WO2005069960A2 - Cable tricote en alliage d'argent et son procede de fabrication - Google Patents

Cable tricote en alliage d'argent et son procede de fabrication Download PDF

Info

Publication number
WO2005069960A2
WO2005069960A2 PCT/US2005/001989 US2005001989W WO2005069960A2 WO 2005069960 A2 WO2005069960 A2 WO 2005069960A2 US 2005001989 W US2005001989 W US 2005001989W WO 2005069960 A2 WO2005069960 A2 WO 2005069960A2
Authority
WO
WIPO (PCT)
Prior art keywords
silver alloy
knitted
knitted fiber
fashion accessory
silver
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2005/001989
Other languages
English (en)
Other versions
WO2005069960A3 (fr
Inventor
John Lefgren
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Silver Silk LLC
Original Assignee
Silver Silk LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Silver Silk LLC filed Critical Silver Silk LLC
Publication of WO2005069960A2 publication Critical patent/WO2005069960A2/fr
Anticipated expiration legal-status Critical
Publication of WO2005069960A3 publication Critical patent/WO2005069960A3/fr
Ceased legal-status Critical Current

Abstract

Accessoire (20, 40) de mode en fibres tricotées et son procédé de fabrication. L'accessoire comprend au moins un fil (11) en alliage d'argent tricoté de façon à former une structure tridimensionnelle (10), l'alliage d'argent étant un alliage d'argent durci par précipitation. L'accessoire peut comprendre des moyens (22, 24, 42, 44) d'attachement au corps humain et/ou un élément décoratif (28, 30) relié à la structure en fibres tricotées. Selon cette méthode, on produit un fil en alliage d'argent avec au moins un métal d'alliage ; on tricote le fil en alliage d'argent de façon à former une structure en fibres tricotées ; et on durcit par précipitation le fil en alliage d'argent de façon à produire un fil en alliage d'argent durci par précipitation. Le durcissement par précipitation améliore la limite conventionnelle d'élasticité et réduit le volume, ce qui améliore la flexibilité ou souplesse.
PCT/US2005/001989 2004-01-22 2005-01-20 Cable tricote en alliage d'argent et son procede de fabrication Ceased WO2005069960A2 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US53848004P 2004-01-22 2004-01-22
US60/538,480 2004-01-22
US11/039,417 2005-01-19
US11/039,417 US20050189046A1 (en) 2004-01-22 2005-01-19 Knitted silver alloy fashion accessory and method of manufacture

Publications (2)

Publication Number Publication Date
WO2005069960A2 true WO2005069960A2 (fr) 2005-08-04
WO2005069960A3 WO2005069960A3 (fr) 2007-12-21

Family

ID=34810530

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2005/001989 Ceased WO2005069960A2 (fr) 2004-01-22 2005-01-20 Cable tricote en alliage d'argent et son procede de fabrication

Country Status (2)

Country Link
US (1) US20050189046A1 (fr)
WO (1) WO2005069960A2 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2007023308A1 (fr) * 2005-08-23 2007-03-01 Middlesex Silver Co. Limited Fil d'argent
WO2008119093A3 (fr) * 2007-03-30 2008-12-04 Teufelberger Gmbh Produit textile
ITUB20155683A1 (it) * 2015-11-18 2017-05-18 Mauro Mattioli Dal 1978 S R L Catena del tipo a calza per oreficeria e argenteria e macchina per la sua realizzazione

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB0328603D0 (en) * 2003-12-10 2004-01-14 Cole Paul G Silver chain manufacture
US9222150B2 (en) * 2004-06-02 2015-12-29 Peter Gamon Johns Process for making finished or semi-finished articles of silver alloy
US9334589B2 (en) 2009-06-01 2016-05-10 Stephanie J. Eddy Viking knit hand tool
US11525195B2 (en) * 2020-05-27 2022-12-13 Jhih Huei Trading Co., Ltd. Woven textile for bag and bag

