WO2005066245A1 - 樹脂組成物の製造方法およびそれにより製造される樹脂組成物 - Google Patents

樹脂組成物の製造方法およびそれにより製造される樹脂組成物 Download PDF

Info

Publication number
WO2005066245A1
WO2005066245A1 PCT/JP2004/016661 JP2004016661W WO2005066245A1 WO 2005066245 A1 WO2005066245 A1 WO 2005066245A1 JP 2004016661 W JP2004016661 W JP 2004016661W WO 2005066245 A1 WO2005066245 A1 WO 2005066245A1
Authority
WO
WIPO (PCT)
Prior art keywords
raw material
resin
material composition
production method
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2004/016661
Other languages
English (en)
French (fr)
Inventor
Shigetoshi Miyama
Yasuhide Okamoto
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
fA M Inc
Original Assignee
fA M Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by fA M Inc filed Critical fA M Inc
Priority to US10/553,088 priority Critical patent/US20060287441A1/en
Priority to EP20040799566 priority patent/EP1612234B1/en
Priority to AT04799566T priority patent/ATE445664T1/de
Priority to DE200460023596 priority patent/DE602004023596D1/de
Priority to JP2005509644A priority patent/JPWO2005066245A1/ja
Publication of WO2005066245A1 publication Critical patent/WO2005066245A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

　機械的物性に優れるポリエステル樹脂組成物を低コストで製造することができる樹脂組成物の製造方法およびそれにより製造される樹脂組成物を提供する。 　ポリエステル樹脂、ポリオレフィン樹脂および相溶化剤を含む原料組成物を水分の存在下で混練する。前記各成分を混合して原料組成物を調製した後に混練しても良いし、混練する段階で前記各成分を混合して前記原料組成物としても良い。必要に応じて前記原料組成物が植物組織由来成分や無機フィラー等の添加剤を含んでいても良い。また、必要に応じ、前記混練工程において、前記原料組成物構成成分のうち水分以外の少なくとも一つを前記原料組成物中に添加しながら混練することが好ましい。                                                                         

Description

樹脂組成物の製造方法およびそれにより製造される樹脂組成物 技術分野
[0001] 本発明は、榭脂組成物の製造方法およびそれにより製造される榭脂組成物に関す る。
背景技術
[0002] ポリエステル榭脂、特にポリエチレンテレフタレート（PET)榭脂は、軽くて、強ぐさ らに透明性に優れるため、飲料ボトル等に大量に消費されている。 日本国では容器 包装リサイクル法が施行される等、プラスチックに関してはリサイクル社会へ移行する 施策が進められており、今後も世界的な潮流力 PETボトル等のリサイクルが益々望 まれている。一方、 PET榭脂のリサイクル品すなわち再生品は、強度や成形加工性 の点で問題があるため、機械的物性レベルの向上が求められている。さらには PET 榭脂の未使用品においても、将来リサイクル化される場合に備えるため、同様に機械 的物性レベルの向上が求められている。
[0003] ポリエステル榭脂の機械的物性レベル向上の手法のひとつとして、他のポリマー、 例えばポリオレフイン (PO)榭脂とのァロイ化が試みられている。例えば、 PET榭脂（ 使用済）を、アイオノマー榭脂を用 、てポリエチレン榭脂 (使用済)やポリプロピレン榭 脂 (使用済）と相溶化させてポリマーァロイ化し、その機械的物性を向上させる事によ り、前記材料の成形品の用途拡大が図られている（例えば、特許文献 1参照)。しかし ながら、さらなる成形品用途の拡大を図るために、機械的物性を一段と向上させるこ とが求められている。
[0004] 一方、 PET榭脂等のポリエステル榭脂は、吸湿等により非常に加水分解しゃすぐ それが成形加工性や機械的物性の低下の原因となる。そのため、ポリエステル榭脂 を成形加工する際はもちろん、例えばポリマーァロイ材料等に材料加工する際には、 加水分解を防ぐため、厳密な含有水分の管理、すなわち真空乾燥等の高度な乾燥 工程が必須であるとされている。とりわけ、廃棄 PETボトルをフレーク状に粉砕したも の等は、粉砕工程後の洗浄工程で吸収した水分を熱風乾燥等によって除去するが、 完全な除去は非常に困難である。そのため PET榭脂が加水分解を起こし、溶融安定 性や機械的物性の低下を招き易 、。
[0005] PET樹脂から水分を除去する方法として、除湿乾燥機を用いる方法 (特許文献 2) や、未乾燥の PET榭脂をベント式射出成形機に直接供給してベント口から水分を除 去する方法 (特許文献 3および 4)等が提案されている。しかし、手間が掛かる、減圧 が不充分になり易ぐ除湿効果が減退してしまう等の問題があった。
[0006] また、 PET榭脂をその他の榭脂ゃフイラ一等と溶融混練する揚合には、 PET榭脂 の加水分解を防止するために、 PET榭脂やその粉砕品の乾燥のみならず、フィラー 等の乾燥も充分に行なう必要があるとされている。この乾燥の困難さや乾燥にかかる コストが、再生 PETを利用した多様なァロイ化ゃ改質、高機能化への展開を阻む要 因になっている。特に、植物成分系、天然繊維系フイラーゃ微粉状、層状無機フイラ 一等は含水率や吸湿性が高ぐ PETの加水分解を避けるための乾燥に時間とコスト 力 Sかかるという問題があった。
[0007] 特許文献 1：特開 2001—220473号公報
特許文献 2 :特開平 11— 123719号公報
特許文献 3 :特開平 6—315959号公報
特許文献 4：特開平 7— 60803号公報
発明の開示
[0008] したがって、本発明の目的は、機械的物性に優れるポリエステル榭脂組成物を低コ ストで製造することができる榭脂組成物の製造方法およびそれにより製造される榭脂 組成物を提供することを目的とする。
