WO1999064368A1 - Composition additive pour des melanges de materiau de construction a base d'eau - Google Patents

Composition additive pour des melanges de materiau de construction a base d'eau Download PDF

Info

Publication number
WO1999064368A1
WO1999064368A1 PCT/US1999/013052 US9913052W WO9964368A1 WO 1999064368 A1 WO1999064368 A1 WO 1999064368A1 US 9913052 W US9913052 W US 9913052W WO 9964368 A1 WO9964368 A1 WO 9964368A1
Authority
WO
WIPO (PCT)
Prior art keywords
interpolymer
additive composition
building material
homo
olefinically unsaturated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US1999/013052
Other languages
English (en)
Inventor
Thomas Jeszenszky
Jürgen Eiffler
Yvonne Madeleine Goerlach-Doht
Heiko Dahms
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dow Chemical Co
Original Assignee
Dow Chemical Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Chemical Co filed Critical Dow Chemical Co
Priority to AU44318/99A priority Critical patent/AU4431899A/en
Publication of WO1999064368A1 publication Critical patent/WO1999064368A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne une composition additive pour des mélanges de matériau de construction à base d'eau. Cette composition comprend (a) un éther de cellulose, un éther d'amidon, de la gomme de guar et/ou de la gomme xanthane; (b) un homo- ou interpolymère de méthacrylamide ou d'acrylamide, et (c) un homo- ou interpolymère non réticulé comprenant un ou des groupes carboxyles non saturés en oléfine, contenant un composé sous forme polymérisée. La composition additive est particulièrement utile dans les plâtres à pulvériser.
PCT/US1999/013052 1998-06-10 1999-06-09 Composition additive pour des melanges de materiau de construction a base d'eau Ceased WO1999064368A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU44318/99A AU4431899A (en) 1998-06-10 1999-06-09 Additive composition for water-based building material mixtures

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GB9812504.0 1998-06-10
GBGB9812504.0A GB9812504D0 (en) 1998-06-10 1998-06-10 Additive composition for water-based building material mixtures

Publications (1)

Publication Number Publication Date
WO1999064368A1 true WO1999064368A1 (fr) 1999-12-16

Family

ID=10833520

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1999/013052 Ceased WO1999064368A1 (fr) 1998-06-10 1999-06-09 Composition additive pour des melanges de materiau de construction a base d'eau

Country Status (3)

Country Link
AU (1) AU4431899A (fr)
GB (1) GB9812504D0 (fr)
WO (1) WO1999064368A1 (fr)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002098817A1 (fr) * 2001-06-02 2002-12-12 Henkel Kommanditgesellschaft Auf Aktien Retardateur de prise de platre
DE102007016783A1 (de) 2007-04-05 2008-10-09 Dow Wolff Cellulosics Gmbh Methylhydroxypropylcellulose (MHPC) für mineralisch gebundene Baustoffsysteme
DE102007016726A1 (de) 2007-04-07 2008-10-09 Dow Wolff Cellulosics Gmbh Methylhydroxyethylhydroxypropylcellulose (MHEHPC) in mineralisch gebundenen Baustoffsystemen
EP1701926A4 (fr) * 2003-12-10 2011-06-15 Innovative Construction And Building Materials Llc Composite organique-inorganique
KR20110074586A (ko) * 2008-10-16 2011-06-30 다우 글로벌 테크놀로지스 엘엘씨 피드스톡의 보유 및 분배
WO2013085897A2 (fr) 2011-12-09 2013-06-13 Dow Global Technologies Llc Procédé pour réduire l'agglomération dans du plâtre de gypse ou des compositions de remplissage comprenant de l'éther de cellulose
US8465586B2 (en) 2010-07-28 2013-06-18 Dow Global Technologies Llc Polysaccharide derivatives having an adjusted particle morphology for hydrolytically setting compositions
WO2014043168A3 (fr) * 2012-09-14 2014-05-08 Dow Global Technologies Llc Compositions de mélange sec comprenant du gypse et des agglomérats d'éther de cellulose
WO2016160663A1 (fr) * 2015-03-30 2016-10-06 Dow Global Technologies Llc Éther de cellulose modifié présentant une meilleure aptitude au façonnage à utiliser dans des applications de mortier de lissage a base gypse et de produit de jointoiement

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3920025A1 (de) * 1989-06-20 1991-01-03 Aqualon Gmbh Additivgemische auf basis von alkyl-, alkyl-hydroxyalkyl- und/oder hydroxyalkylzellulosen fuer moertel, spachtelmassen und/oder putzmassen auf gipsbasis und ihre anwendung in diesen bauhilfsmitteln
EP0530768A1 (fr) * 1991-09-03 1993-03-10 Hoechst Aktiengesellschaft Combination d'additifs pour améliorer l'aptitude au traitement de mélanges aqueux de matériaux de construction
GB2298860A (en) * 1995-03-16 1996-09-18 Sandoz Ltd Cement spraying admixture
EP0736553A2 (fr) * 1995-04-07 1996-10-09 SKW Trostberg Aktiengesellschaft Copolymères à base d'oxyalkylèneglykol et dérivés d'acides dicarboxyliques insaturés

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3920025A1 (de) * 1989-06-20 1991-01-03 Aqualon Gmbh Additivgemische auf basis von alkyl-, alkyl-hydroxyalkyl- und/oder hydroxyalkylzellulosen fuer moertel, spachtelmassen und/oder putzmassen auf gipsbasis und ihre anwendung in diesen bauhilfsmitteln
EP0530768A1 (fr) * 1991-09-03 1993-03-10 Hoechst Aktiengesellschaft Combination d'additifs pour améliorer l'aptitude au traitement de mélanges aqueux de matériaux de construction
GB2298860A (en) * 1995-03-16 1996-09-18 Sandoz Ltd Cement spraying admixture
EP0736553A2 (fr) * 1995-04-07 1996-10-09 SKW Trostberg Aktiengesellschaft Copolymères à base d'oxyalkylèneglykol et dérivés d'acides dicarboxyliques insaturés

Cited By (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002098817A1 (fr) * 2001-06-02 2002-12-12 Henkel Kommanditgesellschaft Auf Aktien Retardateur de prise de platre
EP1701926B1 (fr) 2003-12-10 2016-03-02 Saint-Gobain Placo Composite organique-inorganique
EP1701926A4 (fr) * 2003-12-10 2011-06-15 Innovative Construction And Building Materials Llc Composite organique-inorganique
EP3002264A1 (fr) * 2003-12-10 2016-04-06 Saint-Gobain Placo Composite organique-inorganique
DE102007016783A1 (de) 2007-04-05 2008-10-09 Dow Wolff Cellulosics Gmbh Methylhydroxypropylcellulose (MHPC) für mineralisch gebundene Baustoffsysteme
DE102007016726A1 (de) 2007-04-07 2008-10-09 Dow Wolff Cellulosics Gmbh Methylhydroxyethylhydroxypropylcellulose (MHEHPC) in mineralisch gebundenen Baustoffsystemen
KR101697073B1 (ko) 2008-10-16 2017-01-17 다우 글로벌 테크놀로지스 엘엘씨 피드스톡의 보유 및 분배
US8569401B2 (en) * 2008-10-16 2013-10-29 Dow Global Technologies, Llc Storing and distributing a feeder product
US20110281979A1 (en) * 2008-10-16 2011-11-17 Mienolf Brackhagen Storing and distributing a feeder product
KR20110074586A (ko) * 2008-10-16 2011-06-30 다우 글로벌 테크놀로지스 엘엘씨 피드스톡의 보유 및 분배
US8465586B2 (en) 2010-07-28 2013-06-18 Dow Global Technologies Llc Polysaccharide derivatives having an adjusted particle morphology for hydrolytically setting compositions
CN103946179B (zh) * 2011-12-09 2018-03-27 陶氏环球技术有限公司 一种减少含有纤维素醚的石膏灰泥或填料组合物中团聚的方法
WO2013085897A3 (fr) * 2011-12-09 2013-07-25 Dow Global Technologies Llc Procédé pour réduire l'agglomération dans du plâtre de gypse ou des compositions de remplissage comprenant de l'éther de cellulose
CN103946179A (zh) * 2011-12-09 2014-07-23 陶氏环球技术有限公司 一种减少含有纤维素醚的石膏灰泥或填料组合物中团聚的方法
WO2013085897A2 (fr) 2011-12-09 2013-06-13 Dow Global Technologies Llc Procédé pour réduire l'agglomération dans du plâtre de gypse ou des compositions de remplissage comprenant de l'éther de cellulose
US10457600B2 (en) 2011-12-09 2019-10-29 Dow Global Technologies Llc Method for reducing agglomeration in gypsum plaster or filling compositions comprising cellulose ether
WO2014043168A3 (fr) * 2012-09-14 2014-05-08 Dow Global Technologies Llc Compositions de mélange sec comprenant du gypse et des agglomérats d'éther de cellulose
US20180044239A1 (en) * 2015-03-30 2018-02-15 Dow Global Technologies Llc Modified cellulose ether with improved workability for use in gypsum smoothing mortar and joint filler applications
JP2018510119A (ja) * 2015-03-30 2018-04-12 ダウ グローバル テクノロジーズ エルエルシー 石膏平滑化モルタル及び目地材用途での使用のための作業性が改善された修飾セルロースエーテル
WO2016160663A1 (fr) * 2015-03-30 2016-10-06 Dow Global Technologies Llc Éther de cellulose modifié présentant une meilleure aptitude au façonnage à utiliser dans des applications de mortier de lissage a base gypse et de produit de jointoiement

Also Published As

Publication number Publication date
GB9812504D0 (en) 1998-08-05
AU4431899A (en) 1999-12-30

Similar Documents

Publication Publication Date Title
US5387626A (en) Additive combination for improving the processing properties of water-containing mixtures of building materials
US6187887B1 (en) Water-soluble or water-swellable copolymers containing sulfonic groups and methods of preparation
US8314170B2 (en) Dispersing agents
AU2003276941B2 (en) Additive for hydraulically setting systems, the hydraulically setting mixtures and the use thereof
RU2004110386A (ru) Стабилизированные поливиниловым спиртом редиспергируемые порошки с разжижающими свойствами
CN107586366B (zh) 一种改性聚羧酸减水剂及其制备方法
EP0846090A1 (fr) Agent de melange pour beton
CA2563774A1 (fr) Systemes a base de ciment utilisant des agents de retention d'eau prepares a partir de linters de coton brut
SK1582004A3 (en) Superplasticizer for concrete and self-leveling compounds
EP2158265B1 (fr) Mélange de copolymères
WO1999064368A1 (fr) Composition additive pour des melanges de materiau de construction a base d'eau
EP0537872A1 (fr) Additives inhibiteurs de la corrosion pour ciments hydrauliques et compositions les contenant
US6573326B2 (en) Thickeners based on vinyl alcohol copolymers
JP3093105B2 (ja) 自己充填性コンクリート混和剤
WO2013058912A1 (fr) Mucilages destinés à des compositions à prise hydraulique
JP4562957B2 (ja) セメント系押出し成形体用混和剤
JP3226125B2 (ja) セメント分散剤
JP3522633B2 (ja) 押出成形セメント製品用添加剤
EP1194482B1 (fr) Ouvrabilite et temps d'emploi ameliores dans un mortier de maconnerie et procede de fabrication correspondant
CN107955106A (zh) 一种混凝土流动性稳定剂的制备方法
WO1999036449A1 (fr) Copolymeres intrinsequement peu moussant et utilisation en tant qu'additifs pour ciment
JP2003002714A (ja) 水硬性組成物用分散剤
JP4562953B2 (ja) 貧配合水硬性組成物用分散剤
JPS59162157A (ja) セメント分散剤
CN116234783B (zh) 以高固体和低粘度制备聚(氧化烯)丙烯酸类聚合物的方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AL AM AT AU AZ BA BB BG BR BY CA CH CN CZ DE DK EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG US UZ YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SL SZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase