WO2017090689A1 - Verre feuilleté, verre à vitres pour automobiles et verre à vitres pour bâtiments - Google Patents

Verre feuilleté, verre à vitres pour automobiles et verre à vitres pour bâtiments Download PDF

Info

Publication number
WO2017090689A1
WO2017090689A1 PCT/JP2016/084823 JP2016084823W WO2017090689A1 WO 2017090689 A1 WO2017090689 A1 WO 2017090689A1 JP 2016084823 W JP2016084823 W JP 2016084823W WO 2017090689 A1 WO2017090689 A1 WO 2017090689A1
Authority
WO
WIPO (PCT)
Prior art keywords
laminated glass
glass
thickness
transparent
value
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2016/084823
Other languages
English (en)
Japanese (ja)
Inventor
千恵子 室伏
室伏　英伸
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AGC Inc
Original Assignee
Asahi Glass Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Asahi Glass Co Ltd filed Critical Asahi Glass Co Ltd
Publication of WO2017090689A1 publication Critical patent/WO2017090689A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un verre feuilleté (1) pourvu d'une première feuille de verre (10), d'une première couche adhésive transparente (16), d'une couche d'isolation thermique transparente (14) ayant des pores indépendants avec coques, d'une seconde couche adhésive transparente (18) et d'une seconde feuille de verre (12), dans cet ordre. La valeur de A dans la formule (1) est inférieure ou égale à 7,4 × 105 et la valeur de B dans la formule (2) est d'au moins 35 (dans les formules, D est la taille des pores (nm), P est la porosité, di est l'épaisseur (mm) de la couche d'isolation thermique transparente, dg est l'épaisseur totale (mm) des feuilles de verre et da est l'épaisseur totale (mm) des couches adhésives transparentes).
PCT/JP2016/084823 2015-11-26 2016-11-24 Verre feuilleté, verre à vitres pour automobiles et verre à vitres pour bâtiments Ceased WO2017090689A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2015231013A JP2019014608A (ja) 2015-11-26 2015-11-26 合わせガラス、自動車用窓ガラスおよび建物用窓ガラス
JP2015-231013 2015-11-26

Publications (1)

Publication Number Publication Date
WO2017090689A1 true WO2017090689A1 (fr) 2017-06-01

Family

ID=58763427

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/084823 Ceased WO2017090689A1 (fr) 2015-11-26 2016-11-24 Verre feuilleté, verre à vitres pour automobiles et verre à vitres pour bâtiments

Country Status (2)

Country Link
JP (1) JP2019014608A (fr)
WO (1) WO2017090689A1 (fr)

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP4074667A4 (fr) * 2019-12-12 2023-12-20 Sekisui Chemical Co., Ltd. Couche intermédiaire pour verre feuilleté et verre feuilleté
WO2022260041A1 (fr) * 2021-06-10 2022-12-15 Ａｇｃ株式会社 Procédé de fabrication de vitre avec composant métallique destinée à être utilisée dans un véhicule
CN117412877A (zh) * 2021-06-10 2024-01-16 Ａｇｃ株式会社 带部件的车辆用窗玻璃的制造方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008222529A (ja) * 2007-03-15 2008-09-25 Agc Glass Kenzai Engineering Co Ltd 合わせガラス及び合わせガラスの製造方法
JP2009285864A (ja) * 2008-05-27 2009-12-10 Bridgestone Corp 熱線遮蔽膜、及びこれを用いた熱線遮蔽性合わせガラス
JP2010100778A (ja) * 2008-10-27 2010-05-06 Denki Kagaku Kogyo Kk シート及びその製造方法
WO2013168714A1 (fr) * 2012-05-08 2013-11-14 コニカミノルタ株式会社 Verre stratifié

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008222529A (ja) * 2007-03-15 2008-09-25 Agc Glass Kenzai Engineering Co Ltd 合わせガラス及び合わせガラスの製造方法
JP2009285864A (ja) * 2008-05-27 2009-12-10 Bridgestone Corp 熱線遮蔽膜、及びこれを用いた熱線遮蔽性合わせガラス
JP2010100778A (ja) * 2008-10-27 2010-05-06 Denki Kagaku Kogyo Kk シート及びその製造方法
WO2013168714A1 (fr) * 2012-05-08 2013-11-14 コニカミノルタ株式会社 Verre stratifié

Also Published As

Publication number Publication date
JP2019014608A (ja) 2019-01-31

Similar Documents

Publication Publication Date Title
WO2017090686A1 (fr) Verre feuilleté, verre à vitres pour des automobiles et verre à vitres pour des bâtiments
CN101573229B (zh) 制造耐火玻璃制品的方法
WO2004000549A1 (fr) Verre stratifie
JP7748350B2 (ja) ガラス積層体
JP2021147295A (ja) 熱線遮蔽合わせ透明基材
KR101615601B1 (ko) 알루미네이트-변성 또는 보레이트-변성 이산화규소를 가진 광투과성 방열부재
WO2017155066A1 (fr) Pare-brise
KR20150022930A (ko) 열선 차폐용 적층 구조체
KR101019498B1 (ko) 텅스텐브론즈 화합물을 함유한 열차단필름과 그 제조방법
WO2017090689A1 (fr) Verre feuilleté, verre à vitres pour automobiles et verre à vitres pour bâtiments
JP4848872B2 (ja) 窓用合わせガラス
WO2018092779A1 (fr) Stratifié antibuée et procédé de fixation de feuille antibuée
WO2018097101A1 (fr) Verre feuilleté
WO2017065114A1 (fr) Verre feuilleté
WO2017154510A1 (fr) Pare-brise
JP4828444B2 (ja) 合わせガラス
JP2007203474A (ja) 透明樹脂積層シート
CN206983435U (zh) 一种隔热保温汽车玻璃
CN108621491B (zh) 一种汽车用隔热保温板及其制备方法
KR101222936B1 (ko) 아미노실란을 이용한 수계 자외선 및 적외선 차단 코팅제 및 이를 사용하여 제조된 코팅막
CN202786023U (zh) 光致变色玻璃
WO2010041571A1 (fr) Matériau de feuilletage pour verres feuilletés et verres feuilletés
WO2017090690A1 (fr) Verre feuilleté, verre à vitres pour des automobiles et verre à vitres pour des bâtiments
CN203831896U (zh) 一种阻燃隔热膜
Xu et al. Manufacturing of automotive laminated windshields

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16868632

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16868632

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP