WO2004073436A1 - Fixable interlining material, method for the production thereof, and use thereof - Google Patents

Fixable interlining material, method for the production thereof, and use thereof Download PDF

Info

Publication number
WO2004073436A1
WO2004073436A1 PCT/EP2003/001670 EP0301670W WO2004073436A1 WO 2004073436 A1 WO2004073436 A1 WO 2004073436A1 EP 0301670 W EP0301670 W EP 0301670W WO 2004073436 A1 WO2004073436 A1 WO 2004073436A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyamide
coating
copolyamide
powder
sub
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2003/001670
Other languages
German (de)
French (fr)
Other versions
WO2004073436A9 (en
Inventor
Hans-Jürgen Preuss
Gerhard Thoenissen
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hansel Textil GmbH
Original Assignee
Hansel Textil GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hansel Textil GmbH filed Critical Hansel Textil GmbH
Priority to PCT/EP2003/001670 priority Critical patent/WO2004073436A1/en
Priority to DE10394096T priority patent/DE10394096A5/en
Priority to AU2003208875A priority patent/AU2003208875A1/en
Publication of WO2004073436A1 publication Critical patent/WO2004073436A1/en
Publication of WO2004073436A9 publication Critical patent/WO2004073436A9/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

The invention relates to a fixable interlining material comprising a coating which is based on a copolyamide and guarantees the maximum requirements regarding care treatments while allowing finishing treatments such as garment dyeing, stone washing, enzyme washing, and bleaching to be done regardless of the substrate used. Said coating essentially comprises the components polycaprolactam (polyamide 6, PA 6) and/or polyundecanamide (polyamide 11, PA 11) and/or polylaurinlactam (polyamide 12, PA 12) and/or polyhexamethylene adipamide (polyamide 6.6, PA 6.6), the moieties of said components being as follows (in percent by weight): polyamide 6: maximum 45 to 55, minimum 10 to 22; polyamide 6.6: maximum 75 to 85, minimum 20 to 45; polyamide 12 and/or polyamide 11: maximum 50 to 70, minimum 18 to 30. Preferably, the moieties are selected such that the melting temperatures range between 110 and 150 DEG C, especially between 120 and 145 DEG C. Preferably, polyamide 12 and/or polyamide 11 is/are combined with only one of the two other polyamides. The invention further relates to a method for producing the interlining material and the use thereof.

Description

Fixierbarer Einlagestoff sowie Verfahren zu seiner Herstellung und dessen Verwendung Fixable interlining material and method for its production and its use

Die Erfindung betrifft einen fixierbaren Einlagestoff mit einer Beschichtung auf der Basis eines Copolyamids. Die Erfindung betrifft zudem ein Verfahren zur Herstellung des Einlagestoffes sowie seine Verwendung.The invention relates to a fixable interlining with a coating based on a copolyamide. The invention also relates to a method for producing the interlining and its use.

Einlagestoffe bestehen aus einem Substrat, z.B. einem Gewebe, einer Wirkware oder einem Vliesstoff. Das Basismaterial des Substrats kann für ein Gewebe Cv/PES, PES, Co, Co/PES, Co/CV, Co/Wo, sowie für Wirkware PES, Cv/PES, PES/Co, PA/Co, PA/CV und für Vliesstoffe PA, PA/PES, PES, PES/Cv sein. Zur Beschichtung werden heißsiegelfähige thermoplastische Kleber, z.B. Copolye- ster, Copolyamide, Polyethylen, Ethylenvinylacetat, Polyvinylchlorid verwendet. Die Beschichtung wird z.B. als Pulverpunkt, Doppelpunkt, Pastenpunkt oder durch Streubeschichtung aufgebracht .Interlinings consist of a substrate, e.g. a woven fabric, a knitted fabric or a nonwoven fabric. The base material of the substrate can be for a fabric Cv / PES, PES, Co, Co / PES, Co / CV, Co / Wo, as well as for knitwear PES, Cv / PES, PES / Co, PA / Co, PA / CV and for Nonwovens PA, PA / PES, PES, PES / Cv. Heat-sealable thermoplastic adhesives, e.g. Copolyester, copolyamides, polyethylene, ethylene vinyl acetate, polyvinyl chloride used. The coating is e.g. applied as powder point, colon, paste point or by scatter coating.

Aus dem Einlagenstoff wird eine Einlage zugeschnitten und mit einem Oberstoff durch Klebung fixiert. Von einer Beschichtung wird verlangt, dass sie eine sehr gute Haftung, Sicherheit gegen Rück- und Durchschlag sowie einen weichen Griff gewährleistet.An insert is cut from the insert material and fixed with an outer material by gluing. A coating is required to ensure very good adhesion, security against kickback and puncture as well as a soft grip.

Fixierungen können Probleme beim Pflegen von Textilerzeugnissen bereiten. Auch aus diesem Grund wurden Pflegekennzeichen in Form von Symbolen für das Waschen, Bleichen, Bügeln, chemisch Reinigen und Trocknen geschaffen, die den Verbraucher über passende Pflegebehandlungen informieren. Falsche Pflegebehandlungen können ein Kleidungsstück unbrauchbar machen. Derzeit ist kein Fixiereinlagestoff bekannt, der den Höchstanforderungen aller Pflegebehandlungen entspricht. Höchstanforderungen sind derzeit:Fixations can cause problems when maintaining textile products. For this reason too, care labels were created in the form of symbols for washing, bleaching, ironing, chemical cleaning and drying, which inform the consumer about suitable care treatments. Improper care treatments can make a garment unusable. There is currently no known fixer that meets the maximum requirements of all care treatments. The highest requirements are currently:

Waschen: maximale Waschtemperatur 95 °C.Washing: maximum washing temperature 95 ° C.

Pflegeprozess : normale mechanische Beanspruchung, normales Spülen, normales SchleudernCare process: normal mechanical stress, normal rinsing, normal spinning

Bleichen:Bleaching:

Pflegeprozess : ChlorbleicheCare process: chlorine bleach

Bügeln:Iron:

Pflegeprozess : Bügeln bei einer maximalen Sohlentemperatur von 200 °CCare process: ironing at a maximum sole temperature of 200 ° C

Chemische Reinigung: Pflegeprozess : Reinigung mit allen handelsüblichen Reinigungsmitteln mit normaler chemischer ReinigungChemical cleaning: Care process: cleaning with all commercially available cleaning agents with normal chemical cleaning

Trocknen im Tumbler: Pflegeprozess : Keine Einschränkung bezüglich der Trockentemperatur nach dem WaschprozessDrying in a tumbler: Care process: No restriction regarding the drying temperature after the washing process

Wetclean: Waschen mit 40 °C; Trocknen mit 60 °C.Wetclean: wash at 40 ° C; Drying at 60 ° C.

Alle bekannten fixierbaren Einlagestoffe unterliegen Pflegebeschränkungen, sei es z.B. bezüglich der Waschtemperatur und/oder des Bügeins und/oder bezüglich der chemischen Reinigung und/oder bezüglich des Trocknens . Diese Einschränkungen verursachen einen erheblichen Aufwand bei der Hertstellung von Textilerzeugnissen, weil die richtige Auswahl der Einlagestoffe schwierig ist und Besonderheiten bei der Verarbeitung der Einlagestoffe erforderlich sind. Hinzu kommt, dass neuzeitliche Behandlungsverfahren von Textilerzeugnissen wie Garment-Dyeing, Stone-Wash, Enzym- Wash, Bleaching die Erzeugnisse und insbesondere die Einlagen, erheblich beanspruchen und deren Funktion nachteilig beeinflussen.All known fixable interlinings are subject to care restrictions, e.g. with regard to the washing temperature and / or the ironing and / or with regard to the chemical cleaning and / or with respect to the drying. These restrictions cause considerable effort in the production of textile products because the correct selection of the interlining materials is difficult and special features are required when processing the interlining materials. In addition, modern treatment processes for textile products such as garment dyeing, stone wash, enzyme wash and bleaching place considerable stress on the products and in particular the liners and adversely affect their function.