[0009] 前記課題を解決するために、本発明の製造方法は、榭脂組成物の製造方法であ つて、前記榭脂組成物は、ポリエステル榭脂、ポリオレフイン榭脂および相溶化剤を 含む原料組成物から製造され、前記原料組成物を水分の存在下で混練する混練ェ 程を有する製造方法である。
[0010] 本発明の製造方法によれば、機械的物性に優れるポリエステル榭脂組成物を低コ ストで製造することができる。
発明を実施するための最良の形態 [0011] 前記の通り、従来は、ポリエステル榭脂およびそれを含む組成物の加工の際には 加水分解を防ぐための乾燥工程が不可欠であるとされてきた。そして、この乾燥の困 難さや乾燥に力かるコストが、ポリエステル榭脂製品、特に再生 PET榭脂製品の機 械的物性向上および用途拡大を妨げていた。
[0012] しかし、本発明者らは、鋭意検討の結果、ポリエステル榭脂、ポリオレフイン樹脂お よび相溶化剤を含む原料組成物を混練して榭脂組成物を製造する際には、前記原 料組成物を乾燥する必要がないばかりか、逆に水分が存在することで機械的物性に 優れる榭脂組成物が得られることを見出した。この知見は従来の常識を覆すものであ り、原材料の含水量や吸湿性への懸念を払拭し、かつ乾燥工程等を不要とするポリ エステル榭脂組成物の製造が可能であることが判明した。
[0013] 本発明の製造方法において、水分が存在することで前記のような効果が得られる 理由は必ずしも明らかではないが、例えば以下のように考えられる。すなわち、水分 の存在により、前記相溶化剤の、ポリエステル榭脂およびポリオレフイン樹脂との反応 性や親和性が向上し、ァロイ化がさらに促進される。同時に、水分が前記相溶化剤 により消費されることでポリエステル榭脂の加水分解反応が抑制される。このため極 めて優れた機械的物性や成形加工性を有する榭脂組成物を得ることが可能となる。
[0014] 本発明の製造方法により、機械的物性に優れるポリエステル榭脂組成物を低コスト で製造することが可能となった。そればかりか、本発明の製造方法により得られた榭 脂組成物を成形加工等する際にも、前記榭脂組成物の加水分解を防ぐための厳密 な含有水分管理や真空乾燥工程等の乾燥工程を全て省略することもできる。このた め機械的物性に優れる榭脂製品を低コストで製造することが可能である。
[0015] 以下、本発明の実施形態について説明するが、本発明はこの実施形態には限定さ れず、本発明の趣旨を逸脱しない限りあらゆる変更が可能である。
[0016] 本発明の榭脂組成物の原料組成物は、前記の通り、ポリエステル榭脂、ポリオレフ イン榭脂および相溶化剤を含むが、本発明の趣旨を逸脱しない限りこれら以外の成 分を適宜含んでいても良い。以下、具体的に説明する。
[0017] 本発明に使用可能なポリエステル榭脂、ポリオレフイン榭脂および相溶化剤は特に 限定されず、公知のものを用いることができる。しかし、本発明によれば、前記の通り 機械的物性に優れる榭脂組成物が得られやすいため、例えば、従来は使用困難だ つたリサイクル材等も使 、やす 、。
[0018] 前記ポリエステル榭脂は特に限定されず、公知のものを適宜用いることができる力 例えば、ポリエチレンテレフタレート（PET)を含むことが好ましい。 PETは、周知の通 り、テレフタル酸を酸成分に、エチレングリコールをグリコール成分に用いた、主鎖に エステル結合を有する高分子量の熱可塑性ポリエステルである。その他、前記ポリェ ステル樹脂としては、例えば、酸成分として、イソフタル酸、オルトフタル酸、ナフタレ ンジカルボン酸、シユウ酸、アジピン酸、 1, 4ーシクロへキサンジカルボン酸等を、グリ コール成分として、ジエチレングリコール、プロピレングリコール、 1, 4 ブタンジォー ル、 1, 6—へキサンジオール、 1, 4ーシクロへキサンジメタノール、ビスフエノール A、 ポリエチレングリコール、ポリテトラメチレングリコール等を用いたものも使用できる。こ れら酸成分およびダリコール成分はそれぞれ一種類ずつ用いても良いし、二種類以 上共重合させても良い。具体的なポリエステル榭脂としては、例えば、 PETの他に、 ポリブチレンテレフタレート、ポリシクロへキシレンジメチレンテレフタレート等がある。 また、これらポリエステル榭脂は単独で用いても良いが、異なる化学構造のものを二 種類以上併用しても良ぐ例えばポリエチレンテレフタレート（PET)とポリブチレンテ レフタレート（PBT)との混合物等であっても良い。
[0019] 前記ポリエステル榭脂の形態も特に限定されず、どのような形態でも良い。例えば、 PETであれば、ボトル用、射出成形用、繊維用、フィルム用、シート用等として通常巿 販されているものを用いることができる。その他、未使用のペレット状製品はもちろん 、 PETボトル由来のものに代表される、フレーク状、ペレット状、パウダー状等のリサィ クル (再生）品、ケミカルリサイクル品等、形状や使用 ·再生経緯を限定されない。
[0020] 本発明の製造方法に用いるポリエステル榭脂は、前記の通り未使用品でも良いが 、例えば、リサイクル (再生)材由来のポリエステル榭脂を含むことが、製造コスト低減 および資源の有効利用等の観点力も好ましい。特に、 PETボトルは、回収量が多い にも関わらず、前記の通り、従来は乾燥の困難さが再利用の妨げとなっていた。しか し、本発明の製造方法を用いれば、手間やコストの力かる乾燥工程を用いなくとも機 械的物性等に優れるポリエステル榭脂組成物を製造できるため、使用済 PETボトル 等の資源としての利用価値を大いに高めることが期待できる。
[0021] 本発明に用いる PET榭脂の重合度は、特に限定されないが、固有粘度（25°C、ォ ルソクロ口フエノール中）が 0. 1-1. 0のものが好ましい。なお、本発明において、数 値範囲を限定している場合は、厳密にその数値範囲内であっても良いが、およそ (約 )その数値範囲内であっても良い。例えば、「固有粘度 0. 1-1. 0」と記載している場 合は、固有粘度が、厳密に 0. 1-1. 0でも良いが、約 0. 1-1. 0でも良ぐ「20重量 部以下」と記載している場合は、厳密に 20重量部以下でも良いし、約 20重量部以下 であっても良い。
[0022] また、本発明に用いるポリエステル榭脂は、高純度なものを用いても良いが、本発 明の効果を著しく損なわない範囲内で他の榭脂を含んでいても良い。前記他の榭脂 の含有量は特に限定されないが、通常は前記ポリエステル榭脂の重量を超えない程 度である。前記他の樹脂の種類も特に限定されないが、例えば、ポリスチレンやアタリ 口-トリルーブタジエン スチレン共重合体 (ABS)の様なスチレン系榭脂、エンジニア リング榭脂等の熱可塑性榭脂や、熱硬化性榭脂等が挙げられる。さらに、本発明に 使用可能なポリエステル榭脂としては、主にガスノ リャ性を改良した PETボトル (例え ば温ペット、ホットペットとも称される）から再生された PET榭脂、および、ポリアミド榭 脂、エチレン ビニルアルコール共重合榭脂等を混合または混練したポリエステル榭 脂、ならびに、それらを PET榭脂と多層化したり、シュリンクフィルムにして包装化した PET系ボトル、その他、各種成形品力ゝらの再生品や粉砕品等も挙げられる。なお、 前記ポリアミド榭脂としては、例えばナイロン 6、ナイロン 66 (ナイロンはデュポン社の 商品名）等が挙げられ、とりわけメタキシリレンジァミンとアジピン酸とを重縮合して得 られるポリアミド榭脂（ポリアミド MXD6と称されることがある）がよく用いられている。
