WO2015037397A1 - Film de revêtement dur, et miroir en film - Google Patents

Film de revêtement dur, et miroir en film Download PDF

Info

Publication number
WO2015037397A1
WO2015037397A1 PCT/JP2014/071583 JP2014071583W WO2015037397A1 WO 2015037397 A1 WO2015037397 A1 WO 2015037397A1 JP 2014071583 W JP2014071583 W JP 2014071583W WO 2015037397 A1 WO2015037397 A1 WO 2015037397A1
Authority
WO
WIPO (PCT)
Prior art keywords
hard coat
layer
coat layer
mass
film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2014/071583
Other languages
English (en)
Japanese (ja)
Inventor
威史 濱
克行 温井
祐也 山本
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujifilm Corp
Original Assignee
Fujifilm Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujifilm Corp filed Critical Fujifilm Corp
Publication of WO2015037397A1 publication Critical patent/WO2015037397A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention fournit un film de revêtement dur et un miroir en film, lequel film de revêtement dur est équipé d'une couche de revêtement dur qui satisfait des propriétés de résistance à l'adhésion de sable ainsi que de l'huile, de résistance aux éraflures et de résistance à la salissure. Le film de revêtement dur possède un corps de support, et la couche de revêtement dur disposée sur ce dernier. La couche de revêtement dur comprend un poly(méth)acrylate, et au moins une sorte d'oxyde métallique. La teneur en oxyde métallique est de 1 à 50% en masse pour la quantité totale de poly(méth)acrylate. À la surface de la couche de revêtement dur, l'énergie libre superficielle est inférieure ou égale à 30mN/m, la valeur de résistance superficielle est inférieure à 1×1013Ω au carré, et la dureté au crayon est supérieure ou égale à 2H.
PCT/JP2014/071583 2013-09-12 2014-08-18 Film de revêtement dur, et miroir en film Ceased WO2015037397A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2013189619A JP2015054461A (ja) 2013-09-12 2013-09-12 ハードコートフィルム
JP2013-189619 2013-09-12

Publications (1)

Publication Number Publication Date
WO2015037397A1 true WO2015037397A1 (fr) 2015-03-19

Family

ID=52665515

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/071583 Ceased WO2015037397A1 (fr) 2013-09-12 2014-08-18 Film de revêtement dur, et miroir en film

Country Status (2)

Country Link
JP (1) JP2015054461A (fr)
WO (1) WO2015037397A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20170027307A1 (en) * 2014-06-30 2017-02-02 Komy Co., Ltd. Mirror for aircraft crew members
WO2018128073A1 (fr) * 2017-01-06 2018-07-12 コニカミノルタ株式会社 Membrane auto-réparatrice, film auto-réparateur et procédé de production d'une membrane auto-réparatrice
US20220187194A1 (en) * 2019-03-28 2022-06-16 Carl Zeiss Spectroscopy Gmbh Measurement light source and measuring arrangement for detecting a reflection spectrum

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN107207639A (zh) 2015-09-24 2017-09-26 Jsr株式会社 乳液组合物及其制造方法、以及层叠体及其制造方法
CN113412190B (zh) * 2019-02-06 2023-09-26 日产化学株式会社 抗静电硬涂用固化性组合物
KR102024032B1 (ko) * 2019-05-15 2019-09-24 주식회사 퍼시픽인터켐코포레이션 내긁힘성 향상제 및 이를 이용하는 수지 조성물
KR102332887B1 (ko) 2019-10-01 2021-11-30 동우 화인켐 주식회사 하드코팅 필름 및 이를 포함하는 화상표시장치
KR102327415B1 (ko) 2019-10-01 2021-11-17 동우 화인켐 주식회사 하드코팅 필름 및 이를 포함하는 화상표시장치
KR102327414B1 (ko) * 2019-10-01 2021-11-17 동우 화인켐 주식회사 하드코팅 필름 및 이를 포함하는 화상표시장치

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2009066991A (ja) * 2007-09-14 2009-04-02 Sumitomo Osaka Cement Co Ltd 帯電防止・表面保護膜付きフィルム、その製造方法、及びそれの製造用塗料
JP2010139878A (ja) * 2008-12-12 2010-06-24 Fujifilm Corp 光学積層体の製造方法
WO2011096320A1 (fr) * 2010-02-05 2011-08-11 コニカミノルタオプト株式会社 Miroir sous forme de film, miroir sous forme de film permettant une production d'énergie solaire thermique et dispositif de réflexion permettant une production d'énergie solaire photovoltaïque
WO2012026312A1 (fr) * 2010-08-25 2012-03-01 コニカミノルタオプト株式会社 Film miroir pour la conversion thermodynamique, procédé pour la production d'un film miroir pour la conversion thermodynamique et dispositif réfléchissant pour la conversion thermodynamique
JP2012047861A (ja) * 2010-08-25 2012-03-08 Konica Minolta Opto Inc フィルムミラー、その製造方法、及び太陽光集光用フィルムミラー
WO2012057003A1 (fr) * 2010-10-27 2012-05-03 コニカミノルタオプト株式会社 Miroir à film pour la production d'énergie solaire et dispositif de réflexion pour la production d'énergie solaire
WO2012133517A1 (fr) * 2011-03-31 2012-10-04 コニカミノルタアドバンストレイヤー株式会社 Miroir et dispositif réfléchissant permettant de produire de l'énergie solaire
JP2012232538A (ja) * 2011-05-09 2012-11-29 Konica Minolta Advanced Layers Inc フィルムミラー、太陽光反射用ミラー及び太陽熱発電用反射装置

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2009066991A (ja) * 2007-09-14 2009-04-02 Sumitomo Osaka Cement Co Ltd 帯電防止・表面保護膜付きフィルム、その製造方法、及びそれの製造用塗料
JP2010139878A (ja) * 2008-12-12 2010-06-24 Fujifilm Corp 光学積層体の製造方法
WO2011096320A1 (fr) * 2010-02-05 2011-08-11 コニカミノルタオプト株式会社 Miroir sous forme de film, miroir sous forme de film permettant une production d'énergie solaire thermique et dispositif de réflexion permettant une production d'énergie solaire photovoltaïque
WO2012026312A1 (fr) * 2010-08-25 2012-03-01 コニカミノルタオプト株式会社 Film miroir pour la conversion thermodynamique, procédé pour la production d'un film miroir pour la conversion thermodynamique et dispositif réfléchissant pour la conversion thermodynamique
JP2012047861A (ja) * 2010-08-25 2012-03-08 Konica Minolta Opto Inc フィルムミラー、その製造方法、及び太陽光集光用フィルムミラー
WO2012057003A1 (fr) * 2010-10-27 2012-05-03 コニカミノルタオプト株式会社 Miroir à film pour la production d'énergie solaire et dispositif de réflexion pour la production d'énergie solaire
WO2012133517A1 (fr) * 2011-03-31 2012-10-04 コニカミノルタアドバンストレイヤー株式会社 Miroir et dispositif réfléchissant permettant de produire de l'énergie solaire
JP2012232538A (ja) * 2011-05-09 2012-11-29 Konica Minolta Advanced Layers Inc フィルムミラー、太陽光反射用ミラー及び太陽熱発電用反射装置

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20170027307A1 (en) * 2014-06-30 2017-02-02 Komy Co., Ltd. Mirror for aircraft crew members
US10349726B2 (en) * 2014-06-30 2019-07-16 Komy Co., Ltd Mirror for aircraft crew members
WO2018128073A1 (fr) * 2017-01-06 2018-07-12 コニカミノルタ株式会社 Membrane auto-réparatrice, film auto-réparateur et procédé de production d'une membrane auto-réparatrice
US20220187194A1 (en) * 2019-03-28 2022-06-16 Carl Zeiss Spectroscopy Gmbh Measurement light source and measuring arrangement for detecting a reflection spectrum
US11953426B2 (en) * 2019-03-28 2024-04-09 Carl Zeiss Spectroscopy Gmbh Measurement light source and measuring arrangement for detecting a reflection spectrum

Also Published As

Publication number Publication date
JP2015054461A (ja) 2015-03-23

Similar Documents

Publication Publication Date Title
WO2015037397A1 (fr) Film de revêtement dur, et miroir en film
US20160170192A1 (en) Composite film and film mirror for solar light reflection
JP5741586B2 (ja) 太陽熱発電用フィルムミラー、太陽熱発電用フィルムミラーの製造方法及び太陽熱発電用反射装置
JP5924261B2 (ja) 積層ポリエステルフィルムおよびハードコートフィルム
EP2660632A1 (fr) Pellicule fonctionnelle, miroir pelliculaire et dispositif réfléchissant permettant de produire une puissance thermique solaire
JPWO2008044398A1 (ja) ハードコートフィルム、その製造方法及び反射防止フィルム
JP6127956B2 (ja) タッチパネル用保護フィルム
WO2007123138A1 (fr) Filtre utilisé pour l'affichage
KR20140060516A (ko) 스크래치 또는 마모 손상 후 자가-복구 표면 특성을 갖는 외부 용도를 위한 중합체성 물질
JP2010106061A (ja) 耐候性ハードコートフィルム、及び紫外線硬化性樹脂組成物
WO2013122012A1 (fr) Film miroir, procédé de fabrication de celui-ci, et miroir réfléchissant utilisant celui-ci
JP2016137666A (ja) 光反射フィルム、ならびにこれを用いた光反射体および光反射装置
US20150198753A1 (en) Film mirror
WO2015146314A1 (fr) Stratifié, procédé de production de celui-ci, plaque réfléchissante, film miroir, revêtement antibactérien, film conducteur et corps conducteur de chaleur
JP2016190487A (ja) 転写シート、ハードコート積層体及びハードコート積層体の製造方法
JP5794232B2 (ja) 太陽熱発電用フィルムミラー、その製造方法及び太陽熱発電用反射装置
JP6402952B2 (ja) 紫外線硬化性樹脂層
JP2006028470A (ja) 汚染防止塗料、汚染防止シートおよびその製造方法
EP2634606A1 (fr) Miroir à film pour la production d'énergie solaire et dispositif de réflexion pour la production d'énergie solaire
JP2011031575A (ja) 積層体及び積層体の製造方法
WO2013141304A1 (fr) Miroir à film, et dispositif de réflexion pour la génération d'énergie solaire
WO2015037549A1 (fr) Film composite
WO2013054869A1 (fr) Miroir pour réflexion de lumière solaire, et dispositif de réflexion pour génération d'énergie thermique solaire
JPWO2012043606A1 (ja) 太陽熱発電用フィルムミラー、太陽熱発電用フィルムミラーの製造方法及び太陽熱発電用反射装置
WO2015146296A1 (fr) Stratifié et son procédé de production, plaque de réflexion, revêtement antibactérien, film conducteur et conducteur de chaleur

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14843992

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase