WO2006071423A1 - Structure absorbante avec amas d'agregats - Google Patents

Structure absorbante avec amas d'agregats Download PDF

Info

Publication number
WO2006071423A1
WO2006071423A1 PCT/US2005/043003 US2005043003W WO2006071423A1 WO 2006071423 A1 WO2006071423 A1 WO 2006071423A1 US 2005043003 W US2005043003 W US 2005043003W WO 2006071423 A1 WO2006071423 A1 WO 2006071423A1
Authority
WO
WIPO (PCT)
Prior art keywords
fibers
absorbent structure
thermoplastic binder
aggregate clusters
aggregate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2005/043003
Other languages
English (en)
Inventor
Shannon Kathleen Melius
Jeffrey Mark Lafortune
Michael John Faulks
David Arthur Fell
Michael Barth Venturino
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kimberly Clark Worldwide Inc
Kimberly Clark Corp
Original Assignee
Kimberly Clark Worldwide Inc
Kimberly Clark Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kimberly Clark Worldwide Inc, Kimberly Clark Corp filed Critical Kimberly Clark Worldwide Inc
Priority to MX2007007399A priority Critical patent/MX2007007399A/es
Publication of WO2006071423A1 publication Critical patent/WO2006071423A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention se rapporte à une structure absorbante comprenant une macrostructure absorbante dans laquelle est incorporée une pluralité d'amas d'agrégats. Les amas d'agrégats comportent une périphérie, un intérieur et des fibres liantes thermoplastiques. Les fibres liantes thermoplastiques comportent des extrémités de fibre liante thermoplastique. Les extrémités de fibre liante thermoplastique se trouvent à la périphérie des amas d'agrégats. L'intérieur des amas d'agrégats est pratiquement dépourvu d'extrémités de fibre liante thermoplastique. La macrostructure absorbante et les amas d'agrégats peuvent également inclure des fibres liantes thermoplastiques, des fibres courtes, des particules super-absorbantes et des éléments similaires. Le procédé de fabrication des structures absorbantes inclut une première structure absorbante, la division de la première structure absorbante pour créer des amas d'agrégats, la formation d'un courant d'amas d'agrégats, la formation d'un courant de fibres polymères, la réunion du courant d'amas d'agrégats et du courant de fibres polymères en un courant de produit unique et la fabrication d'une seconde structure absorbante. Le procédé peut inclure en outre des fibres courtes, des particules super-absorbantes et des éléments similaires.
PCT/US2005/043003 2004-12-23 2005-11-28 Structure absorbante avec amas d'agregats Ceased WO2006071423A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
MX2007007399A MX2007007399A (es) 2004-12-23 2005-11-28 Estructura absorbente con racimos agregados.

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US11/021,043 2004-12-23
US11/021,043 US20060141891A1 (en) 2004-12-23 2004-12-23 Absorbent structure with aggregate clusters

Publications (1)

Publication Number Publication Date
WO2006071423A1 true WO2006071423A1 (fr) 2006-07-06

Family

ID=36182411

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2005/043003 Ceased WO2006071423A1 (fr) 2004-12-23 2005-11-28 Structure absorbante avec amas d'agregats

Country Status (4)

Country Link
US (1) US20060141891A1 (fr)
KR (1) KR20070097449A (fr)
MX (1) MX2007007399A (fr)
WO (1) WO2006071423A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019069882A1 (fr) * 2017-10-03 2019-04-11 花王株式会社 Absorbant et article absorbant
JP2019063471A (ja) * 2017-10-03 2019-04-25 花王株式会社 吸収体及び吸収性物品

