WO2016026761A1 - Procédé de préparation d'acide acrylique par déshydratation d'acide 3-hydroxypropionique - Google Patents

Procédé de préparation d'acide acrylique par déshydratation d'acide 3-hydroxypropionique Download PDF

Info

Publication number
WO2016026761A1
WO2016026761A1 PCT/EP2015/068644 EP2015068644W WO2016026761A1 WO 2016026761 A1 WO2016026761 A1 WO 2016026761A1 EP 2015068644 W EP2015068644 W EP 2015068644W WO 2016026761 A1 WO2016026761 A1 WO 2016026761A1
Authority
WO
WIPO (PCT)
Prior art keywords
process according
weight
acid
acrylic acid
hydroxypropionic acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2015/068644
Other languages
English (en)
Inventor
Regine Helga BEBENSEE
Marta ZAJACZKOWSKI-FISCHER
Veronika Wloka
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BASF SE
Original Assignee
BASF SE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BASF SE filed Critical BASF SE
Publication of WO2016026761A1 publication Critical patent/WO2016026761A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Cette invention concerne un procédé de préparation d'acide acrylique par vaporisation d'acide 3-hydroxypropionique aqueux et déshydration de l'acide 3-hydroxypropionique vaporisé, en présence d'un catalyseur d'oxyde d'aluminium présentant une quantité spécifiée de centres acides.
PCT/EP2015/068644 2014-08-18 2015-08-13 Procédé de préparation d'acide acrylique par déshydratation d'acide 3-hydroxypropionique Ceased WO2016026761A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP14181282 2014-08-18
EP14181282.6 2014-08-18

Publications (1)

Publication Number Publication Date
WO2016026761A1 true WO2016026761A1 (fr) 2016-02-25

Family

ID=51383572

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2015/068644 Ceased WO2016026761A1 (fr) 2014-08-18 2015-08-13 Procédé de préparation d'acide acrylique par déshydratation d'acide 3-hydroxypropionique

Country Status (1)

Country Link
WO (1) WO2016026761A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022114546A1 (fr) * 2020-11-24 2022-06-02 주식회사 엘지화학 Procédé de production d'acide acrylique
WO2022114545A1 (fr) * 2020-11-24 2022-06-02 주식회사 엘지화학 Procédé de production d'acide acrylique

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050222458A1 (en) * 2004-04-02 2005-10-06 Liliana Craciun Preparation of acrylic acid derivatives from alpha-or beta-hydroxy carboxylic acids
US20130274520A1 (en) * 2012-04-11 2013-10-17 The Procter & Gamble Company Purification Of Bio Based Acrylic Acid To Crude And Glacial Acrylic Acid
WO2013192451A1 (fr) * 2012-06-20 2013-12-27 Opx Biotechnologies, Inc. Déshydratation de l'acide 3-hydroxypropionique en acide acrylique

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050222458A1 (en) * 2004-04-02 2005-10-06 Liliana Craciun Preparation of acrylic acid derivatives from alpha-or beta-hydroxy carboxylic acids
US20130274520A1 (en) * 2012-04-11 2013-10-17 The Procter & Gamble Company Purification Of Bio Based Acrylic Acid To Crude And Glacial Acrylic Acid
WO2013192451A1 (fr) * 2012-06-20 2013-12-27 Opx Biotechnologies, Inc. Déshydratation de l'acide 3-hydroxypropionique en acide acrylique

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022114546A1 (fr) * 2020-11-24 2022-06-02 주식회사 엘지화학 Procédé de production d'acide acrylique
WO2022114545A1 (fr) * 2020-11-24 2022-06-02 주식회사 엘지화학 Procédé de production d'acide acrylique

Similar Documents

Publication Publication Date Title
JP5612575B2 (ja) グリセロールからバイオ資源のプロピオン酸を製造する方法
JP5914655B2 (ja) 改善された脱水反応方法
JP2016515645A (ja) メチルメタクリレートの製造方法
CN102482187B (zh) 从丙三醇制备生物来源化的丙烯酸的方法
JP2001247510A (ja) アクリル酸の製造方法
JP6191696B2 (ja) イソブチレンの製造方法、メタクリル酸の製造方法、およびメタクリル酸メチルの製造方法
US9353042B2 (en) Production of acetates from acetic acid and alcohols
CN1907932B (zh) 一种由甲醇生产二甲醚的方法
JP5572393B2 (ja) アクリル酸の製造方法
US9487466B2 (en) Process for producing acrylic acids and acrylates
US20110237828A1 (en) Acrolein production method and acrylic acid production method
WO2016026761A1 (fr) Procédé de préparation d'acide acrylique par déshydratation d'acide 3-hydroxypropionique
US9199910B2 (en) Process for production of methacrylic acid esters
US9120743B2 (en) Integrated process for the production of acrylic acids and acrylates
WO2016026763A1 (fr) Procédé de préparation d'acide acrylique faisant appel à un catalyseur d'alumine hétérogène
JP7355226B2 (ja) イソブチレンの製造方法、メタクリル酸の製造方法及びメタクリル酸メチルの製造方法
KR20160055167A (ko) 아크릴산으로부터 프로피온산의 분리
US20130165695A1 (en) Process conditions for producing acrylic acid
JP5401024B2 (ja) アクロレインの製造方法およびアクリル酸の製造方法
JP5401023B2 (ja) アクロレインの製造方法およびアクリル酸の製造方法
BRPI0409191B1 (pt) Processo para oxidação direta parcial catalisada heterogeneamente de propano e/ou de isobutano a pelo menos um dos produtos alvo, ácido acrílico, ácido metacrílico
JP5401022B2 (ja) アクロレインの製造方法およびアクリル酸の製造方法
US20130253224A1 (en) Process for Producing Acrylic Acids and Acrylates

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15750728

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15750728

Country of ref document: EP

Kind code of ref document: A1