[0023] 次に、前記ポリオレフイン (PO)榭脂について説明する。本発明に使用可能な PO 榭脂は特に限定されないが、例えば、低密度ポリエチレン (LDPE)、直鎖状低密度 ポリエチレン (LLDPE)、高密度ポリエチレン (HDPE)等の各種ポリエチレン、ポリプ ロピレン（PP)、ポリ— 1ーブテン、ポリイソブチレン、プロピレンとエチレンとのランダム 共重合体およびブロック共重合体 (任意に、プロピレンおよびエチレンと共重合可能 な単量体、および架橋性単量体の少なくとも一方を含んでいても良い）、エチレン プロピレン ジェン三元共重合体（エチレンとプロピレンとの比率は特に限定されず、 ジェン成分含有量も特に限定されないが例えば 50重量％以下）、ポリメチルペンテ ン、環状構造を含むポリオレフイン（例えば、シクロペンタジェンと、エチレンおよびプ ロピレンの少なくとも一方との共重合体）、エチレンまたはプロピレンの少なくとも一方 とその他のモノマー（例えば、酢酸ビニル、メタクリル酸アルキルエステル、アクリル酸 エステル、芳香族アルキルエステル、芳香族ビニル等のビ-ルイ匕合物等であり、含有 量は例えばエチレンまたはプロピレンに対し 50重量％以下）とのランダム共重合体、 ブロック共重合体およびグラフト重合体等を挙げることができ、これらはそれぞれ単独 で用いても良いし二種類以上併用しても良い。また、これらを二種類以上併用する場 合、必要に応じてグラフトコポリマー等の相溶化剤を併用することもできる。上記 PO 榭脂の製造方法は特に制限されない。また、 PO榭脂の立体規則性に関しても特に 限定されず、例えば、低アイソタクチシティ一のものから、メタ口セン触媒により製造さ れる高立体規則性ァイソタクチックまたはシンジオタクチックのもの等が挙げられる。
[0024] 前記ポリオレフイン榭脂は、例えば、ポリエチレン、ポリプロピレン、およびプロピレン とエチレンとの共重合体力 なる群力 選択される少なくとも一つを含むことが好まし い。これらのなかでも、低密度ポリエチレン (LDPE)、直鎖状低密度ポリエチレン (LL DPE)、高密度ポリエチレン（HDPE)等のポリエチレン、ポリプロピレン（PP)、ならび に、プロピレンとエチレンとのランダム共重合体およびブロック共重合体力 なる群か ら選択される少なくとも一つを含むことがより好ましぐ低密度ポリエチレン (LDPE)、 直鎖状低密度ポリエチレン (LLDPE)、高密度ポリエチレン (HDPE)等のポリェチレ ンを含むことが特に好まし 、。
[0025] また、 PO榭脂のメルトフローインデックス（MFR)は特に制限されな 、が、 50g/10 min.以下が好ましぐ lOg/lOmin.以下がより好ましい。前記 MFRの下限は特に 制限されないが、例えば、 0. lg/10min.以上である。
[0026] 次に、前記相溶化剤について説明する。本発明に用いる相溶化剤は特に限定され ず、種類や構造を問わず用いることができる。前記相溶化剤は、例えば従来と同様 のものが使用可能であるが、榭脂組成物の性能を向上させる観点から、例えば、ポリ エステル榭脂と PO榭脂との反応性や親和性等を高めたり、相溶、ァロイ化したり、こ れらの榭脂間の反応を促進したり、親和性を高めたり、お互いの分散性を向上したり 、適切な形態制御を発現したりするのに適した相溶化剤が好ましい。前記相溶化剤 は単独で用いても二種類以上併用しても良 、。
[0027] 前記相溶化剤は、例えば、エチレン系共重合体、アイオノマー榭脂、および変性水 添ポリマー成分力もなる群力も選択される少なくとも一つを含むことが好ましい。なお 、本発明では、「エチレン系共重合体」とは、エチレン系不飽和化合物を含む共重合 体を言い、エチレン系不飽和化合物以外の共重合成分としては、例えば、酸無水基 、エポキシ基、カルボキシル基、カルボン酸エステル等の極性基を含有する（変性さ れた)化含物が好ましい。また、前記「エチレン系不飽和化合物」とは、エチレン結合 すなわち炭素 炭素間二重結合を含む化合物を言い、例えばエチレンでも良いしそ れ以外の化合物でも良い。
[0028] 前記エチレン系共重合体において、エチレン系不飽和化合物と共重合する化合物 としては、例えば、アクリル酸、メタクリル酸、マレイン酸、フマル酸、ィタコン酸等の不 飽和カルボン酸およびその無水物；アクリル酸メチル、メタクリル酸メチル、マレイン酸 ジメチル、マレイン酸モノメチル、フマル酸ジェチル、ィタコン酸ジメチル、シトラコン 酸ジェチル、テトラヒドロ無水フタル酸ジメチル等の不飽和カルボン酸のエステル；グ リシジルアタリレート、グリシジルメタタリレート、 p—スチリルカルボン酸グリシジル等の 不飽和モノカルボン酸のグリシジルエステル；マレイン酸、ィタコン酸、シトラコン酸、 ブテントリカルボン酸等の不飽和ポリカルボン酸のモノグリシジルエステルあるいはポ リグリシジルエステル；ァリルグリシジルエーテル、 2—メチルァリルグリシジルエーテル 、 o—ァリルフエノールのグリシジルエーテル等の不飽和グリシジルエーテル等が挙げ られる。前記エチレン系不飽和化合物は、例えば、ォレフィン類、炭素数 2— 6の飽 和カルボン酸のビュルエステル類、炭素数 1一 8の飽和アルコール成分とアクリル酸 またはメタクリル酸とのエステル類およびマレイン酸エステル類およびメタクリル酸エス テル類およびフマル酸エステル類、ハロゲン化ビュル類、スチレン類、二トリル類、ビ -ルエーテル類およびアクリルアミド類等が挙げられる。より具体的には、エチレン、 プロピレン、ブテン 1、酢酸ビニル、アクリル酸メチル、アクリル酸ェチル、メタクリル 酸メチル、マレイン酸ジェチル、フマル酸ジェチル、塩化ビニル、塩化ビ-リデン、ス チレン、アクリロニトリル、イソブチルビ-ルエーテルおよびアクリルアミド等が挙げら れる。これらの中でもエチレン、プロピレンが好ましぐ特にエチレンが好ましい。
[0029] 前記エチレン系共重合体は、例えば、エチレンを第 2成分として酢酸ビニル、アタリ ルアクリル酸メチル等の第 3成分を共重合したものであれば、本発明の榭脂組成物 の耐衝撃性をさらに向上させることができるという理由力もより好ましい。前記第 3成 分は単独でも二種類以上併用しても良ぐその量は特に限定されないが、例えば前 記エチレン系共重合体の 20重量％以下、好ましくは 5— 15重量％である。これらは、 一般に、不飽和エポキシィ匕合物との二元共重合体またはエチレンおよび不飽和ェポ キシ化合物を含む三元共重合体として使用される。
[0030] 本発明の相溶化剤に用いるエチレン系共重合体のなかでも、とりわけ好ましいのは 、エポキシ基含有エチレン系共重合体である。本発明では、「エポキシ基含有ェチレ ン系共重合体」とは、不飽和エポキシ化合物とエチレン系不飽和化合物とを共重合 成分として含む共重合体を言う。前記エポキシ基含有エチレン系共重合体の組成比 率に特に限定はないが、エチレン系不飽和化合物の合計 100重量部に対して、共 重合された不飽和エポキシ化合物が、例えば 0. 1— 50重量部、好ましくは 1一 30重 量部である。これらのエポキシ基含有エチレン系共重合体は単独で用いても良いし 二種類以上併用しても良い。
[0031] なお、本発明では、「不飽和エポキシィ匕合物」とは、その分子中に、エチレン系不飽 和化合物と共重合し得る不飽和基およびエポキシ基を含む化合物を言 、、例えば、 不飽和グリシジルエステル類、不飽和ダルシジルエーテル類等が挙げられる。より具 体的には、例えば、グリシジノレアタリレート、グリシジルメタアタリレート、ィタコン酸ダリ シジルエステル類、ァリルダルシジルエーテル、 2—メチルァリルグルシジルエーテル 、スチレン p ダルシジルエーテル等が挙げられる。なかでもグリシジルメタアタリレ ートが特に好ましい。
[0032] 次に、本発明の相溶化剤に使用可能なアイオノマー榭脂は、特に限定されないが 、例えば、（i)ホスト高分子の主鎖に部分的に側鎖イオン基が存在する側鎖型、 (ii) 両末端に例えばカルボン酸基が存在するホスト高分子あるいはオリゴマーに金属ィ オンが中和する事により高分子化したテレグリック型、（iii)主鎖に陽イオンを有し、そ こに陰イオンが結合したアイォネン型、の各型のアイオノマー樹脂が挙げられる。 ホスト高分子のイオン基に対する対イオンとしては、 Li+、 Na+、 K+等のアルカリ金属ィ オン、 Mg2+、 Ca2+、 Sr2+、 Ba2+等のアルカリ土類金属イオン、 Zn \ Cu Mn Ni2+、 Co2+、 Co3+、
Figure imgf000010_0001
Cr3+等の遷移金属イオンが用いられる。また、陽イオンホスト高分 子に対しては、例えばハロゲン化物イオン、特に Cl—、 Br―、 Γ等の陰イオンが用いられ る。アイオノマー榭脂は、特に限定されないが、例えば、エチレンーメタクリル酸共重 合体アイオノマー、エチレン アクリル酸共重合体アイオノマー、プロピレン メタタリ ル酸共重合体アイオノマー、プロピレン アクリル酸共重合体アイオノマー、ブチレン アクリル酸共重合体アイオノマー、エチレン ビュルスルホン酸共重合体アイオノマ 一、スチレンーメタクリル酸共重合体アイオノマ一.スルホン化ポリスチレンアイオノマ 一、フッ素系アイオノマー、テレケリックポリブタジエンアクリル酸アイオノマー、スルホ ン化エチレン プロピレン ジェン共重合体アイオノマー、水素化ポリペンタマ一アイ オノマー、ポリペンタマ一アイオノマー、ポリ（ビュルピリジゥム塩）アイオノマ一'ポリ（ ビュルトリメチルアンモ -ゥム塩）アイオノマー、ポリ（ビュルべンジルホスホ-ゥム塩） アイオノマー、スチレン一ブタジエンアクリル酸共重合体アイオノマー、ポリウレタンァ ィオノマ一.スルホン化スチレン 2—アクリルアミドー 2—メチルプロパンサルフェイトァ ィオノマー、酸-アミンアイオノマー、脂肪族系アイォネン、芳香族系アイォネン等が 挙げられる。これらアイオノマー榭脂は、単独で用いても良いし、必要に応じて 2種以 上を混合して用いてもよい。これらアイオノマー樹脂のうち、エチレンーメタクリル酸共 重合体アイオノマー、エチレン アクリル酸共重合体アイオノマーが好まし 、。
[0033] また、本発明の相溶化剤に使用可能な変性水添ポリマー成分は、特に限定されな いが、例えば、酸無水基、エポキシ基、カルボキシル基、カルボン酸エステル等で変 性された、水添スチレンブタジエンラバー、スチレン 'エチレンブチレン'ポリエチレン ブロック共重合体、ポリエチレン.エチレンブチレン ·ポリエチレン ブロック共重合体 、スチレン'エチレン'プロピレン 'スチレン ブロック共重合体、スチレン 'エチレン'プ ロピレン ブロック共重合体等が挙げられる。これらは、単独で用いても良いし 2種類 以上を組み合わせて用いることもできる。
[0034] 次に、本発明の製造方法では、前記の通り、ポリエステル榭脂、ポリオレフイン榭脂 および相溶化剤以外の成分を適宜用いても良いが、例えば、前記原料組成物が、目 的に応じた添加剤をさらに含むことが好ましぐ前記添加剤は、例えば、植物組織由 来成分および無機フィラーの少なくとも一方を含むことがより好ましい。前記添加剤に より、場合によっては、本発明の榭脂組成物の機械的物性をさらに向上させたり、そ の成形品の外観や寸法精度の向上等を図ることもできる。さらに、塗装性、難燃性や 導電性等の新たな機能性等を付与することも可能である。以下、前記添加剤につい てより具体的に説明する。
[0035] 前記添加剤に使用可能な植物組織由来成分としては、例えば、木材 (例えば、松、 杉、ヒノキ等の針葉榭材、ブナ、シィ、ユーカリ等の広葉榭材)、籾殻、麦殻、竹、紙、 古紙、ダンボール、ノ ルプ、草、茶葉、牛乳パック、落花生の殻、サトウキビの滓、果 実の殻、藁、スターチ、コーヒーやココアの製造時搾り残滓等が挙げられる。これらは 、必要に応じて、粉砕機、ドライパルプ製造装置、レフアイナ一、グラインダ、エンドミ ル、パルパ一、解繊機等を用いて粉砕物や繊維化物とした後に用いても良い。前記 植物組織由来成分としては、ヤシやビン口ウジユウ等の果実繊維、コゥゾゥ、ミツマタ 、ジユート、ケナフ等のじん皮繊維、マニラ麻、サイザル葉脈繊維その他農作物の残 滓等も挙げられる。これら植物組織由来成分は単独で用いても二種類以上併用して も良ぐ形状、大きさ等も特に限定されない。
[0036] 前記植物組織由来成分の種類は、本発明の榭脂組成物の成形品に要求される性 能等に応じて任意に選択すれば良い。例えば、得られる異形成形品に高い木質感 を付与する場合は、木粉や籾殻紛が好ましい。これら粉末は、榭脂組成物が良好な 表面外観を発現するためには、 10メッシュ (網目幅 2000 μ m)の金網を通過する大 きさに微細化されて 、ることが好ましく、より好ましくは 50メッシュ（網目幅 290 μ m)パ ス以下の大きさであり、さらに好ましくは 100メッシュ（網目幅 149 /z m)パス以下の大 きさである。前記粉末の大きさの下限は特に限定されないが、例えば 325メッシュ (網 目幅 44 μ m)パス以上である。
[0037] なお、前記植物組織由来成分は一般的に吸湿性である。本発明の製造方法では、 前記の通り原料組成物を水分の存在下で混練することにより機械的物性等に優れた 榭脂組成物が得られるが、前記植物組織由来成分の含水率が大きすぎる場合等は 、必要に応じて適宜乾燥して用いても良い。
[0038] また、前記添加剤に使用可能な無機フイラ一としては、タルク、炭酸カルシウム、ゥ オラストナイト、炭酸マグネシウム、硫酸カルシウム、硫酸バリウム、酸ィ匕カルシウム、 酸化アルミニウム、酸化チタン、酸化マグネシウム、水酸化マグネシウム、水酸化アル ミニゥム、マイ力、ガラス繊維、ガラスフレーク、ガラスビーズ、炭素繊維、カーボンブラ ック、ケッチェンブラック、 CNT (カーボンナノチューブ）、グラフアイト、シリカ、シリカ 繊維、ケィ酸カルシウム、ケィ酸アルミニウム、カオリン、グラフアイト繊維、ァラミド繊 維、アルミナ繊維、シリカ ·アルミナ繊維、金属粉、金属繊維、チタン酸カリウムゥイス カー、ホウ酸アルミニウムウイスカー、マグネシウム系ゥイスカー、珪素系ゥイスカー、 セピオライト、アスベスト、スラグ繊維、ゾノライト、石膏繊維、ジルコユア繊維、窒化硼 素繊維、窒化珪素繊維、硼素繊維、酸化ジルコニウム、酸化鉄、チタン酸バリウム、 白土等が挙げられ、単独で用いても二種類以上併用しても良い。例えば水酸化マグ ネシゥム、水酸ィ匕アルミニウム等は榭脂組成物に難燃性を付与する目的に適してお り、カーボンブラック、ケッチェンブラック、 CNT (カーボンナノチューブ）、炭素繊維等 は、導電性を付与する目的に適している。
