WO2008004368A1 - Prefilter - Google Patents

Prefilter Download PDF

Info

Publication number
WO2008004368A1
WO2008004368A1 PCT/JP2007/058074 JP2007058074W WO2008004368A1 WO 2008004368 A1 WO2008004368 A1 WO 2008004368A1 JP 2007058074 W JP2007058074 W JP 2007058074W WO 2008004368 A1 WO2008004368 A1 WO 2008004368A1
Authority
WO
WIPO (PCT)
Prior art keywords
prefilter
coating composition
functional group
curing agent
group
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2007/058074
Other languages
English (en)
French (fr)
Inventor
Taro Kuroda
Yoshio Okamoto
Masaru Nagato
Masahiko Maeda
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Daikin Industries Ltd
Original Assignee
Daikin Industries Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Daikin Industries Ltd filed Critical Daikin Industries Ltd
Publication of WO2008004368A1 publication Critical patent/WO2008004368A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Description

明 細 書
プレフィルタ 技術分野
[0001] 本発明は、空気調和機や空気清浄機などの空気調整機に用いられて!/、るプレフィ ルタに関する。
背景技術
[0002] 空気調和機や空気清浄機などの空気調整機の室内の空気の吸い込み箇所には、 空気中の埃や汚れが空気調整機内に取り込まれないように網力 なるプレフィルタが 設けられている。このプレフィルタは通常、合成樹脂製の網と支持枠とから構成され ている。
[0003] 室内の埃や汚れは、綿埃、砂塵、泥、タバコの煙などの不溶性の埃のほか、タバコ のャ-などの水溶性の汚れ、油煙、煤などの油溶性の汚れなど、多岐に亘つており、 プレフィルタに付着する付着物はこれらが複合した形となって 、る。こうした付着した 汚れは光や空気中の酸素などにより変質し、どんどん除去しにくい汚れとなっていく
[0004] また、プレフィルタは網目の大きさ（メッシュ）により、その孔を通過しないものを捕捉 するものであるが、空気中には微細な汚れ (タバコの煙、煤、砂塵など）があり、それら も集塵するために、網を帯電させ、電気的に捕捉することも行われている。その 1つの 方法として、網を構成する繊維の外表面に帯電性に富むフッ素榭脂をコーティング することが提案されており、水洗 、も可能になったと記載されて 、る（特開平 08 - 22 4413号公報、特開平 08— 224414号公報)。
[0005] さらに特開 2006— 122871号公報には、油分を含んだ塵埃の付着を防止するた めにノインダーなどを用いてフッ素榭脂をコーティングすることが提案されて！、る。
[0006] し力し、力力る特開平 08— 224413号公報、特開平 08— 224414号公報には単 にフッ素榭脂をコーティングするとしか記載されておらず、その具体的な解決策は示 されていない。
[0007] たとえば、フッ素榭脂の被膜を形成するには通常は高温での焼成が必要である力 フッ素榭脂よりも耐熱性に乏しい合成樹脂で作製されたプレフィルタにどのようにフッ 素榭脂の被膜を形成させるの力 どのようなフッ素榭脂を用いるのかなど、実施する ために必要な教示がない。
[0008] さらに、一般にフッ素榭脂は他の合成樹脂への密着性がわるぐ単にフッ素榭脂を 付着しただけでは、頻繁な着脱、ブラシでの擦り洗いや拭き取り作業で剥離してしま い、耐久性に問題がある。
[0009] また特開 2006— 122871号公報においてもフッ素榭脂という単語しか記載されて おらず、バインダーが別途必要なことから、フッ素榭脂粒子をプレフィルタの網の合 成榭脂と接着性のょ ヽバインダー中に分散させて被膜を形成することを想定して!/、る ものと考えられる。
[0010] しかし、こうしたフッ素榭脂粒子の分散被膜ではフッ素榭脂の効果を効率的に活か すことは難しぐまた、フッ素榭脂はバインダーとの密着性もわるいので、フッ素榭脂 粒子の脱落も生じ、耐久性に問題が残る。
発明の開示
[0011] 本発明の課題は、従来のプレフィルタと同様な素材のプレフィルタであっても、その 網の表面に耐久性に富み、さらに汚染除去性にも優れた特定の含フッ素ポリマーの 被膜が形成されている空気調整機用のプレフィルタを提供することにある。
[0012] 本発明は、合成樹脂製の網を有する空気調整機用のプレフィルタであって、該網 の表面の一部または全部に含フッ素ポリマーを含む塗料組成物を網の表面に塗布 し硬化させて得られる被膜を有しており、該含フッ素ポリマーを含む塗料組成物が、 ( A)官能基 Xを含有する含フッ素ポリマー、（B)防汚成分および (C)硬化剤を含む組 成物であって、防汚成分 (B)が（B1)官能基 Xおよび Zまたは硬化剤 (C)と反応し得 る官能基 Y1を有する液状のポリジアルキルシロキサン、または（B2)官能基 Xおよび Zまたは硬化剤 (C)と反応し得る官能基 Y2を有する液状のフルォロポリエーテルで ある常温硬化性の塗料組成物であるプレフィルタに関する。
図面の簡単な説明
[0013] [図 1]本発明の空気調整機用のプレフィルタの概略斜視図である。
発明を実施するための最良の形態 [0014] 本発明の合成樹脂製の網を有する空気調整機用のプレフィルタは、該網の表面の 一部または全部に特定の含フッ素ポリマーを含む塗料組成物を網の表面に塗布し 硬化させて得られる被膜を有して ヽる点に特徴を有する。
[0015] この含フッ素ポリマーを含む塗料組成物は、（A)官能基 Xを含有する含フッ素ポリ マー、（B)防汚成分および (C)硬化剤を含む組成物であって、防汚成分 (B)が (B1) 官能基 Xおよび Zまたは硬化剤 (C)と反応し得る官能基 Y1を有する液状のポリジァ ルキルシロキサン、または（B2)官能基 Xおよび Zまたは硬化剤 (C)と反応し得る官 能基 Y2を有する液状のフルォロポリエーテルである常温硬化性の塗料組成物である
[0016] この塗料組成物では、含フッ素ポリマー (A)および防汚成分 (B)の 、ずれもが撥水 撥油性であり、形成される被膜も撥水撥油性になる。
[0017] プレフィルタの表面を撥水撥油性にすることにより水溶性汚れと油性汚れの両方を 埃側に付着させ、比較的大きな埃を除去することで、埃だけではなく水溶性汚れと油 性汚れまでも除去できる。その理由は明確ではないが、一般に、埃の主成分は各種 の繊維からなる綿埃と、珪酸、酸化鉄、酸化アルミニウムなどを主成分とする砂塵で あり、撥水性および撥油性の点からはいずれも中間的な性状である。そのときプレフ ィルタの表面を撥水性と撥油性の 、ずれにぉ 、ても高 ヽ (水も油もはじく）状態にす ると、その撥水性が故に水溶性汚れはプレフィルタ表面よりも埃側に親和し、埃に付 着する。同じぐ油性汚れはプレフィルタ表面の撥油性が故にプレフィルタ表面よりも 埃側に親和し、埃に付着する。
[0018] 本発明において、被膜の撥水撥油性とは、被膜表面の対水接触角および対油接 触角のいずれもが高い性質をいう。具体的には、 80度以上の対水接触角と 35度以 上の対油接触角を有する被膜であることが、水溶性の汚れおよび油溶性の汚れのい ずれもが被膜と親和性が悪く (被膜に付着することがなく）、したがって綿埃や砂塵な どの方に吸収される点力 好ましい。対水接触角および対油接触角の測定方法につ いては後述する。
[0019] さらに好ましい対水接触角は、水性汚れ付着防止性がさらに優れることから 90度以 上、特に 100度以上である。 [0020] さらに好ましい対油接触角は、油汚れ付着防止性がさらに優れることから 45度以上 である。
[0021] また、本発明における被膜では、防汚成分 (B)が官能基の働き (反応）により、硬化 剤 (C)を介して含フッ素ポリマー (A)と強固に結合される。したがって、防汚成分 (B) が被膜から脱落することもなぐ耐久性に富むものになる。
[0022] 力かる含フッ素ポリマーを含む塗料組成物としては、たとえば国際公開第 2004/0
67658号パンフレットに記載されている塗料組成物が具体例、好ましい範囲とともに 例示できる。
[0023] そのなかでも、室内の空気の調整用である空気調整機用などの榭脂製品のプレフ ィルタには、塗料組成物の含フッ素ポリマー (A)が有する官能基 Xとして、水酸基、力 ルボキシル基および Zまたはエポキシ基力 硬化性、プレフィルタの網への密着性 が良好な点で好ましい。
[0024] また、防汚成分 (B)としては、ポリジアルキルシロキサン (B1)が撥水性が良好な点 力 好ましぐポリジアルキルシロキサン（B1)が有する官能基 Y1としては、水酸基、ァ ミノ基および Zまたはエポキシ基力 硬化性、プレフィルタの網への密着性が良好な 点から好ましい。
[0025] 硬化剤 (C)としては、イソシァネートイ匕合物、アミノィ匕合物および Zまたはエポキシ 化合物が、硬化性、プレフィルタの網への密着性が良好な点力 好ましい。
[0026] これらのうち特に、含フッ素ポリマー (A)が有する官能基 Xが水酸基であり、防汚成 分 (B)が有する官能基 Y1または Y2が水酸基またはアミノ基であり、硬化剤 (C)力 Sイソ シァネートイ匕合物である塗料組成物力 特に硬化性、プレフィルタの網への密着性 に優れる点力も好ましい。
[0027] 具体的な好ま 、含フッ素ポリマー (A)としては、たとえばテトラフルォロエチレン（ TFE) Zアルキルビュルエーテル Zヒドロキシブチルビ-ルエーテル（HBVE)系共 重合体、 TFEZアルキルビュルエステル ZHBVE系共重合体、クロ口トリフルォロェ チレン（CTFE) Zアルキルビュルエーテル ZHBVE系共重合体、 TFEZアルキル ビュルエーテル Zマレイン酸系共重合体、 CTFEZアルキルビュルエーテル Zマレ イン酸系共重合体などの共重合体があげられるが、これらに限定されるものではない 。これらのうち特に TFEZアルキルビュルエーテル ZHBVE系共重合体、 TFEZァ ルキルビニルエステル ZHBVE系共重合体力 さらに防汚性、耐油性、硬化剤相溶 性が良好な点力も好まし 、。
[0028] 防汚成分（B)のうち、ポリジアルキルシロキサン（B1)の好ま U、具体例としては、た とえばァミノ変性ポリジアルキルシロキサン、カルビノール変性ポリジアルキルシロキ サン、カルボキシル変性ポリジアルキルシロキサン、エポキシ変性ポリジアルキルシロ キサンなどがあげられ、特にアミノ変性ポリジアルキルシロキサン力 さらに硬化性が 良好な点力も好ましい。
[0029] 防汚成分 (B)のうち官能基 Xおよび Zまたは硬化剤 (C)と反応し得る官能基 Y2を 有する液状のフルォロポリエーテル (B2)の具体例としては、たとえば水酸基、ァミノ 基、エポキシ基、カルボキシル基、チオール基、二トリル基、ヨウ素原子および Zまた は加水分解性アルキルシリケート残基をもったフルォロポリエーテルなどがあげられ る。
[0030] 前記のとおり、防汚成分 (B)としては、ポリジアルキルシロキサン (B1)が好ま U、。
[0031] 防汚成分 (B)の配合量は、含フッ素ポリマー (A)の固形分 100質量部に対して、 0 . 001質量部以上、さらには 0. 01質量部以上、特に 0. 1質量部以上が好ましい。少 なくなりすぎると汚染の付着防止効果や除去性が不充分になる。上限は 30質量部、 さらには 10質量部、特に 3質量部であり、多くなりすぎると塗膜の均一形成が困難に なったり、粘着性がでてきたりする点に配慮する必要が生じてくる。
[0032] 硬化剤 (C)の具体例としては、たとえばイソシァネートイ匕合物、ァミノ化合物および エポキシィ匕合物があげられ、含フッ素ポリマー (A)および防汚成分 (B)が有する官能 基 X、 Y1および Y2との関係で適宜選択する。
[0033] イソシァネートイ匕合物系硬化剤は、含フッ素ポリマー (A)および防汚成分 (B)が有 する官能基 X、 Y1および Y2が水酸基および Zまたはアミノ基である場合に効果的で ある。イソシァネートイ匕合物にはブロックイソシァネートイ匕合物も含まれ、具体例として は、たとえば 2, 4—トリレンジイソシァネート、ジフエ-ルメタン一 4, 4'—ジイソシァネ ート、キシリレンジイソシァネート、イソホロンジイソシァネート、リジンメチルエステルジ イソシァネート、メチルシクロへキシルジイソシァネート、トリメチルへキサメチレンジィ ソシァネート、へキサメチレンジイソシァネート、 n—ペンタン 1, 4ージイソシァネー ト、これらの三量体、これらのァダクト体ゃビユウレット体、これらの重合体で 2個以上 のイソシァネート基を有するもの、また、リジントリイソシァネート（具体的には 2—イソ シアナートェチル 2, 6 ジイソシアナートへキサノエートなど）、さらにはブロック化さ れたイソシァネート類などがあげられる力 これらに限定されるものではな！/、。
[0034] また、加水分解性アルキルシリケート残基を有するイソシァネートイ匕合物も好ましく 使用できる。具体例としては、たとえば OCNC H Si (OCH )
3 6 3 3、 OCNC H Si (OC H
3 6 2
)、 OCNC H Si(OCOCH )、 OCNC H Si (CH ) (OCH )などがあげられる。
5 3 3 6 3 3 3 6 3 3 3
[0035] イソシァネート化合物と含フッ素ポリマー (A)との混合割合は NCOZOH (モル比） で 0. 5〜5. 0力 S好ましく、さらに 0. 8〜1. 5がより好ましい。また、イソシァネートが湿 気硬化タイプの場合は 1. 1〜1. 5が好ましい。
[0036] ァミノ化合物系硬化剤は、含フッ素ポリマー (A)および防汚成分 (B)が有する官能 基 X、 Y1および Y2がカルボキシル基、アミノ基またはエポキシ基である場合に効果的 である。好ましい具体例としては、たとえばメラミン榭脂、尿素樹脂、グアナミン榭脂、 アミンァダクト、ポリアミドなどがあげられる。
[0037] 市販品としては、三井サイテック (株)製のサイメル (商品名）；エアプロダクツ社製の アンカミン (商品名）、ェピリンク (商品名）；ヘンケノレ社製のバーサミン (商品名）、バ 一サミド (商品名）；富士化成工業 (株)製のトーマイド (商品名）、フジキュア一 (商品 名）；第一ゼネラル (株)製のバーサミド (商品名）；ジャパンエポキシレジン (株)製の ェピキュア一 (商品名）；三和化学 (株)製のサンマイド (商品名）；味の素 (株)製のェ ポメート（商品名）などがあげられる。
[0038] エポキシィ匕合物系硬化剤は、含フッ素ポリマー (A)および防汚成分 (B)が有する 官能基 X、 Y1および Y2がカルボキシル基、アミノ基またはエポキシ基である場合に効 果的である。たとえばエポキシ榭脂、エポキシ変性シランカップリング剤などがあげら れ、市販品としてはジャパンエポキシレジン (株)製のェピコート（商品名）、ェピレック (商品名）；カードライト社製のカードライト（商品名）；日本ュニカー (株)製のコートジ ル 1770 (商品名）、 A— 187 (商品名）などがあげられる。
[0039] 硬化剤 (C)の配合量は、含フッ素ポリマー (A)と防汚成分 (B)の官能基 X、 Y1およ ひ Ύ2の合計当量を 1とした場合、 0. 3当量以上、さらには 0. 5当量以上、特に 0. 8 当量以上が好ましい。少なくなりすぎると硬化が不充分になる。上限は 4当量、さらに は 2当量、特に 1. 5当量であり、多くなりすぎると硬化の均一形成や粘着性の増大な どの点に配慮する必要が生じてくる。
