[go: up one dir, main page]

WO2012011856A1 - Composition pour l'élimination de l'arsenic - Google Patents

Composition pour l'élimination de l'arsenic Download PDF

Info

Publication number
WO2012011856A1
WO2012011856A1 PCT/SE2010/050864 SE2010050864W WO2012011856A1 WO 2012011856 A1 WO2012011856 A1 WO 2012011856A1 SE 2010050864 W SE2010050864 W SE 2010050864W WO 2012011856 A1 WO2012011856 A1 WO 2012011856A1
Authority
WO
WIPO (PCT)
Prior art keywords
water
arsenic
composition
zeolite
iron
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/SE2010/050864
Other languages
English (en)
Inventor
Ferenc LÓNYI
János PAPP
József Valyon
József VÁRI
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Josab International AB
Original Assignee
Josab International AB
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Josab International AB filed Critical Josab International AB
Priority to PCT/SE2010/050864 priority Critical patent/WO2012011856A1/fr
Publication of WO2012011856A1 publication Critical patent/WO2012011856A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne une composition pour l'élimination de l'arsenic de l'eau, la composition comprenant un adsorbant et un support, caractérisée en ce que l'adsorbant comprend un oxyhydroxyde comprenant du Fe, et de l'Al et/ou du Si, et le support comprend de la zéolite, l'adsorbant étant chimiquement lié à la zéolite; un procédé pour la production d'une composition pour l'élimination de l'arsenic de l'eau; et un procédé de traitement de l'eau contenant de l'arsenic.
PCT/SE2010/050864 2010-07-22 2010-07-22 Composition pour l'élimination de l'arsenic Ceased WO2012011856A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/SE2010/050864 WO2012011856A1 (fr) 2010-07-22 2010-07-22 Composition pour l'élimination de l'arsenic

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/SE2010/050864 WO2012011856A1 (fr) 2010-07-22 2010-07-22 Composition pour l'élimination de l'arsenic

Publications (1)

Publication Number Publication Date
WO2012011856A1 true WO2012011856A1 (fr) 2012-01-26

Family

ID=45497073

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/SE2010/050864 Ceased WO2012011856A1 (fr) 2010-07-22 2010-07-22 Composition pour l'élimination de l'arsenic

Country Status (1)

Country Link
WO (1) WO2012011856A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111874953A (zh) * 2020-08-07 2020-11-03 华北科技学院 一种聚合氯化铝铁及其制备方法和阻燃剂组合物
CN116212625A (zh) * 2023-05-09 2023-06-06 明硕环境科技集团股份有限公司 一种高强度羟基氧化铁脱硫剂及其制备方法

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090264280A1 (en) * 2007-01-09 2009-10-22 Nikolay Aleksandrovich BADULIN Sorbent for removing heavy metal ions from water

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090264280A1 (en) * 2007-01-09 2009-10-22 Nikolay Aleksandrovich BADULIN Sorbent for removing heavy metal ions from water

Non-Patent Citations (4)

* Cited by examiner, † Cited by third party
Title
HABUDA STANIC ET AL.: "Arsenite and arsenate sorption by hydrous ferric oxide/polymeric material", DESALINATION, vol. 229, no. 2208, pages 1 - 9 *
HYE JIN HONG ET AL.: "Preparation and Evaluation of Fe-Al Binary Oxide for Arsenic removal: Comparative study with Single Metal Oxides", SEPARATION SCIENCE AND TECHNOLOGY, vol. 45, 2010, pages 1975 - 1981 *
LE ZENG: "A method for preparing silica-containing iron(III) oxide adsorbents for arsenic removal", WATER RESEARCH, vol. 37, 2003, pages 4351 - 4358 *
MOHAN ET AL.: "Arsenic removal from water/wastewater using adsorbents - A critical review", JOURNAL OF HAZARDOUS MATERIALS, vol. 142, 2007, pages 1 - 53 *

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111874953A (zh) * 2020-08-07 2020-11-03 华北科技学院 一种聚合氯化铝铁及其制备方法和阻燃剂组合物
CN111874953B (zh) * 2020-08-07 2022-06-24 华北科技学院 一种聚合氯化铝铁及其制备方法和阻燃剂组合物
CN116212625A (zh) * 2023-05-09 2023-06-06 明硕环境科技集团股份有限公司 一种高强度羟基氧化铁脱硫剂及其制备方法
CN116212625B (zh) * 2023-05-09 2023-09-05 明硕环境科技集团股份有限公司 一种高强度羟基氧化铁脱硫剂及其制备方法

Similar Documents

Publication Publication Date Title
KR100951492B1 (ko) 흡착재 혼합물
Pawar et al. Activated bentonite as a low-cost adsorbent for the removal of Cu (II) and Pb (II) from aqueous solutions: Batch and column studies
Albayati et al. Adsorption of binary and multi heavy metals ions from aqueous solution by amine functionalized SBA-15 mesoporous adsorbent in a batch system
US8110526B2 (en) Arsenic absorbing composition and methods of use
Amer et al. ِAdsorption of lead, zinc and cadmium ions on polyphosphate-modified kaolinite clay
EP0561998B1 (fr) Procede d'elimination des metaux lourds, plus particulierement du plomb, se trouvant dans des systemes aqueux renfermant des ions concurrents, a l'aide de silicates de titane et d'etain amorphes
US6824690B1 (en) Zirconium-modified materials for selective adsorption and removal of aqueous arsenic
JP5482979B2 (ja) 吸着剤
CN111417460A (zh) 用于从流出物中去除污染物的羟基磷灰石复合物及制备方法
EP1569749A1 (fr) Milieu d'extraction de l'arsenic ameliore
Bahabadi et al. Removal of Cd, Cu and Zn ions from aqueous solutions using natural and Fe modified sepiolite, zeolite and palygorskite clay minerals
CA2598074A1 (fr) Produits et procedes permettant de retirer des substances d'une solution aqueuse
Szala et al. Removal of chromium (VI) from aqueous solutions using zeolites modified with HDTMA and ODTMA surfactants
Milićević et al. Removal of heavy metals from aqueous solution using natural and Fe (III) oxyhydroxide clinoptilolite
Shawabkeh et al. Cobalt and zinc removal from aqueous solution by chemically treated bentonite
CN109476512B (zh) 从水中去除砷和重金属的组合物和方法
JP7177703B2 (ja) 層状複水酸化物を用いた浄水装置および浄水方法
TWI672273B (zh) 吸附方法
WO2012011856A1 (fr) Composition pour l'élimination de l'arsenic
Elmorsy et al. A comparative study on Co (II) removal capacity from water samples by sorption using limestone and nanolimestone
US11944952B2 (en) Removing contaminants from water with adsorbents
Irannajad et al. Kinetic, thermodynamic and equilibrium studies on the removal of copper ions from aqueous solutions by natural and modified clinoptilolites
Charoenchai et al. Effect of ternary polymer composites of macroporous adsorbents on adsorption properties for heavy metal removal from aqueous solution
Rasuli et al. Performance of surfactant-modified forms of clinoptilolite and pumice in nitrate removal from aqueous solution
RU2675866C1 (ru) Способ получения композиционного сорбента

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10855085

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 10855085

Country of ref document: EP

Kind code of ref document: A1