WO2003095749A1 - Systeme de confinement a asphalte modifiee par un polymere - Google Patents

Systeme de confinement a asphalte modifiee par un polymere Download PDF

Info

Publication number
WO2003095749A1
WO2003095749A1 PCT/US2003/015165 US0315165W WO03095749A1 WO 2003095749 A1 WO2003095749 A1 WO 2003095749A1 US 0315165 W US0315165 W US 0315165W WO 03095749 A1 WO03095749 A1 WO 03095749A1
Authority
WO
WIPO (PCT)
Prior art keywords
shall
modified asphalt
panel
asphalt
containment system
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2003/015165
Other languages
English (en)
Inventor
Ronald L. Terrel
Karl Yost
Gale Schwiesow
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wilder Construction Co
Original Assignee
Wilder Construction Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wilder Construction Co filed Critical Wilder Construction Co
Priority to AU2003234562A priority Critical patent/AU2003234562A1/en
Publication of WO2003095749A1 publication Critical patent/WO2003095749A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un système de confinement de déchets ou de zones environnementales comprenant de l'asphalte modifiée par un polymère, spécifiquement conçue pour un confinement, et un système d'installation fournissant un couvercle sans soudure sur la zone à confiner. L'asphalte modifiée de l'invention possède une perméabilité inférieure à 1 x 10-7 cm/sec et un contenu en vide d'air inférieur à 3 %. Ledit système d'installation comprend des conceptions de joint correspondant aux mêmes paramètres que le matte d'asphalte modifiée afin de fournir un couvercle ou une garniture de confinement sans soudure pouvant contenir des déchets dangereux au niveau de la récupération et de la conservation des ressources, de sites spéciaux pour l'environnement, de sites de déchets et de zones de confinement environnemental.
PCT/US2003/015165 2002-05-10 2003-05-12 Systeme de confinement a asphalte modifiee par un polymere Ceased WO2003095749A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU2003234562A AU2003234562A1 (en) 2002-05-10 2003-05-12 Polymer-modified asphalt containment system

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US37995902P 2002-05-10 2002-05-10
US60/379,959 2002-05-10

Publications (1)

Publication Number Publication Date
WO2003095749A1 true WO2003095749A1 (fr) 2003-11-20

Family

ID=29420587

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2003/015165 Ceased WO2003095749A1 (fr) 2002-05-10 2003-05-12 Systeme de confinement a asphalte modifiee par un polymere

Country Status (2)

Country Link
AU (1) AU2003234562A1 (fr)
WO (1) WO2003095749A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2912413A1 (fr) * 2007-02-14 2008-08-15 Total France Sa Composition bitumineuse resistante au vieillissement
CN115691711A (zh) * 2022-10-06 2023-02-03 哈尔滨工业大学 一种沥青混合料拌合站溢料预测与稳定性的评价方法
CN116026125A (zh) * 2023-03-24 2023-04-28 河北四正北方新型材料科技有限公司 一种防水卷材胎体用节能效果好的烘干设备
CN117051638A (zh) * 2023-08-23 2023-11-14 昆山市交通工程集团有限公司 一种沥青下面层施工工艺

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1035879A (en) * 1964-11-06 1966-07-13 Lloyd French Bramble Asphalt lining
FR2495664A1 (fr) * 1980-08-28 1982-06-11 Meple Materiaux Etancheite Ent Nouveaux materiaux d'etancheite assurant l'independance de la premiere couche des revetements d'etancheite
FR2625243A1 (fr) * 1987-12-24 1989-06-30 Soprema Sa Systeme d'etancheisation des toitures
EP0420747A2 (fr) * 1989-09-29 1991-04-03 Societe De Pavage Et Des Asphaltes De Paris,Societe Anonyme Dite S P A P A Feuille bitumineuse d'étanchéité destinée à recevoir une couche d'asphalte coulé

