WO2009043376A1 - Système d'isolation électrique à résistance accrue au claquage électrique - Google Patents

Système d'isolation électrique à résistance accrue au claquage électrique Download PDF

Info

Publication number
WO2009043376A1
WO2009043376A1 PCT/EP2007/060504 EP2007060504W WO2009043376A1 WO 2009043376 A1 WO2009043376 A1 WO 2009043376A1 EP 2007060504 W EP2007060504 W EP 2007060504W WO 2009043376 A1 WO2009043376 A1 WO 2009043376A1
Authority
WO
WIPO (PCT)
Prior art keywords
filler material
component
electrical insulation
insulation system
pretreated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2007/060504
Other languages
English (en)
Inventor
Martin Carlen
Xavier Kornmann
Andrej Krivda
Felix Greuter
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ABB Research Ltd Switzerland
Original Assignee
ABB Research Ltd Switzerland
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ABB Research Ltd Switzerland filed Critical ABB Research Ltd Switzerland
Priority to EP07820881A priority Critical patent/EP2195813A1/fr
Priority to CN200780100938A priority patent/CN101816049A/zh
Priority to PCT/EP2007/060504 priority patent/WO2009043376A1/fr
Publication of WO2009043376A1 publication Critical patent/WO2009043376A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Cette invention se rapporte à un système d'isolation électrique à résistance accrue au claque électrique, ledit système d'isolation électrique comprenant un composant polymère durci dans lequel sont incorporés un matériau de remplissage classique et un matériau de remplissage prétraité sélectionné. Dans ce système, (a) le composant polymère durci est sélectionné parmi des systèmes à résine époxy, des polyesters, des polyamides, du polytérephtalate de butylène, des polyuréthanes et du polydicyclopentadiène ; (b) le matériau de remplissage classique est un matériau de remplissage connu ayant une granulométrie moyenne comprise dans la plage de 1 µm à 500 µm, présent en une quantité comprise dans la plage de 40 % à 65 % en poids, calculée par rapport au poids total du système d'isolation ; et (c) le matériau de remplissage prétraité sélectionné est sélectionné parmi la silice, le quartz, ou un silicate, ou est un mélange de ces composés, avec une granulométrie moyenne comprise dans la plage de 1 µm à 500 µm, ledit matériau de remplissage sélectionné ayant été prétraité avec un composé d'intercalation et ledit matériau de remplissage prétraité étant présent en une quantité de 1 % à 30 % en poids, calculée par rapport au poids du matériau de remplissage classique présent dans le système d'isolation.
PCT/EP2007/060504 2007-10-03 2007-10-03 Système d'isolation électrique à résistance accrue au claquage électrique Ceased WO2009043376A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
EP07820881A EP2195813A1 (fr) 2007-10-03 2007-10-03 Système d'isolation électrique à résistance accrue au claquage électrique
CN200780100938A CN101816049A (zh) 2007-10-03 2007-10-03 具有提高的电击穿强度的电绝缘体系
PCT/EP2007/060504 WO2009043376A1 (fr) 2007-10-03 2007-10-03 Système d'isolation électrique à résistance accrue au claquage électrique

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/EP2007/060504 WO2009043376A1 (fr) 2007-10-03 2007-10-03 Système d'isolation électrique à résistance accrue au claquage électrique

Publications (1)

Publication Number Publication Date
WO2009043376A1 true WO2009043376A1 (fr) 2009-04-09

Family

ID=39495576

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2007/060504 Ceased WO2009043376A1 (fr) 2007-10-03 2007-10-03 Système d'isolation électrique à résistance accrue au claquage électrique

Country Status (3)

Country Link
EP (1) EP2195813A1 (fr)
CN (1) CN101816049A (fr)
WO (1) WO2009043376A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102254648A (zh) * 2010-03-26 2011-11-23 Abb研究有限公司 电绝缘和绝缘产品的生产
CN102725802A (zh) * 2010-02-03 2012-10-10 Abb研究有限公司 电绝缘体系
WO2012095321A3 (fr) * 2011-01-14 2012-11-22 Lothar Ginzel Dispositif pour améliorer les propriétés électriques d'un revêtement d'un conducteur ou analogue au moyen de matériaux isolants, et procédé d'utilisation de ce dispositif
CN103021590A (zh) * 2012-12-20 2013-04-03 揭东县白石塑料厂 工程塑料绝缘子及其制造方法
US20150080508A1 (en) * 2012-04-20 2015-03-19 The Board Of Regents Of The University Of Texas System Thermal barrier mixtures and uses thereof
EP3671763A1 (fr) * 2018-12-20 2020-06-24 Nexans Câble électrique comprenant au moins une couche réticulée
CN119307031A (zh) * 2024-12-16 2025-01-14 赣州祺琳新材料有限公司 一种耐高温高压电力管及其制备方法

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103424418B (zh) * 2013-08-15 2016-02-17 国家电网公司 一种盆式绝缘子线状缺陷数字射线检测试块及制作方法
CN103694636B (zh) * 2013-12-10 2015-12-09 中国科学院过程工程研究所 一种电气绝缘环氧树脂组合物、制备方法及其用途
CN106117859A (zh) * 2016-08-04 2016-11-16 陈毅忠 一种可瓷化耐火电器开关材料的制备方法
CN106242582B (zh) * 2016-08-15 2021-09-24 董琳维 一种表面耐磨的绝缘子及其制造方法
CN106751467A (zh) * 2016-11-23 2017-05-31 哈尔滨理工大学 一种环氧树脂基微纳米复合材料及其制备方法
CN110283542A (zh) * 2019-07-02 2019-09-27 南通东泰电工器材有限公司 电机线圈制造用填充绝缘材料及其制备方法
CN115159537A (zh) * 2022-08-08 2022-10-11 中国轻工业陶瓷研究所 一种纳米高岭土的制备方法

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6238790B1 (en) * 1999-05-26 2001-05-29 Siemens Westinghouse Power Corporation Superdielectric high voltage insulation for dynamoelectric machinery
WO2006008422A1 (fr) * 2004-07-13 2006-01-26 Areva T & D Sa Procede de fabrication d'un isolateur pour une utilisation en haute tension

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ATE447763T1 (de) * 2002-08-02 2009-11-15 Abb Research Ltd Fester isolator und verfahren zur herstellung eines festen isolators
JP2004277735A (ja) * 2003-02-27 2004-10-07 Sanyo Chem Ind Ltd 硬化性樹脂組成物およびその硬化物
EP1851774A4 (fr) * 2005-02-09 2010-07-14 Abb Research Ltd Matiere de caoutchouc de silicone
CN101189686B (zh) * 2005-05-04 2013-01-02 Abb研究有限公司 电绝缘材料，电力设备和生产电绝缘材料的方法

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6238790B1 (en) * 1999-05-26 2001-05-29 Siemens Westinghouse Power Corporation Superdielectric high voltage insulation for dynamoelectric machinery
WO2006008422A1 (fr) * 2004-07-13 2006-01-26 Areva T & D Sa Procede de fabrication d'un isolateur pour une utilisation en haute tension

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102725802A (zh) * 2010-02-03 2012-10-10 Abb研究有限公司 电绝缘体系
CN102254648A (zh) * 2010-03-26 2011-11-23 Abb研究有限公司 电绝缘和绝缘产品的生产
WO2012095321A3 (fr) * 2011-01-14 2012-11-22 Lothar Ginzel Dispositif pour améliorer les propriétés électriques d'un revêtement d'un conducteur ou analogue au moyen de matériaux isolants, et procédé d'utilisation de ce dispositif
US20150080508A1 (en) * 2012-04-20 2015-03-19 The Board Of Regents Of The University Of Texas System Thermal barrier mixtures and uses thereof
US10280369B2 (en) * 2012-04-20 2019-05-07 Board Of Regents Of The University Of Texas System Thermal barrier mixtures and uses thereof
CN103021590A (zh) * 2012-12-20 2013-04-03 揭东县白石塑料厂 工程塑料绝缘子及其制造方法
EP3671763A1 (fr) * 2018-12-20 2020-06-24 Nexans Câble électrique comprenant au moins une couche réticulée
FR3090986A1 (fr) * 2018-12-20 2020-06-26 Nexans Câble électrique comprenant au moins une couche réticulée
CN119307031A (zh) * 2024-12-16 2025-01-14 赣州祺琳新材料有限公司 一种耐高温高压电力管及其制备方法

Also Published As

Publication number Publication date
EP2195813A1 (fr) 2010-06-16
CN101816049A (zh) 2010-08-25

Similar Documents

Publication Publication Date Title
EP2195813A1 (fr) Système d'isolation électrique à résistance accrue au claquage électrique
EP2532010B1 (fr) Systeme d'isolation electrique
KR20090033226A (ko) 경화 가능한 에폭시 수지 조성물
EP2230267B1 (fr) Procédé de préparer des résines époxy durcissable
US8399577B2 (en) Curable epoxy resin composition
EP1978049B1 (fr) Composition de résine époxy durcissable
US8545977B2 (en) Polymer concrete electrical insulation
RU2528845C2 (ru) Прямая заливка
US20110027532A1 (en) Surface modified electrical insulation system
WO2013123648A1 (fr) Composition époxy durcissable comprenant de la fibre de verre broyée
CN102482400B (zh) 环氧树脂组合物
JP2005251543A (ja) 高電圧機器用の絶縁樹脂組成物、絶縁材料とその製造方法、および絶縁構造体
JP5659030B2 (ja) 高電圧機器用絶縁樹脂組成物の製造方法
EP1635364A1 (fr) Enroulement encapsulé d'un transformateur de type sec

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 200780100938.9

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07820881

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2007820881

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 1803/CHENP/2010

Country of ref document: IN

NENP Non-entry into the national phase

Ref country code: DE