[0039] 前記無機フィラーの使用にあたっては、必要に応じて集束剤、表面処理剤等を併 用することが好ましい。前記集束剤および表面処理剤としては、例えば、エポキシ系 化合物、イソシァネート系化合物、シラン系化合物、チタネート系化合物等の官能性 化合物が挙げられる。これらの化合物は、あらかじめ無機フィラーに表面処理、集束 処理等を施すことで用いる力 または原料組成物調製の際同時に添加してもよい。
[0040] また、前記添加剤は、例えば、発泡剤を含んで!/、ても良 、。発泡剤は特に限定され ず、榭脂組成物製造に用いられる公知の発泡剤等を適宜用いることができるが、例 えば、二酸化炭素、窒素、炭化水素 (例えばブタン、ペンタン等）、フロン、代替フロン 等の気体、これら気体の超臨界流体、ァゾジカルボンアミド (ADCA)、 N, N—ジ-ト ロソペンタテトラミン、ァゾビスイソブチ口-トリル (AIBN)、タエン酸、重曹等の熱分解 型発泡剤、空気、水等が挙げられる。これら発泡剤は、単独で用いても良いし、必要 に応じて 2種以上を併用しても良い。なお、これら発泡剤は、その種類や発泡機構等 に応じ、前記原料組成物における前記添加剤として、混練前または混練中に添加し ても良いし、または、別途、混練後に添加しても良い。このとき、発泡剤を添加する方 法も特に限定されないが、例えば、混合しても良いし含浸させても良い。なお、水を 発泡剤として用いる場合は、例えば、別途、混練後（ァロイ化後）に添加することが好 ましい。
[0041] その他、前記添加剤としては、目的に応じた所望の特性を榭脂組成物に付与する ために、一般に熱可塑性榭脂に添加される公知の添加剤を適宜用いても良い。この ような添加剤として、例えば、酸化防止剤、加工安定剤、光安定剤や紫外線吸収剤 等の各種安定剤、難燃剤、可塑剤、軟化剤、滑剤、離型剤、帯電防止剤、耐衝撃改 良剤、染料や顔料等の着色剤、結晶化促進剤、結晶核剤、防腐剤、防カビ剤、防蟻 剤等を配合することができる。前記着色剤は特に限定されず、どのようなものでも良 いが、例えば二酸ィ匕チタン、酸化コバルト、群青、紺青、弁柄、銀朱、鉛白、鉛丹、黄 鉛、ストロンチウムクロメート、チタニウムイェロー、チタンブラック、ジンククロメート、鉄 黒、モリブデン赤、モリブデンホワイト、リサージ、リトポン、カーボンブラック、ェメラル ドグリーン、ギネー緑、カドミウム黄、カドミウム赤、コバルト青、ァゾ顔料、フタロシア- ンブルー、イソインドリノン、キナクリドン、ジォキサジンバイオレット、ペリノンペリレン 等が挙げられ、これらを単独でまたは 2種類以上を組み合わせて用いることができる 。これらの中でも、天然の木質感を出すためには黄色酸化チタン、弁柄 (酸化鉄)等 が好ましい。
[0042] また、前記原料組成物は、本発明の趣旨を逸脱しな ヽ範囲で、ポリエステル榭脂お よびポリオレフイン榭脂以外の他の熱可塑性榭脂 (例えば、アクリル榭脂、フッ素榭脂 、ポリアミド、ポリフエ-レンサルファイド、ポリエーテルエーテルケトン、ポリアセタール 、ポリカーボネート、ポリスルホン、ポリフエ-レンオキサイド等）、熱硬化性榭脂、およ び軟質熱可塑性榭脂等を含有することもできる。
[0043] 次に、本発明の製造方法についてさらに具体的に説明する。
[0044] 本発明の製造方法は、前記原料組成物を水分の存在下で混練する以外は従来の 榭脂組成物の製造方法と同様に行なっても良いし、必要に応じて適宜変更を加えて も良 、が、例えば以下のようにして実施することができる。
[0045] すなわち、まず、ポリエステル榭脂、ポリオレフイン榭脂、相溶化剤、および必要に 応じて前記添加剤等を準備し、これらを含む原料組成物を調製する。前記原料組成 物中におけるポリエステル榭脂の配合量は特に限定されないが、ポリエステル榭脂、 ポリオレフイン榭脂および相溶化剤の重量の合計に対し、好ましくは 10— 99. 8重量 %、より好ましくは 20— 95重量％、さらに好ましくは 50— 95重量％である。前記ポリ エステル榭脂配合量が 10— 99. 8重量％の範囲内であれば、成形カ卩ェ性および榭 脂組成物の機械的物性等の観点から好ま 、。
[0046] 前記原料組成物中におけるポリオレフイン (PO)榭脂の配合量は特に限定されな いが、ポリエステル榭脂、ポリオレフイン榭脂および相溶化剤の重量の合計に対し、 好ましくは 0. 1— 90重量％、より好ましくは 5— 80重量％、さらに好ましくは 10— 50 重量％である。前記 PO榭脂配合量は 0. 1重量％以上が榭脂組成物の機械的物性 の観点力 好ましぐ 90重量％以下が成形性ゃ榭脂組成物成形品の剛性等の観点 力 好ましい。
[0047] 前記原料組成物中における相溶化剤の配合量は特に限定されな ヽが、ポリエステ ル榭脂、ポリオレフイン榭脂および相溶化剤の重量の合計に対し、好ましくは 0. 1— 20重量％、より好ましくは 0. 5— 15重量％、さらに好ましくは 1一 10重量％である。 前記相溶化剤配合量は 0. 1重量％以上が榭脂組成物の機械的物性の観点力 好 ましぐ 20重量％以下が製造コストゃ榭脂組成物の成形加工性等の観点力 好まし い。
[0048] 前記原料組成物中における添加剤の配合量は特に限定されな ヽが、ポリエステル 榭脂、ポリオレフイン榭脂および相溶化剤の重量の合計 100重量部当たり、好ましく は 1一 200重量部、より好ましくは 10— 100重量部、さらに好ましくは 15— 80重量部 である。前記添加剤配合量は、 1重量部以上が、榭脂組成物の機械的物性のさらな る向上や新たな機能の付与効果等の観点から好ましぐ 200重量部以下が、榭脂組 成物の成形加工性や成形品の外観等の観点カゝら好ましい。
[0049] 次に前記原料組成物を水分の存在下で混練して目的の榭脂組成物を得る。以下 、混練条件等について具体的に説明する。
[0050] 本発明の製造方法では、前記各成分を混合して原料組成物を調製した後に混練 しても良いし、混練する段階で前記各成分を混合して前記原料組成物としても良い。 また、必要に応じ、前記混練工程において、前記原料組成物構成成分のうち水分以 外の少なくとも一つを前記原料組成物中に添加しながら混練することが好ましい。例 えば、前記添加剤が発泡剤を含む場合、発泡剤は、前述の通り、その種類や発泡機 構等に応じ、混練前に前記原料組成物中に含有させても良いし、混練中に添加して も良い。また、発泡剤は、場合によっては、混練後に別途添加して良いことも前述の 通りである。
[0051] 本発明の製造方法では、水分は、その成分内容や温度の制限は特に無ぐ例えば 水道水、井戸水、工業用水、蒸留水、飲料専用水、自然 ·天然水、河川，湖水、湧出 水、水蒸気等が挙げられるが、いずれも不純物の極力少ないものが好ましい。また、 前記水分として、氷塊、氷粉、氷粒等を用いても良い。前記水分の温度は特に限定 されず、室温でも問題ないが、より高温であれば、相溶化剤の機能を高める観点や、 混練装置の運転性や効率の向上を図る観点力も好ましい。具体的には、前記水分 は、温度 40°C以上の水および水蒸気の少なくとも一方を含むことが好ましぐ 80°C 以上の熱水や水蒸気を含むことがより好ましい。混練方法も特に限定されないが、例 えば、せん断力による練りをカ卩えることが可能な混練装置を用いて混練することがで きる。前記混練装置も特に限定されないが、例えば、ロール-一ダー、バンバリ一ミキ サー、インターミックス、一軸押出機、二軸押出機等が挙げられ、好ましくは二軸押出 機、より好ましくはベント (脱気口）等の孔部を一つ以上備える二軸押出機である。ま た、前記混練装置は一種類のみ用いても良いが、二種類以上の混練装置を用い、 複数回混練しても良い。
[0052] 前記原料組成物に対する水分の添加方法も特に限定されず、例えば、あらかじめ 前記原料組成物が水分を含む状態で前記混練工程に移行しても良いし、前記混練 工程において、前記原料組成物中に水分を添加しながら混練しても良い。もちろん、 あらかじめ前記原料組成物が水分を含む場合でも、必要に応じて前記混練工程中 に適宜水分を添加して良い。特に、前記混練工程において、前記原料組成物構成 成分のうち水分以外の少なくとも一つを前記原料糸且成物中に添加しながら混練する 場合は、前記原料組成物中に水分を添加しながら混練することがより好ましい。
[0053] 前記原料組成物に対する水分の添加量は特に限定されないが、本発明の効果を 充分に発揮する観点から、多すぎずかつ少なすぎな!、量に適宜設定することが好ま しい。具体的には、前記原料組成物が水分を含む状態で前記混練工程に移行する 場合、前記混練工程移行直前の前記原料組成物中の水分含有量が、水分以外の 前記原料組成物構成成分の合計 100重量部当たり 0. 01— 20重量部が好ましぐよ り好ましくは 0. 01— 10重量部、さらに好ましくは 0. 05— 7重量部である。前記水分 含有量がこのような範囲であれば本発明の効果が充分に発揮されやすぐまた、混 練装置が例えば押出機の場合、前記水分含有量が 20重量部以下であればスクリュ 一後方部への水分の逆流現象等が発生し難 、ため好ま U、。
[0054] また、前記混練工程にお!、て、前記原料組成物中に、水分および前記原料組成物 構成成分のうち水分以外の少なくとも一つを添加しながら混練する場合は、前記水 分の 1時間当たりの添加量は、上記と同様の観点から、水分以外の前記原料組成物 構成成分の 1時間当たりの添加量合計 100重量部当たり 0. 01— 20重量部が好まし ぐより好ましくは 0. 01— 10重量部、さらに好ましくは 0. 05— 7重量部である。なお 、水分以外の前記原料組成物構成成分の添加方法として、例えば、押出機等の混 練装置の材料供給口から供給する方法を用いることができ、その場合、水分以外の 前記原料組成物構成成分の添加量 (供給量)を、混練押出吐出量もしくは押出吐出 量、または単に押出量、吐出量等と呼ぶことがある。
[0055] 前記原料組成物に対する水分添加量の好ましい範囲は前記の通りである力 この 水分添加量は、例えば前記原料組成物における各構成成分の配合量等に応じて適 宜調整すると、特に本発明の効果が発揮されやすい。前記各構成成分として使用す る具体的な物質の種類等にもよるので一概には言えないが、前記原料組成物中に おいて相溶化剤の含有率が大きい場合は水分添加量も多めにする方が本発明の効 果が発揮されやすい傾向がある。また、相溶化剤ほどではないがポリオレフイン榭脂 含有率も水分添加量との相関性があり、ポリオレフイン榭脂含有率が大きい場合は水 分添加量を多めにする方が本発明の効果が発揮されやす ヽ傾向がある。
[0056] 本発明の製造方法における原料組成物調製および水分添加の方法としては、より 具体的には、例えば、
(i)事前にヘンシェルミキサー（三井鉱山株式会社の商品名）やタンブラ一で所定量 の水分を原料組成物に混合し、その後、前記原料組成物を混練装置へ供給する方 法、
(ii)あらカゝじめ、水分以外の全ての原料組成物構成成分をヘンシェルミキサーやタン ブラーで混合して原料組成物を調製後、あるいは、（自動)計量装置で個別に所定 量の各原料組成物構成成分を混練装置の材料供給口へ供給しながら、その材料供 給口から、所定量 (水分以外の全原料組成物構成成分の供給量 (押出吐出量)見合 い)の水分を、一定量ずつ供給する方法、
(iii)あら力じめ、水分以外の全ての原料組成物構成成分を、ヘンシェルミキサーゃタ ンブラーで混合した後、あるいは、（自動)計量装置で個別に所定量の各原料組成物 構成成分を混練装置の材料供給口へ供給しながら、材料供給口以外の 1ケ所以上 のベント等の孔部から、所定量 (水分以外の全原料組成物構成成分の供給量 (押出 吐出量)見合 、)の水分を一定量ずつ供給する方法、
(iv)あらかじめ、水分以外の各原料組成物構成成分の所定量を（自動)計量装置で 個別に混練装置の材料供給口や他の孔部へ併行供給しながら、同時に、混練装置 の材料供給口や材料供給口以外の 1ケ所以上のベント等の孔部から、所定量 (水分 以外の全原料組成物構成成分の供給量 (押出吐出量)見合!、)の水分を一定量ず つ供給する方法、等が挙げられる。
[0057] 上記以外の混練条件は特に限定されず、例えば各成分の溶融や混練がスムーズ に行なわれるように適宜設定すれば良い。温度設定は、混練時において、混練装置 のシリンダー等の内部温度を、例えば 260°C— 310°Cの範囲とすることが好ましぐ 2 70°C— 300°Cの範囲がより好ましい。また、混練装置が二軸押出機等の連続押出機 の場合のスクリュー回転数は、各成分を充分混練出来るレベルであれば良いが、 30 一 lOOOrpmの範囲が好ましぐ 50— 600rpmの範囲力より好ましい。
[0058] このように、前記原料組成物を水分の存在下で混練して目的の榭脂組成物を得る ことができるが、本発明の榭脂組成物の製造方法は、さらにその他の工程を適宜含 んでいても良い。例えば、混練して得られた榭脂組成物を適宜成形する工程をさら に含むことが好ましい。成形方法は特に限定されず、公知の方法を用いることができ るが、例えば、混練装置が押出機である場合は、混練後、そのまま押出成形により成 形すれば良い。
[0059] また、本発明の榭脂組成物の製造方法は、前記原料組成物を水分の存在下で混 練した後、発泡剤を添加して発泡させる工程をさらに含んでいても良い。または、前 記原料組成物が、添加剤として発泡剤を含んでいても良ぐ発泡剤は混練前に前記 原料組成物中に含有させても良 、し、混練中に添カ卩しても良 、ことは前述の通りであ る。この場合、前記原料組成物を水分の存在下で混練することにより発泡させても良 いし、または混練後に発泡させても良い。本発明の榭脂組成物の製造方法における 発泡方法は特に限定されないが、例えば、超臨界流体により発泡させる方法等が好 ましぐ超臨界二酸ィ匕炭素および超臨界窒素のうち少なくとも一方を用いる方法が特 に好ましい。また、混練後に発泡させる方法としては、例えば、いわゆる注型発泡等 がある。
[0060] 以上のようにして本発明の榭脂組成物の製造方法を実施することができる。
[0061] 本発明の榭脂組成物は、本発明の製造方法により製造されることで機械的物性に 優れ、低コストで製造できるが、この製造方法に限定されず、どのような製造方法で 製造しても良い。また、本発明の榭脂組成物の形態も特に限定されず、あらゆる形態 が可能であり、例えば、公知の熱可塑性榭脂組成物と同様の形態で用いることがで きる。例えば、本発明の榭脂組成物が発泡体である場合は、発泡シート、発泡ボード 、発泡マット、発泡厚板、発泡トレー、発泡型物等の形態が可能である。
[0062] 本発明の榭脂組成物の用途は特に限定されず、各種榭脂製品に幅広く使用でき るが、例えば、建築用材料、日常生活用品、工業部品、土木資材、農業資材、包装 資材、物流資材、導電材料等に使用できる。また、本発明の榭脂組成物が発泡体で ある場合は、例えば、断熱材、緩衝材、軽量化材、包装材、運搬材、被覆材等に使 用できる。断熱材は、例えば、建築用断熱材、工業部品用断熱材、物流資材用断熱 材等であっても良い。
実施例
[0063] 次に、本発明の榭脂組成物の製造方法およびそれにより得られる榭脂組成物の実 施例について説明する。
[0064] [I]原材料 本実施例で製造した榭脂組成物の原材料は以下に示すとおりである。
(1)ポリエステル榭脂 (成分 A)
A— 1 :三菱レイヨン製 PET榭脂（商品名ダイヤナイト「KR582」、固有粘度 =0. 65 ( 25°C、オルソクロロフエノール中）、未使用ペレット）
A— 2：お茶用等の巿販の PETボトルの空きボトルを粉砕してフレーク状にしたもの（ 固有粘度 =0. 70 (25°C、オノレソクロロフエノーノレ中））
(2)ポリオレフイン (PO)榭脂 (成分 B)
B-1 :日本ポリエチレン製、直鎖状ポリエチレン（商品名「UF440」、 MFR(190°C) = 1. 7g/ min.、未使用ペレット）
(3)相溶化剤 (成分 C)
C-1：エチレンーグリシジルメタタリレート（6重量0 /0)共重合体、ペレット
C-2：エチレンーグリシジルメタタリレート（12重量0 /0)共重合体、ペレット
C-3：エチレンーメタクリル酸共重合体アイオノマー、ペレット
(4)添加剤 (成分 D)
D-1：植物組織由来成分 (松の粉砕粉、平均粒度 = 75メッシュ（210 μ m) )
D— 2 :無機フィラー（タルク、平均粒径 = 5 m、中国産原石を粉砕分級したもの、パ ウダ一）
(5)水分 (成分 E)
E - 1 :室温の水（水道水）
E-2： 82°Cの熱水（水道水を加熱し熱水化したもの）
[0065] [II]混練装置
本実施例で用いた混練装置は、以下に示すとおりである。
BT30 (商品名）：プラスチック工学研究所製、二軸押出機、スクリュー径 30mm KTX80 (商品名）：神戸製鋼所製、二軸押出機、スクリュー径 77mm
[0066] [III]物性評価方法
本実施例で製造した榭脂組成物の物性評価は、次に示すとおりの評価方法で行つ た。
(1)試験片調製:本実施例で製造した榭脂組成物を JIS標準試験片 CFIS - K7162の 1A型、 t=4mm)に成形し、それを用いて物性評価を行なった。前記試験片は、新 潟鉄工製射出成形機 AN100型 (商品名）を用いて成形 (成形温度 260°C、金型温 度 80°C)すること〖こより調製した。
(2)引張強度'伸び:東洋精機製ストログラフ VE10D型 (商品名）で測定した。測定 条件【ぉ13—1^7161、：《：7162に準拠し、引張速度 = 50mmZmin.、気温 23°Cおよ び相対湿度 50%条件下で測定した。
(3)曲げ弾性率:東洋精機製ストログラフ VEIOD型 (商品名）で測定した。測定条件 ίお IS— K7171に準拠し、曲げ速度 = 2mmZmin.、気温 23°Cおよび相対湿度 50 %条件下で測定した。
(4)アイゾット衝撃強度：東洋精機製デジタル衝撃試験機 DG— UB型 (商品名）で測 定した。測定条件〖お IS - K7110に準拠し、ノッチ付、気温 23°Cおよび相対湿度 50 %条件下で測定した。
(5)ロックウェル硬度：東洋精機製デジタルロックウェル硬度計 E型（商品名）で測定し た。測定条件 ίお IS-K7202-2に準拠し、 Rスケール、気温 23°Cおよび相対湿度 50 %条件下で測定した。
(榭脂組成物の製造）
以下のようにして 15種類の榭脂組成物を製造した。それぞれを実施例 1一 11およ び比較例 1一 4とする。すなわち、まず、各組成物製造用の原料成分を、下記表 1に 示す比率で準備した。表 1中、成分 A— Cの各成分の配合量は、成分 A— Cの重量 合計に対する重量％で示している。成分 Dの配合量は、成分 A— Cの重量合計 100 重量部に対する重量部で示している。そして、成分 Eの添加量は、混練時における 1 時間当たりの添加量であり、成分 A—成分 C (実施例 9および 10は成分 A—成分 D) の 1時間当たりの添加量合計 100重量部に対する添加量 (重量部）で示している。ま た、表 1中に成分の種類および配合量を示していない場合、その成分は用いなかつ たことを示す。
[表 1] ポリエステル
PO樹脂 相溶化剤 添加剤 水分
番号 棚旨
(成分 (成分 C) (成分 D) (成分 E)
(成分 A) 灘 配合 配合 配合 配合 添加 乾 機 種類 種類 種類 翻 量 燥
(%) (%) (%) (¾) (部） 難例
1 A— 1 67 B— 1 30 C 1 3 —— E - 1 0.2 無 BT30
2 A— 1 67 B— 1 30 C一 1 3 —— E - 1 2 BT30
3 A - 1 67 B— 1 30 C一 1 3 —— E 2 2 BT30
4 A— 1 82 B— 1 15 C一 1 3 —— E— 1 2 BT30
5 A- 1 69 B— 1 30 C- 1 1 —— E— 1 2 BT30
6 A - 2 67 B - 1 30 C一 1 3 —— E— 1 2 4m BT30
7 A- 1 67 B- 1 30 C 2 3 —— E- 1 2 BT30
8 A— 1 67 B— 1 30 3 —— E- 1 2 無 BT30
9 A— 1 67 B- 1 30 C-2 3 D - 1 30 E- 1 2 BT30
10 A— 2 67 B- 1 30 C-2 3 D-2 30 E - 1 2 BT30
11 A— 1 67 B— 1 30 C一 1 3 —— E 1 2 KTX80 m
1 A- 1 70 B- 1 30 有 BT30
2 A— 1 67 B— 1 30 C一 1 3 有 BT30
3 A- 1 70 B- 1 30 E- 1 0.1 有 BT30
4 A- 1 70 B— 1 30 E— 1 2 有 BT30
次に、各成分を混合および混練するに先立ち、比較例 1 4については成分 A— 1 を 120°Cで 10時間乾燥した。実施例 1 11につ 、ては各成分の事前乾燥は特に行 なわなかった。そして、実施例 1 11および比較例 1 4のそれぞれについて、前記 表 1に示す配合で、成分 A、成分 B、および成分 C (比較例 1 3および 4については 成分 cは用いず)を、タンブラ一ミキサーで充分混合した。この混合物を混練押出機 BT30 (但し実施例 11のみ KTX80)中に一定量ずつ添カ卩しながら 280°Cで溶融お よび混練し、さらに造粒し、目的とする榭脂組成物をペレットとして得た。このとき、実 施例 9および 10においては、成分 D— 1、 D— 2は、別供給口から、自動供給装置で所 定量を同時供給した。また、実施例 1一 11、比較例 1および 2については、水分 (成 分 E)を、材料供給口から定量供給ポンプ (東京理化器械製)を用いて所定量注入し ながら、溶融、混練および造粒した。
(物性評価）
上記のようにして得られた榭脂組成物のペレットをそれぞれ射出成形機へ供して成 形し、評価用試験片を調製して評価を行った。なお、射出成形に際しては、ペレット の事前乾燥は特に行なわな力つた。その評価結果を下記表 2に示す。
[表 2]
引張搬 引張伸び 曲け ¾性率 アイ'/ット衝撃 ロックウェル鹏
番号
MP a % MP a J/m
実施例
1 30. 6 211 1136 59 83
2 31. 4 315 1156 63 85
