SU836179A1 - Flux for refining tin bronz - Google Patents
Flux for refining tin bronz Download PDFInfo
- Publication number
- SU836179A1 SU836179A1 SU792819257A SU2819257A SU836179A1 SU 836179 A1 SU836179 A1 SU 836179A1 SU 792819257 A SU792819257 A SU 792819257A SU 2819257 A SU2819257 A SU 2819257A SU 836179 A1 SU836179 A1 SU 836179A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- flux
- refining
- bronz
- tin
- zinc oxide
- Prior art date
Description
(54) ФЛЮС ДЛЯ РАФИНИРОВАНИЯ ОЛОВЯННЫХ БРОНЗ(54) FLUX FOR TIN BRONZ REFINING
ции, которые выпускаютс промышленностью .industry.
Флюс испытан в лабораторных уело ВИЯХ дл рафинировани олов нных бронз. Дл этого навеску бронзы весом 3 кг расплавл ют в графитовом тигле/ перемешивают с флюсом в коли честве 1-3% от веса шихты в зависи|Мости от количества содержащихс вThe flux was tested in laboratory laboratories for the refining of tin bronzes. For this, a weight of 3 kg of bronze is melted in a graphite crucible / mixed with a flux in an amount of 1-3% by weight of the charge, depending on the amount of
расплаве примесей и ведут рафинирование при 1150-1200с в течение 35 мин.melt of impurities and refining at 1150-1200s for 35 minutes.
Применение флюса дл рафинировани снижает содержание в металле алюмини с 0/3 до , кремни с 0,2 до 0,02%, железа с 3 до 0,35%. Результаты испытаний различных составов приведены в таблице.The use of flux for refining reduces the content of aluminum in metal from 0/3 to silicon, from 0.2 to 0.02%, and iron from 3 to 0.35%. The test results of different compositions are given in the table.
Claims (2)