WO2013064849A4 - Glass fiber reinforced thermoset plastic waste doped concrete composition and process for preparation the same - Google Patents
Glass fiber reinforced thermoset plastic waste doped concrete composition and process for preparation the same Download PDFInfo
- Publication number
- WO2013064849A4 WO2013064849A4 PCT/HU2012/000118 HU2012000118W WO2013064849A4 WO 2013064849 A4 WO2013064849 A4 WO 2013064849A4 HU 2012000118 W HU2012000118 W HU 2012000118W WO 2013064849 A4 WO2013064849 A4 WO 2013064849A4
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- concrete
- glass fiber
- plastic waste
- fiber reinforced
- thermoset plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
The invention relates to concrete doped with glass fiber reinforced thermoset plastic waste, process for preparing the same and a lightweight dry concrete premix usable in said process.
Claims
1. Concrete product, which contains the following components expressed in % by volume of the concrete:
1 1 to 16 % (v/v) cement,
6 to 16 % (v/v) glass fiber reinforced ground thermoset plastic waste, having particle size from 300 μηι to 5 mm,
0 to 2 % (v/v) other additives,
3 to 10 % (v/v) filtered purified water,
the rest are graded river gravel and pit sand in 1 : 1 ratio by volume.
2. Lightweight dry concrete premix containing glass fiber reinforced ground thermoset plastic waste, cement and optionally other dry additives commonly used in the preparation of concrete, wherein the particle size of the ground plastic waste is at least one order of magnitude larger than the particle size of the Portland cement.
3. The lightweight dry concrete premix according to claim 2, which is in the form of unit portions.
4. The concrete premix of lightweight structure according to claim 2, wherein the average particle size of the glass fiber reinforced ground thermoset plastic waste is 300 μπι to 5 mm.
5. Process for preparing concrete product according to claim 1 by embedding glass fiber reinforced ground thermoset plastic waste in hydraulic grout, characterized in that the glass fiber reinforced thermoset plastic waste is separated from foreign materials, then ground optionally in multiple steps to form ground plastic waste having particle size from 300 μπι to 5 mm, then
a) cement, graded gravel, sand, water, said glass fiber reinforced ground thermoset plastic waste and optionally other additives commonly used in the preparation of concrete mortar are mixed applying wet technology, or
b) cement, gravel and sand, said glass fiber reinforced ground thermoset plastic waste and optionally other dry additives commonly used in the preparation of concrete mortar are mixed and homogenized applying dry technology to form a dry premix, to which water and optionally other dry and/or wet additives commonly used in the preparation of concrete mortar are added with continuous agitating, before use, and after carrying out process step a) or b) the final consistency of the concrete mortar is optionally adjusted with continuous agitating and the resultant concrete mortar is poured and allowed to set.
6. Process for preparing concrete product by embedding glass fiber reinforced ground thermoset plastic waste in hydraulic grout, characterized in that the lightweight dry concrete premix according to any of claims 2 to 4 is mixed with graded gravel, sand, water and optionally other additives commonly used in the preparation of concrete mortar, the final consistency of the concrete mortar is adjusted and the resultant concrete mortar is poured and allowed to set.
7. The process according to claim 6 characterized in that the grout is placed with pouring, self-spreading technology or with framework technology, in batch type process or continuous process, or discrete elements are prepared.
8. The concrete product according to claim 1, the concrete premix of lightweight structure according to claim 2 or the process according to claim 5 or 6, wherein the glass fiber reinforced thermoset plastic waste is glass fiber reinforced thermoset SMC and/or BMC waste comprising more than 10 % by volume of glass fiber.
9. Concrete product prepared from the concrete premix of lightweight structure according to claims 2 to 4 by the process according to claim 6.
10. The concrete product according to claim 1 or 9, which is a concrete building element or a discrete element, preferably a pre-product, a cover element or a mobil element.
