WO2014092753A1 - Système et article de garnissage réfractaire - Google Patents

Système et article de garnissage réfractaire Download PDF

Info

Publication number
WO2014092753A1
WO2014092753A1 PCT/US2013/029422 US2013029422W WO2014092753A1 WO 2014092753 A1 WO2014092753 A1 WO 2014092753A1 US 2013029422 W US2013029422 W US 2013029422W WO 2014092753 A1 WO2014092753 A1 WO 2014092753A1
Authority
WO
WIPO (PCT)
Prior art keywords
article
refractory
phosphate
edge
adhesive mortar
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2013/029422
Other languages
English (en)
Inventor
Jens Decker
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Stellar Materials Inc
Original Assignee
Stellar Materials Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Stellar Materials Inc filed Critical Stellar Materials Inc
Publication of WO2014092753A1 publication Critical patent/WO2014092753A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne des processus pour constituer ou réparer une structure utilisée dans une application à haute température, moyennant quoi un garnissage d'article réfractaire qui est vitrifié sur la face la plus proche d'une paroi de la structure est utilisé pour constituer ou remplacer une partie de la surface réfractaire dans une telle structure. Les articles réfractaires peuvent être liés chimiquement et/ou mécaniquement à un mortier-colle capable de réagir chimiquement avec le matériau utilisé pour constituer la brique, afin de former une surface sensiblement monolithique à haute résistance qui résiste à la pénétration par les sels de fondant, augmentant de manière spectaculaire la durée de vie de la réparation. Le processus permet un faible coût et une réparation durable des structures utilisées dans des applications à haute température, qui était auparavant irréalisable. L'invention concerne aussi des articles réfractaires avec un enduit de vernissage sur au moins une partie de ceux-ci qui empêche la pénétration des sels de fondant. En option, les articles réfractaires peuvent être utilisés dans un système conjointement avec un mortier-colle complémentaire.
PCT/US2013/029422 2012-12-14 2013-03-06 Système et article de garnissage réfractaire Ceased WO2014092753A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201261737163P 2012-12-14 2012-12-14
US61/737,163 2012-12-14

Publications (1)

Publication Number Publication Date
WO2014092753A1 true WO2014092753A1 (fr) 2014-06-19

Family

ID=50934799

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2013/029422 Ceased WO2014092753A1 (fr) 2012-12-14 2013-03-06 Système et article de garnissage réfractaire

Country Status (1)

Country Link
WO (1) WO2014092753A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018075680A1 (fr) * 2016-10-18 2018-04-26 Saint-Gobain Ceramics & Plastics, Inc. Revêtement en céramique et procédé de formation
CN111848189A (zh) * 2020-07-24 2020-10-30 湖南省娄底市宏冶炉料有限责任公司 新型耐冲刷耐热震式冲击砖及制备方法和稳流器

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4040809A (en) * 1976-03-26 1977-08-09 Ppg Industries, Inc. Glazed refractory support for delivering glass to a forming chamber
US6267066B1 (en) * 2000-03-15 2001-07-31 Saint-Gobain Industrial Ceramics Refractory tile system for boiler tube/heat exchanger
RU2228310C2 (ru) * 2002-04-05 2004-05-10 Открытое акционерное общество "Комбинат "Магнезит" Огнеупорный мертель
WO2012006507A2 (fr) * 2010-07-08 2012-01-12 Stellar Materials Incorporated Élément structural réfractaire

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4040809A (en) * 1976-03-26 1977-08-09 Ppg Industries, Inc. Glazed refractory support for delivering glass to a forming chamber
US6267066B1 (en) * 2000-03-15 2001-07-31 Saint-Gobain Industrial Ceramics Refractory tile system for boiler tube/heat exchanger
RU2228310C2 (ru) * 2002-04-05 2004-05-10 Открытое акционерное общество "Комбинат "Магнезит" Огнеупорный мертель
WO2012006507A2 (fr) * 2010-07-08 2012-01-12 Stellar Materials Incorporated Élément structural réfractaire

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
GUZMANA I., KHIMICHESKAYA TEKHNOLOGIYA KERAMIKI, POD RED., 2003, YA. MOSKVA, pages 438,301 *

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018075680A1 (fr) * 2016-10-18 2018-04-26 Saint-Gobain Ceramics & Plastics, Inc. Revêtement en céramique et procédé de formation
US10295260B2 (en) 2016-10-18 2019-05-21 Saint-Gobain Ceramics & Plastics, Inc. Ceramic liner and method of forming
US11181321B2 (en) 2016-10-18 2021-11-23 Saint-Gobain Ceramics & Plastics, Inc. Ceramic liner and method of forming
CN111848189A (zh) * 2020-07-24 2020-10-30 湖南省娄底市宏冶炉料有限责任公司 新型耐冲刷耐热震式冲击砖及制备方法和稳流器

Similar Documents

Publication Publication Date Title
US20130189493A1 (en) Refractory lining article and system
US20230109549A1 (en) Porous refractory cast material, its use and production
CA2940682C (fr) Materiau de reparation de sole de haut fourneau
BR112012024123B1 (pt) Composição refratária
US20040138048A1 (en) Refractory system for glass melting furnaces
WO2014031574A1 (fr) Composition réfractaire et procédé de formation d'article à partir de celle-ci
US20120304904A1 (en) Refractory structural element
CA1055053A (fr) Refractaires monolithiques
WO2014092753A1 (fr) Système et article de garnissage réfractaire
Sengupta Manufacturing and properties of refractories
EP1765744B1 (fr) Composition réfractaire de grande résistance
RU2348595C2 (ru) Способ изготовления изделий из огнеупорной массы (варианты)
US11059750B2 (en) Single additive refractory materials suitable for multiple application methods
US8747546B2 (en) Calcium enriched refractory material by the addition of calcium carbonate
Montgomery Heat-resisting and refractory concretes
NO159376B (no) Sementaktig materiale og anvendelse av dette.
JP2001141372A (ja) 耐火物ブロック、その製造方法及び溶湯容器
CA2703869A1 (fr) Matiere refractaire enrichie en calcium grace a l'ajout de carbonate de calcium
Lee et al. Basic Refractories in the Cement Process
CS213420B1 (cs) Žárovzdorné tmely a nátěrové hmoty.
CS277026B6 (cs) Žáruvzdorná hmota, zejména pro torkret

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13863134

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13863134

Country of ref document: EP

Kind code of ref document: A1