 고교가부시키가이샤 접합 유리용 중간막, 롤체 및 접합 유리의 제조 방법
CN113227013A (zh) * 2018-12-28 2021-08-06 积水化学工业株式会社 夹层玻璃用中间膜、卷体以及夹层玻璃的制造方法
US12304174B2 (en) 2018-12-28 2025-05-20 Sekisui Chemical Co., Ltd. Laminated glass interlayer, roll body, and laminated glass manufacturing method
WO2020137851A1 (fr) 2018-12-28 2020-07-02 積水化学工業株式会社 Couche intercalaire de verre feuilleté, corps de rouleau, et procédé de fabrication d'un verre feuilleté
JPWO2020137851A1 (ja) * 2018-12-28 2021-11-04 積水化学工業株式会社 合わせガラス用中間膜、ロール体及び合わせガラスの製造方法
CN110045502A (zh) * 2019-03-23 2019-07-23 深圳京龙睿信科技有限公司 抬头显示器
US12226987B2 (en) 2019-08-09 2025-02-18 Sk Microworks Co., Ltd. Bonding film, and light-transmitting laminate including same
CN114206610A (zh) * 2019-08-09 2022-03-18 Skc株式会社 接合用膜及包括其的透光层叠体
US11548262B2 (en) 2019-08-09 2023-01-10 Skc Co., Ltd. Bonding film, and light-transmitting laminate including same
KR20210071208A (ko) * 2019-12-06 2021-06-16 에스케이씨 주식회사 접합용 필름 및 이를 포함하는 광투과 적층체
KR102363360B1 (ko) * 2019-12-06 2022-02-14 에스케이씨 주식회사 접합용 필름 및 이를 포함하는 광투과 적층체
US20220143949A1 (en) * 2019-12-31 2022-05-12 Skc Co., Ltd. Lamination film and light-transmitting laminate including same
CN114174390B (zh) * 2019-12-31 2023-10-31 爱思开迈克沃有限公司 接合用薄膜及包括该薄膜的透光层叠体
CN114174390A (zh) * 2019-12-31 2022-03-11 Skc株式会社 接合用薄膜及包括该薄膜的透光层叠体
KR102363361B1 (ko) * 2019-12-31 2022-02-14 에스케이씨 주식회사 접합용 필름 및 이를 포함하는 광투과 적층체
WO2021137501A3 (fr) * 2019-12-31 2021-08-26 에스케이씨 주식회사 Film de stratification et stratifié transmettant la lumière le comprenant
KR20210085840A (ko) * 2019-12-31 2021-07-08 에스케이씨 주식회사 접합용 필름 및 이를 포함하는 광투과 적층체
WO2023200013A1 (fr) * 2022-04-15 2023-10-19 積水化学工業株式会社 Couche intercalaire pour verre feuilleté et son procédé de production et verre feuilleté et son procédé de production

Also Published As

Publication number Publication date
TW201718429A (zh) 2017-06-01
JPWO2017039004A1 (ja) 2018-06-21

Similar Documents

Publication Publication Date Title
JP6170638B1 (ja) 合わせガラス用中間膜及び合わせガラス
JP6229076B2 (ja) 合わせガラス用中間膜及び合わせガラス
WO2017039004A1 (fr) Film intercouches pour verre feuilleté, et verre feuilleté
JP6581596B2 (ja) 合わせガラス用中間膜及び合わせガラス
WO2017104632A1 (fr) Couche intermédiaire pour verre feuilleté, corps de cylindre, et verre feuilleté
KR102341992B1 (ko) 접합 유리용 중간막 및 접합 유리
JP6449524B1 (ja) 合わせガラス用中間膜及び合わせガラス
JPWO2018181418A1 (ja) 合わせガラス用中間膜、ロール体及び合わせガラス
JP7084140B2 (ja) 合わせガラス用中間膜及び合わせガラス
JP2020073423A (ja) 合わせガラス用中間膜及び合わせガラス
JP7269390B2 (ja) 合わせガラス用中間膜及び合わせガラス
JP7201583B2 (ja) 合わせガラス
JP7332271B2 (ja) 合わせガラス
JP7150430B2 (ja) 合わせガラス及びヘッドアップディスプレイシステムの製造方法
JP7100975B2 (ja) 合わせガラス
KR102513368B1 (ko) 접합 유리용 중간막 및 접합 유리
JP6484351B2 (ja) 合わせガラス用中間膜、ロール体及び合わせガラス
JP7112386B2 (ja) 合わせガラス用中間膜及び合わせガラス

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2016558414

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16842033

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16842033

Country of ref document: EP

Kind code of ref document: A1