WO2003022937A1 - Sols de polysiloxane thermodurcissables et durcissables par rayonnement actinique, leur procede d'obtention et leur utilisation - Google Patents

Sols de polysiloxane thermodurcissables et durcissables par rayonnement actinique, leur procede d'obtention et leur utilisation Download PDF

Info

Publication number
WO2003022937A1
WO2003022937A1 PCT/EP2002/009734 EP0209734W WO03022937A1 WO 2003022937 A1 WO2003022937 A1 WO 2003022937A1 EP 0209734 W EP0209734 W EP 0209734W WO 03022937 A1 WO03022937 A1 WO 03022937A1
Authority
WO
WIPO (PCT)
Prior art keywords
dual
hydrolyzable
cure
polysiloxane
group
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2002/009734
Other languages
German (de)
English (en)
Inventor
Hubert Baumgart
Peter Hommes
Manuela Niemeier
Ulrike RÖCKRATH
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BASF Coatings GmbH
Original Assignee
BASF Coatings GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BASF Coatings GmbH filed Critical BASF Coatings GmbH
Publication of WO2003022937A1 publication Critical patent/WO2003022937A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Des sols de polysiloxane thermodurcissables et durcissables par rayonnement actinique (sols de polysiloxane à durcissement double) sont obtenus par hydrolyse et condensation (A) d'au moins un composé du silicium hydrolysable, de formule générale (I):XmSi(R-Yn)4-m (I),dans laquelle les indices et les variables ont les significations ci-après : m : égal à 1, 2 ou 3 ; n : égal à 1, 2 ou 3 ; X : reste hydrolysable ; R : reste organique à deux liaisons, non hydrolysable ; Y : groupe isocyanate bloqué ; en présence (B) d'au moins un composé renfermant au moins un groupe fonctionnel réactif ayant au moins une liaison activable par rayonnement actinique et au moins un groupe fonctionnel réagissant avec des isocyanates. L'invention concerne en outre un procédé d'obtention des produits précités et leur utilisation comme couches de revêtement, adhésifs et produits d'étanchéification, ou pour la production de ceux-ci.
PCT/EP2002/009734 2001-09-05 2002-08-30 Sols de polysiloxane thermodurcissables et durcissables par rayonnement actinique, leur procede d'obtention et leur utilisation Ceased WO2003022937A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE2001143414 DE10143414A1 (de) 2001-09-05 2001-09-05 Thermisch und mit aktinischer Strahlung härtbare Polysiloxan-Sole, Verfahren zu ihrer Herstellung und ihre Verwendung
AE10143414.6 2001-09-05

Publications (1)

Publication Number Publication Date
WO2003022937A1 true WO2003022937A1 (fr) 2003-03-20

Family

ID=7697737

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2002/009734 Ceased WO2003022937A1 (fr) 2001-09-05 2002-08-30 Sols de polysiloxane thermodurcissables et durcissables par rayonnement actinique, leur procede d'obtention et leur utilisation

Country Status (2)

Country Link
DE (1) DE10143414A1 (fr)
WO (1) WO2003022937A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2005053861A1 (fr) * 2003-12-01 2005-06-16 Basf Coatings Ag Couche de finition transparente thermodurcie, son procede de production et son utilisation
CN109689814A (zh) * 2016-09-09 2019-04-26 信越化学工业株式会社 底漆组合物和幕墙单元
CN111286034A (zh) * 2020-04-03 2020-06-16 苏州天山新材料技术有限公司 有机硅聚合物、包含其的混合物和有机硅胶粘剂

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE10348544A1 (de) * 2003-10-20 2005-05-19 Basf Coatings Ag Thermisch und mit aktinischer Strahlung härtbare Pulverslurries, Verfahren zu ihrer Herstellung und ihre Verwendung
JP2005298759A (ja) * 2004-04-15 2005-10-27 Nippon Paint Co Ltd クリヤー塗料組成物及びクリヤー塗膜形成方法
DE102008000721A1 (de) * 2008-03-18 2009-09-24 Evonik Degussa Gmbh Strahlenhärtbare Formulierungen
EP2108463B8 (fr) 2008-04-11 2019-10-09 BASF Coatings GmbH Procédé de fabrication de peintures fantaisie et leur utilisation
DE102015224049A1 (de) * 2015-12-02 2017-06-08 Schaeffler Technologies AG & Co. KG Primerschicht aus einem anorganisch-organischen-Hybridpolymerwerkstoff

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE4011044A1 (de) * 1990-04-05 1991-10-10 Fraunhofer Ges Forschung Silane, verfahren zu ihrer herstellung und ihre verwendung zur herstellung von polymerisaten und polykondensaten
EP1036827A2 (fr) * 1999-03-11 2000-09-20 Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. Procédé de fabrication de peintures exposables aux intempéries