Aufgabe der Erfindung ist, universell verwendbare Einlagestoffe mit Beschichtungen zu schaffen, die fixiert mit einem textilen Flächengebilde Pflegebehandlungen bis zu den Hochstanforderungen gewährleisten. Darüber hinaus sollen die Beschichtungen der fixierten Einlagestoffe sowie insbesondere auch die Substrate der Einlagestoffe geeignet sein, Veredelungsbehandlungen wie Garment-Dyeing, Stone-Wash, Enzym-Wash und Bleaching zu ermöglichen.The object of the invention is to provide universally usable interlinings with coatings that are fixed with a textile Ensure fabric care treatments up to the highest requirements. In addition, the coatings of the fixed interlining materials and in particular also the substrates of the interlining materials should be suitable for enabling finishing treatments such as garment dyeing, stone wash, enzyme wash and bleaching.

Diese Aufgabe wird durch die Merkmale des Anspruchs 1 gelöst. Vorteilhafte Weiterbildungen der Erfindung werden in den Unteransprüchen gekennzeichnet .This object is solved by the features of claim 1. Advantageous developments of the invention are characterized in the subclaims.

Nach der Erfindung werden Substrate ausgewählt, die den vorgegebenen Anforderungen, ggf . den Höchstanforderungen für die Pflegebehandlungen und den Anforderungen von Veredelungsbehandlungen genügen. Derartige Substrate sind z.B. PES, PES/Co, Co-Gewebe und PES-Gewirke und Wasserstrahlverfestigte Vliesstoffe.According to the invention, substrates are selected that meet the specified requirements, if necessary. meet the maximum requirements for nursing treatments and the requirements of finishing treatments. Such substrates are e.g. PES, PES / Co, co-woven and PES knitted fabrics and hydroentangled nonwovens.

Zudem werden aus der Vielzahl von Beschichtungsmitteln Copolya- mide als Beschichtungsmittel ausgewählt .In addition, copolyamides are selected as coating agents from the large number of coating agents.

Copolyamide sind zwar gebräuchliche Beschichtungsmittel für Substrate. Gleichwohl gewährleisten nur wenige die Bedingungen der Hochstanforderungen, die nach der Aufgabe der vorliegenden Erfindung zu erfüllen sind.Copolyamides are common coating agents for substrates. Nonetheless, only a few guarantee the conditions of the highest requirements which are to be met according to the object of the present invention.

Die erfindungsgemäß verwendeten Copolyamide, die den Höchstanforderungen der Pflegebehandlungen und Veredelungsbehandlungen genügen und mit jeglichem Substrat verwendbar sind, weisen im Wesentlichen die folgenden Bestandteile auf :The copolyamides used according to the invention, which meet the highest requirements of care and finishing treatments and can be used with any substrate, essentially have the following components:

Polycaprolactam (Polyamid 6, PA 6) Polyundecanamid (Polyamid 11, PA 11) Polylaurinlactam (Polyamid 12, PA 12) Polyhexamethylenadipinamid (Polyamid 6 . 6 , PA 6 . 6) Dabei gewährleisten die folgenden aus Fig. 1 erkennbaren, schraffierten Zusammensetzungsbereiche in Gew.-%, die erfindungsgemäß ausgewählt sind und die Zusammensetzungslücken aufweisen, die gewünschten Hochstanforderungen der Pflegebehandlungen sowie die Anforderungen der Veredelungsbehandlungen.Polycaprolactam (polyamide 6, PA 6) polyundecanamide (polyamide 11, PA 11) polylaurine lactam (polyamide 12, PA 12) polyhexamethylene adipinamide (polyamide 6, 6, PA 6, 6) The following hatched composition areas in% by weight, which can be seen in FIG. 1 and which are selected according to the invention and have the composition gaps, ensure the desired high requirements of the care treatments as well as the requirements of the finishing treatments.

Polyamid 12Polyamide 12

Polyamid 6 Polyamid 6.6 und/oder Polyamid 11Polyamide 6, polyamide 6.6 and / or polyamide 11

Max. M . Max. Min. Max . Min . 45-55 10-22 75-85 20-45 50-75 18-30 vorzugsw. 48-53 15-20 78-83 20-40 58-62 20-28Max. M Max. Min. Max. Min. 45-55 10-22 75-85 20-45 50-75 18-30 preferably 48-53 15-20 78-83 20-40 58-62 20-28

Dabei kann - wie sich aus Fig. 1 ergibt - Polyamid 12 und/oder Polyamid 11 allein mit einem der beiden anderen Polyamide kombiniert werden. In jedem Fall ist die Bedingung zu erfüllen, dass die Schmelztemperaturen zwischen 110 und 150 °C, insbesondere zwischen 120 und 145 °C liegen. Demgemäß sind die obigen Zusammensetzungsbereiche zu beachten und die Zusammensetzungen entsprechend zu wählen.1, polyamide 12 and / or polyamide 11 can be combined alone with one of the other two polyamides. In any case, the condition must be met that the melting temperatures are between 110 and 150 ° C, in particular between 120 and 145 ° C. Accordingly, the above composition ranges must be observed and the compositions selected accordingly.

Vorzugsweise wird Polyamid 12 anstelle von Polyamid 11 verwendet.Polyamide 12 is preferably used instead of polyamide 11.

Bei Verwendung dieser ausgewählten, schmelzklebenden Copolyamide können relativ niedrige Fugentemperaturen beim Fixieren von Einlagezuschnitten mit einem Oberstoff oder dergleichen von z.B. 127 °C bis 143 °C auf allen bekannten Pressensystemen eingestellt werden. Diese Fugentemperaturen führen zur dauerhaften Haftung zwischen den textilen Flächengebilden aus Einlagestoff und Oberstoff, die die genannten Anforderungen bezüglich Pflege und Veredelung erfüllen. Dabei können z.B. die folgenden Druckeinstellungen an bekannten Pressen, insbesondere für Frontfixierungen verwendet werden: Plattenpressen 200—500 p/cm 2When using these selected, melt-adhesive copolyamides, relatively low joint temperatures when fixing insert blanks with an outer fabric or the like can be set, for example, from 127 ° C. to 143 ° C. on all known press systems. These joint temperatures lead to permanent adhesion between the textile fabrics made of interlining and outer fabric, which meet the above-mentioned requirements with regard to care and finishing. The following pressure settings can be used on known presses, especially for front fixings: Plate presses 200-500 p / cm 2

Durchlaufpressen 3— 5 barContinuous presses 3 - 5 bar

(alte Generation)(old generation)

Durchlaufpressen (neue Generation) , 20— 40 N/cm2 eine Druckwalze ist als luftgefüllter Schlauch ausgebildetContinuous presses (new generation), 20 - 40 N / cm 2 a pressure roller is designed as an air-filled hose

Durchlaufpressen (neue Generation) , 3— 8 N/cm2 mit Druckwalzenpaaren Stahl/Gummi oder Gummi/GummiContinuous presses (new generation), 3 - 8 N / cm 2 with pressure roller pairs steel / rubber or rubber / rubber

Die bevorzugte Fixierdauer beträgt 12 bis 20, insbesondere 13 bis 18 Sekunden.The preferred fixing time is 12 to 20, in particular 13 to 18 seconds.

Die erfindungsgemäßen Einlagestoffe erfüllen zudem insbesondere auch alle Anforderungen bezüglich Rück- und Durchschlagsicherheit sowie eines weichen textilen Griffs.The interlining materials according to the invention also in particular also meet all the requirements with regard to back and puncture resistance and a soft textile handle.

Die ausgewählten Copolyamide können für verschiedene bekannte Beschichtungen wie Pastenpunkt, Pulverpunkt, Doppelpunkt und StreubeSchichtung verwendet werden. Bevorzugt wird die Pastenpunkt- oder Doppelpunktbeschichtung. Dafür werden die üblichen Beschichtungsverfahren und die Copolyamide mit üblichen Korngrößen und Korngrößenverteilungen verwendet . Z.B. werden Korngrößen für Pasten zwischen 0 und 90 μm und für Puderpunkte zwischen 0 und 140 μm und für Doppelpunkte 60 bis 220 μm gewählt.The selected copolyamides can be used for various known coatings such as paste point, powder point, colon and scatter coating. The paste point or colon coating is preferred. The usual coating processes and the copolyamides with the usual grain sizes and grain size distributions are used for this. For example, grain sizes for pastes between 0 and 90 μm and for powder points between 0 and 140 μm and for colons between 60 and 220 μm are selected.

Für den erfindungsgemäßen Zweck werden vorzugsweise folgende Pastenzusammensetzungen in Gew.-% verwendet:The following paste compositions are preferably used in% by weight for the purpose according to the invention:

Wasser 40-70Water 40-70

Entschäumer 0 , 1—0 , 3Defoamer 0, 1--0, 3

Weichmacher 0 , 5—3 , 0Plasticizer 0, 5-3, 0

Copolyamid-Pulver 0 - 80 μm 25—40Copolyamide powder 0 - 80 µm 25-40

Lauf- und Druckhilfsmittel A 2,0—5,7Running and printing aids A 2.0-5.7

Verdicker/Dispergator 2 , 0—6 , 0Thickener / dispersant 2, 0 - 6, 0

Laufhilfsmittel B 2 , 0-5 , 0 zusätzlich 0,001 Gew.-% Lithiumsalz Das folgende Beispiel 1 zeigt eine besonders gute Pastenzusammensetzung in Gew.-% auf.Walking aids B 2, 0-5, 0 additionally 0.001% by weight lithium salt The following example 1 shows a particularly good paste composition in% by weight.

Beispiel 1;Example 1;

Wasser 57,6 Entschäumer 0,3 Gemisch aus Fettsäure- estern, höheren Kohlenwasserstoffen mit carbonsauren SalzenWater 57.6 Defoamer 0.3 Mixture of fatty acid esters, higher hydrocarbons with carboxylic acid salts

Weichmacher 2,0 N-monosubstituiertes Sulfonamid mit geringem WasseranteilPlasticizer 2.0 N-monosubstituted sulfonamide with low water content

Copolyamid-Pulver 30,0 0 - 80 μmCopolyamide powder 30.0 0 - 80 μm

Lauf- und Druck3,0 Mischung eines wässrigen hilfsmittel A Polycarbonsäuresalzes mit Polyethylenglycol , Polyetherdiurethan, wasserlöslichen Polyamiden und aliphatischen Gly- colethernRunning and pressure 3.0 Mixture of an aqueous auxiliary A polycarboxylic acid salt with polyethylene glycol, polyether diurethane, water-soluble polyamides and aliphatic glycol ethers

Verdicker/ 4,1 wässrige Zubereitung von Dispergator wasserlöslichen Polyamiden, neutralisierter Polyacrylsäure, wenig Netzmittel und Paraffin- ölThickener / 4.1 aqueous preparation of dispersant water-soluble polyamides, neutralized polyacrylic acid, little wetting agent and paraffin oil

Laufhilfsmittel B 3, 0 wässrige Lösung von Säu- reamiden und Polyethern zusätzlich 0,001 Gew.-% Lithiumsalz zur Erkennung dieser PastendispersionWalking aids B 3.0 aqueous solution of acid amides and polyethers plus 0.001% by weight lithium salt to detect this paste dispersion

Für eine erfindungsgemäße Doppelpunkt-Beschichtung werden bevorzugt die folgenden Zusammensetzungen in Gew.-% für die Unterpunktpaste verwendet .For a colon coating according to the invention, the following compositions in% by weight are preferably used for the sub-point paste.

Wasser 45-60Water 45-60

Verdicker/ 3 , 0-4 , 5 Dispergator Wasser 45—60Thickener / 3, 0-4, 5 dispersant Water 45-60

Copolyamid-Pulver 0 - 80μm 25—38 (ausgewählte Zusammensetzung gemäß Erfindung)Copolyamide powder 0 - 80μm 25-38 (selected composition according to the invention)

Lauf- und Druckhilfsmittel A 7,0—9,0Running and printing aids A 7.0-9.0

Dipropylenglykol 2 , 0—3 , 5 zusätzlich 0,001 Gew.-% LithiumsalzDipropylene glycol 2, 0-3, 5 additionally 0.001% by weight lithium salt

Auf diese Unterpunktpaste wird erfindungsgemäß ein erfindungs- gemäßes Copolyamidstreupulver aufgestreut, das einen höheren Schmelzpunkt hat als das Copolyamid der Unterpunktpaste.According to the invention, a copolyamide scattering powder according to the invention is sprinkled onto this sub-point paste, which has a higher melting point than the copolyamide of the sub-point paste.

Das folgende Beispiel 2 zeigt eine besonders gute Unterpunktpastenzusammensetzung in Gew.-%.The following example 2 shows a particularly good sub-dot paste composition in% by weight.

Beispiel 2 :Example 2:

Wasser 55,0Water 55.0

Verdicker/ 4,0 wässrige Zubereitung von Dispergator wasserlöslichen Polyamiden neutralisierter Po- lyacrylsäure, wenig Netzmittel und ParaffinölThickener / 4.0 aqueous preparation of dispersant, water-soluble polyamides, neutralized polyacrylic acid, little wetting agent and paraffin oil

Copolyamidpulver 31,0 Vernetzer auf Basis Iso- mit aminogruppen- cyanat ist im Copolyamid aktivem Vernetzer eingebautCopolyamide powder 31.0 crosslinker based on iso- with amino group cyanate is built into the copolyamide active crosslinker

Lauf- und Druck- 7,0 Mischung eines wässrigen hilfsmittel A Polycarbonsäuresalzes mit Polyethylenglycol , Polyetherdiurethan, wasserlöslichen Polyamiden und aliphatischen Gly- colethernRunning and pressure 7.0 mixture of an aqueous auxiliary A polycarboxylic acid salt with polyethylene glycol, polyether diurethane, water-soluble polyamides and aliphatic glycol ethers

Haftvermittler zum 3 , 0 Dipropylenglykol Substrat und zum Copolyamid zusätzlich 0,001 Gew.-% Lithiumsalz zur Erkennung Auf die Unterpunktpaste wird erfindungsgemäß ein erfindungsgemäß ausgewähltes Copolyamidpulver in an sich bekannter Weise aufgestreut, woraus die Doppelpunktbeschichtung resultiert. Verwendet wird Copolyamidpulver mit einem Kornband zwischen 60 und 220 μm, insbesondere zwischen 80 und 180 μm.Adhesion promoter to the 3, 0 dipropylene glycol substrate and to the copolyamide an additional 0.001% by weight lithium salt for detection According to the invention, a copolyamide powder selected in accordance with the invention is sprinkled onto the sub-point paste in a manner known per se, which results in the colon coating. Copolyamide powder with a grain size between 60 and 220 μm, in particular between 80 and 180 μm, is used.

Anstelle des Thermoplast für die Unterpunktpaste kann aber auch eine an sich bekannte Duroplastpaste verwendet werden, die einen etwas höheren Schmelzpunkt aufweist als die Copolyamidbestreu- ung.Instead of the thermoplastic for the sub-point paste, a thermoset paste known per se can also be used, which has a somewhat higher melting point than the copolyamide scattering.

Nach einer besonderen Ausführungsform der Erfindung wird die bekannte Doppelpunktbeschichtung variiert bzw. ergänzt. Dazu wird ■ der Zubereitung der Unterpunktpaste, insbesondere einer Duroplastzubereitung, ein Copolyamidpulver zugegeben, vorzugsweise in Mengen von 25 bis 35 Gew.-% und vorzugsweise in einer Feinheit von 0 bis 80 μm. Zweckmäßigerweise wird ein erfindungsgemäß ausgewähltes Copolyamidpulver verwendet und insbesondere das Copolyamid verwendet, das aufgestreut wird. Dabei kann das Pulver in Form des Kornbandes . des aufgestreuten Pulvers oder aber mit Korngrößen verwendet werden, die zur Herstellung der Paste eingesetzt werden.According to a special embodiment of the invention, the known colon coating is varied or supplemented. For this purpose, the sub-point paste, in particular a Duroplastzubereitung, a copolyamide is added ■ the preparation, preferably in quantities of 25 microns to 35 wt .-%, and preferably in a fineness from 0 to 80. A copolyamide powder selected according to the invention is expediently used, and in particular the copolyamide which is scattered on is used. The powder can be in the form of the grain belt. of the scattered powder or with grain sizes used to make the paste.

Die zugesetzte Menge ist so zu wählen, dass die Eigenschaften der Unterpunktmasse nicht wesentlich beeinflusst werden. Vorzugsweise werden Mengen zwischen 5 und 15 Gew.- , insbesondere zwischen 6 und 11 Gew.-% zugesetzt.The amount added should be selected so that the properties of the sub-point mass are not significantly affected. Amounts of between 5 and 15% by weight, in particular between 6 and 11% by weight, are preferably added.

In überraschender Weise erhöhen diese geringen Zusatzmengen vor und nach der Fixierung die Haftung zwischen dem Unterpunkt und der Oberpunktbestreuung derart, dass insbesondere die gestellten Anforderungen erfüllt werden können. Zudem ergibt sich auch eine erhöhte Haftung zwischen dem Unterpunkt und dem Einlagestoff, so dass auch diese Haftstelle in überraschender Weise entscheidend verbessert wird. Nach einer weiteren Ausführungsform der Erfindung wird das Copolyamidstreupulver für die Doppelpunktbeschichtung mit geringen Mengen eines Pulvers aus dem Unterpunktmaterial versetzt, und zwar zweckmäßigerweise mit den gleichen Mengen wie beim Zusatz des Copolyamidpulvers zur Unterpunktpaste. Die Korngröße entspricht in diesem Fall vorzugsweise der Korngröße des Copolya- midstreupulvers . Surprisingly, these small additional amounts before and after the fixation increase the adhesion between the sub-point and the top-point spreading in such a way that in particular the requirements can be met. In addition, there is also increased liability between the sub-point and the interlining material, so that this point of detention is surprisingly improved significantly. According to a further embodiment of the invention, the copolyamide scattering powder for the colon coating is mixed with small amounts of a powder from the sub-point material, and expediently with the same amounts as when the copolyamide powder is added to the sub-point paste. In this case the grain size preferably corresponds to the grain size of the copolyamide powder.

Fixierbarer Ein -ung auf der Basis eine Copc Substrat die Hochstanforderui

Figure imgf000012_0001
gewährleistet und Veredelungsb , Stone-Wash, Enzyme-Wash und lie Beschich- tung im WesentlαFixable unit based on a copc substrate the high standard
Figure imgf000012_0001
guaranteed and finishing, stone wash, enzyme wash and lie coating essentially

Polycaprola' äerPolycaprola 'aer

Polyundecanamid (Polyamid XI, PA 11) und/oder Polylaurinlactam (Polyamid 12, PA 12) und/oder Polyhexamethylenadipinamid (Polyamid 6.6, PA 6.6)Polyundecanamide (polyamide XI, PA 11) and / or polylaurine lactam (polyamide 12, PA 12) and / or polyhexamethylene adipinamide (polyamide 6.6, PA 6.6)

sowie die folgenden jeweils maximalen und minimalen Zusammensetzungen in Gew.-% aufweist:and has the following maximum and minimum compositions in% by weight:

Polyamid 12Polyamide 12

Polyamid 6 Polyamid 6.6 und/oder Polyamid 11Polyamide 6, polyamide 6.6 and / or polyamide 11

Max. Min. Max. Mm. Max. Min. 45-55 10-22 75-85 20-45 50-75 18-30Max. Min. Max. Mm. Max. Min. 45-55 10-22 75-85 20-45 50-75 18-30

Wobei vorzugsweise die Zusammensetzungen so gewählt werden, dass die Schmelzemperaturen zwischen 110 und 150 °C, insbesondere 120 und 145°C liegen und wobei vorzugsweise Polyamid 12 und/oder 11 allein mit nur einem der beiden anderen Polyamide kombiniert wird.The compositions are preferably selected such that the melting temperatures are between 110 and 150 ° C., in particular 120 and 145 ° C., and polyamide 12 and / or 11 is preferably combined alone with only one of the other two polyamides.

Einlagestoff nach Anspruch 1 , g e k e n n z e i c h n e t d u r c h die folgenden jeweils maximalen und minimalen Zusammensetzungen der Beschichtung in Gew.-%: Polyamid 12Interlining fabric according to claim 1, characterized by the following maximum and minimum compositions of the coating in% by weight: Polyamide 12

Polyamid 6 Polyamid 6.6 und/oder Polyamid 11Polyamide 6, polyamide 6.6 and / or polyamide 11

Max. Min. Max. Min. Max. Mm. 48-53 15-20 78-83 20-40 58-62 20-28Max. Min. Max. Min. Max. Mm. 48-53 15-20 78-83 20-40 58-62 20-28

3. Einlagestoff nach Anspruch 1 und/oder 2, d a d u r c h g e k e n n z e i c h n e t , d a s s die Beschichtung mit Fugentemperaturen zwischen 127 °C und 143 °C fixierbar ist.3. interlining material according to claim 1 and / or 2, d a d u r c h g e k e n n z e i c h n e t, that the coating with joint temperatures between 127 ° C and 143 ° C is fixable.

4. Einlagestoff nach einem oder mehreren der Ansprüche 1 bis4. interlining material according to one or more of claims 1 to

3, d a d u r c h g e k e n n z e i c h n e t , d a s s die Beschichtung mit folgenden Druckeinstellungen an bekannten Pressen fixierbar, insbesondere front fixierbar ist:3, d a d u r c h g e k e n n z e i c h n e t, that the coating can be fixed to known presses, in particular front-fixed, using the following pressure settings:

Plättenpressen 200—500 p/cm2 Plate presses 200-500 p / cm 2

Durchlaufpressen 3— 5 bar (alte Generation)Continuous presses 3 - 5 bar (old generation)

Durchlaufpressen 20- 40 N/cm2 (neue Generation) , eine Druckwalze ist als luftgefüllter Schlauch ausgebildetContinuous presses 20-40 N / cm 2 (new generation), a pressure roller is designed as an air-filled hose

Durchlaufpressen (neue Genera3- 8 N/cm2 tion) , mit Druckwalzenpaaren Stahl/Gummi oder Gummi/GummiContinuous presses (new generation 3-8 N / cm 2 tion), with pressure roller pairs steel / rubber or rubber / rubber

Einlagestoff nach einem oder mehreren der Ansprüche 1 bis 4, d a d u r c h g e k e n n z e i c h n e t , d a s s die Beschichtung in 12 bis 30, insbesondere 13 bis 18 Sekunden fixierbar ist.Interlining material according to one or more of claims 1 to 4, d a d u r c h g e k e n n z e i c h n e t, that the coating can be fixed in 12 to 30, in particular 13 to 18 seconds.

Einlagestoff nach einem oder mehreren der Ansprüche 1 bisInterlining fabric according to one or more of claims 1 to

5, d a d u r c h g e k e n n z e i c h n e t , d a s s die Beschichtung als Pastenpunkt aufgebracht ist. Wasser 45—605, characterized in that the coating is applied as a paste point. Water 45-60

Copolyamid-Pulver 0 - 80μm 25—38Copolyamide powder 0 - 80 µm 25-38

(ausgewählte Zusammensetzung gemäß Erfindung)(selected composition according to the invention)

Lauf- und Druckhilfsmittel A 7,0-9,0Running and printing aids A 7.0-9.0

Dipropylenglykol 2 , 0—3 , 5 zusätzlich 0,001 Gew.-% LithiumsalzDipropylene glycol 2, 0-3, 5 additionally 0.001% by weight lithium salt

Auf diese Unterpunktpaste wird erfindungsgemäß ein erfindungs- gemäßes Copolyamidstreupulver aufgestreut, das einen höheren Schmelzpunkt hat als das Copolyamid der Unterpunktpaste.According to the invention, a copolyamide scattering powder according to the invention is sprinkled onto this sub-point paste, which has a higher melting point than the copolyamide of the sub-point paste.

Das folgende Beispiel 2 zeigt eine besonders gute Unterpunkt- pastenzusammensetzung in Gew.-%.The following example 2 shows a particularly good sub-point paste composition in% by weight.