[0040] 本発明で用いる塗料組成物は、常温で硬化し得る（常温硬化性)であることが特に 好ましい。常温硬化性とすることで、プレフィルタの網の合成樹脂を劣化させることな く防汚被膜を形成することができる。なお、プレフィルタの網の材料である合成樹脂 の耐熱温度までであれば、加熱して硬化させてもょ 、。
[0041] 本発明に用いる塗料組成物には、各種の他の添加剤を配合してもよ!/ヽ。代表的な 添加剤としては、抗菌剤、光触媒、帯電防止剤、顔料、顔料分散剤、増粘剤、レペリ ング剤、消泡剤、造膜助剤、紫外線吸収剤、艷消し剤、フィラー、コロイダルシリカ、 防カビ剤、シランカップリング剤、皮張り防止剤、酸化防止剤、難燃剤、垂れ防止剤、 防鲭剤、水溶性榭脂 (ポリビニルアルコール、ポリエチレンオキサイドなど）、防腐剤、 凍結防止剤などの塗料用添加剤などがあげられ、本発明の効果を損なわない範囲 で酉己合してもよ ヽ。
[0042] 塗料組成物の形態としては、水性分散型塗料組成物でも、溶剤型塗料組成物でも ょ ヽが、乾燥性が良好な点カゝら溶剤型塗料組成物が好ま ヽ。
[0043] 溶剤型塗料組成物とする場合、有機溶剤としては、たとえばキシレン、トルエンなど の炭化水素系溶剤；酢酸メチル、酢酸ェチル、酢酸ブチルなどのエステル系溶剤； 酢酸エチレングリコールモノメチルエーテル、酢酸プロピレングリコールモノメチルェ 一テル、酢酸プロピレングリコールモノブチルエーテル、ジエチレングリコールジブチ ルエーテル、テトラヒドロフランなどのエーテル系溶剤；メチルェチルケトン、メチルイ ソブチルケトン、アセトンなどのケトン系溶剤； Ν, Ν—ジメチルァセトアミド、 Ν—メチ ルァセトアミド、ァセトアミド、 Ν, Ν—ジメチルホルムアミド、 Ν, Ν—ジェチルホルムァ ミド、 Ν—メチルホルムアミドなどのアミド系溶剤；メタノール、エタノール、イソプロパノ ールなどのアルコール系溶剤；ジメチルスルホキシドなどが例示できる。これらのうち 、特に酢酸ブチル、酢酸プロピレングリコールモノメチルエーテル、酢酸プロピレング リコールモノブチルエーテル、メチルェチルケトン力 溶解性、乾燥性が良好な点か ら好ましい。
[0044] 塗料組成物の固形分濃度としては、通常 1質量％以上、好ましくは 10質量％以上 であり、また 80質量％以下、さらには 50質量％以下であることが好ましい。
[0045] プレフィルタの網を構成する合成樹脂としては、現在使用されているポリプロピレン
、ポリエチレン、ポリアミド、ポリ塩化ビニル、ポリエステル (たとえばポリエチレンテレフ タレート（PET)など）、ポリ塩ィ匕ビユリデンなどでょ 、。
[0046] 以下に特に好ま 、塗料組成物における含フッ素ポリマー (A)、防汚成分 (B)およ び硬化剤 (C)、任意成分 (D)の組合せの具体例を示すが、本発明はこれらに限定さ れるものではない。
[0047] 塗料組成物 1
含フッ素ポリマー (A)：水酸基含有フルォロォレフイン榭脂
防汚成分 (B)：アミノ基含有ポリジアルキルシロキサン
硬化剤 (C)：加水分解性アルキルシリケート残基含有イソシァネート（さらに要すれば ポリイソシァネート）
添加剤（D)：ジブチル錫ジラウレート (DBTDL) (任意）
塗料形態:溶剤型 (溶剤：酢酸プチル、メチルェチルケトン、メチルイソプチルケトン、 酢酸プロピレングリコールモノブチルエーテルなど）
プレフィルタの網の材質：ポリエステル（特に PET)
[0048] 塗料組成物 2
含フッ素ポリマー (A)：フルォロォレフイン樹脂と水酸基含有非フッ素系榭脂とのブレ ンド
防汚成分 (B)：アミノ基含有ポリジアルキルシロキサン
硬化剤 (C)：ポリイソシァネート
添加剤（D)：ジブチル錫ジラウレート (DBTDL) (任意）
塗料形態:溶剤型 (溶剤：酢酸プチル、メチルェチルケトン、メチルイソプチルケトン、 酢酸プロピレングリコールモノブチルエーテルなど）
プレフィルタの網の材質：ポリエステル（特に PET)
[0049] 塗料組成物 3 含フッ素ポリマー (A)：水酸基含有フルォロォレフイン榭脂
防汚成分 (B)：アミノ基含有ポリジアルキルシロキサン
硬化剤（C) :ァミノ化合物
添加剤（D)：パラトルエンスルホン酸
