WO2004067210A1 - Systeme de distribution d'aluminium fondu - Google Patents

Systeme de distribution d'aluminium fondu Download PDF

Info

Publication number
WO2004067210A1
WO2004067210A1 PCT/US2003/002004 US0302004W WO2004067210A1 WO 2004067210 A1 WO2004067210 A1 WO 2004067210A1 US 0302004 W US0302004 W US 0302004W WO 2004067210 A1 WO2004067210 A1 WO 2004067210A1
Authority
WO
WIPO (PCT)
Prior art keywords
container
molten metal
pressure
outlet
molten
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2003/002004
Other languages
English (en)
Inventor
C. Edward Eckert
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to AU2003303822A priority Critical patent/AU2003303822A1/en
Priority to PCT/US2003/002004 priority patent/WO2004067210A1/fr
Publication of WO2004067210A1 publication Critical patent/WO2004067210A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un procédé servant à distribuer ou verser du métal fondu, par exemple, de l'aluminium d'un contenant ou d'une cuve, le taux d'écoulement étant régulé pour minimiser la projection d'aluminium fondu sortant du contenant. Ledit procédé consiste à fournir un contenant destiné à contenir du métal fondu et possédant un orifice de distribution du métal fondu et à engendrer un corps d'aluminium fondu dans le contenant, ledit corps possédant une surface supérieure. Une pression inférieure à la pression atmosphérique est maintenue sur la surface du corps dans la cuve à des fins de régulation du débit de métal fondu à travers ledit orifice. L'augmentation de la pression maintenue dans le contenant jusqu'à atteindre la pression atmosphérique permet de distribuer le métal fondu à travers l'orifice.
PCT/US2003/002004 2003-01-22 2003-01-22 Systeme de distribution d'aluminium fondu Ceased WO2004067210A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
AU2003303822A AU2003303822A1 (en) 2003-01-22 2003-01-22 Dispensing system for molten aluminum
PCT/US2003/002004 WO2004067210A1 (fr) 2003-01-22 2003-01-22 Systeme de distribution d'aluminium fondu

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2003/002004 WO2004067210A1 (fr) 2003-01-22 2003-01-22 Systeme de distribution d'aluminium fondu

Publications (1)

Publication Number Publication Date
WO2004067210A1 true WO2004067210A1 (fr) 2004-08-12

Family

ID=32823160

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2003/002004 Ceased WO2004067210A1 (fr) 2003-01-22 2003-01-22 Systeme de distribution d'aluminium fondu

Country Status (2)

Country Link
AU (1) AU2003303822A1 (fr)
WO (1) WO2004067210A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE1078743B (de) * 1958-12-10 1960-03-31 Unterharzer Berg U Huettenwerk Vorrichtung zum Vergiessen von Metallen
GB2057103A (en) * 1979-01-24 1981-03-25 Dobson Park Ind Molten metal dispenser
US4345467A (en) * 1980-09-15 1982-08-24 Allied Corporation High temperature pressure transducer system
US4717052A (en) * 1986-07-11 1988-01-05 Aluminum Company Of America Molten metal conduit
US20030057615A1 (en) * 2001-09-07 2003-03-27 Eckert C. Edward Dispensing system for molten aluminum

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE1078743B (de) * 1958-12-10 1960-03-31 Unterharzer Berg U Huettenwerk Vorrichtung zum Vergiessen von Metallen
GB2057103A (en) * 1979-01-24 1981-03-25 Dobson Park Ind Molten metal dispenser
US4345467A (en) * 1980-09-15 1982-08-24 Allied Corporation High temperature pressure transducer system
US4717052A (en) * 1986-07-11 1988-01-05 Aluminum Company Of America Molten metal conduit
US20030057615A1 (en) * 2001-09-07 2003-03-27 Eckert C. Edward Dispensing system for molten aluminum

Also Published As

Publication number Publication date
AU2003303822A1 (en) 2004-08-23

Similar Documents

Publication Publication Date Title
US5963580A (en) High efficiency system for melting molten aluminum
US6585928B2 (en) Dispensing system for molten aluminum and method
US6049067A (en) Heated crucible for molten aluminum
US5850073A (en) Electric heating element and heater assembly
CA2062307A1 (fr) Compositions refractaires resistant a l'erosion, aux chocs thermiques et a l'oxydation
RU2087453C1 (ru) Способ наварки огнеупорной керамической массы и копье для распыления порошка при наварке огнеупорной керамической массы
TW200839166A (en) Articles for use with highly reactive alloys
US5939016A (en) Apparatus and method for tapping a molten metal bath
US6069910A (en) High efficiency system for melting molten aluminum
US6444165B1 (en) Heated trough for molten aluminum
US5850072A (en) Electric heater assembly
US4028096A (en) Method of melting metals to reduce contamination from crucibles
US6613118B2 (en) Method of heating molten aluminum in a crucible
US6645270B2 (en) Method of heating a crucible for molten aluminum
US7967057B2 (en) Induction melting apparatus employing halide type crucible, process for producing the crucible, method of induction melting, and process for producing ingot of ultrahigh-purity Fe-, Ni-, or Co-based alloy material
EP0485073A1 (fr) Buse, poche et procédé de pulvérisation
US6470041B2 (en) Heater assembly and heated trough for molten aluminum
US5894541A (en) Electric heater assembly
WO2004067210A1 (fr) Systeme de distribution d'aluminium fondu
US7033538B2 (en) Heated trough for molten aluminum
US20040070121A1 (en) Open and closed metal vessel with which to hold metals hot and to melt them, and for transporting said liquid metals
US5370372A (en) Ladle for molten metal
WO1997016051A1 (fr) Dispositif de chauffage electrique
EP0128987B1 (fr) Tuyère et procédé pour injecter du gaz dans un bain de métal en fusion
EP1219142B1 (fr) Systeme a haut rendement pour chauffer de l'aluminium pour le mettre en fusion

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ OM PH PL PT RO RU SC SD SE SG SK SL TJ TM TN TR TT TZ UA UG UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PT SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: JP

WWW Wipo information: withdrawn in national office

Country of ref document: JP