WO1991017734A1 - Methode de fabrication d'articles absorbants - Google Patents

Methode de fabrication d'articles absorbants Download PDF

Info

Publication number
WO1991017734A1
WO1991017734A1 PCT/GB1991/000736 GB9100736W WO9117734A1 WO 1991017734 A1 WO1991017734 A1 WO 1991017734A1 GB 9100736 W GB9100736 W GB 9100736W WO 9117734 A1 WO9117734 A1 WO 9117734A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
fibres
fibrous
pad
bonding agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/GB1991/000736
Other languages
English (en)
Inventor
Arthur Roger Shipley
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BREGER GIBSON Ltd
Original Assignee
BREGER GIBSON Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BREGER GIBSON Ltd filed Critical BREGER GIBSON Ltd
Publication of WO1991017734A1 publication Critical patent/WO1991017734A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention se rapporte à une méthode permettant de former des serviettes hygiéniques absorbantes, par exemple des couches, laquelle méthode comprend la formation d'une couche de matériau fibreux, la liaison d'au moins quelques-unes des fibres dans ladite couche grâce à la fusion d'un agent de liaison particulaire thermoplastique mélangé avec lesdites fibres, l'agent de liaison étant fabriqué, au moins en partie, à partir d'un matériau qui se dissout dans ou est désintégré par un alcali. La couche comprend de préférence un matériau superabsorbant de façon à en améliorer les propriétés d'absorption de fluide.
PCT/GB1991/000736 1990-05-11 1991-05-09 Methode de fabrication d'articles absorbants Ceased WO1991017734A1 (fr)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
GB909010672A GB9010672D0 (en) 1990-05-11 1990-05-11 Method of forming absorbent articles
GB9010672.5 1990-05-11
GB9100771.6 1991-01-14

Publications (1)

Publication Number Publication Date
WO1991017734A1 true WO1991017734A1 (fr) 1991-11-28

Family

ID=10675883

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB1991/000736 Ceased WO1991017734A1 (fr) 1990-05-11 1991-05-09 Methode de fabrication d'articles absorbants

Country Status (2)

Country Link
GB (2) GB9010672D0 (fr)
WO (1) WO1991017734A1 (fr)

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2003339761A (ja) * 2001-06-08 2003-12-02 Uni Charm Corp 吸収性物品およびその製造方法
US6802932B2 (en) * 2001-06-08 2004-10-12 Uni-Charm Corporation Absorbent article and method of manufacturing the same

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR1572721A (fr) * 1967-06-22 1969-06-27
US3707430A (en) * 1970-06-12 1972-12-26 Celanese Corp Selectively dispersible sanitary structures
EP0067377A2 (fr) * 1981-06-11 1982-12-22 Kimberly-Clark Corporation Serviette hygiénique précontrainte dans le sens latéral
EP0301772A2 (fr) * 1987-07-27 1989-02-01 Bonar Carelle Limited Matériaux non tissés

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR830002836B1 (ko) * 1979-10-22 1983-12-27 킴버리-크라아크 코오포레이션 분비물 흡수체
GR79970B (fr) * 1983-08-15 1984-10-31 Personal Products Co
US4604313A (en) * 1984-04-23 1986-08-05 Kimberly-Clark Corporation Selective layering of superabsorbents in meltblown substrates
US4650479A (en) * 1984-09-04 1987-03-17 Minnesota Mining And Manufacturing Company Sorbent sheet product
GB8512206D0 (en) * 1985-05-14 1985-06-19 Kimberly Clark Ltd Non-woven material
US4758466A (en) * 1987-05-05 1988-07-19 Personal Products Company Foam-fiber composite and process
FR2617020B1 (fr) * 1987-06-26 1993-09-24 Boussac Saint Freres Bsf Matelas absorbant perfectionne, notamment pour des produits d'hygiene, et procede de fabrication en continu de tels matelas

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR1572721A (fr) * 1967-06-22 1969-06-27
US3707430A (en) * 1970-06-12 1972-12-26 Celanese Corp Selectively dispersible sanitary structures
EP0067377A2 (fr) * 1981-06-11 1982-12-22 Kimberly-Clark Corporation Serviette hygiénique précontrainte dans le sens latéral
EP0301772A2 (fr) * 1987-07-27 1989-02-01 Bonar Carelle Limited Matériaux non tissés

Also Published As

Publication number Publication date
GB2243785A (en) 1991-11-13
GB9010672D0 (en) 1990-07-04
GB9100771D0 (en) 1991-02-27

Similar Documents

Publication Publication Date Title
RU2236259C2 (ru) Абсорбирующее изделие и способ его изготовления
US4235237A (en) Absorbent open network structure
AU2018200300B2 (en) Absorbent Structure
US4057669A (en) Method of manufacturing a dry-formed, adhesively bonded, nonwoven fibrous sheet and the sheet formed thereby
US4102340A (en) Disposable article with particulate hydrophilic polymer in an absorbent bed
EP3085346B1 (fr) Support non tissé pour article absorbant
JP4701180B2 (ja) 吸収性構造体の製造方法
US4392861A (en) Two-ply fibrous facing material
US3707430A (en) Selectively dispersible sanitary structures
EP0943025A1 (fr) Couche unitaire absorbante formee par aspiration
JPH0724006A (ja) 吸収性物品
JPH08246395A (ja) 吸収性シート及びその製造方法
US5961763A (en) Sealable nonwoven web
TW200305448A (en) Superabsorbent composite and absorbent articles including the same
JPH05192365A (ja) 強化ウェブを備えた吸収性パッド
US6797360B2 (en) Nonwoven composite with high pre-and post-wetting permeability
US6569274B1 (en) Sealable nonwoven web
CA1273189A (fr) Article absorptif extrude
Gross The evolution of absorbent materials
WO1991017734A1 (fr) Methode de fabrication d'articles absorbants
CA2355746A1 (fr) Article absorbant et son procede de production
EP1835944A1 (fr) Materiau composite absorbant avec agents de liaison hydrosolubles, produits obtenus a partir dudit materiau et procede de fabrication
JP6192364B2 (ja) 吸収性物品
JP2682576B2 (ja) 吸収材
JPH08291455A (ja) 吸収性部材の製造方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AT AU BB BG BR CA CH DE DK ES FI GB HU JP KP KR LK LU MC MG MW NL NO PL RO SD SE SU US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE BF BJ CF CG CH CI CM DE DK ES FR GA GB GR IT LU ML MR NL SE SN TD TG

NENP Non-entry into the national phase

Ref country code: CA

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642