WO2009039579A1 - Récupération d'acide à partir de sulfates métalliques - Google Patents

Récupération d'acide à partir de sulfates métalliques Download PDF

Info

Publication number
WO2009039579A1
WO2009039579A1 PCT/AU2008/001430 AU2008001430W WO2009039579A1 WO 2009039579 A1 WO2009039579 A1 WO 2009039579A1 AU 2008001430 W AU2008001430 W AU 2008001430W WO 2009039579 A1 WO2009039579 A1 WO 2009039579A1
Authority
WO
WIPO (PCT)
Prior art keywords
sulfuric acid
process according
nickel
metal sulfate
solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/AU2008/001430
Other languages
English (en)
Inventor
Eric Girvan Roche
Jaidev Prasad
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BHP SSM Indonesia Holdings Pty Ltd
Original Assignee
BHP Billiton SSM Development Pty Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from AU2007905266A external-priority patent/AU2007905266A0/en
Application filed by BHP Billiton SSM Development Pty Ltd filed Critical BHP Billiton SSM Development Pty Ltd
Publication of WO2009039579A1 publication Critical patent/WO2009039579A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un procédé pour la récupération d'acide sulfurique à partir d'un sulfate métallique en solution. Ce procédé comprend les étapes qui consistent : a) à à utiliser une source d'un sulfate métallique en solution; b) à convertir le sulfate métallique en solution en sel de sulfate métallique cristallisé; c) à calciner le sel de sulfate métallique cristallisé afin d'obtenir l'oxyde métallique et le gaz de dioxyde de soufre correspondants; et d) à générer de l'acide sulfurique.
PCT/AU2008/001430 2007-09-26 2008-09-26 Récupération d'acide à partir de sulfates métalliques Ceased WO2009039579A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
AU2007905266A AU2007905266A0 (en) 2007-09-26 Acid Recovery from Metal Sulfates
AU2007905266 2007-09-26

Publications (1)

Publication Number Publication Date
WO2009039579A1 true WO2009039579A1 (fr) 2009-04-02

Family

ID=40510674

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/AU2008/001430 Ceased WO2009039579A1 (fr) 2007-09-26 2008-09-26 Récupération d'acide à partir de sulfates métalliques

Country Status (1)

Country Link
WO (1) WO2009039579A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102323264A (zh) * 2011-09-30 2012-01-18 中国冶金矿业鞍山冶金设计研究院有限责任公司 一种测定铁矿石中硫含量的方法及装置
CN103773951A (zh) * 2014-01-21 2014-05-07 江苏仁欣化工股份有限公司 含硫酸、盐酸的混合废酸浸出红土镍矿回收镍钴的方法
CN104313320A (zh) * 2014-10-23 2015-01-28 昆明绩驰环保科技有限公司 一种锌电解液中锌镁的强酸饱和结晶分离方法
CN104555947A (zh) * 2015-01-28 2015-04-29 重庆市淡水河谷矿业有限公司 一种资源化利用电解锰渣的方法及系统
CN113460972A (zh) * 2021-07-22 2021-10-01 镇江润晶高纯化工科技股份有限公司 一种超高纯净半导体级硫酸的制备方法
WO2023056505A1 (fr) * 2021-10-05 2023-04-13 Commonwealth Scientific And Industrial Research Organisation Procédé de récupération de métaux de valeur à partir de minerai latéritique contenant du nickel et du cobalt
CN117258533A (zh) * 2023-09-15 2023-12-22 北京予知环境工程有限公司 干法脱硫剂及其组合物、制备方法、应用

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4092401A (en) * 1976-01-09 1978-05-30 Compagnie Royale Asturienne Des Mines Process for reutilization of iron chlorides in aqueous solution
US4225573A (en) * 1979-01-12 1980-09-30 Idemitsu Kosan Company Limited Process for reductive calcining of magnesium sulfate
DE4437550A1 (de) * 1993-10-29 1995-05-04 Bayer Ag Verfahren zur Rückgewinnung von Schwefelsäure aus metallsulfathaltigen Gebrauchtsäuren
JPH10109013A (ja) * 1996-10-04 1998-04-28 Hisaji Koyama 酸化マグネシウム再生硫酸回収型排煙脱硫装置
WO1999059915A1 (fr) * 1998-05-14 1999-11-25 University Of Waterloo Catalyseur et procede d'oxydation de dioxyde de soufre
US6447738B1 (en) * 2000-08-24 2002-09-10 Solv-Ex Corporation Coproducing alumina, iron oxide, and titanium-dioxide from aluminum ore bodies and feedstocks
WO2006043154A1 (fr) * 2004-10-21 2006-04-27 Anglo Operations Limited Lixiviation en presence d'acide chlorhydrique pour l'extraction de metaux de valeur contenus dans le minerai
WO2007070973A1 (fr) * 2005-12-22 2007-06-28 Bhp Billiton Ssm Development Pty Ltd Recuperation d'oxyde de magnesium
WO2007074360A2 (fr) * 2005-11-28 2007-07-05 Anglo Operations Limited Procede de lixiviation en presence d'acide chlorhydrique permettant de recuperer un metal precieux dans un minerai

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4092401A (en) * 1976-01-09 1978-05-30 Compagnie Royale Asturienne Des Mines Process for reutilization of iron chlorides in aqueous solution
US4225573A (en) * 1979-01-12 1980-09-30 Idemitsu Kosan Company Limited Process for reductive calcining of magnesium sulfate
DE4437550A1 (de) * 1993-10-29 1995-05-04 Bayer Ag Verfahren zur Rückgewinnung von Schwefelsäure aus metallsulfathaltigen Gebrauchtsäuren
JPH10109013A (ja) * 1996-10-04 1998-04-28 Hisaji Koyama 酸化マグネシウム再生硫酸回収型排煙脱硫装置
WO1999059915A1 (fr) * 1998-05-14 1999-11-25 University Of Waterloo Catalyseur et procede d'oxydation de dioxyde de soufre
US6447738B1 (en) * 2000-08-24 2002-09-10 Solv-Ex Corporation Coproducing alumina, iron oxide, and titanium-dioxide from aluminum ore bodies and feedstocks
WO2006043154A1 (fr) * 2004-10-21 2006-04-27 Anglo Operations Limited Lixiviation en presence d'acide chlorhydrique pour l'extraction de metaux de valeur contenus dans le minerai
WO2007074360A2 (fr) * 2005-11-28 2007-07-05 Anglo Operations Limited Procede de lixiviation en presence d'acide chlorhydrique permettant de recuperer un metal precieux dans un minerai
WO2007070973A1 (fr) * 2005-12-22 2007-06-28 Bhp Billiton Ssm Development Pty Ltd Recuperation d'oxyde de magnesium

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102323264A (zh) * 2011-09-30 2012-01-18 中国冶金矿业鞍山冶金设计研究院有限责任公司 一种测定铁矿石中硫含量的方法及装置
CN103773951A (zh) * 2014-01-21 2014-05-07 江苏仁欣化工股份有限公司 含硫酸、盐酸的混合废酸浸出红土镍矿回收镍钴的方法
CN104313320A (zh) * 2014-10-23 2015-01-28 昆明绩驰环保科技有限公司 一种锌电解液中锌镁的强酸饱和结晶分离方法
CN104555947A (zh) * 2015-01-28 2015-04-29 重庆市淡水河谷矿业有限公司 一种资源化利用电解锰渣的方法及系统
CN113460972A (zh) * 2021-07-22 2021-10-01 镇江润晶高纯化工科技股份有限公司 一种超高纯净半导体级硫酸的制备方法
WO2023056505A1 (fr) * 2021-10-05 2023-04-13 Commonwealth Scientific And Industrial Research Organisation Procédé de récupération de métaux de valeur à partir de minerai latéritique contenant du nickel et du cobalt
CN117258533A (zh) * 2023-09-15 2023-12-22 北京予知环境工程有限公司 干法脱硫剂及其组合物、制备方法、应用

Similar Documents

Publication Publication Date Title
AU2021218169B2 (en) Recovery of Lithium from Silicate Minerals
CN104520237B (zh) 处理飞灰的方法
CN104302791B (zh) 用于处理赤泥的方法
JP4142848B2 (ja) マグネシウム金属、塩化マグネシウム、マグネサイトおよびマグネシウムをベースとした生成物の単離並びに製造方法
CN113025832B (zh) 一种红土镍矿提取镍同时矿化co2的方法
JP5374042B2 (ja) 鉱石からの有価金属回収のための塩酸存在下での浸出方法
US20090148366A1 (en) Magnesium Oxide Recovery
WO2009039579A1 (fr) Récupération d'acide à partir de sulfates métalliques
WO2013037054A1 (fr) Procédés de préparation d'alumine et de divers autres produits
NO874820L (no) Fremstilling av mg-metall.
AU2014370454B2 (en) Method of producing metal carbonate from an ultramafic rock material
CN101525143A (zh) 一种由红土镍矿制备氧化镁、二氧化硅及氧化镍产品的方法
Gao et al. CO2 mineral sequestration and nickel recovery from laterite ore by using waste copperas
CN101760641B (zh) 从硫酸镁溶液中回收镁的工艺
WO2018218294A1 (fr) Procédé de production d'oxyde de magnésium à partir de cendres volantes ou de scories alcalines
WO2015042692A1 (fr) Procédés de préparation d'alumine et de divers autres produits
KR20070099669A (ko) 산화마그네슘의 제조 방법
CN101760637B (zh) 含镁矿石的浸出工艺
US8152895B2 (en) Production of magnesium metal
Rivera et al. Carbon dioxide as a sustainable reagent in circular hydrometallurgy
Ho et al. Applications of CO2 mineralization for carbon capture, utilization, and storage
CN103097558B (zh) 用于处理液体流出物和回收金属的方法
AU2012297573B2 (en) Method for the recovery of magnesium sulphate and production of magnesium oxide
CN115161478B (zh) 利用含硅镁矿物中的MgO/SiO2通过碳原位高温还原反应提取金属镁的方法
CN101392321A (zh) 微波还原焙烧-赤铁矿沉淀转化法处理含镍红土矿的方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 08800065

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 08800065

Country of ref document: EP

Kind code of ref document: A1