WO2013061923A1 - Adhésif conducteur, module de cellule solaire et procédé de fabrication de module de cellule solaire - Google Patents

Adhésif conducteur, module de cellule solaire et procédé de fabrication de module de cellule solaire Download PDF

Info

Publication number
WO2013061923A1
WO2013061923A1 PCT/JP2012/077238 JP2012077238W WO2013061923A1 WO 2013061923 A1 WO2013061923 A1 WO 2013061923A1 JP 2012077238 W JP2012077238 W JP 2012077238W WO 2013061923 A1 WO2013061923 A1 WO 2013061923A1
Authority
WO
WIPO (PCT)
Prior art keywords
meth
acrylate
solar cell
conductive adhesive
mass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2012/077238
Other languages
English (en)
Japanese (ja)
Inventor
一俊 鈴木
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dexerials Corp
Original Assignee
Dexerials Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dexerials Corp filed Critical Dexerials Corp
Priority to KR1020147013844A priority Critical patent/KR20140098090A/ko
Publication of WO2013061923A1 publication Critical patent/WO2013061923A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention propose : un adhésif conducteur qui est apte à atteindre une excellente fiabilité de connexion en assurant un fort pouvoir adhérent ; et un module de cellule solaire qui est apte à atteindre un rendement élevé de génération d'énergie en reliant des électrodes d'une cellule solaire et des languettes de connexion à l'aide de cet adhésif conducteur. Cet adhésif conducteur est obtenu par dispersion de particules conductrices dans un liant qui contient un initiateur de polymérisation par voie radicalaire, un (méth)acrylate qui ne contient pas un groupe acide phosphorique ou un groupe ester d'acide phosphorique et un (méth)acrylate qui contient un groupe acide phosphorique ou un groupe ester d'acide phosphorique. L'initiateur de polymérisation par voie radicalaire a une température de demi-vie de 1 minute de 110-140°C. Le (méth)acrylate qui contient un groupe acide phosphorique ou un groupe ester d'acide phosphorique est contenu dans une quantité de 0,1-5 parties en masse pour 54 parties en masse du (méth)acrylate qui ne contient pas un groupe acide phosphorique ou un groupe ester d'acide phosphorique.
PCT/JP2012/077238 2011-10-28 2012-10-22 Adhésif conducteur, module de cellule solaire et procédé de fabrication de module de cellule solaire Ceased WO2013061923A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
KR1020147013844A KR20140098090A (ko) 2011-10-28 2012-10-22 도전성 접착제, 태양 전지 모듈 및 태양 전지 모듈의 제조 방법

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011-237362 2011-10-28
JP2011237362A JP5960408B2 (ja) 2011-10-28 2011-10-28 導電性接着剤、太陽電池モジュール、及び太陽電池モジュールの製造方法

Publications (1)

Publication Number Publication Date
WO2013061923A1 true WO2013061923A1 (fr) 2013-05-02

Family

ID=48167755

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2012/077238 Ceased WO2013061923A1 (fr) 2011-10-28 2012-10-22 Adhésif conducteur, module de cellule solaire et procédé de fabrication de module de cellule solaire

Country Status (3)

Country Link
JP (1) JP5960408B2 (fr)
KR (1) KR20140098090A (fr)
WO (1) WO2013061923A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015140408A (ja) * 2014-01-29 2015-08-03 日立化成株式会社 接着剤組成物、接着剤組成物を用いた電子部材、及び半導体装置の製造方法
CN115232573A (zh) * 2021-04-23 2022-10-25 大洲电子材料（株） 高温可分离的导电性粘接剂及太阳能电池模块

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015056463A (ja) * 2013-09-11 2015-03-23 デクセリアルズ株式会社 太陽電池セル、太陽電池モジュール及びその製造方法
JP6441023B2 (ja) * 2014-10-22 2018-12-19 株式会社Adeka 樹脂組成物及び放熱性硬化物
WO2018047597A1 (fr) * 2016-09-06 2018-03-15 株式会社スリーボンド Adhésif électroconducteur thermodurcissable
US11359116B2 (en) 2016-09-06 2022-06-14 Threebond Co., Ltd. Thermocurable electroconductive adhesive
JP6946395B2 (ja) * 2019-10-25 2021-10-06 日本化学工業株式会社 導電性接着剤、それを用いた接着構造体及び電子部品
JP7510292B2 (ja) * 2020-07-17 2024-07-03 京都エレックス株式会社 導電性接着剤組成物

