WO2007140008A2 - Matériaux composites isolants comprenant une couche de papier revêtue résistant à l'eau - Google Patents

Matériaux composites isolants comprenant une couche de papier revêtue résistant à l'eau Download PDF

Info

Publication number
WO2007140008A2
WO2007140008A2 PCT/US2007/012636 US2007012636W WO2007140008A2 WO 2007140008 A2 WO2007140008 A2 WO 2007140008A2 US 2007012636 W US2007012636 W US 2007012636W WO 2007140008 A2 WO2007140008 A2 WO 2007140008A2
Authority
WO
WIPO (PCT)
Prior art keywords
insulation material
layer
composite insulation
foam
styrene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2007/012636
Other languages
English (en)
Inventor
Lee Baker
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dow Reichhold Specialty Latex LLC
Original Assignee
Dow Reichhold Specialty Latex LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Reichhold Specialty Latex LLC filed Critical Dow Reichhold Specialty Latex LLC
Publication of WO2007140008A2 publication Critical patent/WO2007140008A2/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un matériau composite isolant. Le matériau comprend une couche d'un isolant, tel qu'une mousse ou de la fibre de verre, et une couche de papier. La couche de papier est recouverte d'une barrière à la vapeur d'eau, en utilisant une composition de revêtement qui comprend un latex de résine et un composant ayant une structure cristalline lamellaire. Les latex de résine appropriés comprennent des poly(méth)acrylates, des copolymères de butadiène-acrylonitrile carboxylés ou non carboxylés, le polystyrène, des copolymères de styrène-acrylonitrile, des copolymères de styrène-acrylonitrile-butadiène, des copolymères de styrène-acrylates, des copolymères de styrène-butadiène, des copolymères de styrène-butadiène carboxylés, le polychlorure de vinyle, le polyacétate de vinyle, des polyuréthanes à base d'eau, des acryliques vinyliques, le polychlorure de vinylidène, le chlorure d'éthylvinyle, des copolymères d'acétate de vinyle-éthylène et des copolymères, terpolymères et mélanges de ceux-ci. Un agent de mise en suspension pour le composant cristallin lamellaire peut être présent et il s'agit typiquement d'un polymère hydrophile. Les compositions de revêtement peuvent comprendre une cire ou bien elles peuvent être pratiquement exemptes de cire. Un agent hydrophobe autre qu'une cire peut être éventuellement ajouté. La structure cristalline lamellaire peut être non modifiée ou bien elle peut être modifiée pour accroître son caractère hydrophobe. Le matériau composite peut également être sous la forme d'un stratifié de papier Kraft/grille de renforcement/feuille, lequel peut être combiné avec une couche d'isolant si on le souhaite. Les matériaux isolants peuvent être utilisés, par exemple, pour isoler des tuyaux et des canalisations ou d'autres éléments de bâtiments.
PCT/US2007/012636 2006-05-26 2007-05-29 Matériaux composites isolants comprenant une couche de papier revêtue résistant à l'eau Ceased WO2007140008A2 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US80888006P 2006-05-26 2006-05-26
US60/808,880 2006-05-26

Publications (1)

Publication Number Publication Date
WO2007140008A2 true WO2007140008A2 (fr) 2007-12-06

Family

ID=38779278

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2007/012636 Ceased WO2007140008A2 (fr) 2006-05-26 2007-05-29 Matériaux composites isolants comprenant une couche de papier revêtue résistant à l'eau

Country Status (1)

Country Link
WO (1) WO2007140008A2 (fr)

Cited By (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090311936A1 (en) * 2006-07-07 2009-12-17 Saint-Gobain Isover Mineral wool, insulating product and manufacturing process
US20120146297A1 (en) * 2010-12-08 2012-06-14 Mayer Goyenechea Caballero Juan Antonio Textile material impregnated with water base solution
WO2014008148A1 (fr) * 2012-07-03 2014-01-09 3M Innovative Properties Company Revêtements de tuyau à base de siloxane
EP2470718B1 (fr) 2009-08-24 2015-07-29 BASF Corporation Nouveaux pigments minéraux traités pour des revêtements de barrière à base aqueuse
WO2015113013A1 (fr) * 2014-01-27 2015-07-30 3M Innovative Properties Company Matériau électriquement isolant et bande d'enveloppement de conducteurs pour équipements électriques tels que transformateurs
WO2015113012A1 (fr) * 2014-01-27 2015-07-30 3M Innovative Properties Company Matériau isolant électrique et transformateur
US9803088B2 (en) 2009-08-24 2017-10-31 Basf Corporation Enhanced performance of mineral based aqueous barrier coatings
CN108774920A (zh) * 2018-05-31 2018-11-09 河南省亚安绝缘材料厂有限公司 一种防水性能好的绝缘复合纸
EP2274346B1 (fr) * 2008-03-27 2019-03-06 Trinseo Europe GmbH Compositions de revêtement du type latex à base de polyester de vinyle
US10301454B2 (en) 2010-12-08 2019-05-28 Juan Antonio MAYER GOYENECHEA CABALLERO Water-based elastomeric composition for impregnating textile material and uses thereof
US20220177215A1 (en) * 2020-12-07 2022-06-09 Smartech International LP Pith filled honeycomb insulating panels and packages
US11505668B2 (en) 2017-04-05 2022-11-22 Qatar University Insulating plastic foams based on polyolefins
CN118159704A (zh) * 2022-08-31 2024-06-07 包装和装箱技术有限责任公司 耐火零售产品包装材料及其制造方法
WO2025078459A1 (fr) * 2023-10-10 2025-04-17 Neenah Gessner Gmbh Feuille à base de fibres de cellulose imprégnée

Cited By (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090311936A1 (en) * 2006-07-07 2009-12-17 Saint-Gobain Isover Mineral wool, insulating product and manufacturing process
EP2274346B1 (fr) * 2008-03-27 2019-03-06 Trinseo Europe GmbH Compositions de revêtement du type latex à base de polyester de vinyle
US9803088B2 (en) 2009-08-24 2017-10-31 Basf Corporation Enhanced performance of mineral based aqueous barrier coatings
US10513617B2 (en) 2009-08-24 2019-12-24 Basf Corporation Enhanced performance of mineral based aqueous barrier coatings
EP2470718B1 (fr) 2009-08-24 2015-07-29 BASF Corporation Nouveaux pigments minéraux traités pour des revêtements de barrière à base aqueuse
US20120146297A1 (en) * 2010-12-08 2012-06-14 Mayer Goyenechea Caballero Juan Antonio Textile material impregnated with water base solution
US10301454B2 (en) 2010-12-08 2019-05-28 Juan Antonio MAYER GOYENECHEA CABALLERO Water-based elastomeric composition for impregnating textile material and uses thereof
US10053598B2 (en) 2012-07-03 2018-08-21 3M Innovative Properties Company Siloxane-based pipe coatings
WO2014008148A1 (fr) * 2012-07-03 2014-01-09 3M Innovative Properties Company Revêtements de tuyau à base de siloxane
CN105934801A (zh) * 2014-01-27 2016-09-07 3M创新有限公司 电绝缘材料和变压器
WO2015113012A1 (fr) * 2014-01-27 2015-07-30 3M Innovative Properties Company Matériau isolant électrique et transformateur
WO2015113013A1 (fr) * 2014-01-27 2015-07-30 3M Innovative Properties Company Matériau électriquement isolant et bande d'enveloppement de conducteurs pour équipements électriques tels que transformateurs
US11505668B2 (en) 2017-04-05 2022-11-22 Qatar University Insulating plastic foams based on polyolefins
CN108774920A (zh) * 2018-05-31 2018-11-09 河南省亚安绝缘材料厂有限公司 一种防水性能好的绝缘复合纸
US20220177215A1 (en) * 2020-12-07 2022-06-09 Smartech International LP Pith filled honeycomb insulating panels and packages
US11807442B2 (en) * 2020-12-07 2023-11-07 Smartech International LP Pith filled honeycomb insulating panels and packages
CN118159704A (zh) * 2022-08-31 2024-06-07 包装和装箱技术有限责任公司 耐火零售产品包装材料及其制造方法
WO2025078459A1 (fr) * 2023-10-10 2025-04-17 Neenah Gessner Gmbh Feuille à base de fibres de cellulose imprégnée

Similar Documents

Publication Publication Date Title
WO2007140008A2 (fr) Matériaux composites isolants comprenant une couche de papier revêtue résistant à l'eau
RU2753930C2 (ru) Способ изготовления упаковочного материала и упаковочный материал, полученный этим способом
US5102728A (en) Method and composition for coating mat and articles produced therewith
US5837383A (en) Recyclable and compostable coated paper stocks and related methods of manufacture
KR101731662B1 (ko) 수성계 장벽 코팅을 위한 신규한 처리된 무기 안료
RU2622308C2 (ru) Укрепленный связующим текстильный материал, способ его изготовления и его применение
US4946372A (en) Composite paper
US20090104425A1 (en) Fire retardant coating composition for fibrous mat
US20250163697A1 (en) Multifunctional water-borne high solids tile paint
JP2020192737A (ja) 防湿性積層体および紙容器
CA3143263A1 (fr) Tapis de parement sur lesquels il est possible de marcher pour isolation de toit
WO2007140009A2 (fr) Barrière à la vapeur d'eau désintégrable
JP4130880B2 (ja) 壁装材
EP1567717A2 (fr) Carton ondule pouvant etre soumis a un repulpage et resistant a la transmission de la vapeur d'eau
CN118434936A (zh) 涂布纸板
JP3917778B2 (ja) 防湿紙及びその製造方法
JP3703691B2 (ja) 耐水・防湿用樹脂組成物を用いた耐水・防湿紙並びにその製造方法
JP2022158269A (ja) ガスバリア性積層体及びガスバリア性シール紙
JP4741058B2 (ja) 耐水・防湿紙用樹脂組成物及びこれを用いた耐水・防湿紙並びにその製造方法
JP2004051130A (ja) 冷温食品容器の包装方法及び包装に用いる段ボール箱
JP3659332B2 (ja) 紙製帯束バンド
CN102892951B (zh) 用于层合板的面纸/芯纸/纸张
JP4492079B2 (ja) 樹脂含有紙及びそれを基材とする積層耐水紙
CN120882931A (zh) 热封纸和包装袋
JP2023140525A (ja) 防湿性紙、その製造方法、およびそれを用いた段ボールシート

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07795434

Country of ref document: EP

Kind code of ref document: A2

NENP Non-entry into the national phase in:

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 07795434

Country of ref document: EP

Kind code of ref document: A2