WO2010119751A1 - Film de polyester bi-orienté pour une utilisation dans la stratification d'une résine durcissable - Google Patents

Film de polyester bi-orienté pour une utilisation dans la stratification d'une résine durcissable Download PDF

Info

Publication number
WO2010119751A1
WO2010119751A1 PCT/JP2010/054947 JP2010054947W WO2010119751A1 WO 2010119751 A1 WO2010119751 A1 WO 2010119751A1 JP 2010054947 W JP2010054947 W JP 2010054947W WO 2010119751 A1 WO2010119751 A1 WO 2010119751A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
curable resin
resin
polyester film
biaxially stretched
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2010/054947
Other languages
English (en)
Japanese (ja)
Inventor
通久 上野
純平 中尾上
浩一 村田
勝文 熊野
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toyobo Co Ltd
Original Assignee
Toyobo Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toyobo Co Ltd filed Critical Toyobo Co Ltd
Publication of WO2010119751A1 publication Critical patent/WO2010119751A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un film de polyester bi-orienté pour une utilisation dans la stratification d'une résine durcissable, le film comprenant une résine de téréphtalate de polyéthylène et satisfaisant les conditions (1) à (3) : (1) l'épaisseur du film est de 30 à 500 µm; (2) le degré d'orientation plane (?P) du film est de 0,150 à 0,180; et (3) le rapport du degré d'orientation des surfaces axiales entre la surface avant et la surface arrière du film est de 0,80 à 0,98. Lorsque l'épaisseur est inférieure ou égale à 500 µm, un gauchissement potentiel, qui neutralise le durcissement et le rétrécissement d'une résine durcissable se produit facilement, et lorsque l'épaisseur est supérieure ou égale à 30 µm, le film peut conserver sa planéité en tant que film de matériau de base. Lorsque le rapport du degré d'orientation des surfaces axiales entre la surface avant et la surface arrière du film est inférieur ou égal à 0,98, un gauchissement potentiel, qui peut neutraliser lorsqu'une résine durcissable est stratifiée, peut se produire, et lorsque le rapport est supérieur ou égal à 0,80, le film peut conserver sa planéité. Lorsque ?P est supérieur ou égal à 0,150, le film peut conserver sa planéité en tant que film qui peut résister au durcissement et au rétrécissement d'une résine durcissable, et lorsque ?P est inférieur ou égal à 0,180, un gauchissement potentiel, qui neutralise le durcissement et le rétrécissement d'une résine durcissable se produit facilement, et un stratifié peut avoir une précision de surface favorable.
PCT/JP2010/054947 2009-04-13 2010-03-23 Film de polyester bi-orienté pour une utilisation dans la stratification d'une résine durcissable Ceased WO2010119751A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2009-096970 2009-04-13
JP2009096970 2009-04-13
JP2009-096971 2009-04-13
JP2009096971 2009-04-13

Publications (1)

Publication Number Publication Date
WO2010119751A1 true WO2010119751A1 (fr) 2010-10-21

Family

ID=42982416

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2010/054947 Ceased WO2010119751A1 (fr) 2009-04-13 2010-03-23 Film de polyester bi-orienté pour une utilisation dans la stratification d'une résine durcissable

Country Status (2)

Country Link
TW (1) TWI393636B (fr)
WO (1) WO2010119751A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140162051A1 (en) * 2012-12-10 2014-06-12 Mitsubishi Polyester Film Gmbh White, weathering-resistant, biaxially oriented polyester film matt on at least one side, its use and process for its production
JP2015214046A (ja) * 2014-05-08 2015-12-03 帝人デュポンフィルム株式会社 金属板貼合せ成形加工用着色二軸延伸ポリエステルフィルム
US10287433B2 (en) * 2013-06-11 2019-05-14 Toyobo Co., Ltd. Heat-shrinkable polyester film and packages
CN115279607A (zh) * 2020-03-10 2022-11-01 锐思凌光学有限责任公司 安全玻璃用保护性屏障

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101960477B1 (ko) * 2016-09-20 2019-03-20 주식회사 엘지화학 슬립성 및 자외선 차단 기능이 우수한 광학 필름, 및 이를 포함하는 편광판

Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH01131550A (ja) * 1987-11-17 1989-05-24 Fuji Photo Film Co Ltd ポリエステルフィルムの製造方法
JPH0324936A (ja) * 1989-06-22 1991-02-01 Diafoil Co Ltd 二軸配向ポリエステルフィルム
JPH07266416A (ja) * 1994-04-01 1995-10-17 Toray Ind Inc 二軸配向ポリエステルフィルム及びその製造方法
JP2001138463A (ja) * 1999-11-16 2001-05-22 Toyobo Co Ltd 光学用易接着フィルム
JP2003154615A (ja) * 2001-11-21 2003-05-27 Konica Corp 機能性薄膜を有するポリエステルフィルム及び機能性薄膜の形成方法、機能性薄膜積層体、光学フィルム及び画像表示素子
WO2006118255A1 (fr) * 2005-04-28 2006-11-09 Toyo Boseki Kabushiki Kaisha Film de polyester thermoliable, procede de production de cartes a circuit integre ou d’etiquettes a circuit integre a l’aide de ce film, et cartes et etiquettes a circuit integre
JP2006342198A (ja) * 2005-06-07 2006-12-21 Teijin Dupont Films Japan Ltd 二軸配向ポリエステルフィルム
JP2007017667A (ja) * 2005-07-07 2007-01-25 Konica Minolta Holdings Inc 光学フィルムとそれを用いた画像表示素子
JP2007070430A (ja) * 2005-09-06 2007-03-22 Toray Ind Inc 太陽電池用ポリエステルフィルム
JP2008062460A (ja) * 2006-09-06 2008-03-21 Konica Minolta Holdings Inc 光学フィルムとそれを用いた画像表示素子
JP2008081571A (ja) * 2006-09-27 2008-04-10 Aica Kogyo Co Ltd ハードコート剤及びハードコートフィルム