塗料形態:溶剤型 (溶剤：酢酸プチル、メチルェチルケトン、メチルイソプチルケトン、 酢酸プロピレングリコールモノブチルエーテルなど）
プレフィルタの網の材質：ポリエステル（特に PET)
[0050] 塗料組成物 4
榭脂 (A)：カルボキシル基含有フルォロォレフイン榭脂
防汚成分 (B)：アミノ基含有ポリジアルキルシロキサン
硬化剤（C) :ァミノ化合物
添加剤（D)：ジブチル錫ジラウレート (DBTDL) (任意）
塗料形態:溶剤型 (溶剤：酢酸プチル、メチルェチルケトン、メチルイソプチルケトン、 酢酸プロピレングリコールモノブチルエーテルなど）
プレフィルタの網の材質：ポリアミド
[0051] 本発明のプレフィルタは空気調整機用のプレフィルタである。空気調整機としては、 家庭用か業務用かを問わず、空気調和機、空気清浄機、除湿機、加湿器、換気扇な どがあげられ、それぞれの製造会社や機種により、形状や大きさなどは異なるが、基 本的に、図 1に概略斜視図として示すように、支持枠 1と網 2とからなり、網 2は一体と なった合成樹脂の繊維 3で構成されている。もちろん、繊維 3の織布でもよいが、縦 糸や横糸がずれることもあり、繊維同士は熱または接着剤により接着されている。
[0052] また、プレフィルタの形状は、集塵のしゃすさ、圧損の軽減、掃除のしゃすさ、掃除 の頻度などを考慮して、各種のものが採用できる。たとえば、網の織り方としては、立 体織りが、比較的目が細かく（細かい埃まで取りやすく）、埃を捕集しても圧損が上が り難い (掃除の頻度が少なくて済む)点力もよく使われているが、近年は、凹凸が少な く掃除がしゃす 、平織りのタイプも使われるようになってきて!/、る。
[0053] 網の目開き (メッシュ）は、適用する空気調整機の種類、機種、用途、形態などによ り異なる力 家庭用の空気調和機では通常 25〜80メッシュ (約 250 m〜約 lmm) である。
[0054] 本発明で使用するプレフィルタは、平織りでも立体織りでも、亀甲織りでもスパイラ ル織りでも、またプリーツ有りでも無しでもよぐ公知のプレフィルタに合わせたものを 提供することができる。
[0055] プレフィルタの網への塗布方法としては、スプレー塗装、デイツビング塗装、ロール 塗装などが使用でき、プレフィルタの形状、大きさ、材質などによって適切な方法を採 用すればよい。また、プライマー塗料を予め塗装してもよい。
[0056] 塗装後、乾燥し、硬化剤による硬化を促せる。硬化は加熱してもよ 、が、上記のと おり、常温で放置することが網の劣化を防ぐ観点力 好ましい。
[0057] 形成する被膜の膜厚は、通常 0. 1 μ m以上、さらには 1 μ m以上、特に 2 m以上 であることが、フィルタの清掃性 (粘着汚れがフィルタにこびり付き難ぐ埃や砂塵に 吸収され易い）が良好なことから好ましぐ 50 m以下、さらには 30 m以下、特に 1 0 m以下であることが、塗装時におけるフィルタの目詰まりを防ぐ上で、また、圧力 損失の増加を抑制するのに加え、塗装に力かる塗料費用（必要以上に塗料を使わな い)や塗装費用（必要以上に塗装したり、乾燥時間を要したりしない)を抑えることや、 塗料の剥がれを防止することから好ま U、。
[0058] 被膜は網の表面全部 (連続被膜)でも、一部（不連続被膜)でもよ!/ヽ。プレフィルタ が可撓性でその取扱い時に変形することを考慮すると、一部 (不連続被膜）にするこ とが、被膜のひび割れなどが生じず、好ましい。不連続被膜を形成するには、たとえ ば塗料組成物の溶剤として網の合成樹脂に対して親和性の低いものを使用する方 法、塗装方法を工夫する (スプレー、グラビア塗装等)方法などがある。
[0059] また、拭き取り性を向上させるために、被覆された網の表面に滑水性を付与するこ とが望ましい。良好な滑水性とは、転落角測定法で測定した水滴の転落角が 50度以 下で、へキサデカンの油滴の転落角が 10度以下であることをいう。滑水性を高めるた めには、たとえば被覆された網の表面に適正な凹凸を形成する方法などが例示でき る。