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2006199825A (ja) * 2005-01-20 2006-08-03 Soken Chem & Eng Co Ltd 異方導電性接着テープおよび配線基板異方導電接着体
JP2006241215A (ja) * 2005-03-01 2006-09-14 Toray Ind Inc 可撓性フィルム基板用部材
JP2008085227A (ja) * 2006-09-28 2008-04-10 Sanyo Electric Co Ltd 太陽電池モジュール
JP2010037539A (ja) * 2008-07-11 2010-02-18 Sony Chemical & Information Device Corp 異方性導電フィルム
WO2011001908A1 (fr) * 2009-07-01 2011-01-06 積水化学工業株式会社 Résine de liant pour pâte conductrice, pâte conductrice, et élément de cellule solaire
JP2011509332A (ja) * 2008-01-11 2011-03-24 エルジー・ケム・リミテッド 粘着剤組成物、それを含む粘着偏光板及び液晶表示装置
WO2011093321A1 (fr) * 2010-01-26 2011-08-04 三洋電機株式会社 Module de cellule solaire, et procédé de fabrication de celui-ci

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102942883B (zh) * 2006-04-26 2015-08-26 日立化成株式会社 粘接带及使用其的太阳能电池模块

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2006199825A (ja) * 2005-01-20 2006-08-03 Soken Chem & Eng Co Ltd 異方導電性接着テープおよび配線基板異方導電接着体
JP2006241215A (ja) * 2005-03-01 2006-09-14 Toray Ind Inc 可撓性フィルム基板用部材
JP2008085227A (ja) * 2006-09-28 2008-04-10 Sanyo Electric Co Ltd 太陽電池モジュール
JP2011509332A (ja) * 2008-01-11 2011-03-24 エルジー・ケム・リミテッド 粘着剤組成物、それを含む粘着偏光板及び液晶表示装置
JP2010037539A (ja) * 2008-07-11 2010-02-18 Sony Chemical & Information Device Corp 異方性導電フィルム
WO2011001908A1 (fr) * 2009-07-01 2011-01-06 積水化学工業株式会社 Résine de liant pour pâte conductrice, pâte conductrice, et élément de cellule solaire
WO2011093321A1 (fr) * 2010-01-26 2011-08-04 三洋電機株式会社 Module de cellule solaire, et procédé de fabrication de celui-ci

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015140408A (ja) * 2014-01-29 2015-08-03 日立化成株式会社 接着剤組成物、接着剤組成物を用いた電子部材、及び半導体装置の製造方法
CN115232573A (zh) * 2021-04-23 2022-10-25 大洲电子材料（株） 高温可分离的导电性粘接剂及太阳能电池模块
CN115232573B (zh) * 2021-04-23 2024-03-26 大洲电子材料（株） 高温可分离的导电性粘接剂及太阳能电池模块

Also Published As

Publication number Publication date
JP2013098230A (ja) 2013-05-20
JP5960408B2 (ja) 2016-08-02
KR20140098090A (ko) 2014-08-07

Similar Documents

Publication Publication Date Title
JP5960408B2 (ja) 導電性接着剤、太陽電池モジュール、及び太陽電池モジュールの製造方法
JP5840418B2 (ja) 導電性接着剤及び太陽電池モジュール
JP5415396B2 (ja) 太陽電池モジュールの製造方法及び太陽電池モジュール
JP5446420B2 (ja) 太陽電池モジュール及びその製造方法
JP5886588B2 (ja) 導電性接着剤、並びに、それを用いた太陽電池モジュール、及びその製造方法
JP5707110B2 (ja) 導電性接着材料、太陽電池モジュール及びその製造方法
JP6247059B2 (ja) 導電性接着剤、太陽電池モジュール、及び太陽電池モジュールの製造方法
WO2011132682A1 (fr) Module de cellule solaire et procédé de production de celui-ci
JP6154625B2 (ja) 導電性接着剤、太陽電池モジュール、及び太陽電池モジュールの製造方法
JP2015228457A (ja) 太陽電池用導電性接着剤、太陽電池モジュール、及び太陽電池モジュールの製造方法
WO2012099257A1 (fr) Module de cellules solaires et procédé de fabrication d'un module de cellules solaires
JP2016048807A (ja) 導電性接着剤、並びに、それを用いた太陽電池モジュール、及びその製造方法
EP2816612A1 (fr) Agent adhésif conducteur de l'électricité, module de cellule solaire et procédé de fabrication de module de cellule solaire
TWI537985B (zh) A conductive adhesive for a solar cell and a method of connecting the solar cell module and a solar cell module using the same
JP2016178312A (ja) 太陽電池用導電性接着剤及びこれを用いた接続方法、太陽電池モジュール、太陽電池モジュールの製造方法
WO2012073702A1 (fr) Module de pile solaire, et procédé de fabrication de celui-ci
JP5692347B2 (ja) 導電接着剤
HK1195671A (en) Solar cell conductive adhesive and connection method using same, solar cell module, and method for producing solar cell module
JP2016001765A (ja) 太陽電池モジュール及び太陽電池モジュールの製造方法
HK1187153A (zh) 太阳能电池模块及太阳能电池模块的制造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12843614

Country of ref document: EP

Kind code of ref document: A1

DPE2 Request for preliminary examination filed before expiration of 19th month from priority date (pct application filed from 20040101)
NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20147013844

Country of ref document: KR

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 12843614

Country of ref document: EP

Kind code of ref document: A1