US20120240725A1

US20120240725A1 - Carbon composite agglomerate for producing reduced iron and method for producing reduced iron using the same

Info

Publication number: US20120240725A1
Application number: US13/386,158
Authority: US
Inventors: Takeshi Sugiyama; Shohei Yoshida; Kyoichiro Fujita; Ryota Misawa
Original assignee: Kobe Steel Ltd
Current assignee: Kobe Steel Ltd
Priority date: 2009-07-21
Filing date: 2010-07-21
Publication date: 2012-09-27
Also published as: EP2458020B1; RU2012106122A; CA2766256A1; AU2010274314A1; KR101313367B1; KR20120031080A; WO2011010667A1; EP2458020A1; CN102471812A; JP2011042869A; AU2010274314B2; JP5466590B2; CN102471812B; CA2766256C; EP2458020A4

Abstract

Provided is a carbon composite briquette which is used as the raw material of a movable hearth furnace for producing reduced iron having a sufficient carbon content and a higher crushing strength, and also provided is a method for producing reduced iron using the carbon composite briquette. The carbon composite briquette for producing reduced iron has a total SiO₂+Al₂O₃+CaO+MgO content that is between 7 and 15 mass %; an MgO content that is between 0.1 and 6 mass %; an Al₂O₃/SiO₂mass ratio that is between 0.34 and 0.52; a CaO/SiO₂mass ratio that is between 0.25 and 2.0; and a C content such that between 1 and 9 mass % of C is retained in the resulting reduced iron.

Description

TECHNICAL FIELD

The present invention relates to a carbon composite agglomerate used as a material for a moving hearth furnace for producing reduced iron, and a method for producing reduced iron using such a carbon composite agglomerate.

BACKGROUND ART

Various techniques for producing reduced iron by reducing carbon composite agglomerates through heating with a rotary hearth furnace have been proposed (for example, refer to Patent Literatures 1 to 3).
Such reduced iron produced is used as an iron material for a blast furnace, a converter, an electric furnace, or the like. The reduced iron is demanded to have a C content as high as possible for improving the energy efficiency of such a furnace and a strength as high as possible for not producing powder. As an indicator for evaluating the strength of reduced iron usable for such furnaces, crushing strength is generally used. In the case of a material for a blast furnace, as a desirable crushing strength for bearing handling from discharging from a rotary hearth furnace to charging into a blast furnace and the load pressure of charged materials in the blast furnace, 180 kgf/briquette (about 1760 N/briquette) or more is demanded. In the case of a material for a converter or an electric furnace, since it is not necessary to consider load pressure in such a furnace, a crushing strength smaller than that in the case of a raw material for a blast furnace will suffice. However, in view of using reduced iron in general-purpose applications, the establishment of a technique that achieves a C content as high as possible and a crushing strength of 180 kgf/briquette (about 1760 N/briquette) or more has been demanded.

CITATION LIST

Patent Literature

PTL 1: Japanese Unexamined Patent Application Publication No. 2004-269978
PTL 2: Japanese Unexamined Patent Application Publication No. 2009-35820
PTL 3: Japanese Unexamined Patent Application Publication No. 2009-52138

SUMMARY OF INVENTION

Technical Problem

Accordingly, an object of the present invention is to provide a carbon composite agglomerate used as a material for a moving hearth furnace for producing reduced iron, the carbon composite agglomerate providing reduced iron having a sufficiently high carbon content and an increased crushing strength; and a method for producing reduced iron using such a carbon composite agglomerate.

Solution to Problem

An invention according to Claim 1 is a carbon composite agglomerate for producing reduced iron, the carbon composite agglomerate being used as a material for a moving hearth furnace for producing reduced iron, wherein, in the carbon composite agglomerate, a total content of SiO₂, Al₂O₃, CaO, and MgO is 7 to 15 mass %, a MgO content is 0.1 to 6 mass %, a mass ratio of Al₂O₃/SiO₂is 0.34 to 0.52, a mass ratio of CaO/SiO₂is 0.25 to 2.0, and a C content is such that 1 to 9 mass % of C remains in reduced iron produced from the carbon composite agglomerate.
An invention according to Claim 2 is the carbon composite agglomerate for producing reduced iron according to Claim 1, having a porosity of 37.5% or less.
An invention according to Claim 3 is the carbon composite agglomerate for producing reduced iron according to Claim 1 or 2, wherein an average grain size d50 of a carbonaceous material in the carbon composite agglomerate measured by a laser diffraction scattering grain size distribution measurement method is 30 μm or less.
An invention according to Claim 4 is the carbon composite agglomerate for producing reduced iron according to any one of Claims 1 to 3, at least containing ironmaking dust.
An invention according to Claim 5 is a method for producing reduced iron by reducing the carbon composite agglomerate for producing reduced iron according to any one of Claims 1 to 4, through heating with a moving hearth furnace, wherein the moving hearth furnace is divided into a plurality of zones in a moving direction of a hearth and a final zone of the plurality of zones has an oxidizing atmosphere.
An invention according to Claim 6 is the method for producing reduced iron according to Claim 5, wherein the oxidizing atmosphere of the final zone has a gas oxidation degree OD of 1.0 or more, and
OD=(CO₂+H₂O+2O₂)/(CO₂+H₂O+O₂+CO+H₂)
[where a unit of CO₂, H₂O, O₂, CO, and H₂is vol %].

Advantageous Effects of Invention

According to the present invention, by making the slag component composition of a carbon composite agglomerate and the amount of C remaining in a reduced iron product obtained by reducing the carbon composite agglomerate be in specific ranges, reduced iron having a sufficiently high carbon content and an increased crushing strength can be produced.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a graph illustrating the influence of the slag component composition of carbon composite briquettes on the crushing strength of reduced iron.

FIG. 2 illustrates a FeO—Ca—O—Al₂O₃—SiO₂phase diagram for explaining the relationship between the slag component of carbon composite briquettes and the liquidus temperature.

FIG. 3 illustrates a MgO—Ca—O—Al₂O₃—SiO₂phase diagram for explaining the relationship between the slag component of carbon composite briquettes and the liquidus temperature.

FIG. 4( a) is a sectional view illustrating the internal structure of a carbon composite briquette reduced in a reducing atmosphere and FIG. 4( b) is a sectional view illustrating the internal structure of a carbon composite briquette reduced in an oxidizing atmosphere.

FIG. 5 is a graph illustrating the relationship between the C content of reduced iron and the crushing strength of reduced iron.

FIG. 6 is a graph illustrating the relationship between the porosity of carbon composite briquettes and the crushing strength of reduced iron.

FIG. 7 is a graph illustrating the grain size distribution of blast-furnace wet dust.

FIG. 8 illustrates blast-furnace wet dust observed with an electron microscope.

DESCRIPTION OF EMBODIMENTS

Hereinafter, the present invention will be described further in detail.

Embodiment 1

A feature of the present invention is to make the slag component composition and carbon content of carbon composite briquettes be in specific ranges. As a result, a reduced iron product that is more suitable as an iron material for a blast furnace, an electric furnace, a converter, or the like, has a sufficiently high carbon content, and has an increased crushing strength can be obtained.
Specifically, the following carbon composite briquettes are preferably used. In the carbon composite briquettes, the total content of SiO₂, Al₂O₃, CaO, and MgO is 7 to 15 mass %; the MgO content is 0.1 to 6 mass %; the mass ratio of Al₂O₃/SiO₂is 0.34 to 0.52; and the mass ratio of CaO/SiO₂is 0.25 to 2.0 (more preferably 0.25 to 1.5, particularly preferably 0.25 to 1.0). In addition, the C content of the carbon composite briquettes is adjusted such that 1 to 9 mass % of C remains in a reduced iron product obtained by reducing the carbon composite briquettes.
Hereinafter, reasons for the numerical limitations on such parameters will be described.

The total content of SiO₂, Al₂O₃, CaO, and MgO in carbon composite briquettes substantially equals to the slag component content of the carbon composite briquettes. When the slag component content of carbon composite briquettes is excessively low, the effect of promoting sintering of metallic iron by melting of the slag component is not provided. When the slag component content of carbon composite briquettes is excessively high, reduced iron obtained by reducing the carbon composite briquettes has an excessively high slag content, which inhibits the sintering reaction of metallic iron to decrease the strength of the reduced iron. In addition, the reduced iron has a low iron grade. The total content of SiO₂, Al₂O₃, CaO, and MgO in carbon composite briquettes is preferably in the range of 7 to 15 mass %.
Note that all the carbon composite briquettes used in heating reduction tests described below had a total content of SiO₂, Al₂O₃, CaO, and MgO in the range of 7 to 15 mass %.

