WO2011097547A1 - Séparation de tungstène à partir de solutions de molybdate d'ammonium - Google Patents

Séparation de tungstène à partir de solutions de molybdate d'ammonium Download PDF

Info

Publication number
WO2011097547A1
WO2011097547A1 PCT/US2011/023852 US2011023852W WO2011097547A1 WO 2011097547 A1 WO2011097547 A1 WO 2011097547A1 US 2011023852 W US2011023852 W US 2011023852W WO 2011097547 A1 WO2011097547 A1 WO 2011097547A1
Authority
WO
WIPO (PCT)
Prior art keywords
tungsten
molybdenum
calcium
iron
molybdate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2011/023852
Other languages
English (en)
Inventor
Leonid N. Shekhter
Xiong WEI
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LITZ JOHN K
Orchard Material Tech LLC
Original Assignee
LITZ JOHN K
Orchard Material Tech LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LITZ JOHN K, Orchard Material Tech LLC filed Critical LITZ JOHN K
Priority to US13/577,678 priority Critical patent/US20130243673A1/en
Publication of WO2011097547A1 publication Critical patent/WO2011097547A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un procédé pour la séparation de tungstène à partir de molybdène et, plus particulièrement, à partir de solutions de molybdate d'ammonium. Le procédé comprend la dissolution de trioxyde de molybdène de qualité technique dans une solution aqueuse d'hydroxyde d'ammonium, puis l'addition à la solution aqueuse de certains composés générant un métal, permettant ainsi de générer un précipité qui contient du tungstène. Le calcium, le fer et le manganèse sont les composés générateurs de métal préférés selon l'invention. Certaines valeurs de température et de pH du système, telles que décrites, sont préférées pour la précipitation du tungstène à partir de la solution de molybdate d'ammonium.
PCT/US2011/023852 2010-02-08 2011-02-07 Séparation de tungstène à partir de solutions de molybdate d'ammonium Ceased WO2011097547A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US13/577,678 US20130243673A1 (en) 2010-02-08 2011-02-07 Separation of tungsten from ammonium molybdate solutions

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US30237810P 2010-02-08 2010-02-08
US61/302,378 2010-02-08
US87538510A 2010-09-03 2010-09-03
US12/875,385 2010-09-03

Publications (1)

Publication Number Publication Date
WO2011097547A1 true WO2011097547A1 (fr) 2011-08-11

Family

ID=44355821

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2011/023852 Ceased WO2011097547A1 (fr) 2010-02-08 2011-02-07 Séparation de tungstène à partir de solutions de molybdate d'ammonium

Country Status (1)

Country Link
WO (1) WO2011097547A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106092814A (zh) * 2016-06-15 2016-11-09 赣州华兴钨制品有限公司 除钼渣中钼和钨的测定方法
CN113025818A (zh) * 2021-03-19 2021-06-25 中南大学 一种从钼酸盐溶液中催化沉淀分离回收钨的方法
CN114672670A (zh) * 2022-02-25 2022-06-28 信丰华锐钨钼新材料有限公司 一种高效沉淀低浓度钼酸钠溶液中Mo的方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1292559A (en) * 1917-04-30 1919-01-28 Carl Andersen Process of separating tungsten compounds from substances.
US4115513A (en) * 1977-08-16 1978-09-19 Westinghouse Electric Corp. Processing of ammonium paratungstate from tungsten ores
US4514368A (en) * 1982-09-24 1985-04-30 Chevron Research Company Leaching nickel, cobalt, molybdenum, tungsten, and vanadium from spent hydroprocessing catalysts
US4515756A (en) * 1980-12-09 1985-05-07 Occidental Research Corporation Process for extracting tungsten or molybdenum from solution
US4999169A (en) * 1988-10-26 1991-03-12 Gte Products Corporation Method for separating tungsten from molybednum

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1292559A (en) * 1917-04-30 1919-01-28 Carl Andersen Process of separating tungsten compounds from substances.
US4115513A (en) * 1977-08-16 1978-09-19 Westinghouse Electric Corp. Processing of ammonium paratungstate from tungsten ores
US4515756A (en) * 1980-12-09 1985-05-07 Occidental Research Corporation Process for extracting tungsten or molybdenum from solution
US4514368A (en) * 1982-09-24 1985-04-30 Chevron Research Company Leaching nickel, cobalt, molybdenum, tungsten, and vanadium from spent hydroprocessing catalysts
US4999169A (en) * 1988-10-26 1991-03-12 Gte Products Corporation Method for separating tungsten from molybednum

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106092814A (zh) * 2016-06-15 2016-11-09 赣州华兴钨制品有限公司 除钼渣中钼和钨的测定方法
CN113025818A (zh) * 2021-03-19 2021-06-25 中南大学 一种从钼酸盐溶液中催化沉淀分离回收钨的方法
CN114672670A (zh) * 2022-02-25 2022-06-28 信丰华锐钨钼新材料有限公司 一种高效沉淀低浓度钼酸钠溶液中Mo的方法
CN114672670B (zh) * 2022-02-25 2023-10-10 信丰华锐钨钼新材料有限公司 一种高效沉淀低浓度钼酸钠溶液中Mo的方法

Similar Documents

Publication Publication Date Title
US20130243673A1 (en) Separation of tungsten from ammonium molybdate solutions
Brown et al. Tungsten
Cardarelli Materials handbook: a concise desktop reference
Ayanda et al. A review of niobium-tantalum separation in hydrometallurgy
Ilhan et al. The investigation of dissolution behavior of gangue materials during the dissolution of scheelite concentrate in oxalic acid solution
US5441712A (en) Hydrometallurgical process for producing zinc oxide
Gaur et al. Recycling of rhenium-containing wire scrap
CA3055831C (fr) Procede de recuperation de vanadium
SE532674C2 (sv) Förfarande för klorering av malmer, slagger, glödspån, skrot, pulver och andra tillgångar som innehåller utvinnbara metaller
CN108910851A (zh) 一种由锂磷铝石制备含锂化合物的方法
WO2011097547A1 (fr) Séparation de tungstène à partir de solutions de molybdate d'ammonium
Ye et al. Recovery of rhenium from tungsten‑rhenium wire by alkali fusion in KOH-K2CO3 binary molten salt
Htwe et al. Study on extraction of niobium oxide from columbite–tantalite concentrate
Surimbayev et al. Acetic acid application as an activating reagent in the intensive cyanidation of gravity concentrates
WO2014158043A1 (fr) Procédé de régénération de rhénium à partir de déchets de superalliages contenant du nickel
Emil-Kaya et al. Comparison of production of mixed rare earth oxide (Nd/Pr oxide) powders by different precipitation agents from NdFeB magnets’ water leaching
Ye et al. Separation of cobalt and tungsten from grinding waste of cemented carbide by a mildly process of chloridizing roasting and water leaching combining
Dimitrijević et al. Recovery of tungsten trioxide from waste diamond core drilling crowns by nitric acid leaching
Khomoksonova et al. Improvement of oxidizing roasting of molybdenite concentrate by addition of magnesite
Churchward et al. Sources and recovery methods for rhenium
RU2437836C1 (ru) Способ извлечения и очистки рения из растворов от переработки жаропрочных сплавов
WO2020170223A1 (fr) Carbonitrure de titane
Yagmurlu SCALE: An Emerging Project for European Scandium Supply
Gouda et al. Review on Tungsten Recovery and Sustainable Practices
Zhang et al. Efficient Extraction and Separation of Rubidium from Rb-Bearing Granite Ore via Roasting Followed by Solvent Extraction

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11740476

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 13577678

Country of ref document: US

122 Ep: pct application non-entry in european phase

Ref document number: 11740476

Country of ref document: EP

Kind code of ref document: A1