3 31. 3 336 1154 65 84
4 30. 9 253 1178 60 84
5 32. 1 183 1 316 51 86
6 31. 3 307 1157 59 84
7 31. 2 401 1155 67 83
8 30. 1 197 1150 51 83
9 31. 1 13 1833 30 87
10 30. 1 65 2005 41 85
11 31. 1 320 1155 63 84 比翻
1 31. 3 6 1244 41 83
2 29. 2 61 1160 55 82
3 30. 9 7 1242 39 83
4 31. 1 5 1240 33 84
[0070] 表 2から分力 通り、実施例 1一 11の榭脂組成物は、いずれも良好な機械的物性を 示した。特に、実施例 1一 8および 11の榭脂組成物は、材料の靭性に直結する引張 伸び性が極めて優れていた。具体的には、実施例 1一 8および 11の榭脂組成物に おける引張伸び数値は、相溶化剤 (成分 C)を加えたが水分 (成分 E)を加えなかった 比較例 2の榭脂組成物と比べて約 3— 6.5倍というきわめて高い数値を示し、その他 の機械的物性についても比較例 2と同等以上であった。
[0071] さらに、添加剤 (成分 D)を加えた実施例 9および 10の榭脂組成物も全体として比 較例 2に劣らない機械的物性を示し、曲げ弾性率ではむしろ比較例 2を大きく上回つ ていた。すなわち、実施例 9および 10の榭脂組成物は、植物組織由来成分や無機フ イラ一を大量に加えたにも関わらず、それらを加えない従来品に劣らない機械的物 性が得られたことが分力ゝつた。特に、無機フィラー (タルク）を加えた実施例 10の榭脂 組成物は引張伸び値にお!、ても比較例 2に劣らな 、値を示したことから、剛性および 高い靭性を要求される様々な用途に本発明の榭脂組成物が有用であることが期待 できる。
[0072] また、実施例 7、 9および 10の榭脂組成物を、それぞれポリ塩化ビュル用異型押出 機で成形して建材用モデル長尺板 (概略寸法 · · ·幅 120mm X平均肉厚 2mm)を得た 。成形性は良好で、得られた建材用モデル長尺板は、良好な外観と表面硬度、強度 および寸法精度を発現した。このように、本発明によれば、例えば、機械的物性等に 優れるのみならず、ポリ塩化ビニルと同様の成形性を持ち、ポリ塩ィ匕ビニルの代替と して使用可能な榭脂組成物を提供することもできる。
産業上の利用の可能性
[0073] 以上説明した通り、本発明によれば、機械的物性に優れるポリエステル榭脂組成物 を低コストで製造することができる製造方法およびそれにより製造される榭脂組成物 を提供することができる。本発明の榭脂組成物の用途は特に限定されず、各種榭脂 製品に幅広く使用できる。特に、本発明によれば、優れた機械的物性、成形性、外 観、強度および寸法安定精度を有し、また、ポリ塩化ビニル用成形設備への適用性 にも優れる榭脂組成物を提供し、各種建材や、日常生活用品、工業部品等への重 要な素材として利用することも可能である。さらに、本発明によれば、大量に発生しつ つある PETボトルの破砕品等の PET樹脂リサイクル材を主原料として榭脂組成物を 製造する事も出来るため、環境保護面においても重要な材料製造技術および素材 を提供できる。

Claims

請求の範囲
[I] 榭脂組成物の製造方法であって、前記榭脂組成物は、ポリエステル榭脂、ポリオレフ イン榭脂および相溶化剤を含む原料組成物から製造され、前記原料組成物を水分 の存在下で混練する混練工程を有する製造方法。
[2] 前記ポリエステル榭脂がポリエチレンテレフタレート（PET)を含む請求項 1に記載の 製造方法。
[3] 前記ポリエステル榭脂が、リサイクル (再生)材由来のポリエステル榭脂を含む請求項 1に記載の製造方法。
[4] 前記原料組成物中における前記ポリエステル榭脂の重量が、前記ポリエステル榭脂
、ポリオレフイン榭脂および相溶化剤の重量の合計に対し、 10— 99. 8重量0 /0である 請求項 1に記載の製造方法。
[5] 前記ポリオレフイン榭脂力 ポリエチレン、ポリプロピレン、およびプロピレンとエチレン との共重合体力 なる群力 選択される少なくとも一つを含む、請求項 1に記載の製 造方法。
[6] 前記原料組成物中における前記ポリオレフイン (PO)榭脂の重量力 前記ポリエステ ル榭脂、ポリオレフイン榭脂および相溶化剤の重量の合計に対し、 0. 1一 90重量0 /0 である請求項 1に記載の製造方法。
[7] 前記相溶化剤が、エチレン系共重合体、アイオノマー榭脂、および変性水添ポリマ 一成分力 なる群力 選択される少なくとも一つを含む請求項 1に記載の製造方法。
[8] 前記原料組成物中における前記相溶化剤の重量が、前記ポリエステル榭脂、ポリオ レフイン榭脂および相溶化剤の重量の合計に対し、 0. 1一 20重量％である請求項 1 に記載の製造方法。
[9] 前記原料組成物が添加剤をさらに含む請求項 1に記載の製造方法。
[10] 前記添加剤が、植物組織由来成分および無機フィラーの少なくとも一方を含む請求 項 9に記載の製造方法。
[I I] 前記原料組成物中における前記添加剤の重量が、前記ポリエステル榭脂、ポリオレ フィン榭脂および相溶化剤の重量の合計 100重量部当たり 1一 200重量部である請 求項 9に記載の製造方法。
[12] 前記原料組成物が水分を含む状態で前記混練工程に移行する請求項 1に記載の 製造方法。
[13] 前記混練工程移行直前の前記原料組成物中の水分含有量が、水分以外の前記原 料組成物構成成分の合計 100重量部当たり 0. 01— 20重量部である請求項 12に記 載の製造方法。
[14] 前記混練工程にお!ヽて、前記原料組成物中に水分を添加しながら混練する請求項 1に記載の製造方法。
[15] 前記混練工程において、前記原料組成物構成成分のうち水分以外の少なくとも一つ を前記原料組成物中に添加しながら混練する請求項 1に記載の製造方法。
[16] 前記混練工程にお!、て、前記原料組成物中に水分を添加しながら混練し、前記水 分の 1時間当たりの添加量が、水分以外の前記原料組成物構成成分の 1時間当たり の添加量合計 100重量部当たり 0. 01— 20重量部である請求項 15に記載の製造方 法。
[17] 前記水分が、温度 40°C以上の水および水蒸気の少なくとも一方を含む請求項 1に 記載の製造方法。
[18] 前記添加剤が発泡剤を含む、請求項 9に記載の製造方法。
[19] 前記原料組成物を水分の存在下で混練することにより発泡させる、請求項 18に記載 の製造方法。
[20] 前記原料組成物を混練後に発泡させる、請求項 18に記載の製造方法。
[21] 前記原料組成物を水分の存在下で混練した後、発泡剤を添加して発泡させる工程 をさらに含む、請求項 1に記載の製造方法。
[22] 請求項 1に記載の製造方法により製造される榭脂組成物。
[23] 発泡体である、請求項 22に記載の榭脂組成物。
[24] 発泡シート、発泡ボード、発泡マット、発泡厚板、発泡トレーまたは発泡型物である、 請求項 23に記載の榭脂組成物。
[25] 請求項 22に記載の榭脂組成物を用いた榭脂製品。
PCT/JP2004/016661 2004-01-07 2004-11-10 樹脂組成物の製造方法およびそれにより製造される樹脂組成物 Ceased WO2005066245A1 (ja)