When the MgO content increases, the melting point of slag increases and the amount of slag melted decreases and hence the strength-development action for reduced iron described below is not sufficiently exhibited. Accordingly, the upper limit of the MgO content is defined as 6 mass %. On the other hand, since ironmaking dust unavoidably contains the MgO component, the lower limit of the MgO content is defined as 0.1 mass %.
Note that all the carbon composite briquettes used in the heating reduction tests described below had a MgO content in the range of 0.1 to 6 mass %.

The inventors of the present invention first investigated the influence of the slag component composition on the crushing strength of a reduced iron product by performing the following heating reduction tests.

(Heating Reduction Tests of Carbon Composite Agglomerates)

Blend materials having various slag component compositions were prepared by adjusting blending proportions of iron ore and an ironmaking dust mixture obtained by mixing ironmaking dusts including blast-furnace dust. The blend materials were formed into carbon composite briquettes having the shape of a pillow and a volume of 6 to 7 cm³with a twin-roll briquetting machine. The briquettes were dried with a dryer so as to have a water content of 1 mass % or less. Examples of the chemical composition of the dried briquettes (hereafter, referred to as “dry briquettes”) are shown in Table 1. In the table, “T. C” represents the total carbon content; “T. Fe” represents the total iron content; “M. Fe” represents a metallic-iron content; “T. Fe” includes Fe₂O₃, FeO, and “M. Fe”; Na, K, and Pb are not present in the form of atoms, but are present in the form of oxides and the like.

TABLE 1

(Unit: mass %)

	T. C	T. Fe	Fe₂O₃	FeO	M. Fe	ZnO	Na	K	Pb

Dry briquettes A	13.77	48.84	24.41	40.48	1.97	2.62	0.54	0.13	0.16
Dry briquettes B	15.68	43.51	59.95	1.81	0.17	2.62	0.044	0.065	0.01

About 44 g of the dry briquettes were placed on an alumina tray, inserted into a horizontal heating furnace heated at 1300° C. and having an atmosphere in which one of the two gases of N₂(100% by volume) and CO₂/N₂(30%/70% by volume) was passed at a flow rate of 3 NL/min, held until the dry briquettes were reduced, subsequently cooled to room temperature in N₂gas atmosphere, and taken out from the furnace. The reduced briquettes were subjected to the measurement of crushing strength. Since a predetermined amount of CO-containing gas is generated from briquettes during the reduction, the heating reduction test in which N₂(100%) gas was passed to provide a reducing gas atmosphere around the briquettes simulates reduction conditions in a reducing atmosphere in an actual rotary hearth furnace; and the reduction test in which the CO₂-containing gas was passed to provide an oxidizing gas atmosphere around the briquettes simulates reduction conditions in the presence of combustion exhaust gas in an actual rotary hearth furnace.

(Results of Heating Reduction Tests)

The measurement results are illustrated in FIG. 1. As illustrated in FIG. 1, the inventors have found that, by making the mass ratio of Al₂O₃/SiO₂be in the range of 0.34 to 0.52 and the mass ratio of CaO/SiO₂be in the range of 0.25 to 1.0, the crushing strength of reduced iron is further increased to 180 kgf/briquette (about 1760 N/briquette) or more.
The reason for which the crushing strength of reduced iron is thus increased by making the mass ratios of the slag component of carbon composite briquettes, that is, CaO/SiO₂and Al₂O₃/SiO₂be in the specific ranges is probably as follows.
As illustrated in FIG. 2, when the specific ranges are plotted in the FeO (constant: 30 mass %)-CaO—Al₂O₃—SiO₂phase diagram, the specific ranges are found to correspond to a region in which the liquidus temperature is a relatively low temperature of about 1200° C. to 1300° C. Accordingly, the slag component (CaO, Al₂O₃, and SiO₂) reacts with wustite (FeO) that is generated during reduction from iron oxide to metallic iron or generated by reoxidation of metallic iron in an oxidizing atmosphere, to thereby have lower melting points; a portion of the reaction products melts to provide a solid-liquid coexistent state; and sintering of metallic iron is promoted.
As is clear from FIG. 2, the specific ranges correspond to a region that does not include the eutectic point P, which is a minimum melting point, and is located slightly away from the eutectic point P toward a high-temperature side. The reason for this is probably as follows. When the slag component of carbon composite briquettes is made to have a composition close to the eutectic point P in FIG. 2, the slag component reacts with wustite (FeO) and the entire amount of the slag component rapidly melts. Such rapid melting of the entire amount of the slag component results in the formation of a large number of cavities in the briquettes, which inhibits promotion of sintering of metallic iron. Thus, high strength is not achieved. In contrast, by making the slag component of carbon composite briquettes be in the specific ranges in FIG. 2, a solid-liquid coexistent state in which not the entire amount of but a portion of the slag component melts is achieved; as a result, the formation of cavities due to melting of slag is suppressed and sintering of metallic iron can be promoted. In summary, the strength development of reduced iron is achieved not by a slag phase but by the sinter structure of metallic iron.
As illustrated in FIG. 3, when the specific ranges are plotted in the MgO (constant: 5 mass %)-Ca—O—Al₂O₃—SiO₂phase diagram, the specific ranges are found to correspond to a region in which the liquidus temperature is about 1300° C. to 1400° C. This liquidus temperature is about 100° C. higher than that in the case in FIG. 2 where FeO is present. This shows that the presence of wustite (FeO) is desirable to facilitate melting of the slag component.
From the test results, CaO/SiO₂of carbon composite briquettes is particularly preferably in the range of 0.25 to 1.0. However, even when an excessive amount of CaO is present in the carbon composite briquettes, a portion of CaO melts and CaO/SiO₂of molten slag can satisfy the range of 0.25 to 1.0. Thus, sintering of metallic iron is promoted by the same action as that described above and the strength of reduced iron is developed. Accordingly, the preferred range of CaO/SiO₂is defined as the range of 0.25 to 2.0 (more preferably 0.25 to 1.5).
The composition of the slag component of carbon composite briquettes can be adjusted by, for example, adjusting blending proportions of a plurality of ironmaking dusts having different slag component compositions and iron ore, or adjusting the amount of CaO source added such as limestone or burnt lime.

