[go: up one dir, main page]

WO2010110762A1 - Mixture for the manufacture of a transmitter and attenuator of the blast impulse of an explosion in a blast hole and a method for manufacturing a suspension - Google Patents

Mixture for the manufacture of a transmitter and attenuator of the blast impulse of an explosion in a blast hole and a method for manufacturing a suspension Download PDF

Info

Publication number
WO2010110762A1
WO2010110762A1 PCT/UA2009/000059 UA2009000059W WO2010110762A1 WO 2010110762 A1 WO2010110762 A1 WO 2010110762A1 UA 2009000059 W UA2009000059 W UA 2009000059W WO 2010110762 A1 WO2010110762 A1 WO 2010110762A1
Authority
WO
WIPO (PCT)
Prior art keywords
water
weight
mixture
suspension
microspheres
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/UA2009/000059
Other languages
French (fr)
Russian (ru)
Other versions
WO2010110762A8 (en
Inventor
Ирина Анатольевна ЛАЗАРЕВA
Татьяна Анатольевна КУРАТЁВА
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from UAA200902580A external-priority patent/UA92260C2/en
Priority claimed from UAU200903893U external-priority patent/UA43408U/en
Application filed by Individual filed Critical Individual
Publication of WO2010110762A1 publication Critical patent/WO2010110762A1/en
Publication of WO2010110762A8 publication Critical patent/WO2010110762A8/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

The invention relates to the mining of large-block stone from rocks in open pits using drilling and blasting operations. A mixture is claimed for the manufacture of a transmitter and attenuator of the blast impulse of an explosion in a blast hole, which transmitter and attenuator is in the form of a nonexplosive substance and can be placed between fuses with an explosive substance having a high detonation rate and the walls of blast holes bored along the edges of a block of rock, said mixture comprising a water-soluble thickening agent in the form of cellulose ether powder in an amount of 40-75% by mass, and hollow hermetic microspheres in an amount of 25-60% by mass. During active agitation, the dry mixture is diluted with water, in a ratio of 1 part per mass of dry mixture to 20-60 parts by mass of water, resulting in the stated relative viscosity.

Description

Смесь для изготовления передатчика и ослабителя детонационного импульса взрыва в шпуре и способ изготовления суспензии Mixture for the manufacture of a transmitter and attenuator for a detonation pulse of an explosion in a hole and a method for manufacturing a suspension

Изобретения относятся к добыче крупноблочного камня из горных пород в карьерах с использованием буровзрывных работ. Известен линейный заряд с пониженным боковым воздействием по заявке на изобретение, которая опубликована в Российской Федерации за JN22002128876 в официальном бюллетене 27.04.2004г., индекс МПК F42BЗ/087. По известному изобретению линейный заряд с пониженным боковым воздействием, состоит из сердцевины из взрывчатого вещества, покрытой оболочкой, причем, оболочка выполнена из материала, ослабляющего детонационный импульс, например, из вспененного полиэтилена.The invention relates to the extraction of large-block stone from rocks in quarries using drilling and blasting. Known linear charge with reduced lateral impact on the application for an invention, which is published in the Russian Federation for JN22002128876 in the official bulletin 04/27/2004, MPC index F42BЗ / 087. According to the known invention, a linear charge with reduced lateral impact consists of a core of explosive coated with a shell, and the shell is made of a material that attenuates the detonation pulse, for example, of foamed polyethylene.

В качестве указанной системы служит стандартный детонирующий шнур с высокой скоростью детонации, который заключен в ослабляющую оболочку, изменяющую детонационный импульс детонирующего шнура. В другом варианте линейный заряд со сниженным боковым влиянием, состоит из взрывчатого вещества, помещенного в оболочку, в которой заряд сформирован из двух и более параллельно расположенных стандартных детонирующих шнуров, заключенных в общую ослабляющую оболочку, изменяющую детонационный импульс. В другом варианте линейный заряд со сниженным боковым влиянием, состоит из взрывчатого вещества, помещенного в оболочку, причем, под дополнительной ослабляющей оболочкой вдоль образующей заряд снабжен направляющей нитью, обеспечивающей вскрытие оболочки. Общими существенными признаками является то, что в качестве передатчика и ослабителя детонационного импульса взрыва в шпуре используют невзрывчатое вещество, расположенное между взрывчатым веществом и стенками шпура .As the specified system, a standard detonating cord with a high detonation velocity is used, which is enclosed in a weakening shell that changes the detonation pulse of the detonating cord. In another embodiment, the linear charge with reduced lateral effect consists of an explosive placed in a shell in which the charge is formed of two or more parallel detonating cords encased in a common attenuating shell that changes the detonation momentum. In another embodiment, the linear charge with reduced lateral effect consists of an explosive substance placed in the shell, and, under the additional attenuating shell along the charge generating section, it is provided with a guiding thread to open the shell. Common essential features is that an explosive substance located between the explosive and the walls of the hole is used as a transmitter and attenuator of the detonation pulse of the explosion in the hole.

Недостатками известного линейного заряда является то, что оболочка изготовляется заранее, поэтому не возможно учесть реальный размер шпура, и отклонение сечения шпура на разных участках длины шпура и потому не обеспечивается плотность прилегания к стенкам шпура, не обеспечивается необходимая равномерность нагрузки при взрывах, отсутствует возможность регулирования передаточной силы и, соответственно, качественное без повреждений отбивание и раскалывание блоков камня горной породы разных категорий прочности по линии ряда шпуров.The disadvantages of the known linear charge is that the shell is made in advance, so it is not possible to take into account the actual size of the hole, and the deviation of the cross-section of the hole in different sections of the length of the hole, and therefore, the adherence to the walls of the hole is not ensured, the required load uniformity during explosions is not provided, there is no regulation transmission power and, accordingly, high-quality, without damage, beating and splitting of rock blocks of different strength categories along a line of a number of holes.

Наиболее близкими являются, описанные в патенте на изобретение N°85774, который выдан в Украине 25.02.2009 г. по заявке на изобретение N° a200707708, поданной 09.07.07, индекс МПК E21C41/26; F42D1/24; F42DЗ/00; F42BЗ/22; F42BЗ/24 смесь и способ изготовления передатчика и ослабителя детонационного импульса взрыва в шпуре и способ добычи блочного камня.The closest are those described in the patent for the invention N ° 85774, which was issued in Ukraine on February 25, 2009 according to the application for the invention N ° a200707708, filed July 9, 2007, IPC index E21C41 / 26; F42D1 / 24; F42DЗ / 00; F42BZ / 22; F42BЗ / 24 mixture and method for manufacturing a transmitter and a detonation detonation damper in a hole and a method for producing block stone.

Согласно прототипу, смесь для изготовления передатчика и ослабителя детонационного импульса взрыва в шпуре, в качестве которого используют невзрывчатое вещество, расположенное между взрывчатым веществом с высокой скоростью детонации и стенками шпура, содержащая водорастворимый загуститель в количестве от 20% до 29% по массе, и стеклянные полые микросферы диаметром от 5 мкм до 100 мкм в количестве от 80% до 71% по массе. В качестве водорастворимого загустителя используют метиловый эфир целлюлозы, или в качестве водорастворимого загустителя используют гидроксиэтилцеллюлозу, или в качестве водорастворимого загустителя используют кросс- сополимер акриловой кислоты. Способ изготовления передатчика и ослабителя детонационного импульса взрыва в шпуре, в котором используют, как передатчик и ослабитель детонационного импульса взрыва для закладки в шпур, невзрывчатое вещество с повышенной вязкостью, разведенное водой. При активном перемешивании разводят сухую смесь, которая содержит водорастворимый загуститель в количестве от 20% до 29% по массе, и стеклянные полые микросферы диаметром от 5 до 100 мкм в количестве от 80% до 71% по массе, в соотношении 1 часть сухой смеси к 35-55 частям воды по массе, выполняют замеры водородного показателя и условной вязкости разбавленной смеси, добавляют компонент корректирующий водородный показатель, доводят водородный показатель до pH6-pH8 и, совместно с разведением водой, достигают заданной условной вязкости.According to the prototype, the mixture for the manufacture of the transmitter and attenuator of the detonation pulse of the explosion in the hole, which is used as an non-explosive substance located between the explosive with a high detonation velocity and the walls of the hole containing water-soluble thickener in an amount of from 20% to 29% by weight, and glass hollow microspheres with a diameter of 5 μm to 100 μm in an amount of 80% to 71% by weight. Cellulose methyl ester is used as the water-soluble thickener, or hydroxyethyl cellulose is used as the water-soluble thickener, or a cross-copolymer of acrylic acid is used as the water-soluble thickener. A method of manufacturing a transmitter and attenuator of a detonation pulse of an explosion in a borehole, in which a non-explosive substance with high viscosity diluted with water is used as a transmitter and attenuator of a detonation pulse of an explosion for laying in a hole. With vigorous stirring, a dry mixture is diluted, which contains a water-soluble thickener in an amount of from 20% to 29% by weight, and glass hollow microspheres with a diameter of 5 to 100 μm in an amount of from 80% to 71% by weight, in the ratio of 1 part of the dry mixture to 35-55 parts by weight of water, measure the hydrogen index and the nominal viscosity of the diluted mixture, add the correcting hydrogen index component, adjust the pH to pH6-pH8 and, together with the dilution with water, achieve the specified nominal viscosity.

Причем сначала, разводят смесь в соотношении 1 часть сухой смеси к 20 частям воды по массе, в качестве щелочного компонента, корректирующего водородный показатель, используют аммиачную воду, добавляют аммиачную воду, выполняют замеры условной вязкости вискозиметром с вместимостью резервуара, 100 мл, с соплом диаметром б мм с высотой сопла 4 мм, добавляют воду в пределах соотношения 1 часть сухой смеси к 55 частям воды по массе, достигают условной вязкости в пределах от 8 до 20 секунд, в зависимости от прочности горной породы. Перемешивание выполняют на протяжении 5 -10 минут. Используют воду с водородным показателем от рН 6,0 до рН 9,0 или используют воду из местных источников, для чего проверяют ее водородный показатель и доводят водородный показатель до рН 4-pH7 перед разведением сухой смеси. Для снижения водородного показателя используют уксус. В разбавленную смесь дополнительно добавляют антифриз. В качестве антифризной добавки используют моноэтиленгликоль или диэтиленгликоль, в количестве от 0,42% до 7,56% по массе от общей массы, разведенной смеси.Moreover, at first, the mixture is diluted in the ratio of 1 part of the dry mixture to 20 parts by weight of water, ammonia water is used as the alkaline component that corrects the hydrogen index, ammonia water is added, conditional viscosity is measured with a viscometer with a tank capacity of 100 ml, with a nozzle diameter b mm with a nozzle height of 4 mm, add water within the ratio of 1 part of the dry mixture to 55 parts by weight of water, achieve a conditional viscosity in the range of 8 to 20 seconds, depending on the strength of the rock. Mixing is performed for 5-10 minutes. Use water with a pH value from pH 6.0 to pH 9.0 or use water from local sources, for which its pH value is checked and the pH value is adjusted to pH 4-pH7 before the dry mixture is diluted. Vinegar is used to lower the pH. Antifreeze is additionally added to the diluted mixture. Monoethylene glycol or diethylene glycol is used as an antifreeze additive in an amount of from 0.42% to 7.56% by weight of the total weight of the diluted mixture.

Способ добычи блочного камня, включающий бурение шпуров в горной породе по границам блока с постоянным шагом, подготовку зарядов, установку зарядов в шпуры и детонирующих шнуров, соединение средств инициирования с оборудованием для привода в действие зарядов, заполнение шпура смесью, которая не содержит взрывчатого материала, снаряжение средством инициирования общей сети, проведение взрыва, причем, шпур заполняют разведенной водой смесью, которая содержит водорастворимый загуститель в количестве от 20% до 29% по сухой массе, и стеклянные полые микросферы диаметром от 5 мкм до 100 мкм в количестве от 80% до 71% по сухой массе.A method for producing block stone, including drilling boreholes in rock along the block boundaries with a constant step, preparing charges, installing charges in boreholes and detonating cords, connecting initiation means with equipment for driving charges, filling the borehole with a mixture that does not contain explosive material, equipment by means of initiating a common network, carrying out an explosion, moreover, the hole is filled with diluted water with a mixture, which contains a water-soluble thickener in an amount of from 20% to 29% by dry weight, and glass hollow microspheres with a diameter of from 5 μm to 100 μm in an amount of from 80% to 71% by dry weight.

Диаметр шпуров в 5-10 раз превышает поперечное сечение детонирующих шнуров.The diameter of the holes is 5-10 times larger than the cross section of detonating cords.

Шпуры диаметром от 25 до 40 мм высверливают по границам блока в горный породе с шагом 150-250 мм , а недобур шпуров по глубине составляет 80-150 мм относительно границ габаритов блока. Одновременно с бурением шпуров, одну грань блока горной породы отделяют от массива горной породы гидроразмывом или отпиливанием.Bore holes with a diameter of 25 to 40 mm are drilled along the block boundaries in the rock with a pitch of 150-250 mm, and the hole depth in the hole is 80-150 mm relative to the boundaries of the block dimensions. Simultaneously with drilling holes, one face of the rock block is separated from the rock mass by hydraulic washing or sawing.

Общими существенными признаками, является то, что смесь для изготовления передатчика и ослабителя детонационного импульса взрыва в шпуре, в качестве которого используют невзрывчатое вещество, с возможностью расположения между шнуров со взрывчатым веществом с высокой скоростью детонации и стенками, высверленных по границам блока горной породы шпуров, которая содержит водорастворимый загуститель и полые микросферы.Common essential features is that the mixture for the manufacture of a transmitter and a detonation detonator of a blast hole in a borehole, using an non-explosive substance, can be placed between cords with an explosive substance with a high detonation velocity and walls drilled along the boundaries of the rock block of the boreholes, which contains a water-soluble thickener and hollow microspheres.

Недостатками известной смеси является высокая чувствительность к качеству воды, особенно кислотности, так как необходимо обеспечивать водородный показатель от рНб до pH7 для качественного разбухания загустителя, создания необходимой вязкости и равномерного распределения микросфер, а так как при разведении кислотность повышается, то необходимо повторно делать анализы и приводить водородный показатель к норме.The disadvantages of the known mixture are its high sensitivity to water quality, especially acidity, since it is necessary to provide a pH value from pHb to pH7 for a qualitative swelling of the thickener, to create the necessary viscosity and uniform distribution of microspheres, and since dilution increases the acidity, it is necessary to re-analyze and bring the hydrogen index to normal.

Целью изобретения является создание смеси продолжительного хранения, из которой изготавливается разведением водой без ограничений ее водородного показателя и жесткости, суспензия, невзрывчатый передатчик и ослабитель детонационного импульса взрыва, с возможностью регулирования передаточной силы, и обеспечения равномерной ослабленной энергии импульса взрыва детонационного шнура в шпуре, для обеспечения качественного, без повреждений, откалывания блоков камня горной породы разных категорий прочности и состояния от массива.The aim of the invention is the creation of a mixture of long-term storage, from which a suspension, non-explosive transmitter and attenuator of the detonation pulse of the explosion is made by diluting with water without restrictions on its hydrogen index and stiffness, with the possibility of regulating the transmission force, and providing a uniform attenuated energy of the explosion pulse of the detonation cord in the hole, for ensuring high-quality, without damage, chipping blocks of rock stone of different categories of strength and condition from the massif.

Согласно изобретению смесь для изготовления передатчика и ослабителя детонационного импульса взрыва в шпуре в качестве которого используют невзрывчатое вещество, с возможностью расположения между шнуров со взрывчатым веществом с высокой скоростью детонации и стенками, высверленных по границам блока горной породы шпуров, содержит в качестве водорастворимого загустителя порошок эфира целлюлозы в количестве от 40% до 75% по массе, и полые герметичные микросферы в количестве от 25% до 60% по массе.According to the invention, a mixture for the manufacture of a transmitter and attenuator of a detonation pulse of an explosion in a borehole as non-explosive substance, with the possibility of placing between cords with an explosive substance with a high detonation velocity and walls drilled along the boundaries of the rock block of the holes, contains cellulose ether powder in an amount of 40% to 75% by weight as a water-soluble thickener, and hollow sealed microspheres in amount from 25% to 60% by weight.

Причем используют полые герметичные микросферы из стекла, которые имеют диаметр от 10 до 100 мкм, с удельным насыпным весом от 0,05 г/см 3 до 0,16г/cм3, или полые герметичные микросферы из керамики , которые имеют диаметр от 50 до 150 мкм, с удельным насыпным весом от ОД г/см3 до 0,3 г/см3, или полые герметичные микросферы из фенолформальдегида, которые имеют диаметр от 50 до 150 мкм, с удельным насыпным весом от 0,1 г/см до 0,3 г/см . В качестве водорастворимого загустителя используют порошок гидроксиэтилцеллюлозы с размером частиц от 0,08 до 0,25 мм с удельным насыпным весом от 0,35 г/см 3 до 0,45г/cм 3 , или порошок метилгидроксиэтилцеллюлозы с размером частиц от 0,08 до 0,28 мм с удельным насыпным весом от 0,2 г/см 3 до 0,5 г/см 3, или порошок карбоксиметилцеллюлозы с размером частиц от 0,10 до 0,28 мм с удельным насыпным весом от 0,4 г/см 3 до 0,8г/cм 3 . Указанная сухая смесь герметично расфасована в полиэтиленовых пакетах или кадках, для длительного хранения и быстро, в необходимом количестве, может разводиться водой, до консистенции при которой через него обеспечивается передача импульса взрыва детонационного шнура необходимой силы на стенки шпура. Отличительными существенными признаками является то, что смесь для изготовления передатчика и ослабителя детонационного импульса взрыва в шпуре содержит в качестве водорастворимого загустителя порошок эфира целлюлозы в количестве от 40% до 75% по массе, и полые герметичные микросферы в количестве от 25% до 60% по массе. Используют полые герметичные микросферы из стекла, которые имеют диаметр от 10 до 100 мкм, с удельным насыпным весом от 0,05 г/см 3 до 0,16 г/см3 или используют полью герметичные микросферы из керамики, которые имеют диаметр от 50 до 150 мкм, с удельным насыпным весом от 0,1 г/см3 до 0,3 г/см3, или используют полые герметичные микросферы из фенолформальдегида, которые имеют диаметр от 50 до 150 мкм, с удельным насыпным весом от 0,1 г/см3 до 0,3 г/см3 . В качестве водорастворимого загустителя используют порошок гидроксиэтилцеллюлозы с размером частиц от 0,08 до 0,25 мм с удельным насыпным весом от 0,35 г/см до 0,45 г/см3, или в качестве водорастворимого загустителя используют порошок метилгидроксиэтилцеллюлозы с размером частиц от 0,08 до 0,28 мм с удельным насыпным весом от 0,2 г/см 3 до 0,5 г/см , или в качестве водорастворимого загустителя используют порошок карбоксиметилцеллюлозы с размером частиц от 0, 10 до 0,28 мм с удельным насыпным весом от 0,4 г/см3 до 0,8 г/см3 .Moreover, hollow sealed glass microspheres are used, which have a diameter of 10 to 100 μm, with a specific bulk density of 0.05 g / cm 3 to 0.16 g / cm 3 , or hollow sealed ceramic microspheres, which have a diameter of 50 to 150 microns, with a specific bulk density of OD g / cm 3 to 0.3 g / cm 3 , or hollow sealed phenol-formaldehyde microspheres that have a diameter of 50 to 150 microns, with a specific bulk density of 0.1 g / cm to 0.3 g / cm. As a water-soluble thickener, hydroxyethyl cellulose powder with a particle size of from 0.08 to 0.25 mm with a specific bulk density of from 0.35 g / cm 3 to 0.45 g / cm 3 , or methyl hydroxyethyl cellulose powder with a particle size of from 0.08 to 0.28 mm with a specific bulk density of from 0.2 g / cm 3 to 0.5 g / cm 3 , or carboxymethyl cellulose powder with a particle size of 0.10 to 0.28 mm with a specific bulk density of 0.4 g / cm 3 to 0.8g / cm 3 . The specified dry mixture is hermetically packaged in plastic bags or tubs, for long-term storage and quickly, in the required amount, can be diluted with water, to the consistency of which the impulse of the detonation cord of the necessary force is transmitted through it to the borehole walls. Distinctive essential features is that the mixture for the manufacture of a transmitter and a detonation detonation pulse attenuator in a hole contains, as a water-soluble thickener, cellulose ether powder in an amount of 40% to 75% by weight, and hollow sealed microspheres in an amount of 25% to 60% by weight mass. Use hollow sealed glass microspheres, which have a diameter of 10 to 100 μm, with a specific bulk density of 0.05 g / cm 3 to 0.16 g / cm 3, or use poly sealed ceramic microspheres, which have a diameter of 50 to 150 microns, with a specific bulk density of from 0.1 g / cm 3 to 0.3 g / cm 3 , or use hollow sealed phenol-formaldehyde microspheres, which have a diameter of from 50 to 150 microns, with a specific bulk density of from 0.1 g / cm 3 to 0.3 g / cm 3 . As a water-soluble thickener, a hydroxyethyl cellulose powder with a particle size of from 0.08 to 0.25 mm with a specific bulk density of 0.35 g / cm to 0.45 g / cm 3 is used , or a methyl hydroxyethyl cellulose powder with a particle size is used as a water-soluble thickener. from 0.08 to 0.28 mm with a specific bulk density of from 0.2 g / cm 3 to 0.5 g / cm, or carboxymethyl cellulose powder with a particle size of from 0, 10 to 0.28 mm s is used as a water-soluble thickener specific gravity from 0.4 g / cm 3 to 0.8 g / cm 3 .

Существенными признаками достаточными для всех случаев является то, что смесь содержит в качестве водорастворимого загустителя порошок эфира целлюлозы в количестве от 40% до 75% по массе, и полые герметичные микросферы в количестве от 25% до 60% по массе.The essential features sufficient for all cases are that the mixture contains, as a water-soluble thickener, cellulose ether powder in an amount of 40% to 75% by weight, and hollow sealed microspheres in an amount of 25% to 60% by weight.

Существенными признаками достаточными в отдельных случаях является то, что используют полые герметичные микросферы из стекла, которые имеют диаметр от 10 до 100 мкм, с удельным насыпным весом от 0,05 г/см 3 до 0,16 г/см или используют полые герметичные микросферы из керамики, которые имеют диаметр от 50 до 150 мкм, с удельным насыпным весом от 0,1 г/см3 до 0,3 г/см3, или используют полые герметичные микросферы из фенолформальдегида, которые имеют диаметр от 50 до 150 мкм, с удельным насыпным весом от 0,1 г/см3 до 0,3 г/см3 . В качестве водорастворимого загустителя используют порошок гидроксиэтилцеллюлозы с размером частиц от 0,08 до 0,25 мм с удельным насыпным весом от 0,35 г/см3 до 0,45 г/см3, или в качестве водорастворимого загустителя используют порошок метилгидроксиэтилцеллюлозы с размером частиц от 0,08 до 0,28 мм с удельным насыпным весом от 0,2 г/см 3 до 0,5 г/см 3, или в качестве водорастворимого загустителя используют порошок карбоксиметилцеллюлозы с размером частиц от 0, 10 до 0,28 мм с удельным насыпным весом от 0,4 г/см3 до 0,8 г/см3 . Изготовленная согласно изобретению смесь расфасована по весу, герметично упакована и в упакованном виде имеет неограниченный срок хранения и позволяет, при разведении водой до заданной вязкости, получить передатчик и регулируемый ослабитель детонационного импульса взрыва в шпуре, который имеет консистенцию, позволяющую заполнить шпур, в котором заложен детонационный шнур, но не заходит в небольшие трещины, передает и равномерно распределяет уменьшенную нагрузку на стенки шпура от взрыва детонационного шнура и обеспечивает качественный раскол по ряду шпуров без внутренних повреждений стенок отколотого блока из горной породы. Для изготовления 1 кг смеси по изобретению берут 0,5 кг порошка гидроксиэтилцеллюлозы производства CE ТИЛОЗ ГМБХ и Ко. КГ (SE Туlоsе GmbН & Со. KG), Германия с размером частиц от 0,1 мм до 0,14 мм, с удельным насыпным весом 0,39 г/см 3 , и стеклянные полые герметичные микросферы диаметром от 30 до 40 мкм с удельным насыпным весом 0,1 г/см 3, которые изготавливаются компанией ЗМ, США в количества 0,5 кг. Указанная сухая смесь сохраняется в герметично запаянном полиэтиленовом пакете, большие объемы смеси хранят в бочках. Длительное хранение обеспечивается отсутствием веществ, которые в сухом виде разрушаются, а при необходимости, смесь быстро разводится водой, что и описано дальше в способе изготовления суспензии. Известен состав донно-устьевой забойки по заявке N°96103232, которая была подана в Российской Федерации 27.02.1996г. и опубликована в официальном бюллетене, индексы МПК E21C37/00, F42D1/24.The essential features sufficient in some cases is that hollow sealed glass microspheres are used, which have a diameter of 10 to 100 μm, with a specific bulk density of 0.05 g / cm 3 to 0.16 g / cm, or use hollow sealed microspheres ceramic, which have a diameter of from 50 to 150 μm, with a specific bulk density of from 0.1 g / cm 3 to 0.3 g / cm 3 , or use hollow sealed phenol-formaldehyde microspheres that have a diameter of from 50 to 150 μm, with a specific bulk density of from 0.1 g / cm 3 to 0.3 g / cm 3 . As a water-soluble thickener, a hydroxyethyl cellulose powder with a particle size of from 0.08 to 0.25 mm with a specific bulk density of from 0.35 g / cm 3 to 0.45 g / cm 3 is used , or a methyl hydroxyethyl cellulose powder with a size of particles from 0.08 to 0.28 mm with a specific bulk density of from 0.2 g / cm 3 to 0.5 g / cm 3 , or carboxymethyl cellulose powder with a particle size of from 0, 10 to 0.28 is used as a water-soluble thickener mm with a specific bulk density of from 0.4 g / cm 3 to 0.8 g / cm 3 . The mixture made according to the invention is packaged by weight, hermetically packed and packed it has an unlimited shelf life and allows, when diluted with water to a predetermined viscosity, to obtain a transmitter and an adjustable attenuator of the detonation pulse of the explosion in the hole, which has a consistency that allows filling the hole in which the detonation cord is laid, but does not enter into small cracks , transfers and evenly distributes the reduced load on the borehole walls from the detonation cord explosion and provides a high-quality split along a number of boreholes without internal damage to the walls of the chipped block ka from the rock. To produce 1 kg of the mixture according to the invention, 0.5 kg of hydroxyethyl cellulose powder produced by CE TILOSE GMBH and Co. is taken. KG (SE Tulose GmbН & Co. KG), Germany with a particle size of from 0.1 mm to 0.14 mm, with a specific bulk density of 0.39 g / cm 3 , and glass hollow sealed microspheres with a diameter of 30 to 40 μm s specific gravity of 0.1 g / cm 3 that are manufactured by the company ZM, USA in the amount of 0.5 kg The specified dry mixture is stored in a hermetically sealed plastic bag, large volumes of the mixture are stored in barrels. Long-term storage is ensured by the absence of substances that are destroyed in a dry form, and if necessary, the mixture is quickly diluted with water, which is described further in the method of manufacturing a suspension. The known composition of the bottom-mouth sting according to the application N ° 96103232, which was filed in the Russian Federation 02/27/1996 and published in the official bulletin, IPC indices E21C37 / 00, F42D1 / 24.

Состав донно-устьевой забойки, содержащей воду, растворимые в воде пламегасители хлориды металлов и структурообразователи, повышающие вязкость системы, которая! представляет собой эмульсию типа "вода в масле" при следующем компонентном составе (мac.)%: пламегасители 10-20 нефтепродукты с температурой кипения не ниже 230° С, эмульгаторы и их смеси, образующие обратные эмульсии, 1,5 -2,5 эфиры жирных кислот и многоатомных спиртов и остальное вода. Общими существенными признаками является изготовление передатчика и ослабителя детонационного импульса взрыва в шпуре в качестве которого изготавливают для закладки в шпур невзрывчатое вещество с повышенной вязкостью разбавленное водой.The composition of the bottom-mouth stump containing water, water-soluble metal chloride flame retardants and structure-forming agents that increase the viscosity of the system, which! represents an emulsion of the type "water in oil" with the following component composition (wt.)%: flame arresters 10-20 oil products with a boiling point of at least 230 ° C, emulsifiers and their mixtures forming inverse emulsions, 1.5-2.5 ethers fatty acids and polyols and the rest is water. Common essential features are the manufacture of a transmitter and attenuator for the detonation pulse of an explosion in a hole, in which an explosive substance with increased viscosity diluted with water.

Недостатками донно-устьевой забойки является то, что она непригодна для добычи качественных блоков, так как такая эмульсия все равно имеет консистенцию и структуру, которая позволяет воде просачиваться в щели и поры горной породы, вдобавок , такая смесь не передает равномерно и не ослабляет детонационный импульс и может использоваться только для забойки. Прототипом является описанный выше способ изготовления передатчика и ослабителя детонационного импульса взрыва в шпуре по патенту Украины N°85774 выданному по заявке JVa а 200707708. Недостатками прототипа является высокая чувствительность к качеству воды, особенно водородному показателю, так как необходимо обеспечивать доливанием аммиачной воды или уксуса водородный показатель в пределах от pH6 до pH7, для качественного разбухания загустителя и создания необходимой вязкости, а так как при разведении кислотность повышается, то необходимо повторно делать анализы и приводить водородный показатель к норме. При превышении нормы аммиачной воды или уксуса возможная коагуляция загустителя и невозможность использования по назначению.The disadvantages of bottom-mouth stagnation is that it is unsuitable for producing high-quality blocks, since such an emulsion still has a consistency and structure that allows water to seep into the cracks and pores of the rock, in addition, this mixture does not transmit evenly and does not weaken the detonation impulse and can only be used for jamming. The prototype is the above-described method of manufacturing the transmitter and attenuator of the detonation pulse of a blast hole in the hole according to Ukrainian patent N ° 85774 issued according to the application JVa a 200707708. The disadvantages of the prototype are high sensitivity to water quality, especially hydrogen, since it is necessary to add hydrogen ammonia or vinegar topping an indicator in the range from pH6 to pH7, for a qualitative swelling of the thickener and the creation of the necessary viscosity, and since dilution increases the acidity, it is necessary to repeat but do tests and bring the pH value to normal. If the norm of ammonia water or vinegar is exceeded, possible coagulation of the thickener and inability to use for its intended purpose.

Целью изобретения является способ создания суспензии, которая обеспечивает передачу и ослабление детонационного импульса взрыва в шпуре от взрывчатого вещества с высокой скоростью детонации, с возможностью регулирования передаточной силы, для обеспечения качественной, без повреждений, добычи и раскалывания блоков горной породы разных категорий прочности и состояния, которая нечувствительна к водородному показателю и жесткости воды, и не нуждается в доливаниях веществ, которые изменяют водородный показатель или жесткость и проведении анализов показателей воды и суспензии.The aim of the invention is a method for creating a suspension, which ensures the transmission and attenuation of the detonation impulse of an explosion in a borehole from an explosive with a high detonation speed, with the ability to control the transmission force, to ensure high-quality, without damage, mining and splitting rock blocks of different strength and condition categories, which is insensitive to the hydrogen index and water hardness, and does not need topping up substances that change the hydrogen index or hardness and carried out and analyzes characteristics of water and slurry.

Способ изготовления суспензии, невзрывчатого вещества с повышенной вязкостью разведенного водой, для закладки в ряд высверленных по границам блока горной породы шпуров и заряженных шнурами со взрывчатым веществом с высокой скоростью детонации, в котором, при активном перемешивании, разводят водой сухую смесь, которая содержит порошок водорастворимого эфира целлюлозы в количестве от 40% до 75% по массе, и полые герметичные микросферы в количестве от 25% до 60% по массе, в соотношении 1 часть по массе сухой смеси к 20- 60 частям по массе воды, достигают заданной условной вязкости.A method of manufacturing a suspension, non-explosive with a high viscosity diluted with water, for laying in a series of holes drilled along the boundaries of the rock block and charged with cords with an explosive with a high detonation velocity, in which, with vigorous stirring, a dry mixture is diluted with water, which contains water-soluble powder cellulose ether in an amount of 40% to 75% by weight, and hollow sealed microspheres in an amount of 25% to 60% by weight, in a ratio of 1 part by the mass of the dry mixture to 20-60 parts by weight of water, reach the specified conditional viscosity.

Условную вязкость выбирают, в зависимости от состояния и прочности горной породы, в пределах от 7,0 до 20, 0 секунд по стандартной кружке ВМС, которая представляет собой цилиндрическую емкость с высотой 80 мм, с внутренним диаметром 69,8 мм, с соплом диаметром 9,5 мм в дне, с отверстиями в стенке диаметром по 4,2 мм расположенными на высоте 25,4 мм и 57,1 мм от дна, изменение уровня суспензии между которыми оценивают в секундах.The conditional viscosity is selected, depending on the condition and strength of the rock, in the range from 7.0 to 20, 0 seconds according to the standard Navy circle, which is a cylindrical container with a height of 80 mm, with an inner diameter of 69.8 mm, with a nozzle diameter 9.5 mm in the bottom, with holes in the wall with a diameter of 4.2 mm located at a height of 25.4 mm and 57.1 mm from the bottom, the change in the level of suspension between which is estimated in seconds.

В морозную погоду в суспензию дополнительно добавляют антифриз, в качестве антифризной добавки используют моноэтиленгликоль или диэтиленгликоль, в количестве от 0,42% до 7,56% по массе от общей массы суспензии.In frosty weather, antifreeze is additionally added to the suspension, monoethylene glycol or diethylene glycol is used as an antifreeze additive, in an amount of from 0.42% to 7.56% by weight of the total weight of the suspension.

Отличительными существенными признаками достаточными во всех случаях является то, что для изготовления суспензии, при активном перемешивании разводят водой сухую смесь, которая содержит порошок водорастворимого эфира целлюлозы в количестве от 40% до 75% по массе, и полые герметичные микросферы в количестве от 25% до 60% по массе, в соотношении 1 часть по массе сухой смеси к 20- 60 частям по массе воды, достигают заданной условной вязкости. Отличительными существенными признаками достаточными в отдельных случаях является то, что условную вязкость выбирают, в зависимости от состояния и прочности горной породы, в пределах от 7,0 до 20,0 секунд по стандартной кружке ВМС, которая представляет собой цилиндрическую емкость с высотой 80 мм, с внутренним диаметром 69,8 мм, с соплом диаметром 9,5 мм в дне, с отверстиями в стенке диаметром по 4,2 мм расположенными на высоте 25,4 мм и 57, 1 мм от дна, изменение уровня суспензии между которыми оценивают в секундах.Distinctive essential features sufficient in all cases is that for the manufacture of a suspension, with active stirring, a dry mixture is diluted with water, which contains a powder of water-soluble cellulose ether in an amount of from 40% to 75% by weight, and hollow sealed microspheres in an amount of from 25% to 60% by weight, in the ratio of 1 part by weight of the dry mixture to 20-60 parts by weight of water, reach a predetermined conditional viscosity. Distinctive essential features sufficient in some cases is that the conditional viscosity is selected, depending on the condition and strength of the rock, in the range from 7.0 to 20.0 seconds in a standard Navy circle, which is a cylindrical container with a height of 80 mm, with an inner diameter of 69.8 mm, with a nozzle with a diameter of 9.5 mm in the bottom, with holes in the wall with a diameter of 4.2 mm located at a height of 25.4 mm and 57, 1 mm from the bottom, the change in the level of suspension between which is evaluated at seconds.

В морозную погоду в суспензию дополнительно добавляют антифриз, в качестве антифризной добавки используют моноэтиленгликоль или диэтиленгликоль, в количестве от 0,42% до 7,56% по массе от общей массы суспензии. Для выполнения способа по изобретению, сухую смесь, которая содержит стеклянные полые герметичные микросферы диаметром от 40 до 50 мкм производства фирмы ЗМ США , в количестве 0,46 кг и порошок метилгидроксиэтилцеллюлозы производства CE ТИЛОЗ IМБХ и Ко. КГIn frosty weather, antifreeze is additionally added to the suspension, monoethylene glycol or diethylene glycol is used as an antifreeze additive, in an amount of from 0.42% to 7.56% by weight of the total weight of the suspension. To perform the method according to the invention, a dry mixture that contains glass hollow sealed microspheres with a diameter of from 40 to 50 microns produced by the company ZM USA, in the amount of 0.46 kg and powder methyl hydroxyethyl cellulose manufactured by CE TILOS IMBH & Co. KG

(Германия) с размером частиц 0,125-0,140 мм и удельным насыпным весом 0,41 г/см 3 , в количестве 0,54 кг разводят, при активном перемешивании, на протяжении 5 минут в 41 литре воды (вода измеряется в литрах в связи с незначительными отклонениями массы от объемного ее измерения). Используют питьевую воду из водопровода , или воду из местных источников - независимо от водородного показателя или жесткости.(Germany) with a particle size of 0.125-0.140 mm and a specific bulk density of 0.41 g / cm 3 , in the amount of 0.54 kg, is diluted, with active stirring, for 5 minutes in 41 liters of water (water is measured in liters in connection with slight deviations of the mass from its volumetric measurement). Use drinking water from a water supply system, or water from local sources - regardless of the pH or hardness.

Для добывания блоков из породы габбро, достигают необходимой вязкости - 10 секунд. Которую проверяют по стандартной кружке ВМС, представляющей собой цилиндрическую емкость с высотой 80 мм, с внутренним диаметром 69,8мм, с соплом диаметром 9,5 мм в дне, с отверстиями в стенке диаметром по 4,2 мм расположенными на высоте 25,4 мм и 57,1 мм от дна. Суспензия готова для заполнения шпуров. При попытке изготовить суспензию из сухой смеси в которой порошок эфира целлюлозы, заложен в количестве большем 75% по массе, а стеклянные полые микросферы в количестве меньшем 25% по массе, при разведении в 40 частях воды по массе, она теряла текучесть и суспензию сложно было загрузить в шпур, передача энергии взрыва неравномерная, а при повышении количества воды до 60 частей по массе, суспензия при взрыве не обеспечивала ослабления энергии взрыва и блоки имели повреждения.To obtain blocks from the gabbro breed, the required viscosity is achieved - 10 seconds. Which is checked by the standard Navy mug, which is a cylindrical container with a height of 80 mm, with an inner diameter of 69.8 mm, with a nozzle with a diameter of 9.5 mm in the bottom, with holes in the wall with a diameter of 4.2 mm located at a height of 25.4 mm and 57.1 mm from the bottom. The suspension is ready to fill holes. When trying to make a suspension from a dry mixture in which the cellulose ether powder was incorporated in an amount of more than 75% by mass, and glass hollow microspheres in an amount of less than 25% by mass, when diluted in 40 parts of water by mass, it lost fluidity and the suspension was difficult load into the borehole, the energy transfer of the explosion is uneven, and when the amount of water increased to 60 parts by weight, the suspension during the explosion did not provide a weakening of the energy of the explosion and the blocks were damaged.

Когда в сухой смеси порошок эфира целлюлозы закладывали в количестве меньшем 40% по массе, а стеклянные полые микросферы в количестве большем 60% по массе, то при разведении в 40 частях воды по массе, повышенная текучесть суспензии создавала ей возможность заполнить щели в горный породе, полые герметичные микросферы всплывали за 10-15 минут, и создавалась неравномерность передачи энергии взрыва по длине шпура, после взрыва образовывались сколы и другие повреждения стенок блока, а из горизонтальных шпуров суспензия вытекала, и необходимо было сверление шпуров выполнять с уклоном относительно горизонта, который также создает угрозу повреждения блока из-за возможности заклинивания. А при добавлении сухой смеси, для уменьшения текучести, энергии взрыва было недостаточно для качественного откалывания блока от горного массива. Стеклянные полые герметичные микросферы диаметром меньше 10 мкм промышленно изготавливаются в ограниченном количестве и не дают стабильных результатов в связи со слипанием между собой, а полые герметичные микросферы диаметром больше 150 мкм не распределяются равномерно, при разведении суспензии, и приводят к неравномерной передаче энергии взрыва по длине шпура.When in a dry mixture the cellulose ether powder was laid in an amount of less than 40% by mass, and glass hollow microspheres in an amount of more than 60% by mass, then when diluted in 40 parts of water by mass, the increased fluidity of the suspension made it possible to fill the gaps in the rock, hollow sealed microspheres floated in 10-15 minutes, and uneven transfer of explosion energy along the length of the hole was created, after the explosion chips and other damage to the block walls formed, and the suspension flowed out from horizontal holes, and it was necessary to Yerlen perform drilling with a slope relative to the horizontal, which also constitutes a threat sector is damaged because of the possibility of jamming. And when adding a dry mixture, to reduce fluidity, the energy of the explosion was not enough for high-quality breaking of the block from the rock mass. Glass hollow sealed microspheres with a diameter of less than 10 microns are industrially produced in a limited number and do not give stable results due to cohesion among themselves, and hollow sealed microspheres with a diameter of more than 150 microns are not distributed evenly when the suspension is diluted, and lead to an uneven transmission of the explosion energy along the length borehole.

Суспензия, согласно изобретению, имеет консистенцию, которая позволяет заполнить шпур в котором заложен детонационный шнур, но не заходит в небольшие трещины, передает и равномерно распределяет уменьшенную регулируемую нагрузку на стенки шпуров от взрыва детонационного шнура и обеспечивает качественный раскол по ряду шпуров без повреждения стенок блока из горной породы. Каждая из частиц порошка загустителя при изготовлении суспензии разбухает захватывает и удерживает полые герметичные микросферы, которые равномерно распределяются и долго сохраняя это положение, находятся на своих местах. Разбавленная с антифризными добавками суспензия позволяет добывать блоки камня в морозные погоды, без повреждения блоков камня и аварийного прекращения работ.The suspension, according to the invention, has a consistency that allows filling the hole in which the detonation cord is laid, but does not go into small cracks, transfers and evenly distributes the reduced adjustable load on the walls of the holes from the detonation cord explosion and ensures a high-quality split along a number of holes without damaging the block walls from the rock. Each of the particles of the thickener powder in the manufacture of the suspension swells, captures and holds hollow sealed microspheres, which are evenly distributed and maintain this position for a long time, are in place. Diluted with antifreeze additives, the slurry can produce stone blocks in frosty weather, without damaging the stone blocks and abnormal termination of work.

Описанные решения позволяют добывать качественный блочный камень из горных пород без повреждения тела блоков с минимальными затратами взрывчатого материала, и минимальным вредным влиянием на экологию, так как зарядами являются сами детонационные шнуры, в которых заложено взрывчатое вещество в малом количестве от 6 до 12 грамм на погонный метр, а описанная водная суспензия передает и распределяет ослабленную энергию взрыва, при взрыве не выделяет токсичных веществ, о чем имеются выводы официальной экспертизы.The described solutions make it possible to produce high-quality block stone from rocks without damaging the body of the blocks with minimal cost of explosive material, and minimal environmental impact, since the charges are detonation cords themselves, which contain explosive in a small amount of 6 to 12 grams per linear meter, and the described aqueous suspension transmits and distributes the weakened energy of the explosion, during the explosion does not emit toxic substances, as there are conclusions of an official examination.

На фиг. 1 показан основной вид на блок камня горной породы с просверленными в горном массиве шпурами;In FIG. 1 shows a basic view of a block of rock stone with bore holes drilled in the massif;

На фиг. 2 показан вид сверху на блок камня в горной породе; На фиг. 3 показан разрез А- А по шпуру. Испытание изобретений проводились при добыче блочного камня горной породы. Составы сухой смеси и изготовление водной суспензии приводятся одновременно с описанием откалывания блоков различной по прочности горной породы.In FIG. 2 shows a top view of a block of stone in a rock; In FIG. 3 shows a section A-A along the hole. A test of the inventions was carried out in the extraction of block stone rock. The compositions of the dry mixture and the manufacture of an aqueous suspension are given simultaneously with a description of the chipping of blocks of different strength rock breed.

Для подготовки к откалыванию блоков, проводили бурение рядов вертикальных шпуров 1 и горизонтальных шпуров 2 диаметром 40 мм по границам блока 3 размерами: длина 3500 мм , ширина 1400 мм , высота 1400 мм в горный породе 4 с постоянным шагом 180 мм . Устанавливали шнуры 5, детонирующие с высокой скоростью, типа ДШ содержащие 9 грамм на погонный метр взрывчатого вещества - тетранитропентаэритрита, объединяли заряды детонирующими шнурами 7 тоже типа /TTTT в общую сетку. Шпуры заполняли разбавленной суспензией 6, варианты которой, при испытании, описаны ниже. Производили взрыв.To prepare for block breaking off, we drilled rows of vertical holes 1 and horizontal holes 2 with a diameter of 40 mm along the boundaries of block 3 with dimensions: length 3500 mm, width 1400 mm, height 1400 mm in rock 4 with a constant pitch of 180 mm. Cords 5 were installed, detonating at a high speed, such as ДС containing 9 grams per linear meter of explosive - tetranitropentaerythritol, charges were combined by detonating cords 7 of the same type / TTTT into a common grid. The holes were filled with diluted suspension 6, variants of which, when tested, are described below. They made an explosion.

Для наглядности оценивания, количественные характеристики приводятся в процентах и частях:For clarity of assessment, quantitative characteristics are given in percent and parts:

1) при проработке подошвы уступа в мягкой горной породе - мраморе . Суспензия изготавливалась разведением сухой смеси с 46% по массе порошка rидроксиэтилцеллюлозы производства CE ТИЛОЗ ГМБХ и Ко. КГ с размером частиц 0,09-0,125 мм, и удельным насыпным весом 0,36 г/см 3 , и 54% по массе полых герметичных не имеющих покрытия микросфер из натриевоборосиликатного стекла диаметром 40 мкм, удельным насыпным весом 0,1 г/см 3 в 36 частях воды по массе относительно одной части по массе сухой смеси, при активном перемешивании на протяжении 9 минут. Вязкость полученной суспензии 14 секунд по стандартной кружке ВМС. В горизонтальных шпурах использовалась легкая забойка из поролона. После взрыва детонирующих шнуров был получен блок длиной 3500 мм , шириной 1400 мм , высотой 1400 мм. При осмотре зафиксировано, что отсутствуют сколы, порывы, трещины и микротрещины;1) when working out the soles of the ledge in soft rock - marble. The suspension was prepared by diluting a dry mixture with 46% by weight of hydroxyethyl cellulose powder manufactured by CE TILOS GMBH and Co. KG with a particle size of 0.09-0.125 mm, and a specific bulk density of 0.36 g / cm 3 , and 54% by weight of hollow sealed uncoated microspheres of sodium borosilicate glass with a diameter of 40 μm, specific gravity of 0.1 g / cm 3 in 36 parts by weight of water relative to one part by weight of the dry mixture, with vigorous stirring for 9 minutes. The viscosity of the resulting suspension is 14 seconds according to a standard Navy circle. In horizontal boreholes, lightweight foam rubber was used. After an explosion of detonating cords, a block was obtained with a length of 3500 mm, a width of 1400 mm, and a height of 1400 mm. Upon examination, it was recorded that there are no chips, gusts, cracks and microcracks;

2) при откалывании блока от массива высокопрочной горной породы- габбро , суспензия изготавливалась разведением при перемешивании на протяжении 8 минут сухой смеси с 58% по массе порошка rидроксиэтилцеллюлозы производства CE ТИЛОЗ ГМБХ и Ко. КГ с размером частиц 0,11-0,15 мм, удельным насыпным весом 0,42 г/см 3 , и 42% по массе стеклянных полых аппретированных герметичных микросфер (покрытых слоем повышающим смачиваемость водой) из нaтpийбopcиликa.тнoгo стекла, диаметром 65 мкм удельным насыпным весом 0,8 г/см 3 в 42 частях воды относительно одной части по массе сухой смеси. Вязкость полученной суспензии 13 секунд по стандартной кружке ВМС.2) when the block was chipped off from the high-strength gabbro rock mass, the suspension was prepared by diluting with stirring for 8 minutes a dry mixture with 58% by weight of hydroxyethyl cellulose powder produced by CE TILOS GMBH and Co. KG with a particle size of 0.11-0.15 mm, a specific bulk density of 0.42 g / cm 3 , and 42% by weight of glass hollow finished sealed microspheres (coated with a layer that increases the wettability of water) made of sodium silicate.tnogo glass with a diameter of 65 μm specific gravity 0.8 g / cm 3 in 42 parts of water relative to one part by weight of the dry mixture. The viscosity of the resulting suspension is 13 seconds according to a standard Navy circle.

После взрыва детонирующих шнуров, был получен блок длиной 3500 мм , шириной 1400 мм , высотой 1400 мм. При осмотре зафиксировано, что отсутствуют сколы, порывы, трещины и микротрещины в стенках.After the explosion of detonating cords, a block was obtained with a length of 3500 mm, a width of 1400 mm, a height of 1400 mm. Upon examination, it was noted that there are no chips, gusts, cracks and microcracks in the walls.

3) при откалывании блока от массива горной породы - габбро суспензия изготавливалась разведением при перемешивании на протяжении 10 минут сухой смеси с 71,4% по массе порошка метилгидроксиэтилцеллюлозы производства CE ТИЛОЗ ГМБХ и Ко КГ с размером частиц 0,1-0,13 мм удельным насыпным весом 0,42 г/см 3 , и 28,6% по массе стеклянных полых герметичных микросфер, диаметром от 20 до 50 мкм удельным насыпным весом 0,06 г/см , для чего сухую смесь при активном перемешивании разводили в 48 частях воды по массе. Вязкость суспензии -16 секунд по стандартной кружке ВМС. В результате взрыва был получен блок длиной 3500 мм , шириной 1400 мм , высотой 1400 мм. При осмотре зафиксировано, что отсутствуют сколы, порывы, трещины и микротрещины.3) when breaking off the block from the rock mass - gabbro, the suspension was prepared by diluting with stirring for 10 minutes a dry mixture with 71.4% by weight of methylhydroxyethyl cellulose powder manufactured by CE TILOS GMBH and Co KG with a particle size of 0.1-0.13 mm specific bulk density of 0.42 g / cm 3 and 28.6% by weight of glass hollow sealed microspheres, with a diameter of from 20 to 50 microns, specific gravity of 0.06 g / cm, for which the dry mixture was diluted with active stirring in 48 parts of water by weight. The viscosity of the suspension is -16 seconds on a standard navy circle. As a result of the explosion, a block was obtained with a length of 3500 mm, a width of 1400 mm, a height of 1400 mm. Upon examination, it was recorded that there are no chips, gusts, cracks and microcracks.

4) при откалывании блока от массива высокопрочной горной породы - габбро суспензия изготавливалась разведением при перемешивании на протяжении 10 минут сухой смеси с 21% по массе порошка гидроксиэтилцеллюлозы производства CE ТИЛОЗ ГМБХ и Ко. КГ с размером частиц 0, 125 мм удельным насыпным весом 0,3 г/см 3 и 79% по массе полых герметичных микросфер из натрийборсиликатного стекла, диаметром 40 мкм удельной насыпным весом 0,17 г/см 3 в 17 частях воды относительно одной части по массе сухой смеси. Вязкость полученной суспензии- 40 секунд по стандартной кружке ВМС. В результате было сложно заполнить шпуры, при взрыве между некоторыми шпурами блок не отделился от горного массива, пришлось дорезать гидроразмывом контур блока, полученный блок длиной 3500 мм , шириной 1400 мм , высотой 1400 мм имел сколы.4) when the block was chipped off from a high-strength rock mass - gabbro suspension was prepared by diluting with stirring for 10 minutes a dry mixture with 21% by weight of hydroxyethyl cellulose powder manufactured by CE TILOZ GMBH and Co. KG with a particle size of 0, 125 mm specific gravity 0.3 g / cm 3 and 79% by weight of hollow sealed microspheres made of sodium borosilicate glass, with a diameter of 40 μm specific gravity 0.17 g / cm 3 in 17 parts of water relative to one part by weight of the dry mixture. The viscosity of the resulting suspension is 40 seconds in a standard Navy circle. As a result, it was difficult to fill the boreholes, during the explosion between some boreholes the block did not separate from the mountain massif, it was necessary to cut the block contour with a hydraulic wash, the resulting block was 3,500 mm long, 1,400 mm wide, 1,400 mm high and had chips.

5) при откалывании блока от массива высокопрочной породы - габбро суспензия изготавливалась разведением при перемешивании на протяжении 8 минут сухой смеси с 46% по массе порошка метилгидроксиэтилцеллюлозы производства CE ТИЛОЗ ГМБХ и Ко КГ с размером частиц 0,14-0,27 мм удельным насыпным весом 0,37 г/см 3 , и 54% по массе керамических полых герметичных микросфер диаметром 30 мкм удельным насыпным весом 0,11 г/см в 42 частях воды относительно одной части по массе сухой смеси, вязкость суспензии 13 секунд по стандартной кружке ВМС. После взрыва, был получен блок длиной 3500 мм , шириной 1400 мм , высотой 1400 мм. При осмотре зафиксировано, что отсутствуют сколы, порывы, трещины и микротрещины.5) when breaking off the block from the high-strength rock mass - gabbro, the suspension was prepared by diluting with stirring for 8 minutes a dry mixture with 46% by weight of methylhydroxyethyl cellulose powder manufactured by CE TILOS GMBH and Co. KG with a particle size of 0.14-0.27 mm specific bulk 0.37 g / cm 3 , and 54% by weight of ceramic hollow sealed microspheres with a diameter of 30 μm, specific gravity 0.11 g / cm in 42 parts of water relative to one part by weight of the dry mixture, the viscosity of the suspension is 13 seconds according to a standard Navy circle. After the explosion, a block was obtained with a length of 3500 mm, a width of 1400 mm, a height of 1400 mm. Upon examination, it was recorded that there are no chips, gusts, cracks and microcracks.

6) при откалывании блока от массива габбро суспензия изготавливалась разведением при перемешивании на протяжении 8 минут сухой смеси с 63% по массе порошка гидроксиэтилцеллюлозы производства CE ТИЛОЗ ГМБХ и Ко. КГ с размером частиц 0,28-0,3 мм удельным насыпным весом 0,46г/cм 3, и 37% по массе боросиликатных полых герметичных микросфер диаметром 60 мкм удельным насыпным весом 0,04 г/см 3 в 65 частях воды относительно одной части по массе сухой смеси, вязкостью полученной суспензии 6 секунд по стандартной кружке ВМС .6) when the block was chipped off from the gabbro massif, the suspension was prepared by diluting with stirring for 8 minutes a dry mixture with 63% by weight of hydroxyethyl cellulose powder manufactured by CE TILOS GMBH and Co. KG with a particle size of 0.28-0.3 mm specific gravity of 0.46 g / cm 3 and 37% by weight of borosilicate hollow sealed microspheres with a diameter of 60 μm specific gravity of 0.04 g / cm 3 in 65 parts of water relative to one parts by weight of the dry mixture, the viscosity of the resulting suspension for 6 seconds in a standard circle of the IUD.

Полученная суспензия была очень жидкой невозможно было удержать ее в горизонтальных шпурах, микросферы быстро всплывали вверх и блок длиной 3500 мм , шириной 1400 мм , высотой 1400 мм имел сколы, порывы, трещины, товарная ценность блока снижена. 7) при откалывании блока от массива мягкой породы-мрамора в морозную погоду при морозе 10 0 C, суспензия изготовлялась разведением при перемешивании на протяжении 8 минут сухой смеси с 39% по массе порошка карбоксиметилцеллюлозы производства CE ТИЛОЗ ГМБХ и Ко. КГ с размером частиц 0,20-0,25 мм удельным насыпным весом 0,42 г/см 3 и 61% по массе фенолформальдегидных полых герметичных микросфер, диаметром 36 мкм удельным насыпным весом 0,3 г/см 3 в 30 частях воды и 2,5 (5,3% от общей массы ) частях диэтиленгликоля относительно одной части по массе сухой смеси. Количество диэтиленгликоля связано непосредственно с температурой в карьере. Условная вязкость- 17 секунд по стандартной кружке ВМС. После взрыва, был получен блок длиной 3500 мм , шириной 1400 мм , высотой 1400 мм. При осмотре зафиксировано, что отсутствуют сколы, порывы, трещины и микротрещины. 8) при откалывании блока от массива мрамора с большим количеством микротрещин, суспензия изготавливалась разведением при перемешивании на протяжении 8 минут сухой смеси с 40% по массе порошка метилгидроксиэтилцеллюлозы производства CE ТИЛОЗ ГМБХ и Ко. КГ с размером частиц 0,20-0,25 мм удельным насыпным весом 0,39 г/см 3 и 60% по массе полых герметичных микросфер из натрийборсиликатного стекла, диаметромThe resulting suspension was very liquid, it was impossible to hold it in horizontal holes, the microspheres quickly surfaced upwards and the block was 3,500 mm long, 1,400 mm wide, 1,400 mm high and had chips, gusts, cracks, and the commodity value of the block was reduced. 7) when the block was chipped off from an array of soft rock-marble in frosty weather at a temperature of 10 0 C, the suspension was prepared by diluting with stirring for 8 minutes a dry mixture with 39% by weight of carboxymethyl cellulose powder manufactured by CE TILOS GMBH and Co. KG with a particle size of 0.20-0.25 mm with a specific bulk density of 0.42 g / cm 3 and 61% by weight of phenol-formaldehyde hollow sealed microspheres, 36 μm in diameter with a specific bulk density of 0.3 g / cm 3 in 30 parts of water and 2.5 (5.3% of the total mass) parts of diethylene glycol relative to one part by weight of the dry mixture. The amount of diethylene glycol is directly related to the temperature in the quarry. Conditional viscosity - 17 seconds on a standard circle of Naval Forces. After the explosion, a block was obtained with a length of 3500 mm, a width of 1400 mm, a height of 1400 mm. Upon examination, it was recorded that there are no chips, gusts, cracks and microcracks. 8) when the block was chipped off from a marble array with a large number of microcracks, the suspension was prepared by diluting with stirring for 8 minutes a dry mixture with 40% by weight of methylhydroxyethyl cellulose powder manufactured by CE TILOS GMBH and Co. KG with a particle size of 0.20-0.25 mm specific gravity of 0.39 g / cm 3 and 60% by weight of hollow sealed microspheres of sodium borosilicate glass, with a diameter

40 мкм удельным насыпным весом 0,09 г/см 3 в 38 частях воды. Условная вязкость40 μm specific gravity of 0.09 g / cm 3 in 38 parts of water. Conditional viscosity

-19 секунд по стандартной кружке ВМС.-19 seconds on a standard Navy mug.

Готовой суспензией, без проблем, были заполнены шпуры, после взрыва был получен блок длиной 3500 мм , шириной 1400 мм , высотой 1400 мм. При осмотре зафиксировано, что отсутствуют сколы, порывы, трещины и микротрещины.The finished suspension, without problems, was filled with bore holes, after the explosion, a block was obtained with a length of 3500 mm, a width of 1400 mm, a height of 1400 mm. Upon examination, it was recorded that there are no chips, gusts, cracks and microcracks.

9) при откалывании блока от массива высокопрочной горной породы - габбро суспензия изготавливалась разведением при перемешивании на протяжении 10 минут сухой смеси с 70% по массе порошка метилгидроксиэтилцеллюлозы производства CE ТИЛОЗ ГМБХ и Ко КГ с размером частиц 0, 1 -0, 13 мм удельным насыпным весом 0,42 г/см 3 , и 30% по массе стеклянных полых герметичных микросфер, диаметром от 20 до 50 мкм удельным насыпным весом 0,06 г/см , для чего сухую смесь при активном перемешивании разводили в 60 частях воды по массе. Вязкость суспензии -9 секунд по стандартной кружке ВМС. В результате взрыва был получен блок длиной 3500 мм , шириной 1400 мм , высотой 1400 мм. При осмотре зафиксировано, что отсутствуют сколы, порывы, трещины и микротрещины.9) when breaking off the block from the high-strength rock mass - gabbro suspension was prepared by diluting with stirring for 10 minutes a dry mixture with 70% by weight of methylhydroxyethyl cellulose powder manufactured by CE TILOS GMBH and Co KG with a particle size of 0, 1-0, 13 mm specific bulk weighing 0.42 g / cm 3 and 30% by weight of glass hollow sealed microspheres, with a diameter of from 20 to 50 microns, specific gravity of 0.06 g / cm, for which the dry mixture was diluted with active stirring in 60 parts of water by weight. The viscosity of the suspension is -9 seconds on a standard Navy mug. As a result of the explosion, a block was obtained with a length of 3500 mm, a width of 1400 mm, a height of 1400 mm. Upon examination, it was recorded that there are no chips, gusts, cracks and microcracks.

10) при откалывании блока от массива высокопрочной породы - габбро суспензия изготавливалась разведением сухой смеси с 42% по массе порошка метилгидроксиэтилцеллюлозы производства CE ТИЛОЗ ГМБХ и Ко КГ с размером частиц 0,14-0,27 мм удельным насыпным весом 0,37 г/см 3 , и 58% по массе керамических полых герметичных микросфер диаметром 30 мкм удельным насыпным весом 0, 11 г/см 3 в 50 частях воды относительно одной части по массе сухой смеси, вязкость суспензии 10 секунд по стандартной кружке ВМС. После взрыва, был получен блок длиной 3500 мм , шириной 1400 мм , высотой 1400 мм. При осмотре зафиксировано, что отсутствуют сколы, порывы, трещины и микротрещины. 10) when breaking off the block from the high-strength rock mass - gabbro, the suspension was prepared by diluting a dry mixture with 42% by weight of methylhydroxyethyl cellulose powder manufactured by CE TILOS GMBH and Co. KG with a particle size of 0.14-0.27 mm specific gravity 0.37 g / cm 3 , and 58% by weight of ceramic hollow sealed microspheres with a diameter of 30 μm, specific gravity of 0.11 g / cm 3 in 50 parts of water relative to one part by weight of the dry mixture, the viscosity of the suspension is 10 seconds according to a standard IUD circle. After the explosion, a block was obtained with a length of 3500 mm, a width of 1400 mm, a height of 1400 mm. Upon examination, it was recorded that there are no chips, gusts, cracks and microcracks.

Claims

Формула Formula 1. Смесь для изготовления передатчика и ослабителя детонационного импульса взрыва в шпуре, в качестве которого используют невзрывчатое вещество, с возможностью расположения между шнуром со взрывчатым веществом с высокой скоростью детонации и стенками, высверленных по границам блока горной породы шпуров, которая содержит водорастворимый загуститель и полые микросферы, отличающаяся тем, что содержит в качестве водорастворимого загустителя порошок эфира целлюлозы в количестве от 40% до 75% по массе, и полые герметичные микросферы в количестве от 25% до 60% по массе.1. A mixture for the manufacture of a transmitter and attenuator of the detonation pulse of an explosion in a hole, which is an non-explosive substance, with the possibility of placing between the cord with an explosive substance with a high detonation velocity and walls drilled along the boundaries of the rock block of the holes, which contains a water-soluble thickener and hollow microspheres, characterized in that it contains, as a water-soluble thickening agent, cellulose ether powder in an amount of from 40% to 75% by weight, and hollow sealed microspheres in an amount ve from 25% to 60% by weight. 2. Смесь по п.1, отличающаяся тем, что используют полые герметичные микросферы из стекла, которые имеют диаметр от 10 до 100 мкм, с удельным насыпным весом от 0,05 г/см 3 до 0,16 г/см3. 3. Смесь по п.l, отличающаяся тем, что используют полые герметичные микросферы из керамики, которые имеют диаметр от 50 до 150 мкм, с удельным насыпным весом от 0,1 г/см3 до 0,2. The mixture according to claim 1, characterized in that hollow sealed glass microspheres are used, which have a diameter of 10 to 100 μm, with a specific bulk density of 0.05 g / cm 3 to 0.16 g / cm 3 . 3. The mixture according to claim 1, characterized in that hollow sealed ceramic microspheres are used, which have a diameter of 50 to 150 microns, with a specific bulk density of 0.1 g / cm 3 to 0, 3 г/см3.3 g / cm 3 . 4. Смесь по п.l, отличающаяся тем, что используют полые герметичные микросферы из фенолформальдегида, которые имеют диаметр от 50 до 150 мкм, с удельным насыпным весом от 0,1 г/см3 до 0,3 г/см3 .4. The mixture according to claim 1, characterized in that hollow sealed phenol-formaldehyde microspheres are used, which have a diameter of 50 to 150 μm, with a specific bulk density of 0.1 g / cm 3 to 0.3 g / cm 3 . 5. Смесь по п.l, отличающаяся тем, что в качестве водорастворимого загустителя используют порошок гидроксиэтилцеллюлозы с размером частиц от 0,08 до 0,25 мм с удельным насыпным весом от 0,35 г/см3 до 0,45 г/см3.5. The mixture according to claim 1, characterized in that a hydroxyethyl cellulose powder with a particle size of 0.08 to 0.25 mm and a specific bulk density of 0.35 g / cm 3 to 0.45 g / cm is used as a water-soluble thickener. 3 . 6. Смесь по п.1, которая отличается тем, что в качестве водорастворимого загустителя используют порошок метилгидроксиэтилцеллюлозы с размером частиц от 0,08 до 0,28мм с удельным насыпным весом от 0,2 г/см 3 до 0,5 г/см 3.6. The mixture according to claim 1, characterized in that as a water-soluble thickener, methylhydroxyethyl cellulose powder with a particle size of from 0.08 to 0.28 mm with a specific bulk density of from 0.2 g / cm 3 to 0.5 g / cm is used 3 . 7. Смесь по п.1, отличающаяся тем, что в качестве водорастворимого загустителя используют порошок карбоксиметилцеллюлозы с размером частиц от 0,10 до 0,28 мм с удельным насыпным весом от 0,4 г/см3 до 0,8 г/см3 . 7. The mixture according to claim 1, characterized in that carboxymethyl cellulose powder with a particle size of from 0.10 to 0.28 mm with a specific bulk density of from 0.4 g / cm 3 to 0.8 g / cm is used as a water-soluble thickener. 3 . 8. Способ изготовления суспензии, невзрывчатого вещества с повышенной вязкостью разведенного водой, для закладки в ряд высверленных по границам блока горной породы шпуров и заряженных шнурами со взрывчатым веществом с высокой скоростью детонации, отличающийся тем, что при активном перемешивании, разводят водой сухую смесь, которая содержит порошок водорастворимого эфира целлюлозы в количестве от 40% до 75% по массе, и полые герметичные микросферы в количестве от 25% до 60% по массе, в соотношении 1 часть по массе сухой смеси к 20- 60 частям по массе воды, достигают заданной условной вязкости.8. A method of manufacturing a suspension, non-explosive with high viscosity diluted with water, for laying in a series of holes drilled along the boundaries of the rock block and charged with cords with explosive a high detonation speed, characterized in that with active stirring, a dry mixture is diluted with water, which contains a powder of water-soluble cellulose ether in an amount of from 40% to 75% by weight, and hollow sealed microspheres in an amount of from 25% to 60% by weight, in the ratio of 1 part by weight of the dry mixture to 20-60 parts by weight of water, reaches a predetermined conditional viscosity. 9. Способ по п.8, отличающийся тем, что условную вязкость выбирают, в зависимости от состояния и прочности горной породы, в пределах от 7,0 до 20, 0 секунд по стандартной кружке ВМС, которая представляет собой цилиндрическую емкость с высотой 80 мм, с внутренним диаметром 69,8 мм, с соплом диаметром 9,5 мм в дне, с отверстиями в стенке диаметром по 4,2 мм расположенными на высоте 25,4 мм и 57, 1 мм от дна, изменение уровня суспензии между которыми оценивают в секундах.9. The method according to claim 8, characterized in that the conditional viscosity is selected, depending on the condition and strength of the rock, in the range from 7.0 to 20, 0 seconds in a standard Navy mug, which is a cylindrical container with a height of 80 mm , with an inner diameter of 69.8 mm, with a nozzle with a diameter of 9.5 mm in the bottom, with holes in the wall with a diameter of 4.2 mm located at a height of 25.4 mm and 57, 1 mm from the bottom, the change in the level of suspension between which evaluate in seconds. 10. Способ по п.8, отличающийся тем, что в суспензию дополнительно добавляют антифриз.10. The method according to claim 8, characterized in that antifreeze is additionally added to the suspension. 11. Способ по п. 10, отличающийся тем, что в качестве антифризной добавки используют моноэтиленгликоль или диэтиленгликоль, в количестве от 0,42% до 7,56% по массе от общей массы суспензии. 11. The method according to p. 10, characterized in that as antifreeze additives use monoethylene glycol or diethylene glycol, in an amount of from 0.42% to 7.56% by weight of the total weight of the suspension.
PCT/UA2009/000059 2009-03-23 2009-11-30 Mixture for the manufacture of a transmitter and attenuator of the blast impulse of an explosion in a blast hole and a method for manufacturing a suspension Ceased WO2010110762A1 (en)