WO2000020496A1 - Spannungsrissbeständige cycloolefincopolymer-komposition - Google Patents

Spannungsrissbeständige cycloolefincopolymer-komposition Download PDF

Info

Publication number
WO2000020496A1
WO2000020496A1 PCT/EP1999/007276 EP9907276W WO0020496A1 WO 2000020496 A1 WO2000020496 A1 WO 2000020496A1 EP 9907276 W EP9907276 W EP 9907276W WO 0020496 A1 WO0020496 A1 WO 0020496A1
Authority
WO
WIPO (PCT)
Prior art keywords
polymer composition
composition according
different
radical
copolymer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP1999/007276
Other languages
English (en)
French (fr)
Inventor
Alexandra Jacobs
Klaus Berger
Wilfried Hatke
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ticona GmbH
Original Assignee
Ticona GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ticona GmbH filed Critical Ticona GmbH
Priority to EP99953747A priority Critical patent/EP1129132A1/de
Priority to US09/806,778 priority patent/US6566475B1/en
Priority to CA002345972A priority patent/CA2345972A1/en
Priority to AU10332/00A priority patent/AU1033200A/en
Priority to JP2000574602A priority patent/JP2002526623A/ja
Publication of WO2000020496A1 publication Critical patent/WO2000020496A1/de
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Die vorliegende Erfindung betrifft eine Polymer-Komposition, enthaltend ein oder mehrere Cycloolefincopolymere und ein oder mehrere Additive geeigneter Zusammensetzung, die sich durch eine verbesserte Beständigkeit gegen Rissbildung unter Spannung an Luft wie auch in Kontakt mit spannungsrissauslösenden Medien auszeichnet.

Description

Beschreibung
Spannuπgsπßbestandige Cycloolefincopolymer-Komposition
Die vorliegende Erfindung betrifft eine Komposition aus Cycloolefmcopolymeren (COC) und Additiven zur Verbesserung der Spannungsrißbestandigkeit Die erfindungsgemaße Polymer-Komposition zeichnet sich durch eine verbesserte Beständigkeit gegen Rißbildung unter Spannung an Luft wie auch in Kontakt mit spannuπgsπßauslosenden Medien aus
Die fehlende Beständigkeit verschiedener Kunststoffe gegen Rißbildung unter Spannung an Luft wie auch in Kontakt mit spanπungsrißauslosenden Medien ist ein gravierendes Problem, da es αie Emsetzbarkeit der Kunststoffe stark einschränkt und die Lebensdauer entsprechender Bauteile verkürzt
Es wurde überraschenderweise gefunden, daß eine Polymer-Komposition die eines oder mehrere Cycloolefincopolymere und eines oder mehrere Additive geeigneter Zusammensetzung enthalt, sich durch eine verbesserte Beständigkeit gegen Rißbildung unter Spannung an Luft wie auch in Kontakt mit spannuπgsπßauslosenden Medien auszeichnet
Die erfindungsgemaße Polymer-Komposition enthalt mindestens ein Cycloolefincopolymer, das hergestellt wird durch Polymerisation von 0,1 bis 99,9 Gew -%, bezogen auf die Gesamtmenge der Moπomeren, mindestens eines polycyclischen Olefiπs der Formel I, II, II', III, IV oder V
Figure imgf000003_0001
Figure imgf000004_0001
Figure imgf000004_0002
Figure imgf000004_0003
Figure imgf000004_0004
Figure imgf000005_0001
worin R1 bis R8 gleich oder verschieden sind und ein Wasserstoffatom oder einen Kohlenwasserstoffrest bedeuten, wobei gleiche Reste in den verschiedenen Formeln eine unterschiedliche Bedeutung haben können, 0 bis 99 9 Gew -% bezogen auf die Gesamtmenge der Mono ereπ, mindestens eines monocyclischen Olefins der Formel VI
C H C H
(VI)
( C H 2 )
worin n eine Zahl von 2 bis 10 ist und 0,1 bis 99,9 Gew -%, bezogen auf die Gesamtmenge der Monomereπ mindestens eines acyc schen 1 -Olefins der Formel VII
ι o
( V I I )
1 1 , 1 2
worin R9 bis R12 gleich oder verscheiden sind und ein Wasserstoffatom oder einen Kohleπwasserstoffrest, bevorzugt einen C6-Cιo-Arylrest oder einen Cι-C8-Alkylrest bedeuten
Bevorzugt sind Cycloolefiπe der Formeln I oder III, worin R1 bis R8 gleich oder verscheiden sind und ein Wasserstoffatom oder einen Kohlenwasserstoffrest, insbesondere einen (C6-Cι0)-Arylrest oder einen (d-C8)-Alkylrest bedeuten, wobei gleiche Reste in den verschiedenen Formeln eine unterschiedliche Bedeutung haben können
Gegebenenfalls werden ein oder mehrere mαnocyclische Olefine der Formel VI für die Polymerisation verwendet
Bevorzugt ist weiterhin ein acyclisches Olefin der Formel VII worin R9 bis R12 gleich oder verscheiden sind und ein Wasserstoffatom oder einen Kohlenwasserstoffrest, bevorzugt eine C6-Cιo-Arylrest oder einen d-Cs-Alkylrest bedeuten, wie Ethyleπ, Propylen
Insbesondere werden Copolymere von polycyclischen Olefinen, vorzugsweise der Formeln I und III, mit Ethylen hergestellt
Besonders bevorzugte polycyclische Olefine sind Norbomeπ und Tetracyclododecen wobei diese durch Cι-C6-Alkyl substituiert sein können Sie werden vorzugsweise mit Ethylen copolymeπsiert Ganz besonders bevorzugt sind Ethylen/Norborπen-Copolymere und Ethyleπ/Tetracyclododecen-Copolymere
Die Herstellung der Cycloolefmpolymere geschieht durch eine heterogene oder homogene Katalyse mit metallorganischen Verbindungen Katalysatorsysteme basierend auf Mischkatalysatoren aus Titansalzen und Aluminiumorganylen werden in DD-A-109 224 und DD-A-237 070 beschreiben EP-A-156 464 beschreibt die Herstellung mit Katalysatoren auf Vanadiumbasis EP-A-283 164, EP-A-407 870, EP-A-485 893 und EP-A-503 422 beschreiben die Herstellung von Cycloolefinpolymeren mit Katalysatoren basierend auf löslichen Metalloceπkomplexen Auf die in diesen Patenten zur Herstellung von Cycioolefmcopolymeren beschriebenen Herstellungsverfahren und verwendeten Katalysatorsysteme wird hiermit ausdrücklich Bezug genommen NOT FURNISHED UPON FILING
NO PRESENTADO(A) EN EL MOMENTO DE LA PRESENT ACION
NON SOUMIS(E) AU MOMENT DU DEPOT
[4-(η5-cyciopentadιenyl)-4,7-dιmethyl-7-pheπyl-(η5-4,5,6,7- tetrahydroιndenyl)]zιrkondιchlorιd
^-(η^S'-tert -butylcyclopentadienylH.y -tπp enyl^η .S.β.y- tetrahydroιndenyl)]zιrkondιchloπd, [4-(η5-3'-tert.-butylcyclopeπtadιenyl)-4,7-dιmethyl-7-phenyl-(η5-4 5 6,7- tetrahydroιndenyl)]zιrkondιchloπd
[4-(ηs-3'-methylcyclopentadιenyl)-4,7,7-tπmethyl-(rι5-4,5,6,7- tetrahydroιndenyl)]zιrkondιchlorιd,
[4-(η5-3'-methylcyclopentadιenyl)-4,7,7-tπphenyl-(η5-4, 5,6,7- tetrahydroιndenyl)]zιrkondιchloπd
[4-(η5-3'-methylcyclopentadιenyl)-4,7-dιmethyl-7-phenyl-(η5-4,5,6 7- tetrahydroιndenyl)]zιrkondιchloπd,
[4-(η5-3'-ιsopropylcyclopentadιenyl)-4,7,7-tπmethyl-(η5-4,5,6,7- tetrahydroιndenyl)]zιrkondιchloπd, [4-(η5-3'-ιsoproplycyclopentadιenyl)-4,7,7-tπphenyl-(η5-4,5,6,7- tetrahydroιndenyl)]zιrkondιchloπd,
[4-(η5-3'-ιsopropylcyclopentadιenyl)-4,7-dιmethyl-7-phenyl-(rι5-4, 5,6,7- tetrahydroιπdeπyl)]zιrkondιchloπd,
[4-(η5-cyclopentadιenyl)(η5-4,5-tetrahydropentalen)]zιrkondιchloπd, [4-(η5-cyclopentadιenyl)-4-methyl-(η5-4,5-tetrahydropentalen)]zιrkoπdιchloπd,
[4-(η5-cyclopentadιenyl)-4-phenyl-(η5-4,5-tetrahydropentalen)]zιrkondιchloπd,
[4-(η5-cyclopentadιenyl)-4-ρhenyl-(η5-4,5-tetrahydropentalen)]zιrkondιchlorιd,
[4-(η5-3'-methyl-cyclopentadιenyl)(η5-4,5-tetrahydropentalen)]zιrkondιchloπd,
[4-(η5-3'-ιsopropylcyclopentadιenyl)(η5-4,5-tetrahydropentalen)]zιrkondιchloπd, [4-(η5-3'-benzyl-cyclopentadιenyl)(η5-4,5-tetrahydropentalen)]zιrkoπdιchloπd,
[2,2,4Tπmethyl-4-(η5-cyclopeπtadιenyl)-(η5-4,5-tetrahydropentaleπ)]- zirkoniumdichloπd,
[2,2,4Tπmethyl-4-(η5-(3,4-Dι-ιsopropyl)cyclopentadιenyl)-(η5-4,5- tetrahydropentalen)]-zιrkonιumdιchloπd
Die für die Zwecke der Erfindung geeigneten Cycloolefincopolymere weisen
Glastemperaturen auf zwischen 0 und 250°C, bevorzugt zwischen 20 und 200°C, besonders bevorzugt zwischen 50 und 180°C Die für die Zwecke der Erfindung geeigneten Cycloolefincopolymere weisen Viskositatszahlen (bestimmt in Dekalin bei 135°C) auf zwischen 10 und 200 ml/g, bevorzugt zwischen 20 und 120 ml/g, oesonαers bevorzugt zwischen 40 und 100 ml/g
Die erfindungsgemaße Polymer-Komposition enthalt außerdem eines oder mehrere Additive geeigneter Zusammensetzung, die aus den folgenden Gruppen ausgewählt werden können Verbindungen auf Basis höherer Fettsauren wie z B Ester epoxidierter Fettsauren oder Amiαe, Mono-, Di-, Tπglyzeπde organischer Sauren wie z B die Mono-, Di-, Tπglyzeπde von Monofettsauren wie Stearinsäure, Ole wie z B Mineralole, Paraffinole, Silikonole oder Weißole, Wachse wie z B Polyolefinwachse oder Montanwachse Ammonium- oder Metall-Salze, besonders Alka metall-Salze organischer Sulphonsauren wie z B verschiedener Alkylsulphonsauren oder Arylalkylsulphonsauren unterschiedlicher Kettenlange
Beispiel für ein Alkahmetall-Salz einer organischen Sulphonsaure ist das Produkt Hostastat HS1 der Firma Claπant, Beisσiel für einen Ester epoxidierter Fettsauren sind die Produkte Vikoflex der Firma Elf Atochem
Die Additive sind in der erfindungsgemaßeπ Polymer-Komposition zu Anteilen von 0,01 bis 25 Gew % enthalten, bevorzugt sind Anteile von 0,1 bis 15 Gew %, besonders bevorzugt sind Anteile von 1 bis 10 Gew %
Die Polymer-Komposition enthaltend mindestens ein Cycloolefincopolymer und mindestens ein Additiv geeigneter Zusammensetzung kann durch übliche Verfahren hergestellt werden, z B durch Vermischen des festen oder flussigen Additivs mit dem Kunststoffgranulat uπα anschließendes Verkneten oder Extrudieren der Kunststoffschmelze Insbesondere können die Komponenten in Form von Pulvern oder Granulaten durch gemeinsame Extrusion aus der Schmelze zu Granulaten oder Chips verarbeitet werden, die anschließend in geformte Gebilde überfuhrt werden können, z B durch Pressen, Extrudieren oder Spritzgießen, Blasformen etc Die erfindungsgemaße Polymer-Komposition kann auch hergestellt werden über sogenannte masterbatches Hierbei werden ein oder mehrere Additive in Mengen von 20 bis 80 Gew -%, bezogen auf die Gesamtmasse der Polymer-Legierung, mit einem oder mehreren Cycloolefiπcopolymeren gemischt (bevorzugt durch gemeinsame Extrusion) und anschließend auf die gewünschte Endkonzentration durch erneutes Mischen (bevorzugt durch gemeinsame Extrusion) mit einem oder mehreren Cycloolefincopolymeren gebracht Diese Methode fuhrt zu einer guten Dispergierung der Additive
Die erfindungsgemaße Polymer-Komposition kann weitere Additive in üblichen Mengen enthalten wie UV-Stabilisatoren optische Aufheller, Antioxidantien, Gleitmittel Weichmacher Anstistatika, Warmestabilisatoren, farbgebende Zusätze wie anorganische oder organische Pigmente oder Farbstoffe, Flammschutzmittel oder verstärkende Zusätze wie Glasfasern, Kohlefasern oder Hochmodulfasern wie Polyaramide oder flussigkπstalline Polyester oder ähnliche Außerdem können sie Füllstoffe wie anorganische Materialien, Talkum, Titandioxid oder ahnliches enthalten
Insbesondere eignet sich die erfindungsgemaße Polymer-Komposition zur Herstellung spπtzgegosseπer, spritzgeblasener, extrusionsgeblasener oder extrudierter Formkorper Außerdem können auch Folien und Fasern aus der erfmdungsgemaßen Polymer-Komposition hergestellt werden
Die erfindungsgemaße Polymer-Komposition eignet sich für eine Vielzahl von Anwendungen im Verpackungsbereich, im Bereich der Medizintechnik, im Bereich optischer Anwendungen und im technischen und Konstruktionsbereich
Die erfindungsgemaße Polymer-Komposition weist eine hohe Spannungsπßbestandigkeit auf Außerdem zeichnet sich die erfindungsgemaße Polymer-Komposition durch eine gute Fließfahigkeit aus, was insbesondere für Spπtzgußanwendungen von Vorteil ist Die mechanischen Eigenschaften wie z B Warmeformstabilitat, Reißdehnung und Kerbschlagzahigkeit lassen sich in weiten Bereichen variieren, so daß vielfaltige Anwendungsbereiche zugänglich sind