When the amount of C remaining in a reduced iron product obtained by reducing carbon composite briquettes is excessively small, in the case of using the reduced iron product as an iron material for a blast furnace, a converter, an electric furnace, or the like, the action of remaining carbon serving as a reductant for reducing unreduced iron oxide (FeO and the like) remaining in the reduced iron product is insufficient. In addition, the effect of increasing the melting speed of metallic iron due to carburization of metallic iron is not provided. On the other hand, when the amount of C remaining in a reduced iron product is excessively large, a large amount of carbon grains remaining in the reduced iron inhibit bonding between metallic iron grains and hence the strength of the reduced iron becomes insufficient. The amount of C remaining in a reduced iron product obtained by reducing carbon composite briquettes is preferably in the range of 1 to 9 mass %.
Note that the C contents of all the reduced iron products obtained by reducing the carbon composite briquettes used in the heating reduction tests described above were in the range of 1 to 9 mass %.
The amount of C remaining in a reduced iron product can be adjusted by adjusting the amount of a carbonaceous material (carbon content) of carbon composite briquettes: for example, in the production of carbon composite briquettes, by adjusting the blending proportion of blast-furnace dust having a high carbon content or adjusting the amount of a carbonaceous material added such as coal or coke powder.
The carbon content Xc of carbon composite briquettes should be specifically set with the following formula (1).
Xc=XcT+XcR (1)
where XcT=(12/16)·Xo; XcT represents a theoretical C amount necessary for completely reducing iron oxide and zinc oxide in the carbon composite briquettes to the metals; XcR represents the amount of C remaining in reduced iron when the iron oxide and zinc oxide have been completely reduced to the metals with the theoretical C amount XcT; and Xo represents the total amount of oxygen of iron oxide and oxygen of zinc oxide in the carbon composite briquettes.
In the formula (1), in addition to reduction of iron oxide, reduction of zinc oxide is considered. This is because, when ironmaking dust is used as a material, the ironmaking dust contains a relatively large amount of zinc oxide and reduction of the zinc oxide requires a relatively large amount of C. Compared with iron oxide and zinc oxide, the contents of oxides of other nonferrous metals such as lead and alkali metals are low and hence these oxides are not considered.
The theoretical C amount is defined on the premise that reduction of 1 mole of oxygen of iron oxide or zinc oxide requires 1 mole of carbon. However, in actual reduction of carbon composite briquettes with a moving hearth furnace, CO gas is generated by reduction (direct reduction) of iron oxide or zinc oxide with carbon and the CO gas causes reduction (gas reduction) of iron oxide or zinc oxide to proceed; accordingly, the amount of carbon required for reduction of 1 mole of oxygen of iron oxide or zinc oxide is less than 1 mole. On the other hand, since carbon composite briquettes are heated by combustion with burners in a moving hearth furnace, the combustion gas consumes a portion of a carbonaceous material (carbon) in the carbon composite briquettes and the portion is not used for reduction of iron oxide or zinc oxide. As a result, the decrease in the C consumption due to the gas reduction substantially cancels out the increase in the C consumption due to burner combustion gas. Accordingly, the theoretical C amount can be regarded as a C amount actually required for reduction.
As described above, the presence of wustite (FeO) in carbon composite briquettes is desirable for facilitating melting of the slag component. Accordingly, in the production of reduced iron by reducing the carbon composite briquettes through heating with a moving hearth furnace such as a rotary hearth furnace, the rotary hearth furnace is preferably divided into a plurality of zones in the moving direction of the hearth and the final zone of the plurality of zones preferably has an oxidizing atmosphere. By making the final zone have an oxidizing atmosphere, as illustrated in FIG. 4( b), metallic iron in the near-surface regions of reduced iron obtained by reducing carbon composite briquettes is reoxidized to form wustite (FeO). As a result, melting of the slag component is facilitated and sintering of metallic iron is further promoted.
FIG. 4 shows comparison in terms of internal structure between the reduced iron obtained by reducing a carbon composite briquette in the reducing atmosphere (FIG. 4( a)) and the reduced iron obtained by reducing a carbon composite briquette in the oxidizing atmosphere (FIG. 4( b)) in the heating reduction tests. Bonding between metallic iron grains proceeds in both of the atmospheres; however, in the reduced iron obtained by reduction in the oxidizing atmosphere (FIG. 4( b)), molten wustite grains (gray) are present in the near-surface region of the briquette and the thickness of bonded metallic iron (white) becomes large. This shows that sintering of metallic iron has proceeded in the reduced iron obtained by reduction in the oxidizing atmosphere (FIG. 4( b)), compared with the reduced iron obtained by reduction in the reducing atmosphere (FIG. 4( a)). The reduced iron in FIG. 4( a) had a crushing strength of about 300 kgf/briquette (about 2940 N/briquette), whereas the reduced iron in FIG. 4( b) had a crushing strength of more than 600 kgf/briquette (about 5880 N/briquette).
Specifically, the final zone is preferably made to have an oxidizing atmosphere having a gas oxidation degree OD of 1.0 or more.
OD=(CO₂+H₂O+2O₂)/(CO₂+H₂O+O₂+CO+H₂)
[where the unit of CO₂, H₂O, O₂, CO, and H₂is vol %].
Herein, the gas oxidation degree OD is defined as follows: OD=(CO₂+H₂O+2O₂)/(CO₂+H₂O+O₂+CO H₂) [where the unit of CO₂, H₂O, O₂, CO, and H₂is vol %] because, when the atmosphere contains the O₂component, the O₂component has an oxidizing capability for metal elements that is twice that of the CO₂component and the H₂O component (for example, reaction formulae Fe+CO₂═FeO+CO, Fe+H₂O═FeO+H₂, and 2Fe+O₂═2FeO show that 1 mole of CO₂or H₂O can oxidize 1 mole of Fe, whereas 1 mole of O₂can oxidize 2 moles of Fe).
The gas oxidation degree of the atmosphere of the final zone can be adjusted by changing, for example, the air-fuel ratio of a burner.