Family Cites Families (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1928429A (en) * 1932-08-02 1933-09-26 Handy & Harman Alloy
US1984225A (en) * 1932-09-14 1934-12-11 Wadsworth Watch Case Company I Age hardening silver of sterling or higher standard
US2377882A (en) * 1942-08-11 1945-06-12 Mallory & Co Inc P R Bearing
NL76863C (fr) * 1947-06-03
US3929475A (en) * 1974-08-05 1975-12-30 Williams Gold Refining Co Tarnish resistant silver based dental casting alloy having superior improved ductility and work hardening characteristics
DE2826812A1 (de) * 1978-06-19 1980-01-03 Wagner Fa Ferd Silberlegierungsdraht fuer schmuckketten
US4810308A (en) * 1987-04-13 1989-03-07 Leach & Garner Company Silver alloys of exceptional and reversible hardness
US4869757A (en) * 1987-04-13 1989-09-26 Leach & Garner Company Silver alloys of exceptional and reversible hardness
FR2658999B1 (fr) * 1990-03-02 1992-07-03 Or Est Articles de joaillerie et procedes de fabrication.
WO1992015189A1 (fr) * 1991-02-20 1992-09-03 Instrument Specialties Company, Inc. Joint d'etancheite a treillis metallique traite a chaud, destine a former un blindage contre les interferences electromagnetiques et les parasites hf
US5876445A (en) * 1991-10-09 1999-03-02 Boston Scientific Corporation Medical stents for body lumens exhibiting peristaltic motion
US5340529A (en) * 1993-07-01 1994-08-23 Dewitt Troy C Gold jewelry alloy
WO1995014112A1 (fr) * 1993-11-15 1995-05-26 Apecs Investment Castings Pty. Ltd. Compositions d'alliages d'argent
US6168071B1 (en) * 1994-11-17 2001-01-02 Peter Gamon Johns Method for joining materials together by a diffusion process using silver/germanium alloys and a silver/germanium alloy for use in the method
US6139652A (en) * 1997-01-23 2000-10-31 Stern-Leach Tarnish-resistant hardenable fine silver alloys
US6381942B1 (en) * 1998-06-19 2002-05-07 Jewelmatic, Inc. Thin walled attached silver filled gold jewelry
JP2001032027A (ja) * 1999-07-22 2001-02-06 Accent:Kk 着磁可能銀合金及び該合金製の磁気装身具
GB0112623D0 (en) * 2001-05-23 2001-07-18 Johns Peter G Method of producing silver-copper alloys

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2007023308A1 (fr) * 2005-08-23 2007-03-01 Middlesex Silver Co. Limited Fil d'argent
WO2008119093A3 (fr) * 2007-03-30 2008-12-04 Teufelberger Gmbh Produit textile
US10159314B2 (en) 2007-03-30 2018-12-25 Teufelberger Gesellschaft M.B.H. Textile product
ITUB20155683A1 (it) * 2015-11-18 2017-05-18 Mauro Mattioli Dal 1978 S R L Catena del tipo a calza per oreficeria e argenteria e macchina per la sua realizzazione

Also Published As

Publication number Publication date
US20050189046A1 (en) 2005-09-01
WO2005069960A3 (fr) 2007-12-21

Similar Documents

Publication Publication Date Title
US6675610B2 (en) Jewelry including shape memory alloy elements
KR950006857B1 (ko) 장신구 및 그 제조 방법
US5816072A (en) Jewelry with links and visible substrate
US4543803A (en) Lightweight, rigid, metal product and process for producing same
JP2007520632A (ja) 白金合金及びその製造方法
US20050189046A1 (en) Knitted silver alloy fashion accessory and method of manufacture
JP5145337B2 (ja) 装飾用棒状体、およびその製造方法
JPWO2008102532A1 (ja) 線状部材、線状部材の製造方法および装身具
TWM601546U (zh) 珠寶組件的組裝構造
JPH05195115A (ja) 装身具および日用品を製造するための合金、ならびに中間製品および予備材料
US7413705B2 (en) Rose-colored gold alloy compositions with reversible hardness characteristics
JP3187872U (ja) 装飾品及び装飾品用キット
US20110061426A1 (en) Jewelry made out of iridium and method of making jewelry out of iridium
KR101284750B1 (ko) 열처리 가공을 이용한 탄성복원력을 갖는 와이어 팔찌 및 그 제조방법
JP2010094150A (ja) 線状部材および装身具
WO2007148351A1 (fr) Bijou portable selon deux différentes configurations stables et procédé de fabrication de celui-ci
KR20180089090A (ko) 펜던트 위치 변경이 가능한 목걸이의 제조 방법 및 목걸이
US20060144086A1 (en) Ball-seam jewelry
US12082663B2 (en) Articulated cross pendant
ITVI950105A1 (it) Leghe a base di oro
US20080298997A1 (en) Platinum Alloy and Method of Production Thereof
US20100018179A1 (en) Planar, generally "u" or "v" shaped chain link
CN205018430U (zh) 一种外套编织物的首饰
JPH06118348A (ja) 形状記憶合金製部材及びそれを使用したメガネ部材
JPH04183403A (ja) 時計用外装部品の製造方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A2

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A2

Designated state(s): BW GH GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase