WO2016187304A1 - Matériau de cellulose ignifugée - Google Patents

Matériau de cellulose ignifugée Download PDF

Info

Publication number
WO2016187304A1
WO2016187304A1 PCT/US2016/033084 US2016033084W WO2016187304A1 WO 2016187304 A1 WO2016187304 A1 WO 2016187304A1 US 2016033084 W US2016033084 W US 2016033084W WO 2016187304 A1 WO2016187304 A1 WO 2016187304A1
Authority
WO
WIPO (PCT)
Prior art keywords
fire
cellulose
cellulose fiber
fiber material
acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2016/033084
Other languages
English (en)
Inventor
Thomas G. SHUTT
William R. Sellars
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NATURE TECH LLC
Original Assignee
NATURE TECH LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from PCT/US2015/031410 external-priority patent/WO2016186645A1/fr
Priority claimed from PCT/US2015/041731 external-priority patent/WO2017014782A1/fr
Application filed by NATURE TECH LLC filed Critical NATURE TECH LLC
Publication of WO2016187304A1 publication Critical patent/WO2016187304A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un matériau de cellulose ignifugée constitué d'une composition chimique ignifuge acide liquide ou d'un sel dérivé de cette composition, et d'un composé alcalin ou d'un composé alcalino-terreux, ainsi que des procédés de production du matériau de cellulose.
PCT/US2016/033084 2015-05-18 2016-05-18 Matériau de cellulose ignifugée Ceased WO2016187304A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
USPCT/US2015/031410 2015-05-18
PCT/US2015/031410 WO2016186645A1 (fr) 2015-05-18 2015-05-18 Matériau de cellulose résistant au feu
PCT/US2015/041731 WO2017014782A1 (fr) 2015-07-23 2015-07-23 Matériau de cellulose résistant au feu
USPCT/US2015/041731 2015-07-23

Publications (1)

Publication Number Publication Date
WO2016187304A1 true WO2016187304A1 (fr) 2016-11-24

Family

ID=56264029

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2016/033084 Ceased WO2016187304A1 (fr) 2015-05-18 2016-05-18 Matériau de cellulose ignifugée

Country Status (1)

Country Link
WO (1) WO2016187304A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019040566A1 (fr) * 2017-08-23 2019-02-28 Ntip Llc Agent ignifuge liquide à base d'eau destiné à être utilisé dans l'isolation de la cellulose

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4168175A (en) 1978-04-26 1979-09-18 Vitrofil Corporation Fire retardant compositions
US4173666A (en) * 1978-09-11 1979-11-06 Quinto Mario J Flame resistant cellulose fiber insulation and process of preparing it
AU4294278A (en) * 1978-12-28 1980-07-03 Draganov S M Rendering cellulosic materials fire-retardant
US4595414A (en) 1981-05-11 1986-06-17 Shutt Thomas C Methods for producing fire retardant cellulosic products
US5429741A (en) * 1989-07-20 1995-07-04 Ecosorb International, Inc. Sludge conditioning
US5534301A (en) 1995-05-10 1996-07-09 Echochem International, Inc. Method for producing cellulose insulation materials using liquid fire retardant compositions
WO2010040066A1 (fr) * 2008-10-03 2010-04-08 Nature Tech Llc Matériau cellulosique ignifuge dépoussiéré
WO2015076842A1 (fr) * 2013-11-25 2015-05-28 Nature Tech Llc Matériau de cellulose résistant au feu

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4168175A (en) 1978-04-26 1979-09-18 Vitrofil Corporation Fire retardant compositions
US4173666A (en) * 1978-09-11 1979-11-06 Quinto Mario J Flame resistant cellulose fiber insulation and process of preparing it
AU4294278A (en) * 1978-12-28 1980-07-03 Draganov S M Rendering cellulosic materials fire-retardant
US4595414A (en) 1981-05-11 1986-06-17 Shutt Thomas C Methods for producing fire retardant cellulosic products
US5429741A (en) * 1989-07-20 1995-07-04 Ecosorb International, Inc. Sludge conditioning
US5534301A (en) 1995-05-10 1996-07-09 Echochem International, Inc. Method for producing cellulose insulation materials using liquid fire retardant compositions
WO2010040066A1 (fr) * 2008-10-03 2010-04-08 Nature Tech Llc Matériau cellulosique ignifuge dépoussiéré
US9045605B2 (en) 2008-10-03 2015-06-02 Nature Tech Llc Dedusted fire-retardant cellulose material
WO2015076842A1 (fr) * 2013-11-25 2015-05-28 Nature Tech Llc Matériau de cellulose résistant au feu

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019040566A1 (fr) * 2017-08-23 2019-02-28 Ntip Llc Agent ignifuge liquide à base d'eau destiné à être utilisé dans l'isolation de la cellulose
US10767306B2 (en) 2017-08-23 2020-09-08 Ntip Llc Water based liquid fire retardant for use in cellulose insulation

Similar Documents

Publication Publication Date Title
WO2017014782A1 (fr) Matériau de cellulose résistant au feu
US20150147478A1 (en) Fire-Resistant Cellulose Material
EP3074457A1 (fr) Matériau de cellulose résistant au feu
US4168175A (en) Fire retardant compositions
US4184969A (en) Fire- and flame-retardant composition
US6673266B2 (en) Fire-retardant petroleum composition
US6652633B2 (en) Fire retardant
US6086998A (en) Non-inflammable fiber product
US10815427B2 (en) Fire-retardant for an insulation product
EP2655550B1 (fr) Poudre ignifuge fongicide et parasiticide
US10767306B2 (en) Water based liquid fire retardant for use in cellulose insulation
US4555447A (en) Blowing wool insulation
US8308997B2 (en) Fire resistant cellulosic materials and method of making the same
WO2016186645A1 (fr) Matériau de cellulose résistant au feu
WO2017053554A1 (fr) Matériaux de cellulose ignifugés hybrides
WO2016187304A1 (fr) Matériau de cellulose ignifugée
US4539045A (en) Non-blooming fire retardants for wood substrates
US20130014672A1 (en) Flame Retardant for Cellulose Based Materials
US20210187782A1 (en) Improved flame retardancy of wood and other cellulose-based materials by in-situ mineralization
US20180298558A1 (en) Hybrid Fire-Retarded Cellulose Materials
US20200277782A1 (en) Fire-retardant for an insulation product
CA1188857A (fr) Produits ignifugeant de type organophosphate
US20250043186A1 (en) Fire-retardant compositions and insulation materials and method of making
US20160348304A1 (en) Flame Retardant for Cellulose Based Materials
GB2037832A (en) Fire-retardant Composition and Method of Rendering Cellulosic Materials Fire-retardant

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16732796

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16732796

Country of ref document: EP

Kind code of ref document: A1