[0060] 転落角の測定は、基材に塗膜を形成し、接触角測定装置で水およびへキサデカン の転落角を測定することにより行う。 [0061] 塗装方法によって、網の目に塗料組成物が残り、網目を潰してしまうことがある。こう した目詰まりが多くなりすぎるとフィルタ機能が損なわれ、また圧損が大きくなる。 目詰 まりの程度は、全体の網目の数の 1Z3以下、さらには 1Z10以下にすることが、良好 な集塵と圧損の抑制、さらにはフィルタ外観が損なわれ難い点力も好ましい。
[0062] 力べしてプレフィルタの網の表面に形成された特定のフッ素榭脂被膜は、タバコの ャ-などの水溶性の汚れだけではなぐ油煙、煤などの油溶性の汚れなどの除去性 に優れて 、るので、簡単な水洗!/、やふき取りで容易に油性水性を問わず除去でき、 し力も網への密着性にも優れているので、可撓性に優れ、さらにブラシなどの使用に も耐え得る耐久性を有して 、る。
[0063] なお、以上にプレフィルタの網の材質として、これまでフッ素榭脂での表面処理が 困難であった合成樹脂について説明してきたが、本発明で用いる塗料組成物は、も ちろん金属、ガラス繊維やセラミック繊維などの耐熱性のプレフィルタに対しても適用 できる。
[0064] プレフィルタの網を構成する金属やセラミックスとしては、ステンレス（SUS304,SUS31 6,SUS316L,SUS430,SUS310Sほか）、ニッケル、モネル、黄銅、丹銅、燐青銅、銅、鉄 、亜鉛引鉄線、鋼、アルミニウム、チタン、ニクロム、ハステロイ、インコネルなどの金属 繊維、酸ィ匕アルミニウム、酸ィ匕ジルコニウム、マイ力、窒化珪素、ガラス、 PZT、黒鉛、 炭素繊維などのセラミックスが例示できる。
実施例
[0065] つぎに実施例をあげて本発明を具体的に説明するが、本発明はこれらの実施例の みに限定されるものではない。
[0066] 実施例 1
含フッ素ポリマー（Α)としてゼッフル GK— 510 (水酸基含有テトラフルォロエチレン 共重合体。水酸基価 60mgKOH,g、酸価 9mgKOH,g、数平均分子量 12000、 フッ素含有率 36質量％、榭脂の屈折率 1. 4、酢酸ブチル溶液、固形分 50質量％) を 100質量部、防汚成分 (B)としてアミノ基含有シリコーンオイル (NUC SILICON E FZ3705 (商品名）。 日本ュニカー (株)製のアミノ変性シリコーンオイル。粘度 230 mm2Zs、ァミノ当量 4000)を 1質量部、硬ィ匕剤（C)としてコロネート HX (商品名）（日 本ポリウレタン (株)製のイソシァネート系硬化剤）を 12質量部、および硬化促進剤と してジブチル錫ジラウレート（DBTDL)の 1%酢酸ブチル溶液を 2質量部配合し、希 釈剤として酢酸ブチル 165質量部、プロピレングリコールモノブチルエーテルァセテ ート 30質量部を配合し、固形分濃度 20質量％の塗料組成物を調製した。
[0067] この塗料組成物を常法により、つぎのプレフィルタにスプレー塗装し、圧縮空気をフ ィルタにあて、 目詰まりをなくした後、 100°Cで 10分間焼き付けし、乾燥'硬化させて 膜の表面にフッ素榭脂被膜を形成させ、本発明のプレフィルタ 1を作製した。
[0068] (プレフィルタの仕様）
支持枠:ポリプロピレン製
網： PET製
網の目開き（メッシュ）：縦 50メッシュ、横 35メッシュ
網の繊維径： 75デニール
寸法：縦 355mm、横 400mm
[0069] 得られたプレフィルタ 1の目詰まりは顕微鏡観察によれば、全体の 1%であった。
[0070] つぎにプレフィルタ 1および被膜を形成する前のプレフィルタ（比較用プレフィルタ） の基材 (PET)について、それぞれの対水接触角および対油接触角を調べた。プレ フィルタ自身の接触角は測定できな 、ので、上記と同様にしてフッ素榭脂被膜を形 成した PETシートと、被膜形成前の PETシートの接触角を測定した。その結果、フッ 素榭脂被膜を形成した PETシート（プレフィルタ 1に相当）の対水接触角は 103度で あり、対油接触角は 50度であった。被膜形成前の PETシート（比較用プレフィルタに 相当）の対水接触角は 80度であり、対油接触角は 15度であった。
[0071] (対水接触角）
接触角計 (協和界面科学 (株)製)を用いて純水の 2 w 1の液量での接触角を測定す る。液を載せてから 1秒後に測定する。