Claims

Patentansprüche
Polymer-Komposition enthaltend eines oder mehrere Cycloolefincopolymere und eines oder mehrere Additive geeigneter Zusammensetzung zur Verbesserung der Spannungsrißbeständigkeit.
Polymer-Komposition nach Anspruch 1 , enthaltend mindestens ein Cycloolefincopolymer, das hergestellt wird durch Polymerisation von 0,1 bis 99,9 Gew.-%, bezogen auf die Gesamtmenge der Monomeren, mindestens eines polycyclischen Olefins der Formel I, II, II', III, IV oder V
Figure imgf000011_0001
Figure imgf000011_0002
Figure imgf000011_0003
Figure imgf000012_0001
Figure imgf000012_0002
Figure imgf000012_0003
worin R bis R8 gleich oder verschieden sind und ein Wasserstoffatom oder einen Kohlenwasserstoffrest bedeuten, wobei gleiche Reste in den verschiedenen Formeln eine unterschiedliche Bedeutung haben können, 0 bis 99,9 Gew.-%, bezogen auf die Gesamtmenge der Monomeren, mindestens eines monocyclischen Olefins der Formel VI C H C H
(VI)
( C H 2 )
worin n eine Zahl von 2 bis 10 ist, und 0,1 bis 99,9 Gew.-%, bezogen auf die Gesamtmenge der Monomeren, mindestens eines acyclischen 1 -Olefins der Formel VII
1 0
( V I I ) i I . 1 2
worin R9 bis R12 gleich oder verscheiden sind und ein Wasserstoffatom oder einen Kohlenwasserstoffrest, bevorzugt einen C6-Cιo-Arylrest oder einen Ci- Cs-Alkylrest bedeuten.
3. Polymer-Komposition nach Anspruch 1 oder 2, wobei Cycloolefine der Formeln I oder III, worin R1 bis Ra gleich oder verschieden sind und ein Wasserstoffatom oder einen Kohlenwasserstoffrest, insbesondere einen (C6-Cιo)-Arylrest oder einen (CrC8)-Alkylrest bedeuten, wobei gleiche Reste in den verschiedenen Formeln eine unterschiedliche Bedeutung haben können.
4. Polymer-Komposition nach einem oder mehreren der Ansprüche 1 bis 3, wobei ein acyclisches Olefin der Formel VII, worin R9 bis R12 gleich oder verschieden sind und ein Wasserstoffatom oder einen Kohlenwasserstoffrest, bevorzugt eine C6-Cι0-Arylrest oder einen Cι-C8-
Alkylrest bedeuten, bevorzugt Ethylen, Propylen.
5. Polymer-Komposition nach einem oder mehreren der Ansprüche 1 bis 4, wobei das Copolymere mit polycyclischen Olefinen, vorzugsweise der Formeln I und III, und mit Ethylen hergestellt wird.
6. Polymer-Komposition nach einem oder mehreren der Ansprüche 1 bis 5, wobei polycyclische Olefine Norbomen und Tetracyclododecen sind, die durch C-i-Cβ-Alkyl substituiert sind.
7. Polymer-Komposition nach einem oder mehreren der Ansprüche 1 bis 6, wobei das Copolymer Ethylen/Norbomeπ-Copolymer oder
Ethylen/Tetracyclododecen-Copolymer ist.
8. Verfahren zur Herstellung der Polymer-Komposition nach einem oder mehreren der Ansprüche 1 bis 7 in an sich bekannter Weise.
9. Verwendung der Polymer-Komposition zur Herstellung spritzgegossener, spritzgeblasener, extrusionsgeblasener oder extrudierter Formkörper, sowie für Folien und Fasern.
10. Verwendung der Formkörper, Folien und Fasern gemäß Anspruch 9 im
Verpackungsbereich, im Bereich der Medizintechnik, im Bereich optischer Anwendungen und im technischen und Konstruktionsbereich
PCT/EP1999/007276 1998-10-01 1999-10-01 Spannungsrissbeständige cycloolefincopolymer-komposition Ceased WO2000020496A1 (de)