Embodiment 2

The Embodiment 1 above describes an example in which the physical internal structure of the carbon composite briquettes is not particularly limited. As for the physical internal structure of carbon composite briquettes, in particular, by making the porosity of carbon composite briquettes be in a specific range, even when the amount of carbon remaining in a reduced iron product obtained by reducing the carbon composite briquettes is large, a sufficiently high crushing strength can be achieved with certainty.
Specifically, carbon composite briquettes having a porosity of 37.5% or less are preferably used.
Hereinafter, the reason for which the porosity of carbon composite briquettes is limited to 37.5% or less will be described.
The inventors of the present invention investigated the influence of various parameters on the crushing strength of reduced iron obtained by preparing carbon composite briquettes from ironmaking dust and reducing the carbon composite briquettes under the same test conditions as in Embodiment 2.
FIG. 5 illustrates the relationship between the C content of reduced iron and the crushing strength of reduced iron. As illustrated in FIG. 5, it has been found that reduced irons having a crushing strength of 180 kgf/briquette (about 1760 N/briquette) or more, which are more suitable as iron materials for a blast furnace and the like, are a reduced iron [region A] having a low C content (C: 1 mass % or more and less than 4 mass %) and a reduced iron [region B] having a high C content (C: 4 mass % or more). Herein, the reduced iron in the region A is an extension of common general technical knowledge (line L in the figure) in which the higher the C content of reduced iron, the lower the crushing strength of the reduced iron becomes. In contrast, the reduced iron in the region B is irrelevant to the common general technical knowledge and a high crushing strength is achieved in spite of a high C content.
The inventors studied the reason why a high crushing strength is achieved in spite of a high C content and, as a result, have found that the porosity of carbon composite briquettes to be reduced influences the crushing strength.
FIG. 6 illustrates the relationship between the porosity of carbon composite briquettes and the crushing strength of reduced iron. As illustrated in FIG. 6, there is a very strong correlation between the porosity of carbon composite briquettes and the crushing strength of reduced iron regardless of the C content of reduced iron.
Accordingly, as illustrated in FIG. 6, by controlling the porosity of carbon composite briquettes to be 37.5% or less, reduced iron having a high crushing strength of 180 kgf/briquette (about 1760 N/briquette) or more can be produced with certainty regardless of the C content.
By making the porosity of carbon composite briquettes be the predetermined value or less, the distance between iron oxide grains in the carbon composite briquettes becomes short and bonding of metallic iron grains (sintering of metallic iron) after reduction is promoted, which probably results in a further increase in the strength of reduced iron.
When the porosity of carbon composite briquettes is made excessively low, bursting tends to occur during reduction. Accordingly, the lower limit of the porosity is preferably 25%.
The porosity of carbon composite briquettes is calculated from the apparent density and true density of carbon composite briquettes:
Porosity(%)=(1−[apparent density]/[true density])×100
where the apparent density of carbon composite briquettes represents the measurement value of the apparent density of dry briquettes; and the true density of carbon composite briquettes represents a weighted average value of true densities of individual materials forming carbon composite briquettes in terms of blending proportions.
In the case of using ironmaking dust as a material, since ironmaking dust has a very small grain size, it may be difficult to compact ironmaking dust. Depending on the type or blending proportion of ironmaking dust used, there are cases where it is difficult to make the porosity of carbon composite briquettes be 37.5% or less by standard forming techniques. In such cases, for example, the following technique may be employed (refer to Japanese Unexamined Patent Application Publication No. 2009-7667): under size after compaction with a briquetting machine is mixed as a recycled material with a new material and returned to the briquetting machine to compact the material to thereby increase the apparent density (that is, decrease the porosity) of carbon composite briquettes.

Embodiment 3

The Embodiments 1 and 2 above describe examples in which the grain size of a carbonaceous material contained in the carbon composite briquettes is not particularly limited. By making the grain size of such a carbonaceous material be in a specific range, the crushing strength of a reduced iron product obtained by reducing the carbon composite briquettes is ensured and the amount of carbon remaining in the reduced iron can be further increased.
Specifically, the average grain size d50 of a carbonaceous material in carbon composite briquettes measured by a laser diffraction scattering grain size distribution measurement method is preferably made 30 μm or less (more preferably, 10 μm or less).
For example, blast-furnace wet dust containing a large amount of carbon grains derived from coke powder or pulverized coal is used as ironmaking dust and the carbon grains of the blast-furnace wet dust are used as a carbonaceous material to prepare carbon composite briquettes. As for reduced iron obtained by reducing such carbon composite briquettes, it has been found that the amount of carbon remaining in the reduced iron can be made high while the crushing strength is ensured. The grain size distribution of the blast-furnace wet dust was measured by a laser diffraction scattering grain size distribution measurement method and the grain size distribution illustrated in FIG. 7 was obtained. FIG. 8 illustrates the blast-furnace wet dust observed with a scanning electron microscope. In FIG. 8, large angular grains are identified as iron oxide; spherical grains are identified as CaO—SiO₂—FeO slag; as for carbon, which is a light element, carbon grains cannot be identified; however, grains other than the large iron oxide grains are fine grains and hence carbon grains are probably fine grains. In summary, it is clear that the grain size of carbon grains is at least equal to or less than the grain size of the entirety of the blast-furnace wet dust (the average grain size d50 is 30 μm) in FIG. 7; and, from the observation result with a scanning electron microscope in FIG. 8, the grain size of carbon grains is probably 10 μm or less in terms of average grain size d50.
Accordingly, the average grain size d50 of a carbonaceous material in carbon composite briquettes measured by a laser diffraction scattering grain size distribution measurement method is preferably 30 μm or less, more preferably 10 μm or less.
The average grain size d50 of a carbonaceous material in carbon composite briquettes may be adjusted, for example, in the following manner. When blast-furnace wet dust is used as a portion of materials, the blending proportion of the dust is adjusted. When coal powder or coke powder is added as a carbonaceous material, the pulverization grain size of such a powder is adjusted.

(Modification)

In the above-described embodiments, as an example of the agglomerate form of carbon composite agglomerates, briquettes are described. Alternatively, pellets may be employed.
In the above-described embodiments, as an example of the furnace type of a moving hearth furnace, a rotary hearth furnace is described. Alternatively, a straight hearth furnace may be employed.
While the present invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.
This application is based on Japanese Patent Application No. 2009-169719 filed on Jul. 21, 2009, the entire contents thereof being hereby incorporated by reference.

INDUSTRIAL APPLICABILITY

The present invention is advantageous as a technique of producing reduced iron from ironmaking dust in ironmaking equipment.

Claims

1: A carbon composite agglomerate comprising C, Fe, SiO₂, Al₂O₃, CaO, and MgO,

wherein:

a total content of SiO₂, Al₂O₃, CaO, and MgO is 7 to 15 mass %,

a MgO content is 0.1 to 6 mass %,

a mass ratio range of Al₂O₃/SiO₂is 0.34 to 0.52,

a mass ratio range of CaO/SiO₂is 0.25 to 2.0, and

wherein the C content is such that 1 to 9 mass % of C remains in reduced iron produced from the carbon composite agglomerate after the agglomerate has been reduced in a moving hearth furnace.

2: The agglomerate of claim 1 having a porosity of 37.5% or less.

3: The agglomerate of claim 1, wherein an average grain size d50 of a carbonaceous material in the agglomerate measured by a laser diffraction scattering grain size distribution measurement method is 30 μm or less.

4: The agglomerate of claim 1, further comprising an ironmaking dust.

5: A method for producing reduced iron by reducing the agglomerate of claim 1, the method comprising heating the agglomerate with a moving hearth furnace, wherein the moving hearth furnace is divided into a plurality of zones in a moving direction of a hearth, and a final zone of the plurality of zones has an oxidizing atmosphere, to obtain reduced iron comprising 1 to 9 mass % C.

6: The method of claim 5, wherein the oxidizing atmosphere of the final zone has a gas oxidation degree OD of 1.0 or more, wherein

OD=(CO₂+H₂O+2O₂)/(CO₂+H₂O+O₂+CO+H₂)

[where a unit of CO₂, H₂O, O₂, CO, and H₂is vol %].

7: The agglomerate of claim 1, wherein a mass ratio range of CaO/SiO₂is 0.25 to 1.5.

8: The agglomerate of claim 1, wherein a mass ratio range of CaO/SiO₂is 0.25 to 1.0.

9: The agglomerate of claim 1, wherein the C content is such that 4 to 9 mass % of C remains in reduced iron produced from the carbon composite agglomerate after the agglomerate has been reduced in a moving hearth furnace.

10: The agglomerate of claim 9 having a porosity of 37.5% or less.

11: The agglomerate of claim 1 having a porosity of 25% to 37.5%.

12: The agglomerate of claim 9 having a porosity of 25% to 37.5%.

13: The agglomerate of claim 1, wherein an average grain size d50 of a carbonaceous material in the agglomerate measured by a laser diffraction scattering grain size distribution measurement method is 10 μm or less.

14: The agglomerate of claim 1, in briquette form.

15: The agglomerate of claim 1, in pellet form.

16: The method of claim 5, wherein the moving hearth furnace is a rotary hearth furnace.

17: The method of claim 5, wherein the moving hearth furnace is a straight hearth furnace.

18: The agglomerate of claim 14, wherein a crushing strength of the reduced iron is at least 180 kgf/briquette.

19: The agglomerate of claim 14, wherein a crushing strength of the reduced iron is at least 300 kgf/briquette.

20: The agglomerate of claim 14, wherein a crushing strength of the reduced iron is at least 600 kgf/briquette.