WO2012024019A1 - Préoxydation de soupapes de moteur et sièges rapportés pour durée de vie améliorée - Google Patents

Préoxydation de soupapes de moteur et sièges rapportés pour durée de vie améliorée Download PDF

Info

Publication number
WO2012024019A1
WO2012024019A1 PCT/US2011/040802 US2011040802W WO2012024019A1 WO 2012024019 A1 WO2012024019 A1 WO 2012024019A1 US 2011040802 W US2011040802 W US 2011040802W WO 2012024019 A1 WO2012024019 A1 WO 2012024019A1
Authority
WO
WIPO (PCT)
Prior art keywords
valve
valve seat
seat insert
exhaust
scale coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2011/040802
Other languages
English (en)
Inventor
Nathaniel S L Phillips
Jeff A. Jensen
Eric Kelsey
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Caterpillar Inc
Original Assignee
Caterpillar Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Caterpillar Inc filed Critical Caterpillar Inc
Publication of WO2012024019A1 publication Critical patent/WO2012024019A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Cette invention concerne un siège de soupape rapporté (50) fonctionnant avec une soupape de façon à ouvrir et fermer sélectivement un passage vers un cylindre (22) dans un moteur à combustion interne (20). Ledit siège de soupape rapporté (50) comprend une base en alliage de cobalt comprenant approximativement au moins 40% en poids de Co et approximativement au moins 5% en poids de Cr. Un revêtement à base de calamine (54) est disposé sur au moins une face d'usure (52) du siège de soupape rapporté (50) destinée à venir en prise avec la soupape, et optionnellement sur une partie de la soupape.
PCT/US2011/040802 2010-08-19 2011-06-17 Préoxydation de soupapes de moteur et sièges rapportés pour durée de vie améliorée Ceased WO2012024019A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US12/859,563 US20120043490A1 (en) 2010-08-19 2010-08-19 Pre-oxidation of engine valves and seat inserts for improved life
US12/859,563 2010-08-19

Publications (1)

Publication Number Publication Date
WO2012024019A1 true WO2012024019A1 (fr) 2012-02-23

Family

ID=45593324

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2011/040802 Ceased WO2012024019A1 (fr) 2010-08-19 2011-06-17 Préoxydation de soupapes de moteur et sièges rapportés pour durée de vie améliorée

Country Status (2)

Country Link
US (1) US20120043490A1 (fr)
WO (1) WO2012024019A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022129647A1 (fr) 2020-12-18 2022-06-23 eV-Technologies Chaussures intelligentes à récupération d'énergie et guidage géolocalisé avec alphabet d'orteils

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6157937B2 (ja) * 2013-06-07 2017-07-05 株式会社東芝 弁装置およびその製造方法
JP5887374B2 (ja) * 2014-03-19 2016-03-16 株式会社リケン 鉄基焼結合金製バルブシート

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1992019391A1 (fr) * 1991-04-29 1992-11-12 Benmin Gong Procede de formation de revetements en oxydes metalliques
EP0730085A1 (fr) * 1995-02-28 1996-09-04 Yamaha Hatsudoki Kabushiki Kaisha Culasse et méthode pour fabriquer un siège de soupapes
EP1582605A1 (fr) * 2000-06-20 2005-10-05 Alloy Technology Solutions, Inc. Alliage à base de fer résistant à l'usure
US20090257906A1 (en) * 2008-04-15 2009-10-15 L.E. Jones Company, Cobalt-rich wear resistant alloy and method of making and use thereof

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE10334703A1 (de) * 2003-07-30 2005-02-24 Daimlerchrysler Ag Ventilsitzringe aus Co oder Co/Mo-Basislegierungen und deren Herstellung

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1992019391A1 (fr) * 1991-04-29 1992-11-12 Benmin Gong Procede de formation de revetements en oxydes metalliques
EP0730085A1 (fr) * 1995-02-28 1996-09-04 Yamaha Hatsudoki Kabushiki Kaisha Culasse et méthode pour fabriquer un siège de soupapes
EP1582605A1 (fr) * 2000-06-20 2005-10-05 Alloy Technology Solutions, Inc. Alliage à base de fer résistant à l'usure
US20090257906A1 (en) * 2008-04-15 2009-10-15 L.E. Jones Company, Cobalt-rich wear resistant alloy and method of making and use thereof

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022129647A1 (fr) 2020-12-18 2022-06-23 eV-Technologies Chaussures intelligentes à récupération d'énergie et guidage géolocalisé avec alphabet d'orteils

Also Published As

Publication number Publication date
US20120043490A1 (en) 2012-02-23

Similar Documents

Publication Publication Date Title
EP0901565B1 (fr) Soupape d'echappement destinee a un moteur a combustion interne
US8430075B2 (en) Superaustenitic stainless steel and method of making and use thereof
US10443456B2 (en) Exhaust valve for an internal combustion engine, and a method of strengthening an annular valve seat area in an exhaust valve
CA2658234C (fr) Alliage haute temperature resistant a l'usure
US7682471B2 (en) Austenitic iron-based alloy
CN103527281A (zh) 用于内燃机中的排气阀的排气阀芯杆
CA3120120C (fr) Alliage a base de ni, produit d`alliage a base de ni et methodes de production
US8129041B2 (en) Article having a protective coating and methods
EP2146121B1 (fr) Dispositif de soupape
JP2970670B1 (ja) 肉盛合金およびエンジンバルブ
US20120043490A1 (en) Pre-oxidation of engine valves and seat inserts for improved life
CA2491754C (fr) Alliages a base de cobalt resistant a l'usure et a la corrosion
US20130220263A1 (en) Valve system for controlling the charge exchange
Larson et al. Engine valves—Design and material evolution
CN113084457A (zh) 一种活塞的金相强化制造方法
US20140345557A1 (en) Thermal Spray Coated Engine Valve for Increased Wear Resistance
Takayama et al. Titanium alloy bar suitable for highly efficient wear-resistance treatment
Larson et al. Application of superalloys in internal combustion engine exhaust valves
WO2018150080A1 (fr) Procédé de revêtement d'un composant de moteur à piston et composant de moteur à piston
HK1019915B (en) An exhaust valve for an internal combustion engine
JP2007270701A (ja) 蒸気タービン用バルブ
HK1152350B (en) Cobalt-rich wear resistant alloy and method of making and use thereof

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11818505

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 11818505

Country of ref document: EP

Kind code of ref document: A1