WO1999051783A1 - Procede de production de fonte en fusion a partir d'oxydes de fer et appareil correspondant - Google Patents

Procede de production de fonte en fusion a partir d'oxydes de fer et appareil correspondant Download PDF

Info

Publication number
WO1999051783A1
WO1999051783A1 PCT/US1999/006248 US9906248W WO9951783A1 WO 1999051783 A1 WO1999051783 A1 WO 1999051783A1 US 9906248 W US9906248 W US 9906248W WO 9951783 A1 WO9951783 A1 WO 9951783A1
Authority
WO
WIPO (PCT)
Prior art keywords
iron
gas
furnace
drier
rotary hearth
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US1999/006248
Other languages
English (en)
Inventor
Larry Lehtinen
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Iron Dynamics Inc
Original Assignee
Iron Dynamics Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Iron Dynamics Inc filed Critical Iron Dynamics Inc
Priority to AU31103/99A priority Critical patent/AU3110399A/en
Publication of WO1999051783A1 publication Critical patent/WO1999051783A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Cette invention a trait à des procédés améliorés de réduction d'oxydes de fer permettant d'obtenir du fer élémentaire à l'aide d'un ou de plusieurs agents de réduction solides de carbone et d'une sole de grillage rotative (600). Selon l'un des aspects préférés de l'invention, le procédé de production de fonte en fusion consiste à introduire rapidement un intermédiaire de fer spongieux chaud dans un four à arc immergé (660) sans pertes significatives de chaleur. D'autres aspects de cette invention concerne des techniques permettant de fragmenter une matière première, du minerai de fer en l'occurrence, à l'aide d'une presse à rouleau (340), des techniques permettant de récupérer et de réutiliser des effluents gazeux d'un four à arc immergé, des techniques de récupération d'une partie notable de la chaleur des effluents gazeux d'une sole de grillage rotative (700), lesquelles techniques débouchent sur des procédés à haut rendement thermique ainsi que sur des méthodes permettant d'agir sur des compositions en phase laitier dans une sole de grillage rotative (600) et dans un four à arc immergé (660) et ce, aux fins d'une manipulation et d'un traitement avantageux de matières servant à la fabrication.
PCT/US1999/006248 1998-04-03 1999-03-22 Procede de production de fonte en fusion a partir d'oxydes de fer et appareil correspondant Ceased WO1999051783A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU31103/99A AU3110399A (en) 1998-04-03 1999-03-22 Method and apparatus for producing molten iron from iron oxides

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US5458998A 1998-04-03 1998-04-03
US09/054,589 1998-04-03

Publications (1)

Publication Number Publication Date
WO1999051783A1 true WO1999051783A1 (fr) 1999-10-14

Family

ID=21992148

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1999/006248 Ceased WO1999051783A1 (fr) 1998-04-03 1999-03-22 Procede de production de fonte en fusion a partir d'oxydes de fer et appareil correspondant

Country Status (2)

Country Link
AU (1) AU3110399A (fr)
WO (1) WO1999051783A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7413592B2 (en) 2004-03-31 2008-08-19 Nu-Iron Technology, Llc Linear hearth furnace system and methods regarding same
WO2014111901A3 (fr) * 2013-01-21 2014-11-06 Chetty Natarajan Channaiah Procédé efficace de production de fer et d'acier à partir de minerai de fer
WO2018025585A1 (fr) * 2016-08-01 2018-02-08 株式会社神戸製鋼所 Procédé de production et appareil de production de fer réduit
EP4219773B1 (fr) 2020-04-30 2024-10-09 SMS group GmbH Procédé de production de fonte brute liquide à partir d'un produit dri

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4701214A (en) * 1986-04-30 1987-10-20 Midrex International B.V. Rotterdam Method of producing iron using rotary hearth and apparatus
US5186741A (en) * 1991-04-12 1993-02-16 Zia Patent Company Direct reduction process in a rotary hearth furnace
US5364441A (en) * 1990-02-13 1994-11-15 Illawarra Technology Corporation Limited Cotreatment of sewage and steelworks wastes
US5567224A (en) * 1995-06-06 1996-10-22 Armco Inc. Method of reducing metal oxide in a rotary hearth furnace heated by an oxidizing flame
US5681367A (en) * 1996-06-20 1997-10-28 Usx Engineers & Consultants, Inc. Method of producing hot metal

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4701214A (en) * 1986-04-30 1987-10-20 Midrex International B.V. Rotterdam Method of producing iron using rotary hearth and apparatus
US5364441A (en) * 1990-02-13 1994-11-15 Illawarra Technology Corporation Limited Cotreatment of sewage and steelworks wastes
US5186741A (en) * 1991-04-12 1993-02-16 Zia Patent Company Direct reduction process in a rotary hearth furnace
US5567224A (en) * 1995-06-06 1996-10-22 Armco Inc. Method of reducing metal oxide in a rotary hearth furnace heated by an oxidizing flame
US5681367A (en) * 1996-06-20 1997-10-28 Usx Engineers & Consultants, Inc. Method of producing hot metal

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7413592B2 (en) 2004-03-31 2008-08-19 Nu-Iron Technology, Llc Linear hearth furnace system and methods regarding same
US7666249B2 (en) 2004-03-31 2010-02-23 Nu-Iron Technology, Llc Linear hearth furnace system and methods regarding same
WO2014111901A3 (fr) * 2013-01-21 2014-11-06 Chetty Natarajan Channaiah Procédé efficace de production de fer et d'acier à partir de minerai de fer
WO2018025585A1 (fr) * 2016-08-01 2018-02-08 株式会社神戸製鋼所 Procédé de production et appareil de production de fer réduit
JP2018021215A (ja) * 2016-08-01 2018-02-08 株式会社神戸製鋼所 還元鉄の製造方法および製造装置
EP4219773B1 (fr) 2020-04-30 2024-10-09 SMS group GmbH Procédé de production de fonte brute liquide à partir d'un produit dri

Also Published As

Publication number Publication date
AU3110399A (en) 1999-10-25

Similar Documents

Publication Publication Date Title
RU2260624C2 (ru) Устройство и способ рециркуляции железосодержащих пыли и шлама в процессе производства чугуна с использованием угля и рудной мелочи
TW558566B (en) Method for producing granular metallic iron
US5972066A (en) Mixed bed iron reduction process
JPH02228411A (ja) 製鉄法
US20110308353A1 (en) Production of iron from metallurgical waste
JP5334240B2 (ja) 製鋼用還元鉄塊成鉱の製造方法
JP2010007182A (ja) 還元鉄製造方法
KR101234388B1 (ko) 환원철의 제조 방법
CA2713442A1 (fr) Procede et systeme pour produire des pepites de fer metallique
JP2000054039A (ja) 鉛含有材料からの金属鉛回収方法
JP3779009B2 (ja) 製鉄ダストからの高品位還元鉄の製造方法
CA2831461C (fr) Utilisation d'une distribution bimodale de carbone dans des briquettes utilisees en vue de la production de nodules metalliques de fer
AU751205B2 (en) Method for producing directly-reduced iron, liquid pig iron and steel
JP2003213312A (ja) 金属鉄の製法
WO1999051783A1 (fr) Procede de production de fonte en fusion a partir d'oxydes de fer et appareil correspondant
JPH0770662A (ja) 亜鉛含有ダスト中の亜鉛除去装置
JP5396991B2 (ja) 高亜鉛含有鉄鉱石を用いた粒鉄製造方法
JPH06330198A (ja) ダスト中の亜鉛の回収方法
JP5103802B2 (ja) 湿ダストの処理方法及び焼結鉱の製造方法
CA1204943A (fr) Methode de production du fer spongieux par reduction directe de matieres a teneur d'oxyde de fer
WO1998059079A1 (fr) Technique de reduction de fer a faible teneur en soufre a l'aide d'un four a sole rotatif
JP5397020B2 (ja) 還元鉄製造方法
US20130118307A1 (en) Device for producing granular metal iron and process for producing granular metal iron
JP3451901B2 (ja) 移動型炉床炉の操業方法
US4981510A (en) Process and apparatus for the production of ferrochromium

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SL SZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
NENP Non-entry into the national phase

Ref country code: KR

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase