WO2012049622A1 - Système adsorbant et appareil permettant un stockage efficace de l'hydrogène et un ravitaillement efficace en hydrogène - Google Patents

Système adsorbant et appareil permettant un stockage efficace de l'hydrogène et un ravitaillement efficace en hydrogène Download PDF

Info

Publication number
WO2012049622A1
WO2012049622A1 PCT/IB2011/054475 IB2011054475W WO2012049622A1 WO 2012049622 A1 WO2012049622 A1 WO 2012049622A1 IB 2011054475 W IB2011054475 W IB 2011054475W WO 2012049622 A1 WO2012049622 A1 WO 2012049622A1
Authority
WO
WIPO (PCT)
Prior art keywords
adsorbent
hydrogen
storage
storage vessel
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/IB2011/054475
Other languages
English (en)
Inventor
Phiroze H Patel
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Publication of WO2012049622A1 publication Critical patent/WO2012049622A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention se rapporte à un système permettant de stocker de l'hydrogène gazeux dans des récipients portables qui peuvent être utilisés dans des applications telles que des automobiles ou d'autres dispositifs similaires. L'invention comprend des cylindres qui sont soit non isolés, soit isolés selon le besoin et qui contiennent un adsorbant à usage spécifique. L'adsorbant présente une morphologie unique, ce qui permet d'avoir un volume de pore important et une aire surfacique importante, ce qui, sous des conditions de température et de pression appropriées, permet l'introduction de l'hydrogène gazeux dans les micropores, les mésopores et les macropores de l'adsorbant, ce qui permet ainsi de maximiser l'adsorption de l'hydrogène. Il faut noter que, selon des paramètres de pression et de température appropriés, plus l'aire surfacique et les volumes des pores de l'adsorbant sont importants, plus le stockage sera important; cette relation est limitée par des limites de traitement pratiques relatives à la pression et à la température.
PCT/IB2011/054475 2010-10-15 2011-10-11 Système adsorbant et appareil permettant un stockage efficace de l'hydrogène et un ravitaillement efficace en hydrogène Ceased WO2012049622A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
IN2862MU2010 IN2010MU02862A (fr) 2010-10-15 2010-10-15
IN2862/MUM/2010 2010-10-15

Publications (1)

Publication Number Publication Date
WO2012049622A1 true WO2012049622A1 (fr) 2012-04-19

Family

ID=45562364

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2011/054475 Ceased WO2012049622A1 (fr) 2010-10-15 2011-10-11 Système adsorbant et appareil permettant un stockage efficace de l'hydrogène et un ravitaillement efficace en hydrogène

Country Status (2)

Country Link
IN (1) IN2010MU02862A (fr)
WO (1) WO2012049622A1 (fr)

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3138560A (en) 1959-12-17 1964-06-23 Engelhard Ind Inc Process for producing palladium on carbon catalysts
US4716736A (en) 1986-01-17 1988-01-05 Syracuse University Metal assisted carbon cold storage of hydrogen
US5653951A (en) 1995-01-17 1997-08-05 Catalytic Materials Limited Storage of hydrogen in layered nanostructures
US6672077B1 (en) 2001-12-11 2004-01-06 Nanomix, Inc. Hydrogen storage in nanostructure with physisorption
US7036324B2 (en) 2002-08-29 2006-05-02 Nanomix Inc. Hydrogen storage and supply system
DE102005023036A1 (de) 2005-05-13 2006-11-16 Deutsches Zentrum für Luft- und Raumfahrt e.V. Wasserstoffspeicher und Verfahren zur Wasserstoffspeicherung
WO2008058231A2 (fr) * 2006-11-08 2008-05-15 Curators Of The University Of Missouri Carbone à grande surface et procédé de production
WO2009056962A2 (fr) 2007-11-01 2009-05-07 Phiroze Patel Système pour stockage et ravitaillement efficace d'hydrogène

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3138560A (en) 1959-12-17 1964-06-23 Engelhard Ind Inc Process for producing palladium on carbon catalysts
US4716736A (en) 1986-01-17 1988-01-05 Syracuse University Metal assisted carbon cold storage of hydrogen
US5653951A (en) 1995-01-17 1997-08-05 Catalytic Materials Limited Storage of hydrogen in layered nanostructures
US6672077B1 (en) 2001-12-11 2004-01-06 Nanomix, Inc. Hydrogen storage in nanostructure with physisorption
US7036324B2 (en) 2002-08-29 2006-05-02 Nanomix Inc. Hydrogen storage and supply system
DE102005023036A1 (de) 2005-05-13 2006-11-16 Deutsches Zentrum für Luft- und Raumfahrt e.V. Wasserstoffspeicher und Verfahren zur Wasserstoffspeicherung
WO2008058231A2 (fr) * 2006-11-08 2008-05-15 Curators Of The University Of Missouri Carbone à grande surface et procédé de production
WO2009056962A2 (fr) 2007-11-01 2009-05-07 Phiroze Patel Système pour stockage et ravitaillement efficace d'hydrogène
WO2009057127A1 (fr) * 2007-11-01 2009-05-07 Patel Phirose Système permettant de stocker efficacement de l'hydrogène et d'assurer une alimentation efficace en hydrogène

Also Published As

Publication number Publication date
IN2010MU02862A (fr) 2014-12-21

Similar Documents

Publication Publication Date Title
US7976620B2 (en) Methods for hydrogen storage and refrigeration
US6834508B2 (en) Hydrogen storage and supply system
Ahluwalia et al. Automotive hydrogen storage system using cryo-adsorption on activated carbon
US7648568B2 (en) Hydrogen storage tank system based on gas adsorption on high-surface materials comprising an integrated heat exchanger
US6591617B2 (en) Method and apparatus for hydrogen storage and retrieval
US8454730B2 (en) Method of operating gas storage and supply system
US20110302933A1 (en) Storage and supply system of liquefied and condensed hydrogen
CN103759134A (zh) 储氢罐
KR20110125206A (ko) 금속 수소화물용 단열 탱크
JPS6362254B2 (fr)
JPS62216901A (ja) 金属援用炭素による水素の低温貯蔵方法及びその装置
WO2007026880A1 (fr) Dispositif de stockage d’hydrogene
EP2187108A2 (fr) Appareil de gestion thermique pour le stockage de gaz
US20040040316A1 (en) Operation of a hydrogen storage and supply system
WO2008035696A1 (fr) Dispositif de stockage d'hydrogÈne et procÉDÉ d'alimentation en hydrogÈne
Shkolin et al. Monolithic microporous carbon adsorbent for low-temperature natural gas storage
Godula‐Jopek Hydrogen storage options including constraints and challenges
EP2217848A2 (fr) Système pour stockage et ravitaillement efficace d'hydrogène
JP4634231B2 (ja) 低温液化ガス貯蔵装置、これを有する動力発生装置及び移動体
WO2012049622A1 (fr) Système adsorbant et appareil permettant un stockage efficace de l'hydrogène et un ravitaillement efficace en hydrogène
JP2007218317A (ja) 低温液体・気体水素貯蔵タンク
JP2006527833A (ja) 流体媒体中への吸収及び／又は混合によるｈ２の貯蔵
WO2005064227A1 (fr) Procede permettant de stocker l'hydrogene sous forme hybride
JP3710594B2 (ja) 自動車用燃料ガスタンク及び自動車用燃料ガススタンド
WO2025177093A2 (fr) Cylindre composite pour le stockage d'hydrogène à des températures cryogéniques, adsorbant pour le stockage d'hydrogène destiné à être utilisé dans des véhicules à moteur de ravitaillement en carburant, procédé de ravitaillement et de distribution d'hydrogène comprimé cryogénique, système embarqué de véhicule, procédé de stockage et de récupération d'hydrogène cryo-refroidi

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11815709

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 11815709

Country of ref document: EP

Kind code of ref document: A1