WO2012013983A1 - Compositions de ciment et de béton contenant du sol - Google Patents

Compositions de ciment et de béton contenant du sol Download PDF

Info

Publication number
WO2012013983A1
WO2012013983A1 PCT/GB2011/051443 GB2011051443W WO2012013983A1 WO 2012013983 A1 WO2012013983 A1 WO 2012013983A1 GB 2011051443 W GB2011051443 W GB 2011051443W WO 2012013983 A1 WO2012013983 A1 WO 2012013983A1
Authority
WO
WIPO (PCT)
Prior art keywords
soil
cement
concrete
ggbs
aggregate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/GB2011/051443
Other languages
English (en)
Inventor
Jeremy Martin Adrian Harrall
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lafarge SA
Original Assignee
Lafarge SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lafarge SA filed Critical Lafarge SA
Priority to EP11754903.0A priority Critical patent/EP2598458A1/fr
Publication of WO2012013983A1 publication Critical patent/WO2012013983A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention porte sur une composition qui comprend du ciment; du laitier de haut fourneau granulé broyé (ggbs) et/ou des cendres volantes (pfa); du granulat fin; du granulat grossier; du sol; et de l'eau, cette composition, après sa prise, donnant un béton contenant du sol.
PCT/GB2011/051443 2010-07-30 2011-07-29 Compositions de ciment et de béton contenant du sol Ceased WO2012013983A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP11754903.0A EP2598458A1 (fr) 2010-07-30 2011-07-29 Compositions de ciment et de béton contenant du sol

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GB201012848A GB201012848D0 (en) 2010-07-30 2010-07-30 Cement-containing compositions
GB1012848.6 2010-07-30

Publications (1)

Publication Number Publication Date
WO2012013983A1 true WO2012013983A1 (fr) 2012-02-02

Family

ID=42799375

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB2011/051443 Ceased WO2012013983A1 (fr) 2010-07-30 2011-07-29 Compositions de ciment et de béton contenant du sol

Country Status (3)

Country Link
EP (1) EP2598458A1 (fr)
GB (1) GB201012848D0 (fr)
WO (1) WO2012013983A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR3016376A1 (fr) * 2014-01-16 2015-07-17 Cematerre Nouveau perfectionnement a un procede de fabrication d'au moins un mur vertical a base de terre
CN105152591A (zh) * 2015-08-08 2015-12-16 常州大学 一种lc35级轻骨料结构混凝土的配制
WO2021180931A1 (fr) * 2020-03-12 2021-09-16 Saint-Gobain Weber France Fabrication d'un mur par projection par voie seche d'une composition comprenant de la terre crue

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3511044A1 (de) * 1985-03-27 1986-10-02 Gauthier 5511 Wincheringen Weber Biologischer beton, isolierbeton
US5700107A (en) * 1995-07-25 1997-12-23 Habour Remediation And Transfer Inc. (Hr&T) Method of soil remediation
WO1999052837A1 (fr) * 1998-04-15 1999-10-21 Road Building International (Barbados) Limited Agent chimique ameliorant les proprietes geothechniques des sols
DE202007006660U1 (de) * 2007-05-10 2007-08-02 Biofol-Film Gmbh Erdboden-Zementmörtel

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR100951032B1 (ko) * 2008-06-09 2010-04-05 허정도 폴리머 시멘트 콘크리트의 원리를 이용한흙-폴리머-시멘트 콘크리트 조성물

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3511044A1 (de) * 1985-03-27 1986-10-02 Gauthier 5511 Wincheringen Weber Biologischer beton, isolierbeton
US5700107A (en) * 1995-07-25 1997-12-23 Habour Remediation And Transfer Inc. (Hr&T) Method of soil remediation
WO1999052837A1 (fr) * 1998-04-15 1999-10-21 Road Building International (Barbados) Limited Agent chimique ameliorant les proprietes geothechniques des sols
DE202007006660U1 (de) * 2007-05-10 2007-08-02 Biofol-Film Gmbh Erdboden-Zementmörtel

Non-Patent Citations (4)

* Cited by examiner, † Cited by third party
Title
KANIRAJ S R ET AL: "Compressive Strength of cement stabilized fly ash-soil mixtures", CEMENT AND CONCRETE RESEARCH, PERGAMON PRESS, ELMSFORD, NY, US, vol. 29, 1 May 1999 (1999-05-01), pages 673 - 677, XP002525765, ISSN: 0008-8846, [retrieved on 20000214], DOI: 10.1016/S0008-8846(99)00018-6 *
KAWAMURA M ET AL: "Compressive strength and density of fly-ash substituted soil-cement concrete", KEY ENGINEERING MATERIALS, TRANS TECH PUBLICATIONS LTD., STAFA-ZURICH, CH, vol. 302-303, 1 January 2006 (2006-01-01), pages 376 - 383, XP008144728, ISSN: 1013-9826 *
See also references of EP2598458A1
V.S. RAMACHANDRAN: "Properties Science and Technology", 1984, NOYES PUBLICATIONS, article "Concrete Admixtures Handbook"

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR3016376A1 (fr) * 2014-01-16 2015-07-17 Cematerre Nouveau perfectionnement a un procede de fabrication d'au moins un mur vertical a base de terre
EP2896604A1 (fr) * 2014-01-16 2015-07-22 Cematerre Nouveau perfectionnement à un procédé de fabrication d'au moins un mur vertical à base de terre
CN105152591A (zh) * 2015-08-08 2015-12-16 常州大学 一种lc35级轻骨料结构混凝土的配制
WO2021180931A1 (fr) * 2020-03-12 2021-09-16 Saint-Gobain Weber France Fabrication d'un mur par projection par voie seche d'une composition comprenant de la terre crue
FR3108115A1 (fr) * 2020-03-12 2021-09-17 Saint-Gobain Weber France Fabrication d’un mur par projection par voie sèche d’une composition comprenant de la terre crue

Also Published As

Publication number Publication date
GB201012848D0 (en) 2010-09-15
EP2598458A1 (fr) 2013-06-05

Similar Documents

Publication Publication Date Title
Nataraja et al. Use of granulated blast furnace slag as fine aggregate in cement mortar
Suksiripattanapong et al. Properties of soft Bangkok clay stabilized with cement and fly ash geopolymer for deep mixing application
Binici et al. Durability properties of concretes made with sand and cement size basalt
Lo et al. Comparison of workability and mechanical properties of self-compacting lightweight concrete and normal self-compacting concrete
Kumar et al. Recycled cement and recycled fine aggregates as alternative resources of raw materials for sustainable cellular light weight flowable material
Sun et al. Study on preparation of inorganic binder stabilized material with large dosage of phosphogypsum
WO2012013983A1 (fr) Compositions de ciment et de béton contenant du sol
Al Adday et al. Fresh and hardened properties of recycled concrete aggregate modified by iron powder and silica
Nguyen-Van et al. Experimental study on pervious cement and pervious geopolymer concretes using sea sand and seawater
Dhanya et al. Evaluation of the mechanical performance of M25 grade recycled aggregate concrete
Babangida et al. Effects of aggregate size on concrete strength
Hashempour et al. The evaluation of the stress-strain characteristics of mcc concrete
Van Dang et al. Experimental study on use fly ash in underground construction concrete
Ravinder et al. Study on compressive strength of concrete on partial replacement of cement with ground granulated blast furnace slag (GGBS)
Hofgård et al. Climate enhanced concrete in the civil engineering industry
Akiije Characteristic and effects of a superplasticizer quantity variation in some concrete strengths optimization
Deshabandu et al. Effect of ordinary Portland cement (OPC) and blended hydraulic cement (BHC) on the behaviour of self-compacting concrete
Daoud et al. Production and properties of high strength concrete for heightening concrete dam in Sudan
Gaba et al. Effect of alccofine and silica fume on strength properties of concrete
Patil et al. Analysis of Strength Parameters of Paving Blocks with inclusion Sea Sand
Galabada et al. Improvement of Earth into Concrete as an Eco-friendly Building Material–Effect of Soil Gradation and Chemical Admixtures
Banerjee et al. Durability of tyre rubber concrete modified with GGBS and silica
WO2021006759A1 (fr) Coulées et mélanges de béton autocompactant pour la production de bétons
Alik et al. Physical and Mechanical Properties of Autoclaved Aerated Concrete (AAC) as Partial Fine Aggregate in Concrete
TERLUMUN et al. APPRAISAL OF SUPPLEMENTARY CEMENTITIOUS MATERIALS IN SELF-COMPACTING CONCRETE

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11754903

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2011754903

Country of ref document: EP