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1035879A (en) * 1964-11-06 1966-07-13 Lloyd French Bramble Asphalt lining
FR2495664A1 (fr) * 1980-08-28 1982-06-11 Meple Materiaux Etancheite Ent Nouveaux materiaux d'etancheite assurant l'independance de la premiere couche des revetements d'etancheite
FR2625243A1 (fr) * 1987-12-24 1989-06-30 Soprema Sa Systeme d'etancheisation des toitures
EP0420747A2 (fr) * 1989-09-29 1991-04-03 Societe De Pavage Et Des Asphaltes De Paris,Societe Anonyme Dite S P A P A Feuille bitumineuse d'étanchéité destinée à recevoir une couche d'asphalte coulé

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
SCHOENIAN E: "ASPHALTBETON - DICHTUNGEN IM DEPONIEBAU", MUELL UND ABFALL, SCHMIDT VERLAG, BERLIN, DE, vol. 23, no. 1, 1991, pages 12,14 - 19, XP000176961, ISSN: 0027-2957 *

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2912413A1 (fr) * 2007-02-14 2008-08-15 Total France Sa Composition bitumineuse resistante au vieillissement
WO2008101809A1 (fr) * 2007-02-14 2008-08-28 Total Raffinage Marketing Composition bitumineuse resistante au vieillissement
CN115691711A (zh) * 2022-10-06 2023-02-03 哈尔滨工业大学 一种沥青混合料拌合站溢料预测与稳定性的评价方法
CN116026125A (zh) * 2023-03-24 2023-04-28 河北四正北方新型材料科技有限公司 一种防水卷材胎体用节能效果好的烘干设备
CN116026125B (zh) * 2023-03-24 2023-05-30 河北四正北方新型材料科技有限公司 一种防水卷材胎体用烘干设备
CN117051638A (zh) * 2023-08-23 2023-11-14 昆山市交通工程集团有限公司 一种沥青下面层施工工艺

Also Published As

Publication number Publication date
AU2003234562A1 (en) 2003-11-11

Similar Documents

Publication Publication Date Title
CN100482742C (zh) 重建道路路面的方法
Perkins Synthesis of warm mix asphalt paving strategies for use in Montana highway construction
Series Designing and Constructing SMA Mixtures—State-of-the-practice
US7077602B2 (en) Method and system for containment, such as a containment cap for solid waste constructed of modified asphalt
Williams et al. Sources, measurements, and effects of segregated hot mix asphalt pavement
WO2003095749A1 (fr) Systeme de confinement a asphalte modifiee par un polymere
Putman et al. Laboratory evaluation of anti-strip additives in hot mix asphalt
Jones et al. Warm-Mix Asphalt Study: Test Track Construction and FirstLevel Analysis of Phase 3b HVS and Laboratory Testing (Rubberized Asphalt, Mix Design# 2)
Cross et al. Cold-in-place recycling in New York State.
Potgieiter Bitumen Rubber Asphalt: Year 2003. Design and Construction Procedure in South Africa
Congress Recommended practice for recycling of bituminous pavements
Jackson et al. Quieter Pavements Survey
Baskandi Bituminous Pavement Recycling–Effective Utilization of Depleting Non-Renewable Resources
Chan et al. New Mix Design Method for Hot-Mix Cold-Laid Mixtures
Noferini Performances and durability of asphalt mixtures made with reclaimed asphalt Pavement
Graham Pavement Preservation Best Practices Technical Briefs
Myers Stone Matrix Asphalt, the Washington Experience
Miller Maintenance and Performance Study of Porous Asphalt in Northern Climates at the Randolph Park & Ride
Nordcbeck Construction of Cold Central Plant Recycling and Cold In-Place Recycling of Asphalt Pavements
Fager Asphalt-rubber overlay on rubblized concrete pavement on I-135
Maupin Field trials of asphalt rubber hot mix in Virginia.
Hajj et al. State-of-the-practice in chip seal, slurry seal, micro surfacing, and thin lift asphalt overlay construction quality assurance
Reckard et al. Asphalt pavement inspector's manual
Sivasubramaniam Validation of Superpave mixture design and analysis procedures using the NCAT test track
Prowell Design, construction, and early performance of hot-mix asphalt stabilizer and modifier test sections.

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NI NO NZ OM PH PL PT RO RU SC SD SE SG SK SL TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: JP

WWW Wipo information: withdrawn in national office

Country of ref document: JP