WO1998012258A1 - Composition de resine styrenique ignifuge - Google Patents

Composition de resine styrenique ignifuge Download PDF

Info

Publication number
WO1998012258A1
WO1998012258A1 PCT/JP1997/003181 JP9703181W WO9812258A1 WO 1998012258 A1 WO1998012258 A1 WO 1998012258A1 JP 9703181 W JP9703181 W JP 9703181W WO 9812258 A1 WO9812258 A1 WO 9812258A1
Authority
WO
WIPO (PCT)
Prior art keywords
weight
rubber
component
flame
particles
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP1997/003181
Other languages
English (en)
Japanese (ja)
Inventor
Kazuyoshi Sueoka
Masanao Kawabe
Kiichi Kometani
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Chemical and Materials Co Ltd
Original Assignee
Nippon Steel Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Chemical Co Ltd filed Critical Nippon Steel Chemical Co Ltd
Publication of WO1998012258A1 publication Critical patent/WO1998012258A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Une composition de résine styrénique comprend 100 parties en poids d'une résine composée essentiellement d'une résine styrénique modifiée par du caoutchouc et 1 à 10 parties en poids d'un agent ignifuge exempt d'atome d'halogène, ladite résine styrénique modifiée par du caoutchouc satisfait les conditions suivantes 1) à 6): 1) 3 % en poids ≤RC≤16 % en poids (RC: teneur en caoutchouc), 2) 0,3 ≤Dw≤0,9 (Dw: diamètre de particulaire moyen au poids de particules de caoutchouc dispersées, νm), 3) une valeur de 5 % à une valeur de 95 % de répartition cumulative du diamètre des particules sur une base pondérale de particules de caoutchouc dispersées sont respectivement nonsupérieure à 1,0 νm et non inférieure à 0,20 νm, 4) le rapport pondéral entre le toluène insoluble et la teneur en caoutchouc est de (1,0 à 2,5) : 1, 5) la proportion de particules présentant une structure de type salami dans toutes les particules de caoutchouc dispersé n'est pas inférieure à 80 %, et 6) la proportion de particules de caoutchouc dispersées, dans lesquelles le nombre de particules de résine styrénique contenu dans les particules de caoutchouc dispersées n'est par supérieur à 20, n'est pas inférieur à 70 % de toutes les particules de caoutchouc dispersées.
PCT/JP1997/003181 1996-09-19 1997-09-10 Composition de resine styrenique ignifuge Ceased WO1998012258A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP24827396 1996-09-19
JP8/248273 1996-09-19

Publications (1)

Publication Number Publication Date
WO1998012258A1 true WO1998012258A1 (fr) 1998-03-26

Family

ID=17175679

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP1997/003181 Ceased WO1998012258A1 (fr) 1996-09-19 1997-09-10 Composition de resine styrenique ignifuge

Country Status (1)

Country Link
WO (1) WO1998012258A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06128339A (ja) * 1992-10-16 1994-05-10 Sumitomo Chem Co Ltd ゴム変性ポリスチレン系樹脂組成物
JPH06329735A (ja) * 1993-05-20 1994-11-29 Daicel Chem Ind Ltd ゴム変性スチレン系樹脂組成物およびその製造方法
JPH08120152A (ja) * 1994-10-24 1996-05-14 Nippon Steel Chem Co Ltd 難燃性スチレン系樹脂組成物
JPH08208940A (ja) * 1995-02-08 1996-08-13 Nippon Steel Chem Co Ltd ゴム変性スチレン系樹脂組成物

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06128339A (ja) * 1992-10-16 1994-05-10 Sumitomo Chem Co Ltd ゴム変性ポリスチレン系樹脂組成物
JPH06329735A (ja) * 1993-05-20 1994-11-29 Daicel Chem Ind Ltd ゴム変性スチレン系樹脂組成物およびその製造方法
JPH08120152A (ja) * 1994-10-24 1996-05-14 Nippon Steel Chem Co Ltd 難燃性スチレン系樹脂組成物
JPH08208940A (ja) * 1995-02-08 1996-08-13 Nippon Steel Chem Co Ltd ゴム変性スチレン系樹脂組成物

Similar Documents

Publication Publication Date Title
TWI393738B (zh) 防焰熱塑性樹脂組成物及其製備方法
KR101473774B1 (ko) 고충격 난연 폴리페닐렌 에테르계 열가소성 수지 조성물
JPH05339417A (ja) 低揮発性難燃耐熱耐衝撃性樹脂組成物
CN1685004A (zh) 阻燃苯乙烯树脂组合物
JP4790804B2 (ja) 難燃性成形組成物
KR100221924B1 (ko) 난연성을 갖는 열가소성 수지 조성물
JP2001214024A (ja) 難燃性スチレン系樹脂組成物
JPH05239338A (ja) 難燃加工した塩素および臭素不含の成形材料
JP4306906B2 (ja) 溶融滴下型難燃性スチレン系樹脂組成物
JP4479934B2 (ja) 難燃性熱可塑性樹脂組成物
JPH10147679A (ja) 難燃性スチレン系樹脂組成物
CN101184806B (zh) 阻燃橡胶改性苯乙烯树脂组合物
WO1998012258A1 (fr) Composition de resine styrenique ignifuge
JPH05287119A (ja) 外観の優れた難燃性樹脂組成物
KR101411825B1 (ko) 차르 형성제, 및 이를 이용한 abs 수지 조성물
KR20010009845A (ko) 난연성을 갖는 열가소성 수지 조성물
EP2215159A1 (fr) Composition de résine ignifuge sans halogène
JP4860804B2 (ja) 難燃性スチレン系樹脂組成物
JP3647189B2 (ja) 樹脂組成物
JP2000129071A (ja) 難燃性スチレン系樹脂組成物
CN112795159B (zh) 一种pc/abs合金组合物及其制备方法和应用
JP3437657B2 (ja) 難燃性スチレン系樹脂組成物
JPH05255598A (ja) 難燃耐衝撃性樹脂組成物
JP3563630B2 (ja) 難燃性スチレン系樹脂組成物
JPH111622A (ja) 難燃性樹脂組成物

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): CN KR US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
122 Ep: pct application non-entry in european phase