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE4011044A1 (de) * 1990-04-05 1991-10-10 Fraunhofer Ges Forschung Silane, verfahren zu ihrer herstellung und ihre verwendung zur herstellung von polymerisaten und polykondensaten
EP1036827A2 (fr) * 1999-03-11 2000-09-20 Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. Procédé de fabrication de peintures exposables aux intempéries

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2005053861A1 (fr) * 2003-12-01 2005-06-16 Basf Coatings Ag Couche de finition transparente thermodurcie, son procede de production et son utilisation
CN109689814A (zh) * 2016-09-09 2019-04-26 信越化学工业株式会社 底漆组合物和幕墙单元
CN111286034A (zh) * 2020-04-03 2020-06-16 苏州天山新材料技术有限公司 有机硅聚合物、包含其的混合物和有机硅胶粘剂

Also Published As

Publication number Publication date
DE10143414A1 (de) 2003-03-27

Similar Documents

Publication Publication Date Title
EP1218434B1 (fr) Copolymeres greffes a base de polyurethanne, ainsi que leur utilisation pour la fabrication de matieres de revetement, d'adhesifs et de masses d'etancheite
EP1232221B1 (fr) Agent d'application contenant un solvant et utilisation
EP1196507B1 (fr) Peinture d'appret et son utilisation pour la production de peintures d'appret et de peintures multicouches a coloration ou a effet
EP1423449B1 (fr) Matieres de revetement durcissables thermiquement et par rayonnement actinique et leur utilisation
EP1226198B1 (fr) Polyurethannes a auto-reticulation et copolymeres greffes a base de polyurethanne et leur utilisation pour la production de matieres de revetement, d'adhesifs et de masses d'etancheite
EP1194491B1 (fr) Vernis et son utilisation pour la production de vernis et de peintures multicouches a coloration ou a effet
EP1397449A1 (fr) Matieres de revetement durcissables par voie thermique et par exposition a un rayonnement actinique, leur procede de production et leur utilisation
EP1425326A1 (fr) Polyurethanes et copolymeres greffes a base de polyurethane, et leur utilisation pour preparer des matieres de revetement, des matieres adhesives et des matieres d'etancheite
EP1373347A1 (fr) Suspensions pulverulentes durcissables thermiquement et par rayonnement actinique, procede de production et utilisation
EP1311579B1 (fr) Procede de preparation des matieres de revetement, des matieres adhesives et des matieres d'etancheite
DE10021139B4 (de) Mehrkomponentenbeschichtungsstoffe, -klebstoffe und -dichtungsmassen und ihre Verwendung
EP1311580B1 (fr) Systemes a composante unique durcissable par reaction thermique et par rayonnement actinique et leur utilisation
WO2002026852A1 (fr) Materiaux de revetement, adhesifs et produits d"etancheite multicomposants durcissables thermiquement et par rayonnement actinique, et leur utilisation
EP1583808B1 (fr) Systeme a plusieurs composants et utilisation de celui-ci dans la fabrication d'un melange a durcissage triple pouvant etre durci sous l'effet de la chaleur et d'un rayonnement actinique
EP1200203B1 (fr) Peinture multicouche de coloration et/ou a effets, son procede de realisation et son utilisation
WO2003022937A1 (fr) Sols de polysiloxane thermodurcissables et durcissables par rayonnement actinique, leur procede d'obtention et leur utilisation
WO2003022938A2 (fr) Melange de matieres durcissables thermiquement et par un rayonnement actinique, son procede de production et son utilisation
DE10200928A1 (de) Organische Dispersionen von oberflächenmodifizierten Nanopartikeln, Verfahren zu ihrer Herstellung und ihre Verwendung
EP1628782A1 (fr) Substances de revetement a une composante thermodurcissables, procede pour le preparer et leur utilisation
DE10020969A1 (de) Mehrkomponentenbeschichtungsstoffe, -klebstoffe und -dichtungsmassen und ihre Verwendung

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BY BZ CA CH CN CO CR CU CZ DK DZ EC EE ES FI GB GD GE GH GM HR ID IL IN IS JP KE KG KP KR KZ LC LK LS LT LU LV MA MD MG MK MN MW MZ NO NZ OM PH PL PT RO RU SD SE SI SK SL TJ TM TN TR TT TZ UA UG UZ VC VN YU ZA ZM

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ UG ZM ZW AM AZ BY KG KZ RU TJ TM AT BE BG CH CY CZ DK EE ES FI FR GB GR IE IT LU MC PT SE SK TR BF BJ CF CG CI GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: JP

WWW Wipo information: withdrawn in national office

Country of ref document: JP