WO2010072999A2 - Procédé de frittage - Google Patents

Procédé de frittage Download PDF

Info

Publication number
WO2010072999A2
WO2010072999A2 PCT/GB2009/002914 GB2009002914W WO2010072999A2 WO 2010072999 A2 WO2010072999 A2 WO 2010072999A2 GB 2009002914 W GB2009002914 W GB 2009002914W WO 2010072999 A2 WO2010072999 A2 WO 2010072999A2
Authority
WO
WIPO (PCT)
Prior art keywords
metal oxide
nanoparticles
feedstock
sintering
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/GB2009/002914
Other languages
English (en)
Other versions
WO2010072999A3 (fr
Inventor
Vladimir Terentyev
Rafkat Takhautdinov
Igor Ivanovich Nosov
Michael James Attfield
George Barry Park
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Oxonica Materials Ltd
Original Assignee
Oxonica Materials Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from GB0823451A external-priority patent/GB0823451D0/en
Priority claimed from GB0909741A external-priority patent/GB0909741D0/en
Application filed by Oxonica Materials Ltd filed Critical Oxonica Materials Ltd
Publication of WO2010072999A2 publication Critical patent/WO2010072999A2/fr
Publication of WO2010072999A3 publication Critical patent/WO2010072999A3/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un procédé de production d'un minerai de métal fritté, ledit procédé consistant à fritter un minerai métallique, un combustible et de l'eau en présence de nanoparticules d'un oxyde de métal de transition ou d'un oxyde de lanthanide.
PCT/GB2009/002914 2008-12-23 2009-12-17 Procédé de frittage Ceased WO2010072999A2 (fr)

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
GB0823451A GB0823451D0 (en) 2008-12-23 2008-12-23 Sinter process
GB0823451.0 2008-12-23
GB0902575.0 2009-02-16
GB0902575A GB0902575D0 (en) 2008-12-23 2009-02-16 Sinter process
GB0909741.1 2009-06-05
GB0909741A GB0909741D0 (en) 2009-06-05 2009-06-05 Sinter process

Publications (2)

Publication Number Publication Date
WO2010072999A2 true WO2010072999A2 (fr) 2010-07-01
WO2010072999A3 WO2010072999A3 (fr) 2010-08-12

Family

ID=41818824

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB2009/002914 Ceased WO2010072999A2 (fr) 2008-12-23 2009-12-17 Procédé de frittage

Country Status (1)

Country Link
WO (1) WO2010072999A2 (fr)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105002352A (zh) * 2013-12-09 2015-10-28 安徽工业大学 一种高性能的球团矿粘结剂的制备方法
WO2017033889A1 (fr) * 2015-08-24 2017-03-02 Ｄｏｗａエレクトロニクス株式会社 Poudre d'argent, son procédé de fabrication et pâte conductrice
JP2017043840A (ja) * 2015-08-24 2017-03-02 Ｄｏｗａエレクトロニクス株式会社 銀粉およびその製造方法、ならびに導電性ペースト
WO2019001180A1 (fr) * 2017-06-29 2019-01-03 东北大学 Procédé de préparation de minerai fritté à partir d'un mélange concentré de magnétite de vanadium-titane comportant du chrome, riche en vanadium et de qualité élevée
CN112342372A (zh) * 2020-08-31 2021-02-09 包头钢铁（集团）有限责任公司 一种改善烧结矿显微结构的方法
CN113801991A (zh) * 2020-06-16 2021-12-17 上海梅山钢铁股份有限公司 一种改善烧结矿质量的方法
CN115747482A (zh) * 2022-12-14 2023-03-07 云南德胜钢铁有限公司 一种低硅、低碱度、钒钛超厚料层烧结方法
CN116119952A (zh) * 2023-01-13 2023-05-16 安徽海鑫矿化材料科技有限公司 一种复合生料煅烧熔解促进剂及其制备方法
US12241030B2 (en) 2022-10-17 2025-03-04 Indian Oil Corporation Limited Additized DME/LPG fuel for improving combustion efficiency

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4543121A (en) * 1984-03-12 1985-09-24 The Mogul Corporation Method of reducing hydrocarbon emissions occurring during iron ore sintering operations
JP2001515957A (ja) * 1997-07-24 2001-09-25 シーメンス アクチエンゲゼルシヤフト 焼結設備の運転方法とその焼結設備
CN1055320C (zh) * 1998-04-29 2000-08-09 宝山钢铁(集团)公司 生产直接还原竖炉和高炉用冷固结球团的方法
US7549427B2 (en) * 2004-07-20 2009-06-23 Board Of Supervisors Of Louisiana State University And Agricultural And Mechanical College Nanolayer catalysts useful in promoting oxidation, and their manufacture and use
RU2304626C1 (ru) * 2005-11-16 2007-08-20 Открытое акционерное общество "Магнитогорский металлургический комбинат" Шихта для производства агломерата
CN100567522C (zh) * 2007-02-14 2009-12-09 宝山钢铁股份有限公司 一种烧结复合添加剂
CN101148695B (zh) * 2007-11-13 2010-09-15 中国科学院过程工程研究所 添加剂改性焦炭降低烧结过程NOx排放的方法