[0072] (対油接触角）
接触角計 (協和界面科学 (株)製)を用 V、て流動パラフィン粘度 70cStの 2 μ 1の液量 での接触角を測定する。液を安定させるため、液を載せてから 10秒後に測定する。
[0073] また、プレフィルタ 1につ 、て、折り曲げ耐久試験を行った結果、 10回の折り曲げ後 でも、脱落した被膜はほとんどなカゝつた。
[0074] (折り曲げ耐久試験方法）
プレフィルタを 180度折り曲げた後に反対方向に 180度折り曲げる操作を 1サイク ルとし、 10サイクル繰り返す。その後、折り曲げ部を目視観察しノヽガレの有無を目視 で観察する。
[0075] つぎにプレフィルタ 1および被膜を形成する前のプレフィルタ（比較用プレフィルタ） をそれぞれ床面積約 15m2の喫煙室の壁上部に設置された空気調和機に取り付け、
1力月運転した後、取り外して洗浄試験に供した。
[0076] (洗浄試験方法）
台所のシンクに水をはり、その中（水中）で、ガーゼを使用して、 2往復拭取りを行う
。評価は、拭取り前後の汚れ状態を目視で行う。
[0077] その結果、本発明のプレフィルタ 1では取り付け時と同様の程度にまで、煙草のャ 二汚れが落ち、ほとんど汚れが分力もなくなつたが、比較用のプレフィルタでは煙草 のャ-汚れはほとんど落ちなかった。
産業上の利用可能性
[0078] 本発明の空気調整機用のプレフィルタによれば、合成樹脂に対して密着性に優れ た含フッ素ポリマーを含む塗料組成物により網の表面に被膜を形成でき、プレフィル タ表面を擦ったり、プレフィルタを折り曲げたりしても脱落することがなぐ取り外し作 業や水洗いなどに対して耐久性に富むプレフィルタを提供することができる。

Claims

請求の範囲
[1] 合成樹脂製の網を有する空気調整機用のプレフィルタであって、該網の表面の一 部または全部に含フッ素ポリマーを含む塗料組成物を網の表面に塗布し硬化させて 得られる被膜を有しており、該塗料組成物が、（A)官能基 Xを含有する含フッ素ポリ マー、（B)防汚成分および (C)硬化剤を含む組成物であって、防汚成分 (B)が (B1) 官能基 Xおよび Zまたは硬化剤 (C)と反応し得る官能基 Y1を有する液状のポリジァ ルキルシロキサン、または（B2)官能基 Xおよび Zまたは硬化剤 (C)と反応し得る官 能基 Y2を有する液状のフルォロポリエーテルである常温硬化性の塗料組成物である プレフイノレタ。
[2] 前記含フッ素ポリマー (A)が有する官能基 Xが、水酸基、カルボキシル基および Z またはエポキシ基である請求の範囲第 1項記載のプレフィルタ。
[3] 前記ポリジアルキルシロキサン (B1)が有する官能基 Y1が、水酸基、アミノ基および
Zまたはエポキシ基である請求の範囲第 1項または第 2項記載のプレフィルタ。
[4] 前記硬化剤 (C)が、イソシァネートイ匕合物、ァミノ化合物および Zまたはエポキシィ匕 合物である請求の範囲第 1項〜第 3項のいずれかに記載のプレフィルタ。
[5] 前記榭脂 (A)が有する官能基 Xが水酸基であり、防汚成分 (B)が有する官能基 Y1 または Y2が水酸基またはアミノ基であり、硬化剤 (C)力イソシァネートイ匕合物である請 求の範囲第 1項記載のプレフィルタ。
[6] 前記常温硬化性の塗料組成物が、さらに抗菌剤を含む請求の範囲第 1項〜第 5項 の！、ずれかに記載のプレフィルタ。
[7] 前記常温硬化性の塗料組成物が、さらに光触媒を含む請求の範囲第 1項〜第 6項 の！、ずれかに記載のプレフィルタ。
[8] 前記網を構成する合成樹脂が、ポリプロピレン、ポリエチレン、ポリアミド、ポリ塩ィ匕 ビュルまたはポリ塩ィ匕ビユリデンである請求の範囲第 1項〜第 7項のいずれかに記載 のプレフィルタ。
[9] 空気調和機用のプレフィルタである請求の範囲第 1項〜第 8項の 、ずれかに記載 のプレフィルタ。
[10] 空気清浄機用のプレフィルタである請求の範囲第 1項〜第 8項のいずれかに記載 のプレフィルタ,
PCT/JP2007/058074 2006-07-05 2007-04-12 Prefilter Ceased WO2008004368A1 (en)