WO1997008253A1 - Fermeture pour recipient, recouverte de peinture en poudre - Google Patents

Fermeture pour recipient, recouverte de peinture en poudre Download PDF

Info

Publication number
WO1997008253A1
WO1997008253A1 PCT/EP1996/003770 EP9603770W WO9708253A1 WO 1997008253 A1 WO1997008253 A1 WO 1997008253A1 EP 9603770 W EP9603770 W EP 9603770W WO 9708253 A1 WO9708253 A1 WO 9708253A1
Authority
WO
WIPO (PCT)
Prior art keywords
powder coating
particle size
container closure
particles
closure according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP1996/003770
Other languages
German (de)
English (en)
Inventor
Peter Nüssen
Leonidas Kiriazis
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BASF Farben und Fasern AG
PPG Industries Inc
Original Assignee
BASF Lacke und Farben AG
PPG Industries Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BASF Lacke und Farben AG, PPG Industries Inc filed Critical BASF Lacke und Farben AG
Priority to JP9509852A priority Critical patent/JPH11511491A/ja
Priority to EP96930109A priority patent/EP0847425A1/fr
Publication of WO1997008253A1 publication Critical patent/WO1997008253A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un système de fermeture pour récipient, composé de préférence de métal ou de plastique peint et d'un élément d'étanchéité, la peinture étant une peinture en poudre à base de résines époxy et de polyesters contenant des groupes carboxyle ou des durcisseurs phénoliques, et/ou à base de polyoléfine, et/ou à base de copolymères et d'ionomères comportant des groupes carboxyle ou anhydride ou des groupes transformables par hydrolyse en groupes carboxyle.
PCT/EP1996/003770 1995-08-28 1996-08-27 Fermeture pour recipient, recouverte de peinture en poudre Ceased WO1997008253A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP9509852A JPH11511491A (ja) 1995-08-28 1996-08-27 粉末コーティングでコートされた容器封止
EP96930109A EP0847425A1 (fr) 1995-08-28 1996-08-27 Fermeture pour recipient, recouverte de peinture en poudre

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE1995131559 DE19531559A1 (de) 1995-08-28 1995-08-28 Pulverlackbeschichteter Behälterverschluß
DE19531559.6 1995-08-28

Publications (1)

Publication Number Publication Date
WO1997008253A1 true WO1997008253A1 (fr) 1997-03-06

Family

ID=7770551

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP1996/003770 Ceased WO1997008253A1 (fr) 1995-08-28 1996-08-27 Fermeture pour recipient, recouverte de peinture en poudre

Country Status (4)

Country Link
EP (1) EP0847425A1 (fr)
JP (1) JPH11511491A (fr)
DE (1) DE19531559A1 (fr)
WO (1) WO1997008253A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS58215464A (ja) * 1982-06-08 1983-12-14 Kirin Brewery Co Ltd 王冠栓
EP0131257A2 (fr) * 1983-07-09 1985-01-16 Hoechst Aktiengesellschaft Procédé pour revêtir des substrats métalliques
DE3727626A1 (de) * 1987-08-19 1989-03-02 Hoechst Ag Verwendung von kunststoffen mit polaren molekuelgruppen zur isolationsbeschichtung von injektionsstopfen und infusionsstopfen sowie beschichtete injektions- und infusionsstopfen
DE4038681A1 (de) * 1990-12-05 1992-06-11 Basf Lacke & Farben Pulverlack und dessen verwendung zur innenbeschichtung von verpackungsbehaeltern und zur schweissnahtabdeckung
WO1993016141A1 (fr) * 1992-02-13 1993-08-19 Basf Lacke + Farben Aktiengesellschaft Vernis en poudre et son utilisation pour l'enduction interieure de recipients d'emballage

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS58215464A (ja) * 1982-06-08 1983-12-14 Kirin Brewery Co Ltd 王冠栓
EP0131257A2 (fr) * 1983-07-09 1985-01-16 Hoechst Aktiengesellschaft Procédé pour revêtir des substrats métalliques
DE3727626A1 (de) * 1987-08-19 1989-03-02 Hoechst Ag Verwendung von kunststoffen mit polaren molekuelgruppen zur isolationsbeschichtung von injektionsstopfen und infusionsstopfen sowie beschichtete injektions- und infusionsstopfen
DE4038681A1 (de) * 1990-12-05 1992-06-11 Basf Lacke & Farben Pulverlack und dessen verwendung zur innenbeschichtung von verpackungsbehaeltern und zur schweissnahtabdeckung
WO1993016141A1 (fr) * 1992-02-13 1993-08-19 Basf Lacke + Farben Aktiengesellschaft Vernis en poudre et son utilisation pour l'enduction interieure de recipients d'emballage

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
DATABASE WPI Derwent World Patents Index; AN 84-026067, XP002023644 *

Also Published As

Publication number Publication date
EP0847425A1 (fr) 1998-06-17
JPH11511491A (ja) 1999-10-05
DE19531559A1 (de) 1997-03-06

Similar Documents

Publication Publication Date Title
DE3879760T2 (de) Gegen Abblätterung wiederstandsfähige Überzugsmittel.
DE3117302C2 (fr)
DE69712076T2 (de) Pulver beschichtungszusammensetzungen und beschichtete oberfläche mit multischicht-auflage
EP0036975B1 (fr) Procédé de fabrication de vernissages à effet métallique et objets plans présentant des vernissages multi-couches à effet métallique résistant aux intempéries
EP0858471B1 (fr) Dispersions aqueuses de peinture en poudre
DE69832196T2 (de) Wärmehärtende pulverzusammensetzungen zur herstellung von überzügen mit schwachem glanz
DE69225058T2 (de) Pulverförmige wärmehärtbare Zusammensetzungen für die Herstellung von matten Überzugsmitteln
DE69307869T2 (de) Wärmehärtende pulverlackzusammensetzungen, die fliessmodifizierer enthalten
DE2455443B2 (de) Verfahren zur Herstellung einer Polyolefinüberzugsschicht auf einer Metalloberfläche
EP0270831A2 (fr) Masse fondue polymérisable exempte de solvant, pauvre ou exempte de monomère, son procédé de préparation et de traitement
DE19535824A1 (de) Vorvernetzte Siliconelastomer-Partikel mit Organopolymerhülle als Formulierungsbestandteil in Pulverlacken
WO1988001287A1 (fr) Agent de revetement aqueux, son procede de fabrication et son utilisation pour revetir des boites de conserve
EP0509393B1 (fr) Revêtement à poudre
EP0100992A2 (fr) Procédé de revêtement de substrats métalliques et utilisation des objets ainsi obtenus
EP2389256B1 (fr) Procédé de traitement anticorrosif
DE3513914C2 (fr)
EP0792921B1 (fr) Peinture en poudre pour boítes de conditionnement
DE4038681A1 (de) Pulverlack und dessen verwendung zur innenbeschichtung von verpackungsbehaeltern und zur schweissnahtabdeckung
DE60116862T2 (de) Verfahren zur bereitung einer pulvrlackzusammensetzung, pulverlackzusammensetzung und verfahren zur bildung des beschichtungsfilms
DE4401438C2 (de) Wärmehärtbares Beschichtungssystem, dessen Herstellung und Verwendung
EP0315010B1 (fr) Résine de revêtement et son application comme poudre de revêtement
EP0847425A1 (fr) Fermeture pour recipient, recouverte de peinture en poudre
DE19523084A1 (de) Wäßrige Pulverlack-Dispersion für Verpackungsbehälter
EP1261670B1 (fr) Matieres de revetement thermodurcissables
DE3832142C2 (fr)

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): JP US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
ENP Entry into the national phase

Ref country code: JP

Ref document number: 1997 509852

Kind code of ref document: A

Format of ref document f/p: F

WWE Wipo information: entry into national phase

Ref document number: 1996930109

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 1996930109

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 1996930109

Country of ref document: EP