WO2012065906A1 - Mortier sec et son utilisation comme enduit - Google Patents

Mortier sec et son utilisation comme enduit Download PDF

Info

Publication number
WO2012065906A1
WO2012065906A1 PCT/EP2011/069900 EP2011069900W WO2012065906A1 WO 2012065906 A1 WO2012065906 A1 WO 2012065906A1 EP 2011069900 W EP2011069900 W EP 2011069900W WO 2012065906 A1 WO2012065906 A1 WO 2012065906A1
Authority
WO
WIPO (PCT)
Prior art keywords
dry mortar
weight
plaster
mortar according
dispersion powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2011/069900
Other languages
German (de)
English (en)
Inventor
Stefan Rossmayer
Michaela SCHWÖD
Thomas Schemm
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Construction Research and Technology GmbH
Original Assignee
Construction Research and Technology GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Construction Research and Technology GmbH filed Critical Construction Research and Technology GmbH
Priority to EP11784629.5A priority Critical patent/EP2640676A1/fr
Publication of WO2012065906A1 publication Critical patent/WO2012065906A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un mortier sec, approprié pour la préparation d'un enduit pour une surface d'un bâtiment, comprenant 0 à 50 % en poids de liant hydraulique, 0 à 35 % en poids d'hydroxyde de calcium, 20 à 86 % en poids de charges, 0,2 à 5 % en poids d'une poudre de dispersion à base d'un terpolymère d'éthylène-laurate de vinyle-chlorure de vinyle et 0 à 40 % en poids d'autres composants, le liant hydraulique et l'hydroxyde de calcium représentant ensemble au moins 8 % en poids du mortier sec. L'invention concerne également l'utilisation de 0,2 à 5 % en poids de poudre de dispersion à base d'un terpolymère d'éthylène-laurate de vinyle-chlorure de vinyle, par rapport au mortier sec, dans un enduit de restauration, pour l'initiation accélérée des propriétés hydrophobes de l'enduit après l'application.
PCT/EP2011/069900 2010-11-15 2011-11-11 Mortier sec et son utilisation comme enduit Ceased WO2012065906A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP11784629.5A EP2640676A1 (fr) 2010-11-15 2011-11-11 Mortier sec et son utilisation comme enduit

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP10191182 2010-11-15
EP10191182.4 2010-11-15

Publications (1)

Publication Number Publication Date
WO2012065906A1 true WO2012065906A1 (fr) 2012-05-24

Family

ID=44993546

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2011/069900 Ceased WO2012065906A1 (fr) 2010-11-15 2011-11-11 Mortier sec et son utilisation comme enduit

Country Status (2)

Country Link
EP (1) EP2640676A1 (fr)
WO (1) WO2012065906A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014009299A3 (fr) * 2012-07-10 2014-03-06 Akzo Nobel Chemicals International B.V. Mélange pulvérulent et procédé de fabrication d'un mortier sec
CN104230266A (zh) * 2014-09-05 2014-12-24 陈浩 高强度干粉砂浆搅拌方法
WO2015090615A1 (fr) * 2013-12-20 2015-06-25 Interbran Systems Ag Mélange sec de matériau de construction et enduit d'isolation thermique résultant
DE102014012190A1 (de) * 2014-08-20 2016-02-25 Saint-Gobain Weber Gmbh Sanierung von mit Pilzen und/oder Algen befallenen Gebäudefassaden
EP3318538B1 (fr) 2016-11-02 2019-08-21 STO SE & Co. KGaA Crépi, système composite isolant et procédé de fabrication d'un système composite isolant

Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2917263A1 (de) 1978-04-27 1979-11-08 Okresni Stavebni P V Opave Diffuser, kondensationsverhindernder, fungizider und frostbestaendiger putzmoertel und verfahren zu seiner fertigung
DE3512322A1 (de) 1985-04-02 1986-10-02 Colfirmit Marthahütte GmbH Fabrik chem. Baustoffe, Mineralmühlen und Edelputzwerke, 8590 Marktredwitz Putz-system
DD291074A5 (de) 1989-12-21 1991-06-20 Bauakademie Ddr Sanierputzmoertel
EP0477900A2 (fr) * 1990-09-27 1992-04-01 Wacker-Chemie Gmbh Composition d'une poudre fluente
DE4402408A1 (de) 1994-01-27 1995-08-03 Wacker Chemie Gmbh Redispergierbare, siliciummodifizierte Dispersionspulverzusammensetzung, Verfahren zu deren Herstellung und deren Verwendung
EP0728715A1 (fr) * 1995-02-23 1996-08-28 Wacker-Chemie GmbH Procédé pour rendre hydrophobe des produits en gypse
DE10037629A1 (de) 2000-08-02 2002-02-14 Skw Bauwerkstoffe Deutschland Wasserlösliche oder wasserquellbare sulfogruppenhaltige assoziativverdickende Copolymere, Verfahren zu deren Herstellung und deren Verwendung
WO2002081399A1 (fr) * 2001-04-09 2002-10-17 James Hardie Research Pty Limited Fibro-ciment monobloc hydroresistant
US20040103814A1 (en) * 2002-11-27 2004-06-03 Do-Chul Shin Waterproof admixture composition for concrete having excellent anti-corrosive performance
WO2005090424A1 (fr) 2004-03-17 2005-09-29 Construction Research & Technology Gmbh Composition polymere et son utilisation comme additif dans des systemes de construction aqueux et dans des systemes de peinture et de revetement a base aqueuse
WO2006002936A1 (fr) * 2004-07-03 2006-01-12 Construction Research & Technology Gmbh Copolymeres solubles dans l'eau, contenant des groupe sulfo, procede pour les preparer, et leur utilisation
WO2008113460A1 (fr) 2007-03-16 2008-09-25 Construction Research & Technology Gmbh Préparation de copolymères contenant des groupes sulfoniques
EP1892228B1 (fr) 2006-07-24 2009-01-21 Akzo Nobel N.V. Utilisation de poudre polymère dans des joints en mortier pour pavés

Patent Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2917263A1 (de) 1978-04-27 1979-11-08 Okresni Stavebni P V Opave Diffuser, kondensationsverhindernder, fungizider und frostbestaendiger putzmoertel und verfahren zu seiner fertigung
DE3512322A1 (de) 1985-04-02 1986-10-02 Colfirmit Marthahütte GmbH Fabrik chem. Baustoffe, Mineralmühlen und Edelputzwerke, 8590 Marktredwitz Putz-system
DD291074A5 (de) 1989-12-21 1991-06-20 Bauakademie Ddr Sanierputzmoertel
EP0477900A2 (fr) * 1990-09-27 1992-04-01 Wacker-Chemie Gmbh Composition d'une poudre fluente
DE4402408A1 (de) 1994-01-27 1995-08-03 Wacker Chemie Gmbh Redispergierbare, siliciummodifizierte Dispersionspulverzusammensetzung, Verfahren zu deren Herstellung und deren Verwendung
EP0728715A1 (fr) * 1995-02-23 1996-08-28 Wacker-Chemie GmbH Procédé pour rendre hydrophobe des produits en gypse
DE10037629A1 (de) 2000-08-02 2002-02-14 Skw Bauwerkstoffe Deutschland Wasserlösliche oder wasserquellbare sulfogruppenhaltige assoziativverdickende Copolymere, Verfahren zu deren Herstellung und deren Verwendung
WO2002081399A1 (fr) * 2001-04-09 2002-10-17 James Hardie Research Pty Limited Fibro-ciment monobloc hydroresistant
US20040103814A1 (en) * 2002-11-27 2004-06-03 Do-Chul Shin Waterproof admixture composition for concrete having excellent anti-corrosive performance
WO2005090424A1 (fr) 2004-03-17 2005-09-29 Construction Research & Technology Gmbh Composition polymere et son utilisation comme additif dans des systemes de construction aqueux et dans des systemes de peinture et de revetement a base aqueuse
WO2006002936A1 (fr) * 2004-07-03 2006-01-12 Construction Research & Technology Gmbh Copolymeres solubles dans l'eau, contenant des groupe sulfo, procede pour les preparer, et leur utilisation
EP1892228B1 (fr) 2006-07-24 2009-01-21 Akzo Nobel N.V. Utilisation de poudre polymère dans des joints en mortier pour pavés
WO2008113460A1 (fr) 2007-03-16 2008-09-25 Construction Research & Technology Gmbh Préparation de copolymères contenant des groupes sulfoniques

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014009299A3 (fr) * 2012-07-10 2014-03-06 Akzo Nobel Chemicals International B.V. Mélange pulvérulent et procédé de fabrication d'un mortier sec
WO2015090615A1 (fr) * 2013-12-20 2015-06-25 Interbran Systems Ag Mélange sec de matériau de construction et enduit d'isolation thermique résultant
DE102014012190A1 (de) * 2014-08-20 2016-02-25 Saint-Gobain Weber Gmbh Sanierung von mit Pilzen und/oder Algen befallenen Gebäudefassaden
CN104230266A (zh) * 2014-09-05 2014-12-24 陈浩 高强度干粉砂浆搅拌方法
EP3318538B1 (fr) 2016-11-02 2019-08-21 STO SE & Co. KGaA Crépi, système composite isolant et procédé de fabrication d'un système composite isolant

Also Published As

Publication number Publication date
EP2640676A1 (fr) 2013-09-25

Similar Documents

Publication Publication Date Title
EP3805181B2 (fr) Procede pour appliquer une composition de matériau de construction à séchage rapide à base d'un liant hybride minéral
WO2012038099A1 (fr) Revêtements de toiture flexibles et imperméables
EP2563738B1 (fr) Liant aluminosilicaté à activation alcaline contenant des billes de verre
EP2603470B1 (fr) Produits de revêtement pour la réalisation de revêtements de flexibilité permanente
WO2010006987A1 (fr) Mélange de matériau de construction silicaté
EP3083522A1 (fr) Mélange sec de matériau de construction et enduit d'isolation thermique résultant
CN103080040A (zh) 用于聚合物面饰料或其他建筑产品的再分散性干燥组合物
EP2271597A1 (fr) Utilisation de coulis d'étanchéité souples pour le traitement de cure de corps en béton frais
EP2640676A1 (fr) Mortier sec et son utilisation comme enduit
AT512620B1 (de) Klebkraftverstärker für Zementzusammensetzungen
WO2012038288A1 (fr) Produits de revêtement pour réaliser des revêtements à flexibilité permanente
WO2021008765A1 (fr) Mélange d'enduit à sec pour une isolation pulvérisable
JP5910156B2 (ja) 耐酸水硬性組成物、モルタル組成物及びモルタル硬化体
EP2099722B2 (fr) Pose hydrofuge de carrelage
WO2012038302A1 (fr) Produits de revêtement pour réaliser des revêtements d'infrastructures imperméables
WO2009037218A1 (fr) Mélange contenant un composé d'ammonium quaternaire et son utilisation
KR20120091697A (ko) 콘크리트 면처리용 시멘트 조성물
US20080264302A1 (en) Curable Composition Containing as Constituent Material Silica Obtained by Decomposing Chrysotile and Cured Object
DE102013007937B4 (de) Verwendung eines mineralischen, hydraulischen Bindemittel in wasserhaltigen Frischmassen, sowie in mineralischen, hydraulischen Trockenmörteln, in mineralischen Frischmörteln und Frischbetonen
JPH07106955B2 (ja) コンクリート構造物の劣化防止方法
WO2010018017A2 (fr) Compositions de matériau de construction en poudre contenant du dialkyle éther à chaîne longue
EP2433918A1 (fr) Composition de matériau de construction et son utilisation pour la déshumidification et/ou la régulation d'humidité de constructions
EP2247671A1 (fr) Matériau comprenant des pores réglables qui contiennent des particules pouvant gonfler en présence d'eau
KR20190021098A (ko) 타일시멘트 모르타르용 첨가제 조성물 및 이를 포함하는 타일시멘트 모르타르
EP4082989A1 (fr) Composé hydrophobe de mortier

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11784629

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2011784629

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: DE