WO2008025998A2 - Structures en verre - Google Patents

Structures en verre Download PDF

Info

Publication number
WO2008025998A2
WO2008025998A2 PCT/GB2007/003308 GB2007003308W WO2008025998A2 WO 2008025998 A2 WO2008025998 A2 WO 2008025998A2 GB 2007003308 W GB2007003308 W GB 2007003308W WO 2008025998 A2 WO2008025998 A2 WO 2008025998A2
Authority
WO
WIPO (PCT)
Prior art keywords
glass
temperature
piece
regions
stub
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/GB2007/003308
Other languages
English (en)
Other versions
WO2008025998A3 (fr
Inventor
Suzanne Furkert
John Rowden
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
University of Bristol
Original Assignee
University of Bristol
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from GB0617320A external-priority patent/GB0617320D0/en
Priority claimed from GB0617321A external-priority patent/GB0617321D0/en
Application filed by University of Bristol filed Critical University of Bristol
Publication of WO2008025998A2 publication Critical patent/WO2008025998A2/fr
Publication of WO2008025998A3 publication Critical patent/WO2008025998A3/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Selon un aspect, l'invention concerne un procédé d'assemblage d'au moins deux pièces de verre, le procédé consistant à disposer les deux pièces de verre dans une structure, la première pièce de verre présentant une zone qui doit être assemblée avec une zone de la seconde pièce de verre, les première et seconde pièces de verre étant agencées de sorte que les zones à assembler sont adjacentes l'une à l'autre; à chauffer les pièces de verre à une température qui est comprise entre le point de trempe et le point de ramollissement du verre; à appliquer une chaleur supplémentaire simultanément sur toutes les parties des zones qui doivent être assemblées, de sorte que la température desdites zones est élevée de façon à être égale ou supérieure au point de ramollissement du verre et que les zones s'assemblent entre elles, et à éliminer la chaleur supplémentaire afin de permettre aux zones des pièces de verre de refroidir à une température qui est comprise entre le point de trempe et le point de ramollissement du verre.
PCT/GB2007/003308 2006-09-01 2007-09-03 Structures en verre Ceased WO2008025998A2 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
GB0617321.5 2006-09-01
GB0617320.7 2006-09-01
GB0617320A GB0617320D0 (en) 2006-09-01 2006-09-01 A glass to glass sealing method
GB0617321A GB0617321D0 (en) 2006-09-01 2006-09-01 Forming a tubulation in a glass surface

Publications (2)

Publication Number Publication Date
WO2008025998A2 true WO2008025998A2 (fr) 2008-03-06
WO2008025998A3 WO2008025998A3 (fr) 2008-07-31

Family

ID=38657092

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB2007/003308 Ceased WO2008025998A2 (fr) 2006-09-01 2007-09-03 Structures en verre

Country Status (1)

Country Link
WO (1) WO2008025998A2 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017027788A1 (fr) * 2015-08-13 2017-02-16 Corning Incorporated Procédé de fabrication d'additif et article manufacturé

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
NL228634A (fr) * 1957-06-18
US3078692A (en) * 1958-05-12 1963-02-26 Libbey Owens Ford Glass Co Process and apparatus for forming multiple sheet glazing units
JP2000344537A (ja) * 1999-06-01 2000-12-12 Nippon Sheet Glass Co Ltd ガラス構造体の製造方法及び該方法により製造されたガラス構造体
DE10053402B4 (de) * 2000-10-24 2008-04-17 Institut für Fügetechnik und Werkstoffprüfung GmbH Verfahren und Vorrichtung zum thermischen Fügen von Bauteilen aus silikatischen Werkstoffen, Silikat-Verbundwerkstoffen und Silikat-Kompositwerkstoffen

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017027788A1 (fr) * 2015-08-13 2017-02-16 Corning Incorporated Procédé de fabrication d'additif et article manufacturé
US11053154B2 (en) 2015-08-13 2021-07-06 Corning Incorporated Additive manufacturing processes and manufactured article
US12221374B2 (en) 2015-08-13 2025-02-11 Corning Incorporated Additive manufacturing processes and manufactured article

Also Published As

Publication number Publication date
WO2008025998A3 (fr) 2008-07-31

Similar Documents

Publication Publication Date Title
US5897927A (en) Seal for vacuum devices and methods for making same
US7305853B2 (en) Method of manufacturing a glass panel
EP1571134A1 (fr) Procede de production d'un panneau en verre sous vide et panneau en verre sous vide produit au moyen de ce procede
EP1741510B1 (fr) Procédé de soudage laser verre sur verre ; Anode et enveloppe sous vide fabriquée au moyen de ce procédé; dispositif d'affichage à émetteur d'électrons comprenant une telle enveloppe sous vide
JP4291883B2 (ja) 平面パネルディスプレー
WO2001012942A1 (fr) Fabrication de panneau de verre sous vide comportant un getter
JP2010170873A (ja) 気密容器及び画像表示装置の製造方法
US5984748A (en) Method for fabricating a flat panel device
JP2010170872A (ja) 気密容器及び画像表示装置の製造方法
JP2010170871A (ja) 気密容器及び画像表示装置の製造方法
WO2008025998A2 (fr) Structures en verre
JP3667256B2 (ja) 電子源の製造装置
KR100799092B1 (ko) 디스플레이 디바이스들을 밀봉하는 방법
EP0042003B1 (fr) Procede de mise en forme d'une entretoise fusible pour panneau d'affichage a plasma
US7165424B2 (en) Method of joining glass plates
JP2000260304A (ja) フラットパネルディスプレイ
JP3422175B2 (ja) ガス放電パネルの製造方法
JP3750250B2 (ja) 電界放射型ディスプレイ及びこの製造方法
KR100701112B1 (ko) 화상 표시 장치 및 그 제조 방법
WO2005015597A1 (fr) Procede de coupe-soudure de tubes a lame de verre
JP2000195426A (ja) 封止方法及び密封容器と画像表示装置及び真空排気装置
AU759904B2 (en) Evacuated glass panel having a getter
JP3385907B2 (ja) プラズマディスプレイパネルの製造方法
KR100416142B1 (ko) 플라즈마 디스플레이 패널의 조립 방법
JP2001313343A (ja) 気密容器及びその製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07804114

Country of ref document: EP

Kind code of ref document: A2

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 07804114

Country of ref document: EP

Kind code of ref document: A2