WO2009154560A1 - Bloc poreux en dioxyde de titane - Google Patents

Bloc poreux en dioxyde de titane Download PDF

Info

Publication number
WO2009154560A1
WO2009154560A1 PCT/SE2009/050756 SE2009050756W WO2009154560A1 WO 2009154560 A1 WO2009154560 A1 WO 2009154560A1 SE 2009050756 W SE2009050756 W SE 2009050756W WO 2009154560 A1 WO2009154560 A1 WO 2009154560A1
Authority
WO
WIPO (PCT)
Prior art keywords
porous
porous block
block
present
bone
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/SE2009/050756
Other languages
English (en)
Inventor
Lars-Magnus Bjursten
Niklas AXÉN
Bengt MJÖBERG
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tigran Technologies AB
Original Assignee
Tigran Technologies AB
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tigran Technologies AB filed Critical Tigran Technologies AB
Publication of WO2009154560A1 publication Critical patent/WO2009154560A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention porte sur un bloc poreux destiné à une implantation dans la zone maxillo-faciale d'un être humain ou d'un animal, le bloc poreux étant constitué de dioxyde de titane, ayant une porosité d'au moins 60 % et étant une structure géométrique présentant une forme lui permettant de s'ajuster au moins à une partie d'un processus alvéolaire dégradé de l'être humain ou de l'animal.
PCT/SE2009/050756 2008-06-19 2009-06-17 Bloc poreux en dioxyde de titane Ceased WO2009154560A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US12934708P 2008-06-19 2008-06-19
US61/129,347 2008-06-19
SE0801444-1 2008-06-19
SE0801444 2008-06-19

Publications (1)

Publication Number Publication Date
WO2009154560A1 true WO2009154560A1 (fr) 2009-12-23

Family

ID=41434299

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/SE2009/050756 Ceased WO2009154560A1 (fr) 2008-06-19 2009-06-17 Bloc poreux en dioxyde de titane

Country Status (1)

Country Link
WO (1) WO2009154560A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110008754A1 (en) * 2009-07-10 2011-01-13 Bassett Jeffrey A Patient-Specific Implants With Improved Osseointegration
US10265189B2 (en) 2016-09-13 2019-04-23 Warsaw Orthopedic, Inc. Interbody spinal fusion device
US12279965B2 (en) 2017-09-08 2025-04-22 Xtant Medical Holdings, Inc. Intervertebral implants, instruments, and methods

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6132470A (en) * 1994-01-27 2000-10-17 W. L. Gore & Associates, Inc. Apparatus and method for protecting prosthetic joint assembly from wear
WO2000064504A2 (fr) * 1999-04-28 2000-11-02 Bruce Medical Ab Corps destine a permettre l'interposition et la croissance de tissu osseux et/ou de tissu conjonctif, et procede de fabrication

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6132470A (en) * 1994-01-27 2000-10-17 W. L. Gore & Associates, Inc. Apparatus and method for protecting prosthetic joint assembly from wear
WO2000064504A2 (fr) * 1999-04-28 2000-11-02 Bruce Medical Ab Corps destine a permettre l'interposition et la croissance de tissu osseux et/ou de tissu conjonctif, et procede de fabrication

Non-Patent Citations (6)

* Cited by examiner, † Cited by third party
Title
CAO, J. ET AL: "Processing of porous, Ti02-ceramics from biological preforms", CERAMICS INTERNATIONAL, vol. 30, 2004, pages 1971 - 1974, XP004534378 *
GHANEM, H. ET AL: "Processing of biomorphic porous Ti02 ceramics by chemical vapor infiltration and reaction (CVI-R) technique", JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, vol. 27, 2007, pages 3433 - 3438, XP022086565 *
HAUGEN, HAVARD ET AL: "Ceramic Ti02-foams: characterisation of a potential scaffold", JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, vol. 24, 2004, pages 661 - 668, XP004551083 *
ROHANIZADEH, R. ET AL: "Preparation of different forms of titanium oxide on titanium surface: Effects on apatite deposition", JOURNAL OF BIOMEDICAL MATERIALS RESEARCH - PART A, vol. 71, no. 2, 2004, pages 343 - 352, XP003026044 *
TAKEMOTO, MITSURU ET AL: "A porous bioactive titanium implant for spinal interbody fusion: an experimental study using a canine model", JOURNAL OF NEUROSURGERY: SPINE, vol. 7, no. 4, 2007, pages 435 - 443, XP003026045 *
YUN, YOUNG HOON ET AL.: "Surface Modification of Sericite Using Ti02 Powders Prepared by Alkoxide Hydrolysis: Whiteness and SPF Indices of Ti02- Adsorbed Sericite", JOURNAL OF MATERIALS SYNTHESIS AND PROCESSING, vol. 10, no. 6, November 2002 (2002-11-01), pages 359 - 365, XP003026043 *

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110008754A1 (en) * 2009-07-10 2011-01-13 Bassett Jeffrey A Patient-Specific Implants With Improved Osseointegration
US9707058B2 (en) * 2009-07-10 2017-07-18 Zimmer Dental, Inc. Patient-specific implants with improved osseointegration
US10265189B2 (en) 2016-09-13 2019-04-23 Warsaw Orthopedic, Inc. Interbody spinal fusion device
US10973651B2 (en) 2016-09-13 2021-04-13 Warsaw Orthopedic, Inc. Interbody spinal fusion device
US11666452B2 (en) 2016-09-13 2023-06-06 Warsaw Orthopedic, Inc. Interbody spinal fusion device
US12279965B2 (en) 2017-09-08 2025-04-22 Xtant Medical Holdings, Inc. Intervertebral implants, instruments, and methods

Similar Documents

Publication Publication Date Title
US12048610B2 (en) Osseointegrative surgical implant and implant surgical kit
US20200275998A1 (en) Porous implant device with improved core
Duraccio et al. Biomaterials for dental implants: current and future trends
CA2673379C (fr) Echafaudage d'oxyde metallique
JP2580677B2 (ja) 人工歯根
US9744007B2 (en) Expandable bone implant
US8454707B2 (en) Biomedical implantable material and methods of producing the same
EP2309945A1 (fr) Implant modulaire avec partie poreuse assujettie
US20060246399A1 (en) Two-part ceramic dental implant
JP2007530202A (ja) 骨組織再生用生物活性人工器官装置の製造方法およびその人工器官装置
EP2750725B1 (fr) Implant dentaire, implant vasculaire et implant tissulaire fabriqués en une structure poreuse tridimensionnelle de polytétrafluorothylène
US20090215007A1 (en) Dental implant with porous trabecular structure
EP2533819B1 (fr) Procédé de préparation d'un corps doté d'une surface ostéoïntégrative
JP2015529526A (ja) 皮質壁を有する足場
WO2009154560A1 (fr) Bloc poreux en dioxyde de titane
US20120310357A1 (en) Porous titanium
CN113069229A (zh) 一种具有多段结构的3d打印根骨植入体
JP2810965B2 (ja) 積層体、人工歯根および歯冠
WO2009004069A1 (fr) Implant dentaire poreux
RU157440U1 (ru) Имплантат для имплантации в костную ткань
RU131607U1 (ru) Внутричелюстной металлический имплантат
Chatterjee et al. Osseointegration–An Overview
Kutty MANUSCRIPT ONE
JPH1094549A (ja) 歯科用インプラント材

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09766950

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 09766950

Country of ref document: EP

Kind code of ref document: A1