14
Priority Applications (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| EP12815754.2A EP2773597A2 (en) | 2011-11-02 | 2012-10-31 | Glass fiber reinforced thermoset plastic waste doped concrete composition and process for preparation the same |
Applications Claiming Priority (2)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| HUP1100606 | 2011-11-02 | ||
| HU1100606A HUP1100606A2 (en) | 2011-11-02 | 2011-11-02 | Method for producing admixtured concrete |
Publications (3)
| Publication Number | Publication Date |
|---|---|
| WO2013064849A2 WO2013064849A2 (en) | 2013-05-10 |
| WO2013064849A3 WO2013064849A3 (en) | 2013-08-22 |
| WO2013064849A4 true WO2013064849A4 (en) | 2013-11-07 |
Family
ID=89990492
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| PCT/HU2012/000118 Ceased WO2013064849A2 (en) | 2011-11-02 | 2012-10-31 | Glass fiber reinforced thermoset plastic waste doped concrete composition and process for preparation the same |
Country Status (3)
| Country | Link |
|---|---|
| EP (1) | EP2773597A2 (en) |
| HU (1) | HUP1100606A2 (en) |
| WO (1) | WO2013064849A2 (en) |
Families Citing this family (4)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN103553497A (en) * | 2013-10-31 | 2014-02-05 | 桂林福冈新材料有限公司 | Improved anti-cracking cement |
| ES2685219B2 (en) | 2017-03-31 | 2019-01-15 | Univ Sevilla | Procedure for the manufacture of mortars with plastic waste and its application in a piece of entrevigado for unidirectional slabs |
| CN113733299A (en) * | 2021-08-18 | 2021-12-03 | 河北宏京新型建材有限公司 | Production process of glass fiber reinforced concrete GRC |
| CN115536295B (en) * | 2022-08-24 | 2023-12-19 | 国能联合动力技术(保定)有限公司 | A kind of preparation method of alkali-resistant recycled fiberglass fiber |
Family Cites Families (8)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JPH0811715B2 (en) * | 1991-10-14 | 1996-02-07 | アサオカ株式会社 | Cement-based lightweight artificial stone and method for producing the same |
| US5422051A (en) * | 1993-06-28 | 1995-06-06 | Sawyers; John P. | Method for recycling plastic into cementitions building products |
| JPH0867546A (en) * | 1994-08-30 | 1996-03-12 | Kubota Corp | Manufacturing method of fiber reinforced cement board |
| JP2000053457A (en) * | 1998-08-07 | 2000-02-22 | Kubota Corp | Manufacturing method of cement mortar |
| JP2000143310A (en) * | 1998-11-04 | 2000-05-23 | Kubota Corp | Cement mortar and method for producing the same |
| US6488766B2 (en) * | 1999-03-15 | 2002-12-03 | Earl T. Balkum | Aggregate using recycled plastics |
| JP2002284563A (en) * | 2001-03-27 | 2002-10-03 | Sumitomo Osaka Cement Co Ltd | Method for manufacturing solidified concrete product and solidified concrete product |
| CZ19924U1 (en) * | 2009-04-06 | 2009-08-17 | Mama Construction Material S. R. O. | Mixture for building purposes |
-
2011
- 2011-11-02 HU HU1100606A patent/HUP1100606A2/en active IP Right Revival
-
2012
- 2012-10-31 EP EP12815754.2A patent/EP2773597A2/en not_active Withdrawn
- 2012-10-31 WO PCT/HU2012/000118 patent/WO2013064849A2/en not_active Ceased
Also Published As
| Publication number | Publication date |
|---|---|
| HUP1100606A2 (en) | 2013-06-28 |
| WO2013064849A3 (en) | 2013-08-22 |
| WO2013064849A2 (en) | 2013-05-10 |
| EP2773597A2 (en) | 2014-09-10 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| DE112012005789B4 (en) | Building material with microencapsulated phase change material, manufacturing method and use of the building material | |
| CN104478349B (en) | A kind of early strong high abrasion gravity flowing levelling mortar repaired for ground and preparation method thereof | |
| CN101864716A (en) | Pavior brick produced by utilizing building wastes and preparation method thereof | |
| WO2013064849A4 (en) | Glass fiber reinforced thermoset plastic waste doped concrete composition and process for preparation the same | |
| CN103449776B (en) | A kind of construction slurry steaming-free air-adding concrete segment and manufacture method thereof | |
| CN103253901A (en) | Concrete bridge-deck rapid paving mortar and preparation method thereof | |
| CN103708798B (en) | A kind of active organosilicon high-performance environment-friendly waterproof powder and the method for using the waterproof powder to prepare waterproof layer | |
| CN103787610A (en) | Pervious concrete additive and preparation method thereof | |
| CN104478340A (en) | Low-cost concrete preparation method | |
| CN104817297A (en) | Rock-soil solidifying agent as well as preparation method and application of rock-soil solidifying agent | |
| CN110421683A (en) | A kind of production technology of building structure integration heat-insulation wall plate | |
| CN103253919A (en) | Preparation method of cement mixture | |
| CN106626053A (en) | Machine-made pre-stressed concrete preparation method | |
| JP6195890B2 (en) | Method for producing early strength lightweight concrete | |
| CN106187057A (en) | A kind of cement-based self-leveling dry powder and mortar and preparation method thereof | |
| CN105198305A (en) | Method for producing wall material with construction waste | |
| CN101885598B (en) | Mortar template for high intensity adjustment | |
| CN103253902A (en) | Ultra-early-strength structure-reinforced mortar and preparation method thereof | |
| CN102828530A (en) | Resin inspection well and manufacturing method thereof | |
| CN108975786A (en) | A kind of preparation method of high-performance fabricated permeable product | |
| CN204687088U (en) | A kind of mixed earth draft machine | |
| CN103526934A (en) | Synchronous construction method for decorative surfaces and wall without bricks | |
| CN107778023A (en) | Noise-reducing concrete | |
| PH22012000600U3 (en) | Steel fiber reinforced concrete | |
| Shin et al. | Influence of the Mixing Factor on the Properties of Concrete Used Artificial Lightweight Aggregates |
Legal Events
| Date | Code | Title | Description |
|---|---|---|---|
| 121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 12815754 Country of ref document: EP Kind code of ref document: A2 |
|
| NENP | Non-entry into the national phase |
Ref country code: DE |
|
| REEP | Request for entry into the european phase |
Ref document number: 2012815754 Country of ref document: EP |
|
| WWE | Wipo information: entry into national phase |
Ref document number: 2012815754 Country of ref document: EP |