≥ispiel 2 :≥example 2:

Wasser 55 , 0Water 55, 0

Verdicker/ 4 , 0 wässrige Zubereitung von Dispergator wasserlöslichen Polyamiden neutralisierter Po- lyacrylsäure, wenig Netzmittel und ParaffinölThickener / 4.0 aqueous preparation of dispersant, water-soluble polyamides, neutralized polyacrylic acid, little wetting agent and paraffin oil

Copolyamidpulver 31,0 Vernetzer auf Basis Iso- mit aminogruppen- cyanat ist im Copolyamid aktivem Vernetzer eingebautCopolyamide powder 31.0 crosslinker based on iso- with amino group cyanate is built into the copolyamide active crosslinker

Lauf- und Druck7,0 Mischung eines wässrigen hilfsmittel A Polycarbonsäuresalzes mit Polyethylenglycol , Polyetherdiurethan, wasserlöslichen Polyamiden und aliphatisehen Gly- colethernRunning and pressure 7.0 mixture of an aqueous auxiliary A polycarboxylic acid salt with polyethylene glycol, polyether diurethane, water-soluble polyamides and aliphatic glycol ethers

Haftvermittler zum 3 , 0 DipropylenglykolAdhesion promoter for 3, 0 dipropylene glycol

Substrat und zumSubstrate and to

Copolyamid zusätzlich 0,001 Gew.-% Lithiumsalz zur Erkennung Auf die Unterpunktpaste wird erfindungsgemäß ein erfindungsgemäß ausgewähltes Copolyamidpulver in an sich bekannter Weise aufgestreut, woraus die Doppelpunktbeschichtung resultiert. Verwendet wird Copolyamidpulver mit einem Kornband zwischen 60 und 220 μm, insbesondere zwischen 80 und 180 μm.Copolyamide additionally 0.001% by weight lithium salt for detection According to the invention, a copolyamide powder selected in accordance with the invention is sprinkled onto the sub-point paste in a manner known per se, which results in the colon coating. Copolyamide powder with a grain size between 60 and 220 μm, in particular between 80 and 180 μm, is used.

Anstelle des Thermoplast für die Unterpunktpaste kann aber auch eine an sich bekannte Duroplastpaste verwendet werden, die einen etwas höheren Schmelzpunkt aufweist als die Copolyamidbestreu- ung.Instead of the thermoplastic for the sub-point paste, a thermoset paste known per se can also be used, which has a somewhat higher melting point than the copolyamide scattering.

Nach einer besonderen Ausführungsform der Erfindung wird die bekannte Doppelpunktbeschichtung variiert bzw. ergänzt. Dazu wird der Zubereitung der Unterpunktpaste, insbesondere einer Duroplastzubereitung, ein Copolyamidpulver zugegeben, vorzugsweise in Mengen von 25 bis 35 Gew.-% und vorzugsweise in einer Feinheit von 0 bis 80 μm. Zweckmäßigerweise wird ein erfindungsgemäß ausgewähltes Copolyamidpulver verwendet und insbesondere das Copolyamid verwendet, das aufgestreut wird. Dabei kann das Pulver in Form des Kornbandes . des aufgestreuten Pulvers oder aber mit Korngrößen verwendet werden, die zur Herstellung der Paste eingesetzt werden.According to a special embodiment of the invention, the known colon coating is varied or supplemented. For this purpose, a copolyamide powder is added to the preparation of the sub-point paste, in particular a thermoset preparation, preferably in amounts of 25 to 35% by weight and preferably in a fineness of 0 to 80 μm. A copolyamide powder selected according to the invention is expediently used, and in particular the copolyamide which is scattered on is used. The powder can be in the form of the grain belt. of the scattered powder or with grain sizes used to make the paste.

Die zugesetzte Menge ist so zu wählen, dass die Eigenschaften der Unterpunktmasse nicht wesentlich beeinflusst werden. Vorzugsweise werden Mengen zwischen 5 und 15 Gew.-%, insbesondere zwischen 6 und 11 Gew.-% zugesetzt.The amount added should be selected so that the properties of the sub-point mass are not significantly affected. Amounts of between 5 and 15% by weight, in particular between 6 and 11% by weight, are preferably added.

In überraschender Weise erhöhen diese geringen Zusatzmengen vor und nach der Fixierung die Haftung zwischen dem Unterpunkt und der Oberpunktbestreuung derart, dass insbesondere die gestellten Anforderungen erfüllt werden können. Zudem ergibt sich auch eine erhöhte Haftung zwischen dem Unterpunkt und dem Einlagestoff, so dass auch diese Haftstelle in überraschender Weise entscheidend verbessert wird. Nach einer weiteren Ausführungsform der Erfindung wird das Copolyamidstreupulver für die Doppelpunktbeschichtung mit geringen Mengen eines Pulvers aus dem Unterpunktmateriäl versetzt, und zwar zweckmäßigerweise mit den gleichen Mengen wie beim Zusatz des Copolyamidpulvers zur Unterpunktpaste. Die Korngröße entspricht in diesem Fall vorzugsweise der Korngröße des Copolya- midstreupulvers . Surprisingly, these small additional amounts before and after the fixation increase the adhesion between the sub-point and the top-point spreading in such a way that in particular the requirements can be met. In addition, there is also increased liability between the sub-point and the interlining material, so that this point of detention is surprisingly improved significantly. According to a further embodiment of the invention, the copolyamide scattering powder for the colon coating is mixed with small amounts of a powder from the sub-point material, expediently with the same amounts as when the copolyamide powder is added to the sub-point paste. In this case the grain size preferably corresponds to the grain size of the copolyamide powder.

Claims

Patentansprücheclaims Fixierbarer Einlagestoff mit einer Beschichtung auf der Basis eine Copolyamids, die unabhängig vom Substrat die Höchstanforderungen von Pflegebehandlungen gewährleistet und Veredelungsbehandlungen wie Garment-Dyeing, Stone-Wash, Enzyme-Wash und Bleaching ermöglicht, wobei die Beschichtung im Wesentlichen die BestandteileFixable interlining with a coating based on a copolyamide, which, regardless of the substrate, ensures the highest standards of care treatments and enables finishing treatments such as garment dyeing, stone wash, enzyme wash and bleaching, whereby the coating essentially contains the components Polycaprolactam (Polyamid 6, PA 6) und/oder Polyundecanamid (Polyamid 11, PA 11) und/oder Polylaurinlactam (Polyamid 12, PA 12) und/oder Polyhexamethylenadipinamid (Polyamid 6.6, PA 6.6)Polycaprolactam (polyamide 6, PA 6) and / or polyundecanamide (polyamide 11, PA 11) and / or polylaurin lactam (polyamide 12, PA 12) and / or polyhexamethylene adipinamide (polyamide 6.6, PA 6.6) sowie die folgenden jeweils maximalen und minimalen Zusammensetzungen in Gew.-% aufweist:and has the following maximum and minimum compositions in% by weight: Polyamid 12Polyamide 12 Polyamid 6 Polyamid 6.6 und/oder Polyamid 11Polyamide 6, polyamide 6.6 and / or polyamide 11 Max. Min. Max. Min. Max. Min. 45-55 10-22 75-85 20-45 50-75 18-30Max. Min. Max. Min. Max. Min. 45-55 10-22 75-85 20-45 50-75 18-30 Wobei vorzugsweise die Zusammensetzungen so gewählt werden, dass die Schmelzemperaturen zwischen 110 und 150 °C, insbesondere 120 und 145°C liegen und wobei vorzugsweise Polyamid 12 und/oder 11 allein mit nur einem der beiden anderen Polyamide kombiniert wird.The compositions are preferably selected such that the melting temperatures are between 110 and 150 ° C., in particular 120 and 145 ° C., and polyamide 12 and / or 11 is preferably combined alone with only one of the other two polyamides. Einlagestoff nach Anspruch 1 , g e k e n n z e i c h n e t d u r c h die folgenden jeweils maximalen und minimalen Zusammensetzungen der Beschichtung in Gew.-%: Polyamid 12Interlining fabric according to claim 1, characterized by the following maximum and minimum compositions of the coating in% by weight: Polyamide 12 Polyamid 6 Polyamid 6.6 und/oder Polyamid 11Polyamide 6, polyamide 6.6 and / or polyamide 11 Max . M . Max. Mm. Max. Min. 48-53 15-20 78-83 20-40 58-62 20-28Max . M. Max. Mm. Max. Min. 48-53 15-20 78-83 20-40 58-62 20-28 Einlagestoff nach Anspruch 1 und/oder 2, d a d u r c h g e k e n n z e i c h n e t , d a s s die Beschichtung mit Fugentemperaturen zwischen 127 °C und 143 °C fixierbar ist.Interlining material according to claim 1 and / or 2, d a d u r c h g e k e n n z e i c h n e t, that the coating with joint temperatures between 127 ° C and 143 ° C is fixable. Einlagestoff nach einem oder mehreren der Ansprüche 1 bis 3, d a d u r c h g e k e n n z e i c h n e t , d a s s die Beschichtung mit folgenden Druckeinstellungen an bekannten Pressen fixierbar, insbesondere frontfixierbar ist:Interlining material according to one or more of Claims 1 to 3, d a d u r c h g e k e n n z e i c h n e t, that the coating can be fixed on known presses, in particular front-fixed, using the following pressure settings: Plättenpressen 200-500 p/cm2 Plate presses 200-500 p / cm 2 Durchlaufpressen 3— 5 bar (alte Generation)Continuous presses 3 - 5 bar (old generation) Durchlaufpressen 20- 40 N/cm2 (neue Generation) , eine Druckwalze ist als luftgefüllter Schlauch ausgebildetContinuous presses 20-40 N / cm 2 (new generation), a pressure roller is designed as an air-filled hose Durchlaufpressen (neue Genera3- 8 N/cm2 tion) , mit Druckwalzenpaaren Stahl/Gummi oder Gummi/GummiContinuous presses (new generation 3-8 N / cm 2 tion), with pressure roller pairs steel / rubber or rubber / rubber Einlagestoff nach einem oder mehreren der Ansprüche 1 bis 4, d a d u r c h g e k e n n z e i c h n e t , d a s s die Beschichtung in 12 bis 30, insbesondere 13 bis 18 Sekunden fixierbar ist.Interlining material according to one or more of claims 1 to 4, d a d u r c h g e k e n n z e i c h n e t, that the coating can be fixed in 12 to 30, in particular 13 to 18 seconds. Einlagestoff nach einem oder mehreren der Ansprüche 1 bisInterlining fabric according to one or more of claims 1 to 5, d a d u r c h g e k e n n z e i c h n e t , d a s s die Beschichtung als Pastenpunkt aufgebracht ist. 5, characterized in that the coating is applied as a paste point. 7. Einlagestoff nach einem oder mehreren der Ansprüche 1 bis 5, d a d u r c h g e k e n n z e i c h n e t , d a s s die Beschichtung als Pulverpunkt aufgebracht ist.7. interlining material according to one or more of claims 1 to 5, d a d u r c h g e k e n n z e i c h n e t, that the coating is applied as a powder point. 8. Einlagestoff nach einem oder mehreren der Ansprüche 1 bis 5, d a d u r c h g e k e n n z e i c h n e t , d a s s die Beschichtung als Streubeschichtung aufgebracht ist.8. interlining material according to one or more of claims 1 to 5, d a d u r c h g e k e n n z e i c h n e t, that the coating is applied as a scatter coating. 9. Einlagestoff nach einem oder mehreren der Ansprüche 1 bis 5, d a d u r c h g e k e n n z e i c h n e t , d a s s die Beschichtung als Doppelpunkt aufgebracht ist.9. interlining material according to one or more of claims 1 to 5, d a d u r c h g e k e n n z e i c h n e t, that the coating is applied as a colon. 10. Einlagestoff nach Anspruch 9, d a d u r c h g e k e n n z e i c h n e t , d a s s die Doppelpunktbeschichtung aus einem Unterpunkt besteht, auf den Pulver aufgestreut ist .10. interlining material according to claim 9, d a d u r c h g e k e n n z e i c h n e t, that the colon coating consists of a sub-point on which powder is sprinkled. 11. Streubeschichtung nach Anspruch 9 und/oder 10, d a d u r c h g e k e n n z e i c h n e t , d a s s der Unterpunkt aus einem Duroplast besteht.11. scatter coating according to claim 9 and / or 10, d a d u r c h g e k e n n z e i c h n e t, that the sub point consists of a thermoset. 12. Streubeschichtung nach Anspruch 9 und/oder 10, d a d u r c h g e k e n n z e i c h n e t , d-a s s der Unterpunkt aus einem Thermoplast besteht.12. scatter coating according to claim 9 and / or 10, d a d u r c h g e k e n n z e i c h n e t, the sub-item consists of a thermoplastic. 13. Einlagestoff nach einem oder mehreren der Ansprüche -9 bis 12, d a d u r c h g e k e n n z e i c h n e t , d a s s das aufgestreute Pulver aus einem erfindungsgemäß ausgewählten Copolyamid besteht . 13. interlining according to one or more of claims -9 to 12, characterized in that the sprinkled powder consists of a copolyamide selected according to the invention. 1 . Einlagestoff nach einem oder mehreren der Ansprüche 9 bis 13, ' d a d u r c h g e k e nn z e i c hn e t , d a s s der Unterpunkt zusätzlich mindestens ein erfindungsgemäß ausgewähltes Copolyamid enthält.1 . Interlining according to one or more of claims 9 to 13, 'dadurchgeke nn zeic et hn, that the sub-point additionally contains at least one selected according to the invention copolyamide. 15. Einlagestoff nach Anspruch 14, d a d u r c h g e k e n n z e i c h n e t , d a s s das Copolyamid das Copolyamid der Streubeschichtung ist.15. interlining material according to claim 14, d a d u r c h g e k e n n z e i c h n e t, that the copolyamide is the copolyamide of the scatter coating. 16. Emlagestoff nach Anspruch 14 und/oder 15, d a du r c h g e k e nn z e i c hn e t , d a s s der Unterpunkt im Wesentlichen aus einem Duroplast besteht.16. Emlagestoff according to claim 14 and / or 15, d a du r c h g e k e nn z e i c hn e t, that the sub-item consists essentially of a thermoset. 17. Einlagestoff nach Anspruch 14 und/oder 15, d a d u r c h g e k e n n z e i c h n e t , d a s s der Unterpunkt im Wesentlichen aus einem anderen, höherschmelzenden erfindungsgemäßen Copolyamid besteht im Vergleich zum Copolyamid der Streubeschichtung.17. interlining material according to claim 14 and / or 15, d a d u r c h g e k e n n z e i c h n e t, that the sub-item consists essentially of a different, higher melting copolyamide according to the invention compared to the copolyamide of the scatter coating. 18. Einlagestoff nach einem oder mehreren der Ansprüche 14 bis 17, d a d u r c h g e k e nn z e i c hn e t , d a s s der Unterpunkt das zusätzliche Copolyamid in- Mengen von 5 bis '15, insbesondere von 6 bis 11 Gew.-% enthält.18. interlining material according to one or more of claims 14 to 17, d a d u r c h g e k e nn z e i c hn e t, as the sub-item contains the additional copolyamide in amounts of 5 to '15, in particular from 6 to 11 wt .-%. 19. Einlagestoff nach einem oder mehreren der Ansprüche 9 bis 18, d a du r c h g e k e n n z e i c h n e t , d a s s die Copolyamidstreubeschichtung zusätzlich eine geringe Menge an Unterpunktmateriäl in Pulverform enthält .19. interlining material according to one or more of claims 9 to 18, because the coating contains additionally a small amount of sub-point materials in powder form. 20. Einlagestoff nach Anspruch 19, d a d u r c h g e k e n n z e i c h n e t , d a s s die Streubeschichtung Unterpunktmateriäl in Mengen von 1 bis 6, insbesondere von 2 bis 4 Gew.-% enthält. 20. interlining material according to claim 19, characterized in that the scatter coating contains sub-point materials in amounts of 1 to 6, in particular from 2 to 4 wt .-%. 21. Verfahren zur Herstellung eines universell verwendbaren, fixierbaren Einlagestoffes nach einem oder mehreren der Ansprüche 1 bis 20, wobei eine Beschichtung mit üblichen Verfahrensweisen auf ein Substrat aufgebracht wird, die im Wesentlichen aus Copolyamid besteht, und die Höchstanforderungen von Pflegebehandlungen erfüllt sowie Veredelungs- behandlungen wie Garment-Dyeing, Stone-Wash, Enzyme-Wash und Bleaching widersteht.21. A method for producing a universally usable, fixable interlining material according to one or more of claims 1 to 20, wherein a coating is applied to a substrate using conventional methods, which essentially consists of copolyamide and meets the highest requirements of care treatments and finishing treatments such as garment dyeing, stone wash, enzyme wash and whitening. 22. Verfahren nach Anspruch 21, d a d u r c h g e k e n n z e i c h n e t , d a s s die Beschichtung auf ein Substrat aufgebracht wird, das ebenfalls die Höchstanforderungen erfüllt und den Pflegebehandlungen widersteht .22. The method of claim 21, d a d u r c h g e k e n n z e i c h n e t that the coating is applied to a substrate that also meets the highest requirements and resists the care treatments. 23. Verfahren nach Anspruch 21 und/oder 22, d a d u r c h g e k e n n z e i c h n e t , d a s s ein Copolyamid folgender jeweils maximaler und minimaler Zusammensetzungen in Gew.-% verwendet wird:23. The method according to claim 21 and / or 22, d a d u r c h g e k e n n z e i c h n e t, that a copolyamide of the following maximum and minimum compositions in wt .-% is used: Polyamid 12Polyamide 12 Polyamid 6 Polyamid 6.6 und/oder Polyamid 11Polyamide 6, polyamide 6.6 and / or polyamide 11 Max. Min. Max. Min. Max. Min. 45-55 10-22 75-85 20-45 50-75 18-30Max. Min. Max. Min. Max. Min. 45-55 10-22 75-85 20-45 50-75 18-30 24. Verfahren nach Anspruch 23, d a d u r c h g e k e n n z e i c h n e t , d a s s ein Copolyamid verwendet wird, das die folgenden jeweils maximalen und minimalen Zusammensetzungen in Gew.-% aufweist:24. The method according to claim 23, d a d u r c h g e k e n n z e i c h n e t, that a copolyamide is used which has the following respectively maximum and minimum compositions in wt .-%: Polyamid 12Polyamide 12 Polyamid 6 Polyamid 6.6 und/oder Polyamid 11Polyamide 6, polyamide 6.6 and / or polyamide 11 Ma . Min. Max. Min. Max. Min. 48-53 15-20 78-83 20-40 58-62 20-28 Ma Min. Max. Min. Max. Min. 48-53 15-20 78-83 20-40 58-62 20-28 25. Verfahren nach einem oder mehreren der Ansprüche 21 bis 24, d a d u r c h g e k e n n z e i c h n e t , d a s s als Beschichtung eine Paste verwendet wird, in der das Copolyamid mit Korngrößen von 0 bis 90 μm enthalten ist.25. The method according to one or more of claims 21 to 24, d a d u r c h g e k e n n z e i c h n e t, that as a coating a paste is used in which the copolyamide with grain sizes from 0 to 90 microns is contained. 26. Verfahren nach einem oder mehreren der Ansprüche 21 bis 24, d a d u r c h g e k e n n z e i c h n e t , d a s s als Beschichtung Pulverpunkte verwendet werden, in denen das Copolyamid mit Korngrößen von 0 bis 140 μm enthalten ist.26. The method according to one or more of claims 21 to 24, d a d u r c h g e k e n n z e i c h n e t, d a s s used as coating powder dots in which the copolyamide with grain sizes from 0 to 140 microns is contained. 27. Verfahren nach einem oder mehreren der Ansprüche 21 bis 24, d a d u r c h g e k e n n z e i c h n e t , d a s s als Beschichtung Doppelpunkte mit einem Unterpunkt und einer pulverförmigen Streubeschichtung verwendet werden, bei denen das Copolyamidstreupulver mit Korngrößen von 60 bis 220 μm vorliegt.27. The method according to one or more of claims 21 to 24, d a d u r c h g e k e n n z e i c h n e t, d a s s used as a coating colons with a sub-point and a powdery scatter coating, in which the copolyamide scattering powder with grain sizes of 60 to 220 microns is present. 28. Verfahren nach Anspruch 27, d a d u r c h g e k e n n z e i c h n e t , d a s s das Copolyamidstreupulver mit Korngrößen zwischen 80 und 180 μm vorliegt.28. The method according to claim 27, d a d u r c h g e k e n n z e i c h n e t, that the copolyamide scattering powder with grain sizes between 80 and 180 microns is present. 29. Verfahren nach einem oder mehreren der Ansprüche 21 bis 25, d a d u r c h g e k e n n z e i c h n e t , d a s s für eine Pastenbeschichtung eine Paste mit folgender Zusammensetzung in Gew.-% verwendet wird:29. The method according to one or more of claims 21 to 25, d a d u r c h g e k e n n z e i c h n e t, that a paste with the following composition in% by weight is used for a paste coating: Wasser 40—70Water 40-70 Entschäumer 0 , 1—0 , 3Defoamer 0, 1--0, 3 Weichmacher 0 , 5—3 , 0 Copolyamid-Pulver 0 - 80 μm 25-40Plasticizer 0.5-3.0 copolyamide powder 0-80 μm 25-40 Lauf- und Druckhilfsmittel A 2,0-5,7Running and printing aids A 2.0-5.7 Verdicker/Dispergator 2 , 0—6, 0Thickener / dispersant 2, 0 - 6, 0 Laufhilfsmittel B 2,0—5,0 zusätzlich 0,001 Gew. -% Lithiumsalz Walking aids B 2.0-5.0 additionally 0.001% by weight lithium salt 30. Verfahren nach Anspruch 29 , d a d u r.c g e k e n n z e i c h n e t , d a s s eine Paste mit folgender Zusammensetzung in Gew.-% verwendet wird:30. The method according to claim 29, d a d u r.c g e k e n n z e i c h n e t, that a paste with the following composition in wt .-% is used: Wasser 57,6 Entschäumer 0,3 Gemisch aus Fettsäure- estern, höheren Kohlenwasserstoffen mit carbonsauren SalzenWater 57.6 Defoamer 0.3 Mixture of fatty acid esters, higher hydrocarbons with carboxylic acid salts Weichmacher 2, 0 N-monosubstituiertes Sulfonamid mit geringem WasseranteilPlasticizer 2, 0 N-monosubstituted sulfonamide with a low water content Copolyamid30, 0 pulver 0 - 80 μmCopolyamid30,0 powder 0 - 80 μm Lauf- und 3,0 Mischung eines wässri- Druckhilfsgen Polycarbonsäure- mittel A salzes mit Polyethy- lenglycol, Polyether- diurethan, wasserlöslichen Polyamiden und aliphatischen Glyco- lethernRunning and 3.0 mixture of an aqueous pressure auxiliary polycarboxylic acid agent A salt with polyethylene glycol, polyether diurethane, water-soluble polyamides and aliphatic glycol ethers Verdicker/ 4,1 wässrige Zubereitung Dispergator von wasserlöslichen Polyamiden, neutralisierter Polyacrylsäu- re, wenig Netzmittel und ParaffinölThickener / 4.1 aqueous preparation Dispersant of water-soluble polyamides, neutralized polyacrylic acid, little wetting agent and paraffin oil Laufhilfs- 3, 0 wässrige Lösung von ittel B Säureamiden und Poly- ethern zusätzlich 0,001 Gew.-% Lithiumsalz zur Erkennung dieser PastendispersionAuxiliary 3, 0 aqueous solution of ittel B acid amides and polyethers additionally 0.001% by weight lithium salt to detect this paste dispersion 31. Verfahren nach einem oder mehreren der Ansprüche 21 bis 24 sowie 27 und/oder 28, d a d u r c h g e k e n n z e i c h n e t , d a s s als Unterpunktpaste für die Doppelpunktebeschichtung eine Paste mit folgender Zusammensetzung in Gew.- verwendet wird: Wasser 45-6031. The method according to one or more of claims 21 to 24 and 27 and / or 28, characterized in that a paste with the following composition by weight is used as the sub-point paste for the colon coating: Water 45-60 Verdicker/- 3,0-4,5 DispergatorThickener / - 3.0-4.5 dispersant Copolyamid-Pulver 0 - 25-38 80μmCopolyamide powder 0 - 25-38 80μm Lauf- und Druckhilfs7 , 0-9 , 0 mittel ARunning and printing aids7, 0-9, 0 medium A Dipropylenglykol 2 , 0—3 , 5 zusätzlich 0,001 Gew.-% LithiumsalzDipropylene glycol 2, 0-3, 5 additionally 0.001% by weight lithium salt 32. Ve fahren nach Anspruch 31 , d a d u r c h g e k e n n z e i c h n e t , d a s s eine Paste mit folgender Zusammensetzung in Gew.-% verwendet wird:32. The method according to claim 31, d a d u r c h g e k e n n z e i c h n e t, that a paste with the following composition in% by weight is used: Wasser 55,0Water 55.0 Verdicker/ 4,0 wässrige Zubereitung Dispergator von wasserlöslichen Polyamiden neutralisierter Polyacrylsäu- re, wenig Netzmittel und ParaffinölThickener / 4.0 aqueous preparation Dispersant of water-soluble polyamides, neutralized polyacrylic acid, little wetting agent and paraffin oil Copolyamid31,0 Vernetzer auf Basis pulver mit Isocyanat ist im Copoaminogruppen- lyamid eingebaut aktivem VernetzerCopolyamide31.0 crosslinker based on powder with isocyanate is an active crosslinker built into the copoamino group lyamide Lauf- und 7,0 Mischung eines wässri- Druckhilfsgen Polycarbonsäure- mittel A salzes mit Polyethy- lenglycol, Polyether- diurethan, wasserlöslichen Polyamiden und aliphatisehen Glyco- lethernRunning and 7.0 mixture of an aqueous pressure auxiliary polycarboxylic acid agent A salt with polyethylene glycol, polyether diurethane, water-soluble polyamides and aliphatic glycol ethers Haftvermitt3 , 0 Dipropylenglykol ler zum Substrat und zum Copolyamid zusätzlich 0,001 Gew. -% Lithiumsalz zur Er- kennung Adhesive 3.0 dipropylene glycol to the substrate and copolyamide plus 0.001% by weight lithium salt for detection 33. Verfahren nach Anspruch 31 und/oder 32, d a d u r c h g e k e nn z e i c h n e t , d a s s ein Copolyamidpulver mit Korngrößen zwischen 60 und 220, insbesondere 80 bis 180 μm aufgestreut wird.33. The method of claim 31 and / or 32, d a d u r c h g e k e nn z e i c h n e t, that a copolyamide powder with grain sizes between 60 and 220, in particular 80 to 180 microns is sprinkled. 34. Verfahren nach einem oder mehreren der Ansprüche 21 bis 24 sowie 27 und/oder 28 und 31 bis 33, d a d u r c h g e k e n n z e i c h n e t , d a s s der Unterpunktpaste ein erfindungsgemäß ausgewähltes Copolyamidpulver zugesetzt wird.34. The method according to one or more of claims 21 to 24 and 27 and / or 28 and 31 to 33, d a d u r c h g e k e n n z e i c h n e t, that a copolyamide powder selected according to the invention is added to the sub-point paste. 35. Verfahren nach Anspruch 34, d a d u r c h g e k e n n z e i c h n e t , d a s s das gleiche Copolyamidpulver zugesetzt wird, das für die Bestreuung der Unterpunktpaste verwendet wird.35. The method of claim 34, d a d u r c h g e k e n n z e i c h n e t that the same copolyamide powder is used, which is used for the spreading of the sub-point paste. 36. Verfahren nach Anspruch 34 und/oder 35, d a d u r c h g e k e n n z e i c h n e t , d a s s ein Bestreuungspulver verwendet wird, das ein zusätzliches Pulver enthält, das dem Thermoplast oder Duroplast der Unterpunktpaste entspricht.36. The method according to claim 34 and / or 35, d a d u r c h g e k e n n e e e c h n e t, that a sprinkling powder is used, which contains an additional powder that corresponds to the thermoplastic or thermoset of the sub-point paste. 37. Verfahren nach Anspruch 36, d a du r c h g e k e n n z e i c h n e t , d a s s als zusätzliches Pulver ein erfindungsgemäß ausgewähltes Copolyamid verwendet wird.37. The method according to claim 36, that a copolyamide selected according to the invention is used as an additional powder. 38. Verfahren nach einem oder mehreren der Ansprüche 34 bis 37, d a d u r c h g e k e n n z e i c h n e t , d a s s das zusätzliche Pulver mit Korngrößen verwendet wird, die den Korngrößen in der Unterpunktpaste ' bzw. der Streubeschichtung entsprechen.38. The method according to one or more of claims 34 to 37, characterized in that the additional powder is used with grain sizes which correspond to the grain sizes in the sub-point paste ' or the scatter coating. 39. Verfahren nach einem oder mehreren der Ansprüche 36 bis 38, d a du r c h g e k e nn z e i c h n e t , d a s s das zusätzliche Pulver in Mengen von 1 bis 6, insbesondere von 2 bis 4 Gew.-% verwendet wird. 39. The method according to one or more of claims 36 to 38, since you can see that the additional powder is used in amounts of 1 to 6, in particular 2 to 4,% by weight. 40. Verwendung eines Einlagestoffes nach einem oder mehreren der Ansprüche 1 bis 20, hergestellt einem Verfahren nach einem oder mehreren der Ansprüche 21 bis 39, d a d u r c h g e k e n n z e i c h n e t , d a s s aus dem Einlagestoff hergestellte Einlagezuschnitte mit einem Oberstoff oder dgl . bei Fugentemperaturen von 127 bis 143 °C fixiert werden.40. Use of an interlining fabric according to one or more of claims 1 to 20, produced by a method according to one or more of claims 21 to 39, d a d u r c h g e k e n n z e i c h n e t, d a s s made from the interlining fabric with an outer fabric or the like. can be fixed at joint temperatures of 127 to 143 ° C. 41. Verwendung nach Anspruch 40, d a d u r c h g e k e nn z e i c h n e t , d a s s mit folgenden Druckeinstellungen an bekannten Pressen fixiert, insbesondere frontfixiert wird:41. Use according to claim 40, d a d u r c h g e k e nn z e i c h n e t, which is fixed to known presses, in particular front-fixed, with the following pressure settings: • Plattenpressen 200-500 p/cm2 • Plate presses 200-500 p / cm 2 Durchlaufpressen 3— 5 barContinuous presses 3 - 5 bar (alte Generation)(old generation) Durchlaufpressen 20— 40 N/cm2 Continuous presses 20-40 N / cm 2 (neue Generation) , eine Druckwalze ist als luftgefüllter Schlauch ausgebildet(new generation), a pressure roller is designed as an air-filled hose Durchlaufpressen (neue Genera- 3— 8 N/cm2 tion) , mit Druckwalzenpaaren Stahl/Gummi oder Gummi/GummiContinuous presses (new generation 3-8 N / cm 2 ), with pairs of pressure rollers steel / rubber or rubber / rubber 42. Verwendung nach Anspruch 40 und/oder 41, d a d u r c h g e k e n n z e i c h n e t , d a s s innerhalb 12 bis 20, insbesondere 13 bis 18 Sekunden fixiert wird. 42. Use according to claim 40 and / or 41, d a d u r c h g e k e n n z e i c h n e t, which is fixed within 12 to 20, in particular 13 to 18 seconds.
PCT/EP2003/001670 2003-02-19 2003-02-19 Fixable interlining material, method for the production thereof, and use thereof Ceased WO2004073436A1 (en)