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2007149600A (ja) * 2005-11-30 2007-06-14 Teijin Dupont Films Japan Ltd 色素増感型太陽電池用積層フィルムおよびそれを用いた色素増感型太陽電池用電極
JP2008221643A (ja) * 2007-03-13 2008-09-25 Nippon Zeon Co Ltd 樹脂型

Patent Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH01131550A (ja) * 1987-11-17 1989-05-24 Fuji Photo Film Co Ltd ポリエステルフィルムの製造方法
JPH0324936A (ja) * 1989-06-22 1991-02-01 Diafoil Co Ltd 二軸配向ポリエステルフィルム
JPH07266416A (ja) * 1994-04-01 1995-10-17 Toray Ind Inc 二軸配向ポリエステルフィルム及びその製造方法
JP2001138463A (ja) * 1999-11-16 2001-05-22 Toyobo Co Ltd 光学用易接着フィルム
JP2003154615A (ja) * 2001-11-21 2003-05-27 Konica Corp 機能性薄膜を有するポリエステルフィルム及び機能性薄膜の形成方法、機能性薄膜積層体、光学フィルム及び画像表示素子
WO2006118255A1 (fr) * 2005-04-28 2006-11-09 Toyo Boseki Kabushiki Kaisha Film de polyester thermoliable, procede de production de cartes a circuit integre ou d’etiquettes a circuit integre a l’aide de ce film, et cartes et etiquettes a circuit integre
JP2006342198A (ja) * 2005-06-07 2006-12-21 Teijin Dupont Films Japan Ltd 二軸配向ポリエステルフィルム
JP2007017667A (ja) * 2005-07-07 2007-01-25 Konica Minolta Holdings Inc 光学フィルムとそれを用いた画像表示素子
JP2007070430A (ja) * 2005-09-06 2007-03-22 Toray Ind Inc 太陽電池用ポリエステルフィルム
JP2008062460A (ja) * 2006-09-06 2008-03-21 Konica Minolta Holdings Inc 光学フィルムとそれを用いた画像表示素子
JP2008081571A (ja) * 2006-09-27 2008-04-10 Aica Kogyo Co Ltd ハードコート剤及びハードコートフィルム

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140162051A1 (en) * 2012-12-10 2014-06-12 Mitsubishi Polyester Film Gmbh White, weathering-resistant, biaxially oriented polyester film matt on at least one side, its use and process for its production
US10287433B2 (en) * 2013-06-11 2019-05-14 Toyobo Co., Ltd. Heat-shrinkable polyester film and packages
JP2015214046A (ja) * 2014-05-08 2015-12-03 帝人デュポンフィルム株式会社 金属板貼合せ成形加工用着色二軸延伸ポリエステルフィルム
CN115279607A (zh) * 2020-03-10 2022-11-01 锐思凌光学有限责任公司 安全玻璃用保护性屏障

Also Published As

Publication number Publication date
TW201041744A (en) 2010-12-01
TWI393636B (zh) 2013-04-21

Similar Documents

Publication Publication Date Title
JP5655380B2 (ja) 硬化性樹脂積層用二軸延伸ポリエステルフィルム
JP5009648B2 (ja) 反射防止フィルム用積層ポリエステルフィルム
JP5700953B2 (ja) 積層ポリエステルフィルム
JP2008209681A (ja) 反射防止フィルム用積層ポリエステルフィルム
WO2011135994A1 (fr) Film polyester stratifié
JP2008183882A (ja) 光学用積層フィルム及びその製造方法、反射防止フィルム並びに画像表示装置
JP6414380B2 (ja) 偏光子保護フィルム及びこれを用いた偏光板、液晶表示装置
JP6232702B2 (ja) 液晶表示装置、偏光板および偏光子保護フィルム
JP5387624B2 (ja) 硬化性樹脂積層体
WO2024014458A1 (fr) Film optique, film à action optique, film facilement adhésif, stratifié optique, plaque de surface, dispositif d'affichage d'image, et plaque polarisante
WO2010119751A1 (fr) Film de polyester bi-orienté pour une utilisation dans la stratification d'une résine durcissable
JP2010247370A (ja) 硬化性樹脂積層用光拡散ポリエステルフィルム
JP5640417B2 (ja) 硬化性樹脂積層用二軸延伸ポリエステルフィルム
KR20120106585A (ko) 편광자 보호 필름
JP5460481B2 (ja) 積層ポリエステルフィルム
JP5031883B2 (ja) 積層ポリエステルフィルム
KR20120106590A (ko) 편광자 보호 필름
JP5014616B2 (ja) 光学用積層ポリエステルフィルム
JP2019059069A (ja) 積層フィルム
JP2022113634A (ja) フレキシブルディスプレイ用ポリエステルフィルム、フレキシブルディスプレイ用積層フィルム、フレキシブルディスプレイ及びフレキシブルディスプレイ装置
JP2010253741A (ja) 積層ポリエステルフィルム
JP4758738B2 (ja) 光学用積層ポリエステルフィルム
JP2006281731A (ja) 積層フィルム
JP2007045024A (ja) 積層ポリエステルフィルム
JP2007047517A (ja) 反射防止フィルム用ポリエステルフィルムおよび反射防止フィルム

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10764336

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 10764336

Country of ref document: EP

Kind code of ref document: A1