Families Citing this family (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ATE523179T1 (de) * 2005-07-26 2011-09-15 Procter & Gamble Flexibler, saugfähiger artikel mit verbesserter anpassung an den körper
WO2007122938A1 (fr) * 2006-03-23 2007-11-01 Kao Corporation article absorbant et son processus de fabrication
JP4863848B2 (ja) * 2006-11-17 2012-01-25 花王株式会社 吸収性物品の吸収体及びその製造方法
US10024000B2 (en) * 2007-07-17 2018-07-17 The Procter & Gamble Company Fibrous structures and methods for making same
US8852474B2 (en) 2007-07-17 2014-10-07 The Procter & Gamble Company Process for making fibrous structures
US7972986B2 (en) 2007-07-17 2011-07-05 The Procter & Gamble Company Fibrous structures and methods for making same
DE102010020050A1 (de) * 2010-05-11 2011-11-17 Ivf Hartmann Ag Wundauflage
US8530721B2 (en) * 2011-03-18 2013-09-10 Kimberly-Clark Worldwide, Inc. Resilient tampon and method for making
JP5579337B1 (ja) 2013-06-11 2014-08-27 ユニ・チャーム株式会社 吸収体、及び当該吸収体を含む吸収性物品
ES2875330T3 (es) * 2014-04-04 2021-11-10 Nanofiber Solutions Llc Composiciones de fibras biocompatibles electrohiladas
AU2016401205B2 (en) 2016-03-31 2022-05-12 Kimberly-Clark Worldwide, Inc. Absorbent cores and methods for forming absorbent cores
RU2698084C1 (ru) 2016-03-31 2019-08-21 Кимберли-Кларк Ворлдвайд, Инк. Впитывающие сердцевины и способы формирования впитывающих сердцевин
WO2017171781A1 (fr) 2016-03-31 2017-10-05 Kimberly-Clark Worldwide, Inc. Noyaux absorbants et procédés de formation de noyaux absorbants
CN108697542B (zh) 2016-03-31 2022-05-24 金伯利-克拉克环球有限公司 吸收芯和形成吸收芯的方法
JP6990095B2 (ja) * 2017-11-28 2022-01-12 花王株式会社 吸収体及び吸収性物品
JP7202167B2 (ja) * 2018-12-13 2023-01-11 花王株式会社 吸収体及び吸収性物品
IT202000019429A1 (it) * 2020-08-06 2022-02-06 Gdm Spa Metodo per realizzare un nastro composito

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4118531A (en) * 1976-08-02 1978-10-03 Minnesota Mining And Manufacturing Company Web of blended microfibers and crimped bulking fibers
US4429001A (en) * 1982-03-04 1984-01-31 Minnesota Mining And Manufacturing Company Sheet product containing sorbent particulate material
EP0294137A1 (fr) * 1987-06-02 1988-12-07 The Procter & Gamble Company Composition de structures absorbantes
EP0306262A1 (fr) * 1987-09-01 1989-03-08 The Procter & Gamble Company Structures absorbantes composites et articles absorbants contenant de telles structures
EP0305620A2 (fr) * 1987-09-01 1989-03-08 Minnesota Mining And Manufacturing Company Nappes de microfibres et étoffes non tissées contenant des nappes de microfibres
EP0608883A1 (fr) * 1993-01-28 1994-08-03 Minnesota Mining And Manufacturing Company Article absorbant
EP1247509A2 (fr) * 2001-04-06 2002-10-09 Uni-Charm Corporation Article absorbant, noyau absorbant pour article absorbant et son procédé de fabrication
WO2005051439A1 (fr) * 2003-11-29 2005-06-09 Paul Hartmann Ag Article hygienique absorbant

Family Cites Families (45)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3773613A (en) * 1971-10-13 1973-11-20 Int Paper Co Method for converting plastic-containing broke to fluff
US3978179A (en) * 1973-09-04 1976-08-31 Reprocess Textile Associates Production of non-woven fabrics
US3890220A (en) * 1973-12-26 1975-06-17 Kimberly Clark Co Fiber waste reclaim system and method
US3909397A (en) * 1973-12-26 1975-09-30 Kimberly Clark Co Fiber recovery system and method of recovery
US4100324A (en) * 1974-03-26 1978-07-11 Kimberly-Clark Corporation Nonwoven fabric and method of producing same
US3901236A (en) * 1974-07-29 1975-08-26 Union Carbide Corp Disposable absorbent articles containing hydrogel composites having improved fluid absorption efficiencies and processes for preparation
DE2918345A1 (de) * 1979-05-07 1980-11-20 Bert Steffens Verfahren zum kontinuierlichen auftrennen von ausschuss von wegwerf-hygieneartikeln in flockigen und/oder geschnitzelten saugwerkstoff einerseits und dessen flaechige umhuellungen andererseits
NZ193857A (en) * 1979-05-29 1984-02-03 New Zealand Ind Gases Separating mixtures by flotation in gas stream;particularly recovery of scrap rubber
US4305507A (en) * 1980-08-15 1981-12-15 Magna-Graphics Corporation Disposable diaper reclaiming apparatus
DE3320125A1 (de) * 1983-06-03 1984-12-06 J.M. Voith Gmbh, 7920 Heidenheim Verfahren und einrichtung zur aufbereitung von altpapier
US4621011A (en) * 1984-04-24 1986-11-04 Kimberly-Clark Corporation Agglomerated cellulosic particles
DE8712723U1 (de) * 1986-12-08 1987-12-17 Hanfspinnerei Steen & Co Gmbh, 2000 Hamburg Absorberflocke
US4879170A (en) * 1988-03-18 1989-11-07 Kimberly-Clark Corporation Nonwoven fibrous hydraulically entangled elastic coform material and method of formation thereof
US4931355A (en) * 1988-03-18 1990-06-05 Radwanski Fred R Nonwoven fibrous hydraulically entangled non-elastic coform material and method of formation thereof
US5171237A (en) * 1989-06-14 1992-12-15 Weyerhaeuser Company Method of making absorbent particles
ES2196102T3 (es) * 1990-10-29 2003-12-16 Knowaste L L C Tratamiento de polimero superabsorbente.
US6238516B1 (en) * 1991-02-14 2001-05-29 Dana L. Watson System and method for cleaning, processing, and recycling materials
US5225045A (en) * 1991-02-14 1993-07-06 Watson Dana L System and method for recycling materials from disposed diapers
US5292075A (en) * 1992-05-29 1994-03-08 Knobbe, Martens, Olson & Bear Disposable diaper recycling process
US5312052A (en) * 1992-06-01 1994-05-17 Dellekamp Michael D Method for reclaiming fiber reinforcement from a composite
US5780368A (en) * 1994-01-28 1998-07-14 Noda; Isao Spray processes using a gaseous flow for preparing biodegradable fibrils, nonwoven fabrics comprising biodegradable fibrils, and articles comprising such nonwoven fabrics
US6074527A (en) * 1994-06-29 2000-06-13 Kimberly-Clark Worldwide, Inc. Production of soft paper products from coarse cellulosic fibers
SE503272C2 (sv) * 1994-08-22 1996-04-29 Moelnlycke Ab Nonwovenmaterial framställt genom hydroentangling av en fiberbana samt förfarande för framställning av ett sådant nonwovenmaterial
US5645542A (en) * 1994-12-29 1997-07-08 Kimberly-Clark Worldwide, Inc. Elastomeric absorbent structure
US5618003A (en) * 1995-03-09 1997-04-08 Bot Chan, Inc. Process and apparatus for reclaiming the components of used disposable sanitary articles
US5952251A (en) * 1995-06-30 1999-09-14 Kimberly-Clark Corporation Coformed dispersible nonwoven fabric bonded with a hybrid system
US5811178A (en) * 1995-08-02 1998-09-22 Kimberly-Clark Worldwide, Inc. High bulk nonwoven sorbent with fiber density gradient
US6224961B1 (en) * 1997-08-01 2001-05-01 The Procter & Gamble Company Absorbent macrostructure made from mixtures of different hydrogel-forming absorbent polymers for improved fluid handling capability
US6362389B1 (en) * 1998-11-20 2002-03-26 Kimberly-Clark Worldwide, Inc. Elastic absorbent structures
US6387495B1 (en) * 1999-04-16 2002-05-14 Kimberly-Clark Worldwide, Inc. Superabsorbent-containing composites
US6376011B1 (en) * 1999-04-16 2002-04-23 Kimberly-Clark Worldwide, Inc. Process for preparing superabsorbent-containing composites
KR100347547B1 (ko) * 1999-07-30 2002-08-07 주식회사 하이닉스반도체 반도체 소자의 캐패시터 제조 방법
US6458240B1 (en) * 2000-01-14 2002-10-01 Georgia-Pacific Corporation Method for removing contaminants from fibers in recycle fiber pulping
US6461086B1 (en) * 2000-11-28 2002-10-08 Kimberly-Clark Worldwide, Inc. Method and apparatus for delivering particulate material to an air stream
US6378179B1 (en) * 2001-01-05 2002-04-30 Gary F. Hirsch System and method for reconstituting fibers from recyclable waste material
US6752907B2 (en) * 2001-01-12 2004-06-22 Georgia-Pacific Corporation Wet crepe throughdry process for making absorbent sheet and novel fibrous product
US6715705B2 (en) * 2001-03-16 2004-04-06 Frank F. Rowley, Jr. Two-stage comminuting and dehydrating system and method
US6632501B2 (en) * 2001-06-06 2003-10-14 Jerry M. Brownstein Loose fiber adsorbent
US6682512B2 (en) * 2001-12-18 2004-01-27 Kimberly-Clark Worldwide, Inc. Continuous biaxially stretchable absorbent with low tension
US20030119394A1 (en) * 2001-12-21 2003-06-26 Sridhar Ranganathan Nonwoven web with coated superabsorbent
US7622020B2 (en) * 2002-04-23 2009-11-24 Georgia-Pacific Consumer Products Lp Creped towel and tissue incorporating high yield fiber
US20030211802A1 (en) * 2002-05-10 2003-11-13 Kimberly-Clark Worldwide, Inc. Three-dimensional coform nonwoven web
US7175727B2 (en) * 2002-08-30 2007-02-13 Kimberley-Clark Worldwide, Inc. Shaped absorbent pads and associated method for making
US20040121683A1 (en) * 2002-12-20 2004-06-24 Joy Jordan Composite elastic material
US6888044B2 (en) * 2002-12-23 2005-05-03 Kimberly-Clark Worldwide, Inc. High capacity absorbent structure and method for producing same

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4118531A (en) * 1976-08-02 1978-10-03 Minnesota Mining And Manufacturing Company Web of blended microfibers and crimped bulking fibers
US4429001A (en) * 1982-03-04 1984-01-31 Minnesota Mining And Manufacturing Company Sheet product containing sorbent particulate material
EP0294137A1 (fr) * 1987-06-02 1988-12-07 The Procter & Gamble Company Composition de structures absorbantes
EP0306262A1 (fr) * 1987-09-01 1989-03-08 The Procter & Gamble Company Structures absorbantes composites et articles absorbants contenant de telles structures
EP0305620A2 (fr) * 1987-09-01 1989-03-08 Minnesota Mining And Manufacturing Company Nappes de microfibres et étoffes non tissées contenant des nappes de microfibres
EP0608883A1 (fr) * 1993-01-28 1994-08-03 Minnesota Mining And Manufacturing Company Article absorbant
EP1247509A2 (fr) * 2001-04-06 2002-10-09 Uni-Charm Corporation Article absorbant, noyau absorbant pour article absorbant et son procédé de fabrication
WO2005051439A1 (fr) * 2003-11-29 2005-06-09 Paul Hartmann Ag Article hygienique absorbant

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019069882A1 (fr) * 2017-10-03 2019-04-11 花王株式会社 Absorbant et article absorbant
JP2019063471A (ja) * 2017-10-03 2019-04-25 花王株式会社 吸収体及び吸収性物品
JP7014577B2 (ja) 2017-10-03 2022-02-01 花王株式会社 吸収体及び吸収性物品
RU2769865C2 (ru) * 2017-10-03 2022-04-07 Као Корпорейшн Впитывающий элемент и впитывающее изделие

Also Published As

Publication number Publication date
KR20070097449A (ko) 2007-10-04
MX2007007399A (es) 2007-07-16
US20060141891A1 (en) 2006-06-29

Similar Documents

Publication Publication Date Title
US20060141891A1 (en) Absorbent structure with aggregate clusters
EP0800411B1 (fr) Structure absorbante elastomere
US6680423B1 (en) Absorbent article having reinforced elastic absorbent core
US6319342B1 (en) Method of forming meltblown webs containing particles
US4655757A (en) Selective layering of superabsorbents in meltblown substrates
US4604313A (en) Selective layering of superabsorbents in meltblown substrates
US6494974B2 (en) Method of forming meltblown webs containing particles
US6417120B1 (en) Particle-containing meltblown webs
US5804512A (en) Nonwoven laminate fabrics and processes of making same
US4724184A (en) Elastomeric polyether block amide nonwoven web
EP0788336B1 (fr) Procede et appareil de fabrication d'articles absorbants extensibles
EP2161361B1 (fr) Tissu non tissé et son processus de fabrication
AU766825B2 (en) Absorbent article with fluid treatment agent
KR101092808B1 (ko) 강화 흡수성 구조체를 갖는 흡수성 제품
KR101811154B1 (ko) 흡수성 구조체를 형성하는 방법
CN1942616A (zh) 包含用作阻碍物的纳米纤维的制品
JP6256944B2 (ja) 吸収性物品
US20020155776A1 (en) Particle-containing meltblown webs
WO2001015650A1 (fr) Article absorbant a couche absorbante plissee extensible
KR20020022783A (ko) 페이싱 및 라이너용 ｃｄ 신장 가능한 천과 같은 부직 물질
WO1996004876A1 (fr) Transport de liquide au moyen d'une structure fibreuse capillaire
JP2004507323A (ja) 適合性の高いパーソナルケア製品
JPH10168726A (ja) 長繊維不織布及びそれを用いた吸収性物品
WO2002044456A2 (fr) Couche fibreuse permettant d'ameliorer le controle de la porosite pour les bandes non tissees
WO2022221633A1 (fr) Bande absorbante destinée à la protection contre les fuites dans des articles absorbants

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2005852332

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: MX/a/2007/007399

Country of ref document: MX

WWE Wipo information: entry into national phase

Ref document number: 1020077013901

Country of ref document: KR

NENP Non-entry into the national phase

Ref country code: DE

WWW Wipo information: withdrawn in national office

Ref document number: 2005852332

Country of ref document: EP