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105002352A (zh) * 2013-12-09 2015-10-28 安徽工业大学 一种高性能的球团矿粘结剂的制备方法
WO2017033889A1 (fr) * 2015-08-24 2017-03-02 Ｄｏｗａエレクトロニクス株式会社 Poudre d'argent, son procédé de fabrication et pâte conductrice
JP2017043840A (ja) * 2015-08-24 2017-03-02 Ｄｏｗａエレクトロニクス株式会社 銀粉およびその製造方法、ならびに導電性ペースト
JP2018016891A (ja) * 2015-08-24 2018-02-01 Ｄｏｗａエレクトロニクス株式会社 銀粉の製造方法
US10381124B2 (en) 2015-08-24 2019-08-13 Dowa Electronics Materials Co., Ltd. Silver powder, manufacturing method therefor, and conductive paste
WO2019001180A1 (fr) * 2017-06-29 2019-01-03 东北大学 Procédé de préparation de minerai fritté à partir d'un mélange concentré de magnétite de vanadium-titane comportant du chrome, riche en vanadium et de qualité élevée
CN113801991A (zh) * 2020-06-16 2021-12-17 上海梅山钢铁股份有限公司 一种改善烧结矿质量的方法
CN112342372A (zh) * 2020-08-31 2021-02-09 包头钢铁（集团）有限责任公司 一种改善烧结矿显微结构的方法
US12241030B2 (en) 2022-10-17 2025-03-04 Indian Oil Corporation Limited Additized DME/LPG fuel for improving combustion efficiency
CN115747482A (zh) * 2022-12-14 2023-03-07 云南德胜钢铁有限公司 一种低硅、低碱度、钒钛超厚料层烧结方法
CN116119952A (zh) * 2023-01-13 2023-05-16 安徽海鑫矿化材料科技有限公司 一种复合生料煅烧熔解促进剂及其制备方法

Also Published As

Publication number Publication date
WO2010072999A3 (fr) 2010-08-12

Similar Documents

Publication Publication Date Title
WO2010072999A2 (fr) Procédé de frittage
US8906131B2 (en) Direct production of iron slabs and nuggets from ore without pelletizing or briquetting
RU2447164C2 (ru) Способ производства окатышей из восстановленного железа и способ производства чугуна
RU2435868C1 (ru) Способ получения брикетированного восстановленного железа и способ получения чугуна
JP5540859B2 (ja) 製鉄用炭材内装塊成鉱およびその製造方法
JP5297077B2 (ja) フェロモリブデンの製造方法
AU2013266036B2 (en) Process for the improvement of reducibility of iron ore pellets
Jin et al. Synergetic utilization of zinc-bearing dust by carbothermic reduction-roasting process: phase transformation and morphological evolution
JP5466590B2 (ja) 炭材内装塊成化物を用いた還元鉄製造方法
JP6294152B2 (ja) 粒状金属鉄の製造方法
NL2029142B1 (en) Process for smelting a metalliferous feedstock
CA2100442C (fr) Procede de production d'alliages d'acier contenant du vanadium
KR910006014B1 (ko) 고환원 크롬광석 펠릿
Xu et al. Novel mode for mineralization and its sintering performance of vanadiferous titanomagnetites
JP3301326B2 (ja) 還元鉄の製造方法
JP2016130341A (ja) マグネタイト鉱石を用いた焼結鉱原料の製造方法
RU2768432C2 (ru) Способ производства офлюсованного железорудного агломерата
JP2007056306A (ja) 焼結鉱の製造方法および焼結鉱の製造用擬似粒子
JP6436317B2 (ja) 焼結鉱製造用の炭材内装造粒粒子およびそれを用いた焼結鉱の製造方法
TW202338102A (zh) 金屬鐵的製造方法
WO2025019935A1 (fr) Composés de fer exothermiques pour la production de pastilles d'oxyde de fer
JP3206324B2 (ja) 焼結鉱の製造方法
EP4555111A1 (fr) Procédé de réduction directe de matériau à base d'oxyde de fer pour la production d'acier, d'éponge de fer ou de fonte
WO2025023052A1 (fr) Procédé de fonctionnement d'un haut-fourneau
JP2023158803A (ja) ニッケル酸化鉱石の製錬方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09796418

Country of ref document: EP

Kind code of ref document: A2

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 09796418

Country of ref document: EP

Kind code of ref document: A2