WO2014155266A1 - Procédé de fabrication de panneaux isolants et panneau correspondant - Google Patents

Procédé de fabrication de panneaux isolants et panneau correspondant Download PDF

Info

Publication number
WO2014155266A1
WO2014155266A1 PCT/IB2014/060082 IB2014060082W WO2014155266A1 WO 2014155266 A1 WO2014155266 A1 WO 2014155266A1 IB 2014060082 W IB2014060082 W IB 2014060082W WO 2014155266 A1 WO2014155266 A1 WO 2014155266A1
Authority
WO
WIPO (PCT)
Prior art keywords
pulp
flakes
panel
feathers
keratin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/IB2014/060082
Other languages
English (en)
Inventor
Valerio Pontarolo
Luca PONTAROLO
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
PONTAROLO ENGINEERING SpA
Pontarolo Engineering SpA
Original Assignee
PONTAROLO ENGINEERING SpA
Pontarolo Engineering SpA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by PONTAROLO ENGINEERING SpA, Pontarolo Engineering SpA filed Critical PONTAROLO ENGINEERING SpA
Publication of WO2014155266A1 publication Critical patent/WO2014155266A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un procédé de fabrication de panneaux à base de plumes d'oiseaux, le procédé comprenant les étapes suivantes consistant à décomposer les plumes jusqu'à l'obtention de flocons et/ou d'une pâte fluide constitués sensiblement de kératine et d'eau, à disposer les flocons et/ou la pâte dans une matrice ayant une forme appropriée, et à compresser mécaniquement la pâte et/ou les flocons dans la matrice, jusqu'à l'agrégation de la pâte de façon à former ledit panneau.
PCT/IB2014/060082 2013-03-28 2014-03-24 Procédé de fabrication de panneaux isolants et panneau correspondant Ceased WO2014155266A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
ITPN2013A000017 2013-03-28
IT000017A ITPN20130017A1 (it) 2013-03-28 2013-03-28 Procedimento per la realizzazione di pannelli isolanti e relativo pannello.

Publications (1)

Publication Number Publication Date
WO2014155266A1 true WO2014155266A1 (fr) 2014-10-02

Family

ID=48184368

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2014/060082 Ceased WO2014155266A1 (fr) 2013-03-28 2014-03-24 Procédé de fabrication de panneaux isolants et panneau correspondant

Country Status (2)

Country Link
IT (1) ITPN20130017A1 (fr)
WO (1) WO2014155266A1 (fr)

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR999094A (fr) * 1952-01-25
WO1996039551A1 (fr) * 1995-06-06 1996-12-12 The United States Of America, Represented By Th Fibres et produits fibreux obtenus a partir de plumes

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR999094A (fr) * 1952-01-25
WO1996039551A1 (fr) * 1995-06-06 1996-12-12 The United States Of America, Represented By Th Fibres et produits fibreux obtenus a partir de plumes

Also Published As

Publication number Publication date
ITPN20130017A1 (it) 2014-09-29

Similar Documents

Publication Publication Date Title
Thapliyal et al. Natural fibers composites: origin, importance, consumption pattern, and challenges
DE4227681C2 (de) Wundabdeckungsmaterial auf der Basis von Kollagenfasern und Verfahren zu seiner Herstellung
Ashton et al. Self-tensioning aquatic caddisfly silk: Ca2+-dependent structure, strength, and load cycle hysteresis
Kurien et al. Chicken feather fiber reinforced composites for sustainable applications
DE2646968A1 (de) Verfahren zur herstellung von atelopeptidkollagen-fasern und daraus hergestellte formkoerper
DE1720131B1 (de) Verfahren und Vorrichtung zum Herstellen eines Formkoerpers aus Proteinfasern
CN101942112A (zh) 一种竹浆海绵制品及其制备方法
Yuanita et al. Multistages preparation for microfibrillated celluloses based on Arenga pinnata “ijuk” fiber
Mortazavi et al. An analysis of structure and properties of a natural cellulosic fiber (Leafiran)
Xiang et al. Surface activity and foaming capacity of aggregates formed between an anionic surfactant and non-cellulosics leached from wood fibers
Stoessel et al. Porous, water-resistant multifilament yarn spun from gelatin
WO2014155266A1 (fr) Procédé de fabrication de panneaux isolants et panneau correspondant
Yazawa et al. Wild silkworm cocoon waste conversion into tough regenerated silk fibers by solution spinning
DE2419559A1 (de) Herstellung eines essbaren kollagens unter verwendung von fluessigem rauch
DE1692199A1 (de) Verfahren zur Herstellung von kuenstlichen verzehrbaren Wursthuellen aus Kollagen
FI2507023T3 (fi) Menetelmä käytettyjen vaatteiden ja kodin tekstiilien kierrättämiseksi
DE1492641A1 (de) Wursthuelle und Verfahren zu ihrer Herstellung
Tan et al. Exploring stimuli-responsive natural processes for the fabrication of high-performance materials
DE2352218A1 (de) Gepresster zelluloseregeneratschwamm
Sharif et al. Cassava leaves as packaging materials
DE659490C (de) Verfahren zur Herstellung kuenstlicher Wursthuellen
ITPN20130016A1 (it) Procedimento per l'ottenimento di un prodotto a partire da piume di uccelli sotto forma di fiocchi o di farina micronizzata ad alto contenuto di cheratina.
Dash et al. High-Intensity Ultrasonication (HIU) Effect on Sunn Hemp Fiber-Reinforced Epoxy Composite: A Physicochemical Treatment Toward Fiber
RU2653732C1 (ru) Способ получения материала из иголок деревьев хвойных пород
US20170002514A1 (en) Method Of Removing Odors From Fibrous Materials Used In Forming Biocomposite Materials

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14719095

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14719095

Country of ref document: EP

Kind code of ref document: A1